CN104387715A - Tpe塑料配方及制备方法 - Google Patents
Tpe塑料配方及制备方法 Download PDFInfo
- Publication number
- CN104387715A CN104387715A CN201410592053.7A CN201410592053A CN104387715A CN 104387715 A CN104387715 A CN 104387715A CN 201410592053 A CN201410592053 A CN 201410592053A CN 104387715 A CN104387715 A CN 104387715A
- Authority
- CN
- China
- Prior art keywords
- tpe
- parts
- plastic
- preparation
- formula
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种TPE塑料配方及制备方法,其包括以下重量份的成分:SEBS 20-35份、TPV 20-35份、PA6 1-10份、EMA 1-10份、白油30-50份、碳酸钙1-10份。采用本发明所制成的TPE塑料,价格便宜、成品率高、性能优良、符合客户不同要求且环保。
Description
技术领域
本发明涉及一种TPE塑料配方及制备方法。
背景技术
随着经济的迅速发展,人类对环保意识的增强和产品要求得不断提高,人们对高要求的塑料需求越来越大。而TPE(Thermoplastic Elastomer热塑性弹性体)是一种具有橡胶的高弹性、高强度、高回弹性,又具有可注塑加工的特征材料,具有无毒环保,有优良的着色性、耐候性和耐温性,加工性能优越,可以循环使用,与PP、PC、PS、ABS等基体材料包覆粘合,也可以单独成型,TPE既具有热塑性塑料的加工性能,又具有硫化橡胶的物理性能,可谓是塑料和橡胶优点的优势组合,因此正在大肆占领原本只属于硫化橡胶的领地。然而该TPE的价格还是较高,成品率较低,急需改进。
发明内容
本发明目的是:提供一种价格便宜、成品率高、性能优良、符合客户不同要求且环保的TPE塑料配方。
本发明的一技术方案是:一种TPE塑料配方,其包括以下重量份的成分:SEBS20-35份、TPV20-35份、PA61-10份、EMA1-10份、白油30-50份、碳酸钙1-10份。
所述SEBS所占比例低于白油所占比例,且与TPV的比例相同,其中PA6、EMA、碳酸钙的比例相同。
本发明的另一技术方案是:一种采用所述TPE塑料配方的制备方法,其先将SEBS、TPV放入搅拌机内,充入白油搅拌,待充分吸油后加入PA6、EMA和碳酸钙加入搅拌机搅拌均匀,再将混合料加入双螺杆挤出机挤出造粒。
其硬度为75°。
本发明优点是:
本发明所制得的TPE塑料价格便宜、成品率高、性能优良、环保、防静电。
具体实施方式
实施例:本发明提供了一种TPE塑料配方的具体实施例,其包括以下重量份的成分:SEBS20-35份、TPV20-35份、PA61-10份、EMA1-10份、白油30-50份、碳酸钙1-10份。
SEBS是以聚苯乙烯为末端段,以聚丁二烯加氢得到乙烯-丁烯共聚物为中间弹性嵌段的线性三嵌共聚物,又称苯乙烯-乙烯-丁烯-苯乙烯嵌段共聚物,不含不饱和双键,具有良好的稳定性和耐老化性,本发明使用高分子SEBS具有很好的拉力。
PA6的化学物理特性和PA66很相似,然而它的熔点较低,而且工艺温度范围很宽,它的抗冲击性和抗溶解性比PA66要好。
EMA丙烯酸甲酯含量8%-4%的乙烯共聚物,乳白色半透明固体,耐环境应力开裂性好,电性能优良。
TPV具有良好的弹性和耐压缩变形性,耐环境,耐老化性相当于三元乙丙橡胶,同时其耐油耐溶剂性能与通用型氯丁橡胶不相上下。
白油是高度精炼产品,具有无色、无味、无毒。碳酸钙的加入一是为了增加粘合性另一个是减少成本。
优选地,本发明先将30公斤SEBS、30公斤TPV放入搅拌机内,充入30公斤白油搅拌,待充分吸油后加入5公斤PA6、5公斤EMA和5公斤碳酸钙加入搅拌机搅拌均匀,再将混合料加入双螺杆挤出机挤出造粒。本配方所制作的产品经检测后与尼龙有很好的粘合性,并具有高度耐磨性,硬度在75°左右。本发明的有益效果是:价格便宜、成品率高、性能优良。
当然上述实施例只为说明本发明的技术构思及特点,其目的在于让熟悉此项技术的人能够了解本发明的内容并据以实施,并不能以此限制本发明的保护范围。凡根据本发明主要技术方案的精神实质所做的等效变换或修饰,都应涵盖在本发明的保护范围之内。
Claims (4)
1.一种TPE塑料配方,其特征在于其包括以下重量份的成分:SEBS20-35份、TPV20-35份、PA61-10份、EMA1-10份、白油30-50份、碳酸钙1-10份。
2.如权利要求1所述的一种TPE塑料配方,其特征在于:所述SEBS所占比例低于白油所占比例,且与TPV的比例相同,其中PA6、EMA、碳酸钙的比例相同。
3.一种采用如权利要求1所述TPE塑料配方的制备方法,其特征在于:先将SEBS、TPV放入搅拌机内,充入白油搅拌,待充分吸油后加入PA6、EMA和碳酸钙加入搅拌机搅拌均匀,再将混合料加入双螺杆挤出机挤出造粒。
4.根据权利要求3所述的制备方法,其特征在于:其硬度为75°。