CN104371221A - Biodegradable medical packaging material and preparation method thereof - Google Patents
Biodegradable medical packaging material and preparation method thereof Download PDFInfo
- Publication number
- CN104371221A CN104371221A CN201410623914.3A CN201410623914A CN104371221A CN 104371221 A CN104371221 A CN 104371221A CN 201410623914 A CN201410623914 A CN 201410623914A CN 104371221 A CN104371221 A CN 104371221A
- Authority
- CN
- China
- Prior art keywords
- wrapping material
- degradable medical
- parts
- medical wrapping
- controls
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a biodegradable medical packaging material and a preparation method thereof. The material comprises the following components: PE, PVC, an antioxidant, an auxiliary antioxidant, ethanediamine, a polyester fiber, gelatin, lecithin, polypropylene, polylactic acid, sodium starch, glycerin, emulsified silicone oil, succinic acid and chitosan. The preparation method comprises the following steps: adding PE, PVC, ethanediamine, the polyester fiber, gelatin, lecithin, polypropylene, sodium starch and chitosan to a reaction kettle; stirring and reacting under a vacuum condition at certain temperature to obtain a mixture 1; adding the residual components to the mixture; stirring and mixing evenly; and extruding and molding in a twin-screw extruder, so as to obtain the biodegradable medical packaging material. The biodegradable medical packaging material disclosed by the invention has good mechanical properties and biodegradable properties, and can be widely applied to the field of packaging.
Description
Technical field
The invention belongs to medical material preparing technical field, be specifically related to a kind of degradable medical wrapping material and preparation method thereof.
Background technology
At present, Chinese Plastics annual production is 3,000,000 tons, and consumption is more than 6,000,000 tons.Whole world plastics annual production is 100,000,000 tons, if the plastics by annual 15% are discarded gauge and are calculated, whole world year, the plastics amount of discarding was exactly 1,500 ten thousand tons, the discarded amount of year plastics of China is more than 1,000,000 tons, the ratio of waste plastic in rubbish accounts for 40%, waste plastics a large amount of is like this buried under the ground as rubbish, brings larger pressure to undoubtedly tilling the land of natively lacking.Plastics are while bringing convenience to the life of people, and also bring the future trouble being difficult to tidy up to environment, people call the disaster that plastics bring to environment " white pollution ".Plastics bag brings conveniently to people's life really, but this conveniently for the moment but brings permanent harm.
In general, the harm of nondegradable popular plastics plastics to the earth includes: 1. plastic bag recovery is worth lower, easily in use except being scattered in avenue, tourist district, plastic construction stablize, not easily degraded by natural microbial bacterium, be not separated for a long time in physical environment.This just means that waste plastic garbage is not if reclaimed, and will become pollutent in the environment and forever exists and constantly accumulate, and can cause high risks to environment.2. affect agricultural development.Waste plastic product is mixed in soil constantly to be accumulated, and can affect farm crop and absorb nutrient and moisture.3. be discarded in the waste plastic product in land or water body, be used as food by animal and swallow, cause animal dead.It is therefore lethal that Qing-hai Lake has 20 family herdsman to have nearly thousand sheep, financial loss about more than 30 ten thousand yuan.Such thing at the zoo, pastoral area, rural area, of common occurrence in ocean.4. plastic waste not only can take a large amount of soil with garbage loading embeading, and occupied soil can not get recovering for a long time, affects the sustainable use in soil.If the waste plastic product entered in domestic refuse is by its landfill, the time of 200 years does not degrade.The singularity of the article that medical package material is packed due to it, therefore the requirement that its wrapping material can reach certain is more needed, as the degradability of material, although carried out certain research both at home and abroad at present in degradation material, but degradation property is still poor, if and use the strong component of degradability to carry out modification to prepare degradation material, the physicals of material does not often reach requirement.
Summary of the invention
The object of the invention is to provide a kind of degradable medical wrapping material and preparation method thereof to overcome above the deficiencies in the prior art, improving physicals and the degradability of material.
The present invention is achieved through the following technical solutions:
A kind of degradable medical wrapping material, comprise in components by weight percent: PE 20-30 part, PVC 30-40 part, oxidation inhibitor 0.5-1.2 part, auxiliary antioxidant 0.3-0.8 part, quadrol 1-5 part, trevira 3-8 part, gelatin 5-10 part, Yelkin TTS 5-10 part, polypropylene 2-8 part, poly(lactic acid) 3-8 part, Starch Sodium 3-7 part, glycerol 2-6 part, silicone emulsion 0.5-2 part, succsinic acid 3-7 part, chitosan 5-10 part.
