CN104357847A - Corrosion inhibitor for sulfur removal of ship engine, and preparation method of corrosion inhibitor - Google Patents
Corrosion inhibitor for sulfur removal of ship engine, and preparation method of corrosion inhibitor Download PDFInfo
- Publication number
- CN104357847A CN104357847A CN201410621683.2A CN201410621683A CN104357847A CN 104357847 A CN104357847 A CN 104357847A CN 201410621683 A CN201410621683 A CN 201410621683A CN 104357847 A CN104357847 A CN 104357847A
- Authority
- CN
- China
- Prior art keywords
- parts
- corrosion inhibitor
- preparation
- marine engine
- sulphur removal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a corrosion inhibitor for sulfur removal of a ship engine. The corrosion inhibitor comprises the following components in parts by weight: 28-38 parts of zinc carbonate, 25-32 parts of sodium molybdate, 24-28 parts of mannich base quaternary ammonium slat, 18-25 parts of propanol, 25-35 parts of benzyl chloride, 5-9 parts of adjacent dehydroabietic vanilla aldehyde amine schiff base, and 12-15 parts of stearamide. The prepared corrosion inhibitor can form excellent solubility together with diesel, and can achieve the effect of preventing corrosion as a good corrosion inhibitor of diesel.
Description
Technical field
The present invention relates to a kind of metal protector, be specifically related to a kind of for marine engine sulphur removal corrosion inhibitor and preparation method thereof.
Background technology
Marine engine is the power of boats and ships, and marine engine is subject to the corrosion of diesel oil and high temperature, compressor casing and piston wear larger.
Summary of the invention
Goal of the invention: in order to overcome the deficiencies in the prior art, the invention provides a kind of for marine engine sulphur removal corrosion inhibitor.
Present invention also offers the preparation method of above-mentioned inhibiter.
Technical scheme: for achieving the above object, one provided by the invention is used for marine engine sulphur removal corrosion inhibitor, its compositions in weight percentage consists of the following composition: zinc carbonate 28 ~ 38 parts, Sodium orthomolybdate 25 ~ 32 parts, Mannich base quaternary ammonium salt 24 ~ 28 parts, propyl alcohol 18 ~ 25 parts, Benzyl Chloride 25 ~ 35 parts, dehydroabietylamine o-vanillin Schiff's base 5 ~ 9 parts, stearylamide 12 ~ 15 parts.
Further, its compositions in weight percentage consists of the following composition: zinc carbonate 32 ~ 38 parts, Sodium orthomolybdate 28 ~ 32 parts, Mannich base quaternary ammonium salt 26 ~ 28 parts, propyl alcohol 20 ~ 25 parts, Benzyl Chloride 28 ~ 35 parts, dehydroabietylamine o-vanillin Schiff's base 8 ~ 9 parts, stearylamide 13 ~ 15 parts.
The above-mentioned preparation method for marine engine sulphur removal corrosion inhibitor, described preparation method comprises the steps:
(1) feed composition is taken according to ingredients weight parts according to claim 1;
(2) above-mentioned raw materials is put and heat mixture in a kettle. evenly, be heated to 68 DEG C of high-speed stirring 20 ~ 40min.
Beneficial effect: the present invention, for conventional art, has following advantage:
Product prepared in the present invention can form good solubility with diesel oil, as the inhibiter that diesel oil is good, can reach the effect preventing from corroding in engine.
Embodiment
Below in conjunction with embodiment, the present invention is further described.
embodiment 1:
A kind of for marine engine sulphur removal corrosion inhibitor, its compositions in weight percentage consists of the following composition: zinc carbonate 38 parts, Sodium orthomolybdate 25 parts, Mannich base quaternary ammonium salt 24 parts, propyl alcohol 18 parts, Benzyl Chloride 25 parts, dehydroabietylamine o-vanillin Schiff's base 5 parts, stearylamide 12 parts.
