CN104354424A - Flame-proof solar cell panel back film and preparation method thereof - Google Patents
Flame-proof solar cell panel back film and preparation method thereof Download PDFInfo
- Publication number
- CN104354424A CN104354424A CN201410647882.0A CN201410647882A CN104354424A CN 104354424 A CN104354424 A CN 104354424A CN 201410647882 A CN201410647882 A CN 201410647882A CN 104354424 A CN104354424 A CN 104354424A
- Authority
- CN
- China
- Prior art keywords
- layer
- solar cell
- cell panel
- parts
- flame retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a flame-proof solar cell panel back film and a preparation method thereof, and relates to the technical field of solar cell panel back films. The back film is a compound film structure containing an inner layer, an outer layer and a middle layer, wherein the outer layer is a weather-proof layer, the middle layer is a PET layer, and the inner layer is a weather-proof bonding layer, the outer layer and the middle layer as well as the middle layer and the inner layer are connected through glue, the weather-proof layer is composed of the following components in parts by mass: 45-70 parts of modified organic silicon resin, 5-10 parts of fire retardant, 3-8 parts of nano-ceramic particles, 4-8 parts of a silane coupling agent, 2-6 parts of asbestos fiber, 5-10 parts of a curing agent and 15-25 parts of solvent. By using the flame-proof resin layer as the weather-proof layer, the flame-proof solar cell panel back film disclosed by the invention not only has high thermal tolerance, but also has excellent weather resistance and corrosion resistance, and is an ideal flame-proof solar cell panel back film.
Description
Technical field
The invention belongs to solar energy back film technical field, particularly a kind of flame retardant solar cell panel notacoria and preparation method thereof.
Background technology
Back film of solar cell is one of solar module encapsulating material.The back seal film that solar cell package is used, generally has three-decker, comprises weathering layer, pet layer or intermediate layer and adhesive linkage from top to bottom, and namely five-layer structure is also be provided with adhesive layer in the middle of weathering layer and intermediate layer and intermediate layer and adhesive linkage.
The main performance of back film of solar cell is encapsulation crystalline silicon; therefore it need reach good air exclusion performance, anti-oxidation and moisture resistant performance; good electrical insulation capability must be had simultaneously, the hydrolysis property etc. of binding can be prevented for a long time, with digital preservation crystalline silicon from the erosion in the external world and guarantee crystalline silicon electricity conversion.
Solar panel operationally, because sunlight irradiates, battery panel components local temperature can be caused to raise, cause component strain, more notably, temperature reaches burning-point, assembly catching fire can be caused, infringement battery panel components and surrounding environment, therefore, the fire resistance of back film of solar cell also should come into one's own.
Application number is the patent document " a kind of flame retardant solar battery back film " of 201310392515.6, disclose a kind of back film of solar cell, described notacoria is provided with anti-flammability weathering layer in the one side of base material, at the another side of base material, anti-flammability adhesive linkage is set, described anti-flammability weathering layer and anti-flammability adhesive linkage are formed by the composition containing fluoropolymer membrane resin being coated in substrate surface, and component and the weight portion thereof of the described composition containing fluoropolymer membrane resin are: fluorine resin 75 ~ 165 parts; Fire retardant 0.8 ~ 3 part; 1.5 ~ 15 parts, curing agent; Solvent 50 ~ 120 parts.
It can thus be appreciated that this technical scheme is at intermediate layer (base material) inside and outside coated on both sides flame-retardant layer, outer weather-resistance flame-retardant layer, and the fire-retardant adhesive linkage of internal layer, by the combination of two flame-retardant layers, improves the fire resistance of notacoria.But its rete, take fluorine resin as material of main part, improve fire resistance by the mode adding simple fire retardant, effect is unsatisfactory, although its weatherability is better, still can not use as fire-retardant notacoria.
Summary of the invention
The technical problem that the present invention solves: for above-mentioned deficiency, overcome the defect of prior art, the object of this invention is to provide a kind of flame retardant solar cell panel notacoria and preparation method thereof.
