CN104385504A - Vulcanization process for rubber hammer - Google Patents
Vulcanization process for rubber hammer Download PDFInfo
- Publication number
- CN104385504A CN104385504A CN201410503530.8A CN201410503530A CN104385504A CN 104385504 A CN104385504 A CN 104385504A CN 201410503530 A CN201410503530 A CN 201410503530A CN 104385504 A CN104385504 A CN 104385504A
- Authority
- CN
- China
- Prior art keywords
- steam pressure
- temperature
- rubber hammer
- vulcanization process
- hour
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a vulcanization process for a rubber hammer. The vulcanization process comprises: 1) sequentially carrying out oil washing and water washing on a rubber hammer, removing dirt on the surface, and then placing into a steam pressure furnace; 2) rapidly heating to achieve the steam pressure furnace temperature of 120-150 DEG C at a rate of 50 DEG C/h, and continuously maintaining the temperature for 30-35 min; 3) reducing the pressure inside the steam pressure furnace to 0.3-0.4 Mpa, and continuously maintaining the pressure for 60-90 min; 4) cooling to achieve the steam pressure furnace temperature of 60 DEG C at a rate of 30 DEG C/h, and maintaining the temperature for 1-2 h; and 5) after completing the temperature maintaining, completely releasing the steam pressure within an hour, and opening cold wind to gradually cool so as to complete the whole vulcanization process. According to the present invention, the operation is simple, the process is clever, and the rubber treated by the vulcanization process of the present invention has characteristics of strong wear resistance, strong corrosion resistance and long service life.
Description
Technical field
The present invention relates to rubber materials, specifically, be related specifically to a kind of rubber hammer sulfuration process.
Background technology
When repairs profession installing floor board, be evenly distributed to make the cement under floor tile and do not occur cavity, often use rubber hammer to knock floor tile.Existing rubber hammer, comprises hammer body and handle, is provided with inner core in hammer body, and hammer body and handle are structure as a whole.Existing rubber hammer is that the rubber adopted there will be rubber fatigue after long-term use, impaired, the problem such as be corroded, and affects the service life of rubber hammer.
Summary of the invention
The object of the invention is to for deficiency of the prior art, provide a kind of rubber hammer sulfuration process, to solve the problem.
Technical problem solved by the invention can realize by the following technical solutions:
Rubber hammer sulfuration process, comprises the steps:
1) by rubber hammer successively oil wash and washing, after removing the dirt on surface, steam pressure stove is put into;
2) with the speed of 50 DEG C/h by the temperature rapid temperature increases of steam pressure stove to 120-150 DEG C, and continue insulation 30-35 minute;
3) by near for the pressure of steam pressure furnace interior 0.3Mpa-0.4Mpa, and pressurize 60-90 minute is continued;
4) with the speed of 30 DEG C/h, the temperature of steam pressure stove is down to 60 DEG C, and is incubated 1-2 hour;
5), after insulation terminates, in one hour, complete released vapour pressure, opens cold wind, makes it to cool gradually, completes whole sulfidation.
Preferably, described step 2) best holding temperature be 140 DEG C, best temperature retention time is 30 minutes.
Preferably, the best temperature retention time of described step 4) is 1 hour.
Compared with prior art, beneficial effect of the present invention is as follows:
Simple to operate, technique is ingenious, and the rubber through process of the present invention has stronger wear-resisting and corrosion resistance, long service life.
Detailed description of the invention
The technological means realized for making the present invention, creation characteristic, reaching object and effect is easy to understand, below in conjunction with detailed description of the invention, setting forth the present invention further.
Embodiment 1
Rubber hammer sulfuration process, comprises the steps:
1) by rubber hammer successively oil wash and washing, after removing the dirt on surface, steam pressure stove is put into;
2) with the speed of 50 DEG C/h by the temperature rapid temperature increases of steam pressure stove to 120 DEG C, and continue insulation 30 minutes;
3) by near for the pressure of steam pressure furnace interior 0.3Mpa, and pressurize 60 minutes are continued;
4) with the speed of 30 DEG C/h, the temperature of steam pressure stove is down to 60 DEG C, and is incubated 1 hour;
5), after insulation terminates, in one hour, complete released vapour pressure, opens cold wind, makes it to cool gradually, completes whole sulfidation.
Embodiment 2
Rubber hammer sulfuration process, comprises the steps:
1) by rubber hammer successively oil wash and washing, after removing the dirt on surface, steam pressure stove is put into;
2) with the speed of 50 DEG C/h by the temperature rapid temperature increases of steam pressure stove to 150 DEG C, and continue insulation 35 minutes;
3) by near for the pressure of steam pressure furnace interior 0.4 Mpa, and pressurize 90 minutes are continued;
4) with the speed of 30 DEG C/h, the temperature of steam pressure stove is down to 60 DEG C, and is incubated 2 hours;
5), after insulation terminates, in one hour, complete released vapour pressure, opens cold wind, makes it to cool gradually, completes whole sulfidation.
More than show and describe general principle of the present invention and principal character and advantage of the present invention.The technical staff of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and description just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (3)
1. rubber hammer sulfuration process, is characterized in that, comprises the steps:
1) by rubber hammer successively oil wash and washing, after removing the dirt on surface, steam pressure stove is put into;
2) with the speed of 50 DEG C/h by the temperature rapid temperature increases of steam pressure stove to 120-150 DEG C, and continue insulation 30-35 minute;
3) by near for the pressure of steam pressure furnace interior 0.3Mpa-0.4Mpa, and pressurize 60-90 minute is continued;
4) with the speed of 30 DEG C/h, the temperature of steam pressure stove is down to 60 DEG C, and is incubated 1-2 hour;
5), after insulation terminates, in one hour, complete released vapour pressure, opens cold wind, makes it to cool gradually, completes whole sulfidation.
2. rubber hammer sulfuration process according to claim 1, is characterized in that, described step 2) best holding temperature be 140 DEG C, best temperature retention time is 30 minutes.
3. rubber hammer sulfuration process according to claim 1, is characterized in that, the best temperature retention time of described step 4) is 1 hour.