CN104386336B - A kind of paper mould matrix material and paper mould flat pallet structure thereof - Google Patents
A kind of paper mould matrix material and paper mould flat pallet structure thereof Download PDFInfo
- Publication number
- CN104386336B CN104386336B CN201410661088.1A CN201410661088A CN104386336B CN 104386336 B CN104386336 B CN 104386336B CN 201410661088 A CN201410661088 A CN 201410661088A CN 104386336 B CN104386336 B CN 104386336B
- Authority
- CN
- China
- Prior art keywords
- matrix material
- leg
- flat pallet
- point
- paper mould
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to packing technique field, disclose a kind of paper mould matrix material, plant amylum in this paper mould matrix material on the basis of log wood-pulp board as filler, sticky rice flour not only plays waterproof action, but also can according to the needs of goods, it may also be useful to the goods that the paper mould matrix material with mentioned component content is made have the effect of significant protection against the tide, mildew-resistant. And a kind of paper pulp mould flat pallet structure that the present invention provides in addition, adopt above-mentioned materials in conjunction with the structure of flat pallet after, its bearing capacity more existing paper mould flat pallet is made to have stronger bearing capacity, its hierachical structure in the fabrication process, avoids and causes, because existing method increases material thickness, the advantage that drying efficiency is low and precision controlling is inaccurate.
Description
Technical field
The present invention relates to packing technique field, particularly relate to a kind of paper mould matrix material and paper mould flat pallet structure thereof.
Background technology
Flat pallet be Storage of Goods, logistics when transporting must one of instrument. At present conventional have Wooden tray, plastic pallet, teel pallet and paper pallet four kinds, and wherein wood pallet, plastic pallet consumption are maximum. Along with the continuous enhancing of people's environmental consciousness, with paper generation wood, become a kind of important development trend with paper for moulding. Paper mould is a kind of green, environmental protection, energy-conservation wrapping material, so, it can be recycled repeatedly to utilize paper mould to make flat pallet, environmental pollution is little and receives much concern, at present, paper mould flat pallet is not yet used widely at present, and its reason mainly contains the following aspects: one, due to plastics sucking moulding limited pressure, paper pulp fiber arrangement tightness is not enough, causes its bearing capacity lower; When two, increasing products thickness, pallet bearing capacity can be improved, but the increase of thickness can cause, and the tray dried cycle is elongated, production efficiency low, and pallet dimension precision is difficult to ensure. In view of this, the bottleneck that contriver exists for existing paper mould flat pallet, has invented a kind of paper mould matrix material and paper mould flat pallet structure thereof.
Summary of the invention
It is an object of the invention to for the deficiencies in the prior art, it is provided that a kind of paper mould matrix material and paper mould flat pallet structure thereof. The goods using this paper mould matrix material to make have the advantage of protection against the tide, mildew-resistant; Described paper mould flat pallet has the advantage that bearing capacity by force, easily manufactures and production precision is high.
For achieving the above object, a kind of paper mould matrix material of the present invention, according to weight percent meter, this matrix material comprises following component:
Log wood-pulp board is 55 ~ 85%;
Plant amylum is 2 ~ 15%;
Sticky rice flour is 0.5 ~ 8%;
Calcium carbonate is 0.2 ~ 5%;
Sodium peroxide is 0.05 ~ 1%;
Polylactic acid adhesive is 0.01 ~ 2%;
Water is 8% ~ 15%.
Preferably, according to weight percent meter, this matrix material comprises following component:
Log wood-pulp board is 70 ~ 75%;
Plant amylum is 7 ~ 12%;
Sticky rice flour is 1 ~ 3%;
Calcium carbonate is 0.3 ~ 1%;
Sodium peroxide is 0.2 ~ 0.8%;
Polylactic acid adhesive is 0.1 ~ 1%;
Water is 10% ~ 14%.
Preferably, according to weight percent meter, this matrix material comprises following component:
Log wood-pulp board is 72%;
Waste paper is 3.5%;
Plant amylum is 8%;
Sticky rice flour is 2%;
Calcium carbonate is 0.5%;
Sodium peroxide is 0.5%;
Polylactic acid adhesive is 0.5%;
Water is 13%.
Preferably, described plant amylum is clover starch or W-Gum.
A kind of paper mould flat pallet structure, comprises top panel, middle panel and lower supporting plate, and described top panel and middle panel are fitting to connection, and described middle panel is fixedly connected with the upper surface of lower supporting plate, and the lower surface of described lower supporting plate is connected with some feets.