Described degradable medical wrapping material, can preferably comprise in components by weight percent: PE 25-28 part, PVC 33-37 part, oxidation inhibitor 0.8-1.1 part, auxiliary antioxidant 0.4-0.7 part, quadrol 3-5 part, trevira 5-7 part, gelatin 6-8 part, Yelkin TTS 7-9 part, polypropylene 5-7 part, poly(lactic acid) 4-6 part, Starch Sodium 5-7 part, glycerol 3-5 part, silicone emulsion 0.8-1.5 part, succsinic acid 4-7 part, chitosan 7-9 part.
Described degradable medical wrapping material, oxidation inhibitor can be antioxidant 1076.
Described degradable medical wrapping material, auxiliary antioxidant can be auxiliary antioxidant GW508.
The preparation method of the degradable medical wrapping material described in more than one any one, comprises the following steps:
Step one, PE, PVC, quadrol, trevira, gelatin, Yelkin TTS, polypropylene, Starch Sodium and chitosan are joined in reactor, be 80-90 DEG C in temperature, vacuum tightness is under the condition of 0.02-0.05MPa, stirring reaction 40-50 minute, stirring velocity is 90-120 rev/min, obtains mixture one;
Step 2, joins remaining ingredient in the mixture one that step one obtains, is uniformly mixed, obtains mixture two;
Step 3, mixture two extrusion moulding in twin screw extruder step 2 obtained, obtains degradable medical wrapping material.
The preparation method of described degradable medical wrapping material, the condition that is uniformly mixed in step 2 can be temperature 50-60 DEG C, stirring velocity 150-180 rev/min, time 30-40 minute.
The preparation method of described degradable medical wrapping material, in step 3, extruding pelletization condition can divide three sections of controls for twin screw extruder cylinder back segment temperature, control respectively at 180-190 DEG C, barrel front-end temperature divides three sections of controls, control respectively at 180-200 DEG C, head temperature divides two sections of controls, controls respectively at 190-210 DEG C.
Degradable medical wrapping material provided by the invention have good physicals and degradability, and wherein tensile strength reaches more than 152MPa, and elongation at break reaches more than 8%, and notched Izod impact strength reaches 19KJ/m
2, to be embedded in soil degradation rate after 30 days under room temperature and to reach more than 55%, degradation property is excellent, can be used as wrapping material and is widely used in packaging.
Embodiment
Embodiment 1
A kind of degradable medical wrapping material, comprise in components by weight percent: PE 20 parts, PVC 30 parts, antioxidant 1076 0.5 part, auxiliary antioxidant GW5080.3 part, quadrol 1 part, 3 parts, trevira, 5 parts, gelatin, 5 parts, Yelkin TTS, polypropylene 2 parts, poly(lactic acid) 3 parts, Starch Sodium 3 parts, glycerol 2 parts, silicone emulsion 0.5 part, succsinic acid 3 parts, chitosan 5 parts.
The preparation method of described degradable medical wrapping material, comprises the following steps:
Step one, joins in reactor by PE, PVC, quadrol, trevira, gelatin, Yelkin TTS, polypropylene, Starch Sodium and chitosan, is 80 DEG C in temperature, vacuum tightness is under the condition of 0.05MPa, stirring reaction 40 minutes, stirring velocity is 90 revs/min, obtains mixture one;
Step 2, joined by remaining ingredient in the mixture one that step one obtains, be uniformly mixed, condition is temperature 50 C, and stirring velocity 150 revs/min, obtains mixture two at 30 minutes time;
Step 3, mixture two extrusion moulding in twin screw extruder that step 2 is obtained, extrusion condition can divide three sections of controls for twin screw extruder cylinder back segment temperature, control at 180 DEG C, 182 DEG C and 185 DEG C respectively, barrel front-end temperature divides three sections of controls, controls at 180 DEG C, 183 DEG C and 187 DEG C respectively, and head temperature divides two sections of controls, control respectively, at 190 DEG C and 193 DEG C, to obtain degradable medical wrapping material.
Embodiment 2
A kind of degradable medical wrapping material, comprise in components by weight percent: PE 25 parts, PVC 33 parts, antioxidant 1076 0.8 part, auxiliary antioxidant GW508 0.4 part, quadrol 3 parts, 5 parts, trevira, 6 parts, gelatin, 7 parts, Yelkin TTS, polypropylene 5 parts, poly(lactic acid) 4 parts, Starch Sodium 5 parts, glycerol 3 parts, silicone emulsion 0.8 part, succsinic acid 4 parts, chitosan 7 parts.