The above-mentioned preparation method for marine engine sulphur removal corrosion inhibitor, described preparation method comprises the steps:
(1) feed composition is taken according to above-mentioned ingredients weight parts;
(2) above-mentioned raw materials is put and heat mixture in a kettle. evenly, be heated to 68 DEG C of high-speed stirring 20 ~ 40min.
embodiment 2:
A kind of for marine engine sulphur removal corrosion inhibitor, its compositions in weight percentage consists of the following composition: zinc carbonate 28 parts, Sodium orthomolybdate 32 parts, Mannich base quaternary ammonium salt 28 parts, propyl alcohol 25 parts, Benzyl Chloride 35 parts, dehydroabietylamine o-vanillin Schiff's base 9 parts, stearylamide 15 parts.
The above-mentioned preparation method for marine engine sulphur removal corrosion inhibitor, described preparation method comprises the steps:
(1) feed composition is taken according to above-mentioned ingredients weight parts;
(2) above-mentioned raw materials is put and heat mixture in a kettle. evenly, be heated to 68 DEG C of high-speed stirring 20 ~ 40min.
embodiment 3:
A kind of for marine engine sulphur removal corrosion inhibitor, its compositions in weight percentage consists of the following composition: zinc carbonate 32 parts, Sodium orthomolybdate 32 parts, Mannich base quaternary ammonium salt 26 parts, propyl alcohol 20 parts, Benzyl Chloride 28 parts, dehydroabietylamine o-vanillin Schiff's base 8 parts, stearylamide 13 parts.
The above-mentioned preparation method for marine engine sulphur removal corrosion inhibitor, described preparation method comprises the steps:
(1) feed composition is taken according to above-mentioned ingredients weight parts;
(2) above-mentioned raw materials is put and heat mixture in a kettle. evenly, be heated to 68 DEG C of high-speed stirring 20 ~ 40min.
embodiment 4:
A kind of for marine engine sulphur removal corrosion inhibitor, its compositions in weight percentage consists of the following composition: zinc carbonate 35 parts, Sodium orthomolybdate 29 parts, Mannich base quaternary ammonium salt 27 parts, propyl alcohol 24 parts, Benzyl Chloride 29 parts, dehydroabietylamine o-vanillin Schiff's base 9 parts, stearylamide 15 parts.
The above-mentioned preparation method for marine engine sulphur removal corrosion inhibitor, described preparation method comprises the steps:
(1) feed composition is taken according to above-mentioned ingredients weight parts;
(2) above-mentioned raw materials is put and heat mixture in a kettle. evenly, be heated to 68 DEG C of high-speed stirring 20 ~ 40min.
The above is only the preferred embodiment of the present invention; be noted that for those skilled in the art; under the premise without departing from the principles of the invention, can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (3)
1., for a marine engine sulphur removal corrosion inhibitor, it is characterized in that; Its compositions in weight percentage consists of the following composition: zinc carbonate 28 ~ 38 parts, Sodium orthomolybdate 25 ~ 32 parts, Mannich base quaternary ammonium salt 24 ~ 28 parts, propyl alcohol 18 ~ 25 parts, Benzyl Chloride 25 ~ 35 parts, dehydroabietylamine o-vanillin Schiff's base 5 ~ 9 parts, stearylamide 12 ~ 15 parts.
2. according to claim 1 for marine engine sulphur removal corrosion inhibitor, it is characterized in that: its compositions in weight percentage consists of the following composition: zinc carbonate 32 ~ 38 parts, Sodium orthomolybdate 28 ~ 32 parts, Mannich base quaternary ammonium salt 26 ~ 28 parts, propyl alcohol 20 ~ 25 parts, Benzyl Chloride 28 ~ 35 parts, dehydroabietylamine o-vanillin Schiff's base 8 ~ 9 parts, stearylamide 13 ~ 15 parts.
3. the preparation method for marine engine sulphur removal corrosion inhibitor described in claim 1 ~ 2, is characterized in that: described preparation method comprises the steps:
(1) feed composition is taken according to ingredients weight parts according to claim 1;
(2) above-mentioned raw materials is put and heat mixture in a kettle. evenly, be heated to 68 DEG C of high-speed stirring 20 ~ 40min.