CN104371169A - Antibacterial polyethylene film - Google Patents
Antibacterial polyethylene film Download PDFInfo
- Publication number
- CN104371169A CN104371169A CN201410621559.6A CN201410621559A CN104371169A CN 104371169 A CN104371169 A CN 104371169A CN 201410621559 A CN201410621559 A CN 201410621559A CN 104371169 A CN104371169 A CN 104371169A
- Authority
- CN
- China
- Prior art keywords
- film
- parts
- polyethylene film
- antibacterial
- antibacterial polyethylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an antibacterial polyethylene film which comprises the following components in parts by weight: 80-100 parts of polyethylene master batch, 0.05-0.09 part of thyme essential oil, 0.6-1 part of citric acid, 3-4 parts of xylitol, 1-5 parts of maleic anhydride, 1-2 parts of nano silicon dioxide or nano calcium carbonate, 0.05-1 part of antioxidant, 2-3 parts of coupling agent and 0.4-0.8 part of dicumyl peroxide. Compared with the prior art, the film can inhibit bacteria around the film from generation. Compared with the common commercially-available PVC (polyvinyl chloride) film, the antibacterial polyethylene film has obvious inhibitory effects on Staphylococcus aureus, Escherichia coli and other bacteria. The antibacterial agent used by the antibacterial polyethylene film is a pure natural plant-extracted antibacterial agent, can be used for a long time, and is safe and nontoxic.
Description
Technical field
The present invention relates to film applications, be specifically related to a kind of polyethylene film, relate to the polyethylene film with bacteriostasis property more specifically.
Background technology
Polyethylene (PVC) film is widely used in the top layer of floor, top ceiling and leather, the superiors of this surface film are paint, the main component in middle layer is polyvinyl chloride, orlop is back of the body coating adhesive, compared with common veneer film, it can merge tightly with other sheet material, within 10 years, even within 15 years, does not come unglued, therefore be loved by the people, become a kind of synthetic materials be widely used.
Traditional PVC film shortcoming bacteria resistance function, though have the research to the PVC film with bacteria resistance function at present, but still Shortcomings.Chinese patent CN103102618A, a kind of TiO2 Ag/PVC compound bacteriostatic film, though this patent adds modification TiO2 Ag in the film, makes film have good bacteriostasis property, but still containing harmful softening agent; Chinese patent CN102101928A, a kind of antimicrobial preservative film, though this patent with the addition of silver ion antimicrobial agent in preservative film, to make it have antibacterial, but wherein still containing phthalic ester plasticizer, and there are some researches show, though silver ion antimicrobial agent has stronger bacteria resistance function, if still harm can be produced to HUMAN HEALTH after accidentally taking in human body.
Thymus vulgaris, the main place of production is France in southern Europe, Spain, Mediterranean Sea state and Egypt, China, belong to evergreen shrubs herbaceous plant, highly not high, leaf is green, flower is pink, thyme oil is then from its flower of distillation and leaf, also somewhat green in moderate yellowish brown, because fragrance has strong herbal medicine and pine tar taste, after being stained with blade of grass juice, taste can be far with oneself, so southern china claims Murraya paniculata (L.) Jack or Leaf and twig of Common Jasminorange.Thyme oil has good fungistatic effect, and the mould common to general environment and bacterium have obvious restraining effect.Current thyme oil is widely used in medicine and household chemicals field, but its applied research in PVC film is very few.
In sum, the deficiency how overcoming prior art existence has become existing PVC film field technical barrier urgently to be resolved hurrily.
Summary of the invention
The object of the invention is to solve the problem of PVC film shortcoming bacteria resistance function in prior art, be to provide a kind of antibacterial polyethylene film, described polyethylene film has bacteria resistance function, environment-protecting asepsis, is widely used in the fields such as building materials furniture film, toy and food product pack.
Concrete technical scheme of the present invention is as follows:
A kind of antibacterial polyethylene film, comprises following raw material according to weight parts:
Preferably comprise following raw material according to weight parts:
Described antioxidant is β-positive octadecanol ester of (3,5-di-tert-butyl-hydroxy phenyl) propionic acid or four [β-(3,5-di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol ester.
Described coupling agent is selected from the one in vinyl three ('beta '-methoxy oxyethyl group), vinyltriethoxysilane, aluminic acid vinegar coupling agent.
Thyme oil oil has fragrant and sweet and strong medicinal herbs taste, taste can spread far, the present invention adopts environmental protection pure natural plant fungistat thyme oil, adopt citric acid, Xylitol and maleic anhydride composite, utilize the synergy of itself and thyme oil, effectively suppress growing of film surrounding bacterial.
Compared with prior art, film of the present invention can suppress the bacteria breed around film, compared with common commercially available PVC film, all has remarkable inhibition to the bacterium such as streptococcus aureus, intestinal bacteria.The fungistat that the present invention uses extracts fungistat for natural plant, can life-time service, safety non-toxic.
Embodiment
Below in conjunction with embodiment, the invention will be further described.