The preparation method of described degradable medical wrapping material, comprises the following steps:
Step one, joins in reactor by PE, PVC, quadrol, trevira, gelatin, Yelkin TTS, polypropylene, Starch Sodium and chitosan, is 85 DEG C in temperature, vacuum tightness is under the condition of 0.03MPa, stirring reaction 42 minutes, stirring velocity is 95 revs/min, obtains mixture one;
Step 2, joined by remaining ingredient in the mixture one that step one obtains, be uniformly mixed, condition is temperature 52 DEG C, and stirring velocity 160 revs/min, obtains mixture two at 33 minutes time;
Step 3, mixture two extrusion moulding in twin screw extruder that step 2 is obtained, extrusion condition can divide three sections of controls for twin screw extruder cylinder back segment temperature, control at 183 DEG C, 185 DEG C and 186 DEG C respectively, barrel front-end temperature divides three sections of controls, controls at 182 DEG C, 185 DEG C and 190 DEG C respectively, and head temperature divides two sections of controls, control respectively, at 193 DEG C and 196 DEG C, to obtain degradable medical wrapping material.
Embodiment 3
A kind of degradable medical wrapping material, comprise in components by weight percent: PE 27 parts, PVC 35 parts, antioxidant 1076 1 part, auxiliary antioxidant GW508 0.6 part, quadrol 4 parts, 6 parts, trevira, 7 parts, gelatin, 8 parts, Yelkin TTS, polypropylene 6 parts, poly(lactic acid) 5 parts, Starch Sodium 6 parts, glycerol 4 parts, silicone emulsion 1.2 parts, succsinic acid 6 parts, chitosan 8 parts.
The preparation method of described degradable medical wrapping material, comprises the following steps:
Step one, joins in reactor by PE, PVC, quadrol, trevira, gelatin, Yelkin TTS, polypropylene, Starch Sodium and chitosan, is 86 DEG C in temperature, vacuum tightness is under the condition of 0.03MPa, stirring reaction 50 minutes, stirring velocity is 110 revs/min, obtains mixture one;
Step 2, joined by remaining ingredient in the mixture one that step one obtains, be uniformly mixed, condition is temperature 58 DEG C, and stirring velocity 170 revs/min, obtains mixture two at 36 minutes time;
Step 3, mixture two extrusion moulding in twin screw extruder that step 2 is obtained, extrusion condition can divide three sections of controls for twin screw extruder cylinder back segment temperature, control at 183 DEG C, 186 DEG C and 188 DEG C respectively, barrel front-end temperature divides three sections of controls, controls at 183 DEG C, 185 DEG C and 200 DEG C respectively, and head temperature divides two sections of controls, control respectively, at 198 DEG C and 204 DEG C, to obtain degradable medical wrapping material.
Embodiment 4
A kind of degradable medical wrapping material, comprise in components by weight percent: PE 28 parts, PVC 37 parts, antioxidant 1076 1.1 parts, auxiliary antioxidant GW5080.7 part, quadrol 5 parts, 7 parts, trevira, 8 parts, gelatin, 9 parts, Yelkin TTS, polypropylene 7 parts, poly(lactic acid) 6 parts, Starch Sodium 7 parts, glycerol 5 parts, silicone emulsion 1.5 parts, succsinic acid 7 parts, chitosan 9 parts.
The preparation method of described degradable medical wrapping material, comprises the following steps:
Step one, joins in reactor by PE, PVC, quadrol, trevira, gelatin, Yelkin TTS, polypropylene, Starch Sodium and chitosan, is 90 DEG C in temperature, vacuum tightness is under the condition of 0.02MPa, stirring reaction 50 minutes, stirring velocity is 116 revs/min, obtains mixture one;
Step 2, joined by remaining ingredient in the mixture one that step one obtains, be uniformly mixed, condition is temperature 58 DEG C, and stirring velocity 175 revs/min, obtains mixture two at 36 minutes time;
Step 3, mixture two extrusion moulding in twin screw extruder that step 2 is obtained, extrusion condition can divide three sections of controls for twin screw extruder cylinder back segment temperature, control at 183 DEG C, 186 DEG C and 190 DEG C respectively, barrel front-end temperature divides three sections of controls, controls at 185 DEG C, 192 DEG C and 198 DEG C respectively, and head temperature divides two sections of controls, control respectively, at 196 DEG C and 205 DEG C, to obtain degradable medical wrapping material.
Embodiment 5
A kind of degradable medical wrapping material, comprise in components by weight percent: PE 30 parts, PVC 40 parts, antioxidant 1076 1.2 parts, auxiliary antioxidant GW508 0.8 part, quadrol 5 parts, 8 parts, trevira, 10 parts, gelatin, 10 parts, Yelkin TTS, polypropylene 8 parts, poly(lactic acid) 8 parts, Starch Sodium 7 parts, glycerol 6 parts, silicone emulsion 2 parts, succsinic acid 7 parts, chitosan 10 parts.