Preferably, described middle panel is provided with pit, and described top panel is provided with the salient that can stretch into described pit, and described salient is fixedly connected with by glue with pit.
Preferably, the cross section of described pit is hexagon, rectangle or rhombus.
Preferably, described feet comprises script body, and one end of described script body is provided with first point of leg and the 2nd point of leg, and the other end of described script body is provided with the 3rd point of leg and the 4th point of leg.
Preferably, between described first point of leg and the 2nd point of leg, it is provided with the first interval trough, between described 3rd point of leg and the 4th point of leg, it is provided with the 2nd interval trough.
Preferably, described feet is hollow structure and one-body molded with described back up pad.
The useful effect of the present invention: a kind of paper mould matrix material of the present invention, plant amylum in this paper mould matrix material on the basis of log wood-pulp board as filler, sticky rice flour not only plays waterproof action, but also can according to the needs of goods, add the time that different content carrys out control degradation, calcium carbonate not only can improve the intensity of goods, under the cooperation of sticky rice flour, also there is the beneficial characteristics that easily row is wet and easily dry, peroxidation sodium and water reaction can generate sodium hydroxide further, object is to be mainly used in plant amylum is risen oxygenizement, the goods using the paper mould matrix material with mentioned component content to make have significant protection against the tide, the effect of mildew-resistant. and a kind of paper pulp mould flat pallet structure that the present invention provides in addition, adopt above-mentioned materials in conjunction with the structure of flat pallet after, its bearing capacity more existing paper mould flat pallet is made to have stronger bearing capacity, its hierachical structure in the fabrication process, avoids and causes, because existing method increases material thickness, the advantage that drying efficiency is low and precision controlling is inaccurate.
Accompanying drawing explanation
Fig. 1 is the perspective view of the paper mould flat pallet of the present invention.
Fig. 2 is the STRUCTURE DECOMPOSITION schematic diagram of the paper mould flat pallet of the present invention.
Fig. 3 is the upward view of Fig. 1.
Fig. 4 is that the A-A of Fig. 3 is to sectional view.
Fig. 5 is the structural representation of the feet of the present invention.
Fig. 6 is another structural representation of the feet of the present invention.
Reference numeral comprises: top panel--and 1, salient--11, middle panel--2, pit--21, lower supporting plate--3, feet--4, first point of leg--the 41, two point of leg--the 42, three point of leg--43,4th point of leg--the 44, first interval trough--the 45, two interval trough--46,3rd interval trough--47,4th parting bead--48, script body 5, shrinks position--6.
Embodiment
Below in conjunction with accompanying drawing, the present invention is described in detail.
Embodiment one.
A kind of paper mould matrix material, according to weight percent meter, this matrix material comprises following component:
Log wood-pulp board is 55%;
Plant amylum is 15%;
Sticky rice flour is 7%;
Calcium carbonate is 5%;
Sodium peroxide is 1%;
Polylactic acid adhesive is 2%.
Water is 15%.
Plant amylum in this paper mould matrix material on the basis of log wood-pulp board as filler, described log wood-pulp board can be the wood-pulp board of trees material, it can also be the wood-pulp board that bamboo and timber are mixed to form, sticky rice flour not only plays waterproof action, but also can according to the needs of goods, add the time that different content carrys out control degradation, such as: when the degradation time of goods is required very fast, can suitably increase the content of sticky rice flour, calcium carbonate not only can improve the intensity of goods, under the cooperation of sticky rice flour, also there is the beneficial characteristics that easily row is wet and easily dry, peroxidation sodium and water reaction can generate sodium hydroxide object further and be to be mainly used in plant amylum is risen oxygenizement, described plant amylum is clover starch or W-Gum, if in actual use, the sodium hydrate content that sodium peroxide generates is not enough, manual mode can also be used to add sodium hydroxide, simultaneously, the gluing glue of described poly(lactic acid) can adopt water-latex type polylactic acid adhesive, in addition, the preparation method of this matrix material is identical with the preparation method of the paper pulp mould of prior art, before preparation, it is necessary to first poly(lactic acid) is heated to 60-70 degree Celsius, reaches molten state, thus makes it mix more abundant with other compositions, the goods using the paper mould matrix material with mentioned component content to make have the effect of significant protection against the tide, mildew-resistant.
Embodiment two.
