CN104371227A - Fluorine-containing plastic processing assistant and preparation method thereof - Google Patents
Fluorine-containing plastic processing assistant and preparation method thereof Download PDFInfo
- Publication number
- CN104371227A CN104371227A CN201410618657.4A CN201410618657A CN104371227A CN 104371227 A CN104371227 A CN 104371227A CN 201410618657 A CN201410618657 A CN 201410618657A CN 104371227 A CN104371227 A CN 104371227A
- Authority
- CN
- China
- Prior art keywords
- combination
- plastic processing
- processing aid
- containing plastic
- fluoro
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a fluorine-containing plastic processing assistant and a preparation method thereof. The assistant comprises the following components in parts by weight: 20-60 parts of fluorine-containing polymer, 20-60 parts of interfacial agent and 15-30 parts of heat stabilizer. The method comprises the following steps: proportionally adding the interfacial agent and heat stabilizer into a reaction kettle, adding the fluorine-containing polymer when the temperature reaches 120-140 DEG C, thoroughly and uniformly mixing, and discharging to obtain the finished product.
Description
Technical field
The present invention relates to field of plastics processing, specifically a kind of preparation method of fluoro-containing plastic processing aid and application.
Background technology
In the extrusion moulding process of TPO, when being blow molded into film as used containing LLDPE LLDPE raw material, there is critical shearing rate.When the shearing rate of Screw Extrusion is lower than critical shearing rate, the film surface of blowing is smooth, along with the shearing rate of Screw Extrusion higher than critical shearing rate time, phenomenon that film surface there will be " shark skin ", Here it is there is melt fracture.
When adding fluorine-containing polymer processing aids (PPA) and adding in TPO, in the process extruded, through the interface that the PPA of particular design can move to polymkeric substance and equipment, form the coating of a layered low-surface energy on the surface of equipment.This coating is the effect that the processing of polymkeric substance serves lubrication, and the shearing force that polyolefine is subject in the molten state significantly reduces, and eliminates " shark skin " phenomenon of film surface, solves melt fracture problem.
Summary of the invention
The object of this invention is to provide a kind of function fluoropolymer additive and preparation method thereof.
The present invention is to solve in the extrusion moulding process of existing TPO, the problem of phenomenon that film surface there will be " shark skin ".
A kind of fluoro-containing plastic processing aid of the present invention, each material component is by weight: fluoropolymer 20-60 part, interfacial agent 20-60 part, thermo-stabilizer 15-30 part.
Described vinylidene fluoride (VDF), tetrafluoroethylene (TFE), R 1216 (HFP), trifluorochloroethylene (CTFE), trifluoro-ethylene (VF3), at least one of perfluoro (alkyl vinyl) ethers or the combination of at least two kinds, in combination, each component ratio is selected arbitrarily.
Described interfacial agent is the combination of at least one in polyester polyol, amphipathic nature block polymer, functional group modification polyoxyethylene glycol or at least two kinds, and in combination, each component ratio is selected arbitrarily; Described amphipathic nature block polymer is poly glycol monomethyl ether or polymethylmethacrylate.
Described thermo-stabilizer is magnesium oxide, boron nitride, aluminium nitride, silicon nitride, silicon carbide, and at least one in ceramic microsphere or the combination of at least two kinds, in combination, each component ratio is selected arbitrarily.
The preparation method of fluoro-containing plastic processing aid of the present invention, the method is: by interfacial agent, thermo-stabilizer in proportion part add in reactor, equitemperature reaches 120-140 Celsius when spending, add fluoropolymer, insulated and stirred 30min, fully mix, discharging, pulverize i.e. obtained finished product with pulverizer.
The structure of this finished product auxiliary agent is that fluoropolymer is coated on the surface of thermo-stabilizer by interfacial agent; The median size of auxiliary agent is 800um ~ 1800um.
Advantage of the present invention: when fluorine-containing polymer processing aids (PPA) of the present invention is added after in TPO, in the process extruded, PPA can move to the interface of polymkeric substance and equipment, the coating of a layered low-surface energy is formed on the surface of equipment, this coating is the effect that the processing of polymkeric substance serves lubrication, the shearing force that polyolefine is subject in the molten state significantly reduces, eliminate " shark skin " phenomenon of film surface, solve melt fracture, reduce die orifice buildup, improve light and the slickness of product, improve simultaneously and extrude output, reduce melt pressure.
The thermo-stabilizer that the present invention uses is a kind of chemical structure of uniqueness.
Embodiment
Below by embodiment, the present invention is specifically described.