Performance evaluation mode and the standard of implementation:
The comprehensive mechanical property of polyethylene film is passed judgment on by test its tensile strength, elongation at break and angle tear strength.Tensile strength, elongation at break press the test of GB/T 1040-2006 method; Angle tear strength presses the test of QB/T 1130-1991 method.Bacteriostasis property, with reference to QB/T2591-2003 " antibiotic plastic-Anti-microbial Performance Tests method and antibacterial effect " (film applicator coating) test, detects bacterial classification: intestinal bacteria and streptococcus aureus.
Embodiment 1
A kind of antibacterial polyethylene film, is made up of following raw material according to weight parts:
Preparation method of the present invention: according to parts by weight by polyethylene master batch, thyme oil, citric acid, Xylitol, maleic anhydride, nano silicon, β-(3,5-di-tert-butyl-hydroxy phenyl) the positive octadecanol ester of propionic acid, vinyltriethoxysilane and dicumyl peroxide add in homogenizer and be warming up to 80 DEG C and be uniformly mixed, deliver to forcing machine, extruder temperature controls at 120 DEG C, after material is delivered to plastics processing mill, material loading is to rolling press again, calender temperature is 150 DEG C, can obtain finished product after calendering, embossing sizing, cooling.
Carry out anti-microbial property test to the film obtained by the present embodiment: its bacteriostasis property test result is: streptococcus aureus bacteriostasis rate is 75%, intestinal bacteria bacteriostasis rate is 88%.
Embodiment 2
A kind of antibacterial polyethylene film, is made up of following raw material according to weight parts:
Preparation method of the present invention: according to parts by weight by polyethylene master batch, thyme oil, citric acid, Xylitol, maleic anhydride, nano silicon, four [β-(3,5-di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol ester, aluminic acid vinegar coupling agent and dicumyl peroxide add in homogenizer and be warming up to 80 DEG C and be uniformly mixed, deliver to forcing machine, extruder temperature controls at 120 DEG C, after material is delivered to plastics processing mill, material loading is to rolling press again, calender temperature is 150 DEG C, can obtain finished product after calendering, embossing sizing, cooling.
Carry out anti-microbial property test to the film obtained by the present embodiment: its bacteriostasis property test result is: streptococcus aureus bacteriostasis rate is 80%, intestinal bacteria bacteriostasis rate is 90%.
Embodiment 3
A kind of antibacterial polyethylene film, is made up of following raw material according to weight parts:
Preparation method of the present invention: according to parts by weight by polyethylene master batch, thyme oil, citric acid, Xylitol, maleic anhydride, nano silicon, four [β-(3,5-di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol ester, aluminic acid vinegar coupling agent and dicumyl peroxide add in homogenizer and be warming up to 80 DEG C and be uniformly mixed, deliver to forcing machine, extruder temperature controls at 120 DEG C, after material is delivered to plastics processing mill, material loading is to rolling press again, calender temperature is 150 DEG C, can obtain finished product after calendering, embossing sizing, cooling.
Carry out anti-microbial property test to the film obtained by the present embodiment: its bacteriostasis property test result is: streptococcus aureus bacteriostasis rate is 78%, intestinal bacteria bacteriostasis rate is 86%.
Embodiment 4
A kind of antibacterial polyethylene film, is made up of following raw material according to weight parts:
Preparation method of the present invention: according to parts by weight by polyethylene master batch, thyme oil, citric acid, Xylitol, maleic anhydride, nano silicon, four [β-(3,5-di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol ester, aluminic acid vinegar coupling agent and dicumyl peroxide add in homogenizer and be warming up to 80 DEG C and be uniformly mixed, deliver to forcing machine, extruder temperature controls at 120 DEG C, after material is delivered to plastics processing mill, material loading is to rolling press again, calender temperature is 150 DEG C, can obtain finished product after calendering, embossing sizing, cooling.
Carry out anti-microbial property test to the film obtained by the present embodiment: its bacteriostasis property test result is: streptococcus aureus bacteriostasis rate is 74%, intestinal bacteria bacteriostasis rate is 89%.
The mechanical performance data of the polyethylene film obtained by each embodiment is in table 1.
Table 1
As can be seen from Table 1, the polyethylene film that the present invention prepares, on the basis with fungistatic effect, can also meet the performance requriements of plastic film own; Have broad application prospects in fields such as building materials furniture, toy and food product pack.
Claims (4)
1. an antibacterial polyethylene film, is characterized in that comprising following raw material according to weight parts:
2. antibacterial polyethylene film according to claim 1, is characterized in that comprising following raw material according to weight parts:
3. antibacterial polyethylene film according to claim 1 and 2, it is characterized in that described antioxidant is β-(3,5-di-tert-butyl-hydroxy phenyl) the positive octadecanol ester of propionic acid or four [β-(3,5-di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol ester.
4. antibacterial polyethylene film according to claim 1 and 2, is characterized in that described coupling agent is selected from the one in vinyl three ('beta '-methoxy oxyethyl group), vinyltriethoxysilane, aluminic acid vinegar coupling agent.