The preparation method of described degradable medical wrapping material, comprises the following steps:
Step one, joins in reactor by PE, PVC, quadrol, trevira, gelatin, Yelkin TTS, polypropylene, Starch Sodium and chitosan, is 90 DEG C in temperature, vacuum tightness is under the condition of 0.04MPa, stirring reaction 50 minutes, stirring velocity is 120 revs/min, obtains mixture one;
Step 2, joined by remaining ingredient in the mixture one that step one obtains, be uniformly mixed, condition is temperature 60 C, and stirring velocity 180 revs/min, obtains mixture two at 40 minutes time;
Step 3, mixture two extrusion moulding in twin screw extruder that step 2 is obtained, extrusion condition can divide three sections of controls for twin screw extruder cylinder back segment temperature, control at 184 DEG C, 187 DEG C and 190 DEG C respectively, barrel front-end temperature divides three sections of controls, controls at 186 DEG C, 194 DEG C and 200 DEG C respectively, and head temperature divides two sections of controls, control respectively, at 204 DEG C and 210 DEG C, to obtain degradable medical wrapping material.
Carry out performance test to the degradable medical wrapping material that above embodiment prepares, concrete outcome is as following table:
As can be seen from above test-results, degradable medical wrapping material provided by the invention have good physicals and degradability, wherein tensile strength reaches more than 152MPa, and elongation at break reaches more than 8%, and notched Izod impact strength reaches 19KJ/m
2, to be embedded in soil degradation rate after 30 days under room temperature and to reach more than 55%, degradation property is excellent, can be used as wrapping material and is widely used in packaging.
Claims (7)
1. degradable medical wrapping material, is characterized in that, comprise in components by weight percent: PE 20-30 part, PVC 30-40 part, oxidation inhibitor 0.5-1.2 part, auxiliary antioxidant 0.3-0.8 part, quadrol 1-5 part, trevira 3-8 part, gelatin 5-10 part, Yelkin TTS 5-10 part, polypropylene 2-8 part, poly(lactic acid) 3-8 part, Starch Sodium 3-7 part, glycerol 2-6 part, silicone emulsion 0.5-2 part, succsinic acid 3-7 part, chitosan 5-10 part.
2. degradable medical wrapping material according to claim 1, is characterized in that, comprise in components by weight percent: PE 25-28 part, PVC 33-37 part, oxidation inhibitor 0.8-1.1 part, auxiliary antioxidant 0.4-0.7 part, quadrol 3-5 part, trevira 5-7 part, gelatin 6-8 part, Yelkin TTS 7-9 part, polypropylene 5-7 part, poly(lactic acid) 4-6 part, Starch Sodium 5-7 part, glycerol 3-5 part, silicone emulsion 0.8-1.5 part, succsinic acid 4-7 part, chitosan 7-9 part.
3. degradable medical wrapping material according to claim 1, is characterized in that, oxidation inhibitor is antioxidant 1076.
4. degradable medical wrapping material according to claim 1, is characterized in that, auxiliary antioxidant is auxiliary antioxidant GW508.
5. the preparation method of the degradable medical wrapping material described in any one of claim 1-4, is characterized in that, comprise the following steps:
Step one, PE, PVC, quadrol, trevira, gelatin, Yelkin TTS, polypropylene, Starch Sodium and chitosan are joined in reactor, be 80-90 DEG C in temperature, vacuum tightness is under the condition of 0.02-0.05MPa, stirring reaction 40-50 minute, stirring velocity is 90-120 rev/min, obtains mixture one;
Step 2, joins remaining ingredient in the mixture one that step one obtains, is uniformly mixed, obtains mixture two;
Step 3, mixture two extrusion moulding in twin screw extruder step 2 obtained, obtains degradable medical wrapping material.
6. the preparation method of degradable medical wrapping material according to claim 5, is characterized in that, the condition that is uniformly mixed in step 2 is temperature 50-60 DEG C, stirring velocity 150-180 rev/min, time 30-40 minute.
7. the preparation method of degradable medical wrapping material according to claim 5, it is characterized in that, in step 3, extruding pelletization condition is that twin-screw extrusion machine barrel back segment temperature divides three sections of controls, control respectively at 180-190 DEG C, barrel front-end temperature divides three sections of controls, control respectively at 180-200 DEG C, head temperature divides two sections of controls, controls respectively at 190-210 DEG C.