In the present embodiment, according to weight percent meter, this matrix material comprises following component:
Log wood-pulp board is 85%;
Plant amylum is 2%;
Sticky rice flour is 4.74%;
Calcium carbonate is 0.2%;
Sodium peroxide is 0.05%;
Polylactic acid adhesive is 0.01%;
Water is 8%.
Other parts of the present embodiment are identical with embodiment one.
Embodiment three.
In the present embodiment, according to weight percent meter, this matrix material is made up of following component:
Log wood-pulp board is 70%;
Plant amylum is 8%;
Sticky rice flour is 5%;
Calcium carbonate is 2.8%;
Sodium peroxide is 0.6%;
Polylactic acid adhesive is 0.6%;
Water is 13%.
Other parts of the present embodiment are identical with embodiment one.
Embodiment four.
Certainly, as reducing costs further, this matrix material also can add certain waste paper, in paper pulp molding forming, the addition of waste paper must have certain control, then affects shaping intensity too much as added content, adds that content is less can not realize again cost-saving maximumization requirement, through repeatedly testing, in the present invention, described waste paper content is 3.5% ~ 10%, in the present embodiment, according to weight percent meter, this matrix material comprises following component:
Log wood-pulp board is 72%;
Waste paper is 3.5%;
Plant amylum is 8%;
Sticky rice flour is 2%;
Calcium carbonate is 0.5%;
Sodium peroxide is 0.5%;
Polylactic acid adhesive is 0.5%;
Water is 13%.
Other parts of the present embodiment are identical with embodiment one.
Embodiment five.
In the present embodiment, according to weight percent meter, this matrix material comprises following component:
Log wood-pulp board is 65%;
Waste paper is 10%;
Plant amylum is 8%;
Sticky rice flour is 2.5%;
Calcium carbonate is 0.5%;
Sodium peroxide is 0.5%;
Polylactic acid adhesive is 0.5%;
Water is 13%.
Other parts of the present embodiment are identical with embodiment one.
See Fig. 1 to Fig. 6, present invention also offers a kind of paper mould flat pallet structure utilizing above-mentioned matrix material to make, comprise top panel 1, middle panel 2 and lower supporting plate 3, described top panel 1 is fitting to connection with middle panel 2, described middle panel 2 is fixedly connected with the upper surface of lower supporting plate 3, and the lower surface of described lower supporting plate 3 is connected with some feets 4. Wherein, described feet 4 arranges the layout type of totally 9 feets 4 by 3 row * 3, such layout type can also facilitate fork truck to carry out from bottom lifting liter when ensureing enough support strengths, in sum, adopt above-mentioned materials in conjunction with the structure of flat pallet after, making its bearing capacity more existing paper mould flat pallet have stronger bearing capacity, its hierachical structure in the fabrication process, avoids and causes, because existing method increases material thickness, the advantage that drying efficiency is low and precision controlling is inaccurate.
In this scheme, described middle panel 2 is provided with pit 21, and described top panel 1 is provided with the salient 11 that can stretch into described pit 21, and described salient 11 is fixedly connected with by glue with pit 21. When assembling, by pit 21 one_to_one corresponding of the salient 11 of top panel 1 with middle panel 2, and apply one layer of glue in salient 11 and pit 21, when salient 11 contacts with pit 21 instantly, can realize being adhesively fixed. Preferably, pit 21 is in honeycomb arrangement, and the structure of this kind of honeycomb arrangement is more firm, can bear bigger pressure.
Further, the cross section of described pit 21 is hexagon, rectangle or rhombus, but is not limited to above-mentioned shape; The cross-sectional shape of salient 11 is consistent with the cross-sectional shape of pit 21.
(see Fig. 5) in the technical program, described feet 4 comprises script body 5, and one end of described script body 5 is provided with first point of leg 41 and the 2nd point of leg 42, and the other end of described script body 5 is provided with the 3rd point of leg 43 and the 4th point of leg 44. this scheme adopts four points of legs to be disperseed by the gravity that script body 5 bears, when there is abrasion in one of them point of leg, under the effect of other three points of legs, good support can also be realized, it is comparatively speaking, the carrying effect having had better, the part contacted with ground due to script body 5 not only to be held the pressure awarding gravity, also to be born the tilting force produced when mobile flat pallet, and it is further, the contact surface on described four points of legs and ground is also provided with contraction position 6 upwards, the inwall of this contraction position 6 reduces the distance supported between inwall, thus expand support strength further.
