CN104372233A - Potassium-sodium alloy die castings - Google Patents
Potassium-sodium alloy die castings Download PDFInfo
- Publication number
- CN104372233A CN104372233A CN201410607453.0A CN201410607453A CN104372233A CN 104372233 A CN104372233 A CN 104372233A CN 201410607453 A CN201410607453 A CN 201410607453A CN 104372233 A CN104372233 A CN 104372233A
- Authority
- CN
- China
- Prior art keywords
- parts
- potassium
- die castings
- sodium
- sodium alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses potassium-sodium alloy die castings consisting of the following materials in parts by weight: 20-35 parts of aluminum trioxide, 10-15 parts of manganese dioxide, 10-14 parts of copper sulfate, 5-8 parts of fine iron powder, 3-5 parts of chromium-molybdenum steel, 6-8 parts of silicon dioxide, 2-8 parts of brass, 3-7 parts of tinplate, 6-8 parts of nickel hydroxide and 15-30 parts of a potassium-sodium alloy. The potassium-sodium alloy die castings disclosed by the invention have the beneficial effects that the potassium-sodium alloy die castings can be used for effectively reducing the flow mark rate and bubble rate in the die castings by adjusting the composition proportion of the die castings; and compared with the prior art, the quality of the potassium-sodium alloy die castings can be increased by 3 to 4 times.
Description
Technical field
The present invention relates to sodium-potassium eutectic die casting.
Background technology
Die casting is a kind of part of pressure die casting, use the pressure die casting machinery pressure die-casting machine installing casting die, the metal such as copper, zinc, aluminum or aluminum alloy being heated to be liquid state is poured into the feeding mouth of pressure die-casting machine, through pressure die-casting machine die casting, cast out the copper of the shape and size of mould restriction, zinc, aluminium part or aluminum alloy part, such part is just called die casting usually.Die casting has different calls in different places, as diecast parts, die-casting, die casting, die casting aluminium, die case zinc part, die casting copper piece, copper die casting, zine pressure casting, aluminium diecasting aluminium diecasting, aluminium pressure alloy-steel casting, aluminium alloy compression casting part etc.
Summary of the invention
Object of the present invention is exactly for above-mentioned defect of the prior art, provides a kind of through improvement, improves the sodium-potassium eutectic die casting of quality of die casting.
To achieve these goals, technical scheme provided by the invention is: sodium-potassium eutectic die casting, is made up of the following material according to parts by weight: aluminium sesquioxide 20-35 part, Manganse Dioxide 10-15 part, copper sulfate 10-14 part, Iron concentrate 5-8 part, chromemolybdenum steel 3-5 part, silicon-dioxide 6-8 part, brass 2-8 part, tinplate 3-7 part, nickel hydroxide 6-8 part, sodium-potassium eutectic 15-30 part.
Further, above-mentioned sodium-potassium eutectic die casting, is made up of the following material according to parts by weight: aluminium sesquioxide 25 parts, Manganse Dioxide 12 parts, 12 parts, copper sulfate, Iron concentrate 6 parts, chromemolybdenum steel 4 parts, silicon-dioxide 7 parts, brass 5 parts, tinplate 5 parts, nickel hydroxide 7 parts, sodium-potassium eutectic 25 parts.
Beneficial effect of the present invention is: sodium-potassium eutectic die casting provided by the invention, by adjusting the composition and ratio of die casting, effectively can reduce the current mark rate in die casting and bubble rate, and compared to prior art, quality can improve 3-4 doubly.
Embodiment
embodiment 1:
Sodium-potassium eutectic die casting, be made up of the following material according to parts by weight: aluminium sesquioxide 20-35 part, Manganse Dioxide 10-15 part, copper sulfate 10-14 part, Iron concentrate 5-8 part, chromemolybdenum steel 3-5 part, silicon-dioxide 6-8 part, brass 2-8 part, tinplate 3-7 part, nickel hydroxide 6-8 part, sodium-potassium eutectic 15-30 part.
embodiment 2:
Sodium-potassium eutectic die casting, is made up of the following material according to parts by weight: aluminium sesquioxide 25 parts, Manganse Dioxide 12 parts, 12 parts, copper sulfate, Iron concentrate 6 parts, chromemolybdenum steel 4 parts, silicon-dioxide 7 parts, brass 5 parts, tinplate 5 parts, nickel hydroxide 7 parts, sodium-potassium eutectic 25 parts.
Last it is noted that the foregoing is only the preferred embodiments of the present invention, be not limited to the present invention, although with reference to previous embodiment to invention has been detailed description, for a person skilled in the art, it still can be modified to the technical scheme described in foregoing embodiments, or carries out equivalent replacement to wherein portion of techniques feature.Within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (2)
1. sodium-potassium eutectic die casting, it is characterized in that, be made up of the following material according to parts by weight: aluminium sesquioxide 20-35 part, Manganse Dioxide 10-15 part, copper sulfate 10-14 part, Iron concentrate 5-8 part, chromemolybdenum steel 3-5 part, silicon-dioxide 6-8 part, brass 2-8 part, tinplate 3-7 part, nickel hydroxide 6-8 part, sodium-potassium eutectic 15-30 part.
2. sodium-potassium eutectic die casting according to claim 1, it is characterized in that, be made up of the following material according to parts by weight: aluminium sesquioxide 25 parts, Manganse Dioxide 12 parts, 12 parts, copper sulfate, Iron concentrate 6 parts, chromemolybdenum steel 4 parts, silicon-dioxide 7 parts, brass 5 parts, tinplate 5 parts, nickel hydroxide 7 parts, sodium-potassium eutectic 25 parts.