The following examples are used to further illustrate the present invention, and can not be interpreted as limiting the scope of the invention.
Embodiment 1:
Be the polycaprolactone butyleneglycol 5Kg of 2000-6000 by molecular weight, magnesium oxide 18Kg, joins in reactor together, is heated to 130 DEG C, then adds fluoropolymer 25Kg.After insulated and stirred 30min, discharging, pulverize with pulverizer, the particle diameter of powder is 1200um, obtained fluorine-containing processing aid.
Embodiment 2:
Be the isopentenol polyoxyethylene ether 5Kg of 2400 by molecular weight, magnesium oxide 18Kg, joins in reactor together, is heated to 130 DEG C, then adds fluoropolymer 25Kg.After insulated and stirred 30min, discharging, pulverize with pulverizer, the particle diameter of powder is 1200um, obtained fluorine-containing processing aid.
Embodiment 3:
Be the polycaprolactone butyleneglycol 5Kg of 2400 by molecular weight, aluminium nitride 16Kg, joins in reactor together, is heated to 130 DEG C, then adds fluoropolymer 28Kg.After insulated and stirred 30min, discharging, pulverize with pulverizer, the particle diameter of powder is 1000um, obtained fluorine-containing processing aid.
Embodiment 4:
Be the isopentenol polyoxyethylene ether 6Kg of 3000 by molecular weight, magnesium oxide 18Kg, joins in reactor together, is heated to 140 DEG C, then adds fluoropolymer 25Kg.After insulated and stirred 30min, discharging, pulverize with pulverizer, the particle diameter of powder is 1000um, obtained fluorine-containing processing aid.
Auxiliary agent of the present invention is mainly used in blown film, after adding fluorine-containing processing aid, its
Effect is: during blown film, and the onset time of eliminating melt fracture is short; The appearance of film surface
The time of striped is obviously more delayed than common fluorine-containing processing aid.This auxiliary agent adding in final finished
Dosage is lower, is 300-400PPm.
Now lift application example to be described.
Application example 1:
By fluorine-containing processing aid 4Kg and linear low density polyethylene (trade mark is LLDPE 1820) 96Kg, mix with homogenizer, on the twin screw extruder in 170 DEG C of extruding pelletizations.By this master batch with 1% addition join containing the linear low density polyethylene LLDPE(trade mark as LLDPE 920NT) mixed plastic in, inflation film manufacturing machine is blow molded into film.
Application example 2:
Be LLDPE 920NT by fluorine-containing processing aid 0.04Kg with containing a certain proportion of linear low density polyethylene LLDPE(trade mark) in mixed plastic (96Kg), mix with homogenizer, inflation film manufacturing machine is blow molded into film.
Application example 3:
By fluorine-containing processing aid 3.5Kg and linear low density polyethylene (trade mark is LLDPE 1820) 96Kg, mix with homogenizer, on the twin screw extruder in 170 DEG C of extruding pelletizations.By this master batch with 1% addition join containing the linear low density polyethylene LLDPE(trade mark as LLDPE 920NT) mixed plastic in, inflation film manufacturing machine is blow molded into film.
Claims (5)
1. a fluoro-containing plastic processing aid, is characterized in that: each material component is by weight:
Fluoropolymer 20-60 part, interfacial agent 20-60 part, thermo-stabilizer 15-30 part.
2. fluoro-containing plastic processing aid according to claim 1, it is characterized in that described fluoropolymer is the combination of at least one in vinylidene fluoride, tetrafluoroethylene, R 1216, trifluorochloroethylene, trifluoro-ethylene, perfluoro (alkyl vinyl) ethers or at least two kinds, in combination, each component ratio is selected arbitrarily.
3. fluoro-containing plastic processing aid according to claim 1, it is characterized in that described interfacial agent is the combination of at least one in polyester polyol, amphipathic nature block polymer, functional group modification polyoxyethylene glycol or at least two kinds, in combination, each component ratio is selected arbitrarily; Described amphipathic nature block polymer is poly glycol monomethyl ether or polymethylmethacrylate.
4. fluoro-containing plastic processing aid according to claim 1, is characterized in that described thermo-stabilizer is magnesium oxide, boron nitride, aluminium nitride, silicon nitride, silicon carbide, at least one in ceramic microsphere or the combination of at least two kinds, in combination, each component ratio is selected arbitrarily.
5. the preparation method of fluoro-containing plastic processing aid according to claim 1, it is characterized in that the method is: by interfacial agent, thermo-stabilizer in proportion part add in reactor, equitemperature reaches 120-140 Celsius when spending, add fluoropolymer, fully mix, discharging can obtain finished product.