In the technical program, between described first point of leg 41 and the 2nd point of leg 42, it is provided with the first interval trough 45, between described 3rd point of leg 43 and the 4th point of leg 44, it is provided with the 2nd interval trough 46. Described first interval trough 45, the 2nd interval trough 46 make feet 4 decrease the use of material, and can also keep the working strength of feet 4.
In the technical program, it is provided with the 3rd interval trough 47 between described first point of leg 41 and the 3rd point of leg 43, it is provided with parting bead 48 between outwardly the 4th between described 2nd point of leg 42 and the 4th point of leg 44, in actual use, what this feet 4 had the 4th parting bead 48 one is arranged facing to the outside of flat pallet, like this, when the one side that multiple feet 4 has the 4th parting bead 48 is all towards flat pallet outside, even if the edge of flat pallet forms an annular reinforcing structure (see Fig. 3 and Fig. 5), thus strengthen the edge loading strength of flat pallet.
In the technical program, the outer wheels profile of described script body 5 is all set to round-corner transition, thus prevents from gathering stress in moulding process, causes the quality problems of goods, and fillet excess processes can also prevent the scratching that it causes by foreign matter.
In the technical program, described feet 4 is hollow structure and one-body molded with described lower supporting plate 3. This kind of integrated mode, decreases manufacture and assembling procedure, and integrated loading strength is better.
Above content is only the better embodiment of the present invention, for the those of ordinary skill of this area, according to the thought of the present invention, all will change in specific embodiments and applications, and this description should not be construed as limitation of the present invention.
Claims (10)
1. a paper mould matrix material, it is characterised in that: according to weight percent meter, this matrix material comprises following component:
Log wood-pulp board is 55 ~ 85%;
Plant amylum is 2 ~ 15%;
Sticky rice flour is 0.5 ~ 8%;
Calcium carbonate is 0.2 ~ 5%;
Sodium peroxide is 0.05 ~ 1%;
Polylactic acid adhesive is 0.01 ~ 2%;
Water is 8% ~ 15%.
2. a kind of paper mould matrix material according to claim 1, it is characterised in that: according to weight percent meter, this matrix material comprises following component:
Log wood-pulp board is 70 ~ 75%;
Plant amylum is 7 ~ 12%;
Sticky rice flour is 1 ~ 3%;
Calcium carbonate is 0.3 ~ 1%;
Sodium peroxide is 0.2 ~ 0.8%;
Polylactic acid adhesive is 0.1 ~ 1%;
Water is 10% ~ 14%.
3. a kind of paper mould matrix material according to claim 1, it is characterised in that: according to weight percent meter, this matrix material comprises following component:
Log wood-pulp board is 72%;
Waste paper is 3.5%;
Plant amylum is 8%;
Sticky rice flour is 2%;
Calcium carbonate is 0.5%;
Sodium peroxide is 0.5%;
Polylactic acid adhesive is 0.5%;
Water is 13%.
4. a kind of paper mould matrix material according to claim 1, it is characterised in that: described plant amylum is clover starch or W-Gum.
5. the molding flat pallet structure made with matrix material according to claim 1, comprise top panel, middle panel and lower supporting plate, it is characterized in that: described top panel and middle panel are fitting to connection, described middle panel is fixedly connected with the upper surface of lower supporting plate, and the lower surface of described lower supporting plate is connected with some feets.
6. a kind of molding flat pallet structure according to claim 5, it is characterised in that: described middle panel is provided with some pits, and described top panel is provided with the salient that can stretch into described pit, and described salient is fixedly connected with by glue with pit.
7. a kind of molding flat pallet structure according to claim 6, it is characterised in that: the cross section of described pit is hexagon, rectangle or rhombus.
8. a kind of molding flat pallet structure according to claim 5, it is characterized in that: described feet comprises script body, one end of described script body is provided with first point of leg and the 2nd point of leg, and the other end of described script body is provided with the 3rd point of leg and the 4th point of leg.
9. a kind of molding flat pallet structure according to claim 8, it is characterised in that: it is provided with the first interval trough between described first point of leg and the 2nd point of leg, between described 3rd point of leg and the 4th point of leg, it is provided with the 2nd interval trough.
10. according to the arbitrary described a kind of molding flat pallet structure of claim 5-9, it is characterised in that: described feet is hollow structure and one-body molded with described lower supporting plate.