CN104372604A - Fiber fabric fire retardant - Google Patents

Abstract

The invention provides a fiber fabric fire retardant. The fiber fabric fire retardant is prepared from the following raw materials in parts by weight: 2-5 parts of polypropylene, 3-8 parts of triethylene glycol diisooctoate, 6-8 parts of chitosan, 7-11 parts of light calcium carbonate, 3-5 parts of polyacrylamide, 5-9 parts of titanium dioxide, 8-14 parts of sodium tripolyphosphate, 10-14 parts of glycol, 1-4 parts of polyether polyol, 3-5 parts of dichloromethane, 4-7 parts of hydroquinone, 6-10 parts of sodium oleoyl amino acid and 9-16 parts of aluminum hydroxide. The fiber fabric fire retardant has the beneficial effects of excellent fire resistance, and the capability of carbonizing fibers to avoid combustion and prevent fire.

Description

A kind of fabric lining fire retardant

Technical field

The present invention relates to a kind of fabric lining fire retardant.

Background technology

Fabric is through being formed by weaving, and due to the cause that it becomes to be grouped into, mostly all inflammable, even if encounter a little Mars, also easily catch fire, fire-retardant for fibre easily permeates in fabric, and fire retardant can be retained between the surface of fabric and fiber after drying.Complicated change reaction can occur under meeting fiery high temperature, and its product has and plays significantly fire-retardant, fireproofing function to processed fabric.But the existing fire retardant scope of application is less, and can not meet user demand, use is restricted.

Summary of the invention

For the deficiencies in the prior art, the technical problem to be solved in the present invention is, provide a kind of fabric lining fire retardant, have good anti-flammability, carbonization appears in fiber, and can not burn, and prevents the generation of fire.

For solving the deficiencies in the prior art, the technical scheme that the present invention takes is: a kind of fabric lining fire retardant, is made up of the raw material of following parts by weight:

Polypropylene 2-5 part, triethylene glycol two tricaprylate 3-8 part, shitosan 6-8 part, precipitated calcium carbonate 7-11 part, polyacrylamide 3-5 part, titanium dioxide 5-9 part, sodium phosphate trimer 8-14 part, ethylene glycol 10-14 part, polyether polyol 1-4 part, carrene 3-5 part, hydroquinones 4-7 part, oleoyl amino acid sodium 6-10 part, aluminium hydroxide 9-16 part.

The invention has the beneficial effects as follows, fabric lining fire retardant of the present invention, having good anti-flammability, there is carbonization in fiber, and can not burn, and prevents the generation of fire.

Detailed description of the invention

embodiment 1

A kind of fabric lining fire retardant, be made up of the raw material of following parts by weight:

Polypropylene 2-5 part, triethylene glycol two tricaprylate 3-8 part, shitosan 6-8 part, precipitated calcium carbonate 7-11 part, polyacrylamide 3-5 part, titanium dioxide 5-9 part, sodium phosphate trimer 8-14 part, ethylene glycol 10-14 part, polyether polyol 1-4 part, carrene 3-5 part, hydroquinones 4-7 part, oleoyl amino acid sodium 6-10 part, aluminium hydroxide 9-16 part.

Claims (1)

1. a fabric lining fire retardant, is characterized in that: be made up of the raw material of following parts by weight:

Polypropylene 2-5 part, triethylene glycol two tricaprylate 3-8 part, shitosan 6-8 part, precipitated calcium carbonate 7-11 part, polyacrylamide 3-5 part, titanium dioxide 5-9 part, sodium phosphate trimer 8-14 part, ethylene glycol 10-14 part, polyether polyol 1-4 part, carrene 3-5 part, hydroquinones 4-7 part, oleoyl amino acid sodium 6-10 part, aluminium hydroxide 9-16 part.