Technical scheme of the present invention: a kind of flame retardant solar cell panel notacoria, for inside and outside two-layer and intermediate layer sandwich diaphragm structure, skin is weathering layer, intermediate layer is pet layer, internal layer is weather-proof adhesive linkage, skin is connected by gluing with intermediate layer and between intermediate layer with internal layer, and weathering layer is made up of each component of following mass fraction: modified organic silicone resin 45-70 part, fire retardant 5-10 part, nano-ceramic particle 3-8 part, silane coupler 4-8 part, asbestos fibre 2-6 part, curing agent 5-10 part and solvent 15-25 part.
As preferably, described fire retardant is at least one of phosphotriester, APP, Firebrake ZB, melamine cyanurate and Noryl.
More preferably, described fire retardant is APP, Firebrake ZB or melamine cyanurate.
More preferably, described fire retardant is melamine cyanurate.
As preferably, described nano-ceramic particle is silicon nitride or nanometer silicon carbide ceramic particle.
As preferably, described curing agent is diethylenetriamine or triethylene tetramine.
As preferably, described solvent is dimethylbenzene or acetone.
A preparation method for flame retardant solar cell panel notacoria, preparation process is as follows:
(1) prepare weathering layer: joined by organic siliconresin in solvent, after mixing, add fire retardant, nano-ceramic particle, asbestos fibre successively, after ultrasonic agitation is even, adds silane coupler and curing agent, constantly stir, after mixing, pour mould into, hot pressing is weathering layer;
(2) outer weathering layer, the weather-proof adhesive linkage of middle pet layer and inner side to be joined lamination by viscose glue, obtain laminar films structural material;
(3) above-mentioned laminar films structural material is carried out vacuum to cold pressing, prepare flame retardant solar cell panel notacoria.
Beneficial effect: flame retardant solar cell panel notacoria provided by the invention is a kind of structure of composite membrane, take PET as intermediate layer, wherein by improving the fire resistance of weathering layer, makes notacoria entirety have good anti-flammability.For reaching good fire resistance, the present invention does not simply add fire retardant, but based on modified organic silicone resin, add fire retardant, and adding asbestos fibre and nano-ceramic particle, nano-ceramic particle has higher temperature tolerance, and can improve corrosion resisting property and the intensity of weathering layer, therefore, the weather resistance of weathering layer, corrosion resisting property and fire resistance can be promoted on the whole.
Therefore, flame retardant solar cell panel notacoria provided by the invention, with the resin bed of flame retardant type for weathering layer, not only has higher temperature tolerance, and its weatherability and corrosion resisting property excellent, be a kind of ideal flame retardant solar cell panel notacoria.
Detailed description of the invention
In order to understand the present invention further, below in conjunction with embodiment, the preferred embodiment of the invention is described, but should be appreciated that these describe just for further illustrating the features and advantages of the present invention, instead of limiting to the claimed invention.
Embodiment 1:
A kind of flame retardant solar cell panel notacoria, for inside and outside two-layer and intermediate layer sandwich diaphragm structure, skin is weathering layer, intermediate layer is pet layer, internal layer is weather-proof adhesive linkage, skin is connected by gluing with intermediate layer and between intermediate layer with internal layer, and weathering layer is made up of each component of following mass fraction: modified organic silicone resin 45 parts, ammonium polyphosphate flame retardant 5 parts, silicon nitride nano ceramic particle 3 parts, silane coupler 4 parts, asbestos fibre 2 parts, diethylenetriamine 5 parts and dimethylbenzene 15 parts.
A preparation method for flame retardant solar cell panel notacoria, preparation process is as follows:
(1) prepare weathering layer: joined by organic siliconresin in solvent, after mixing, add fire retardant, nano-ceramic particle, asbestos fibre successively, after ultrasonic agitation is even, adds silane coupler and curing agent, constantly stir, after mixing, pour mould into, hot pressing is weathering layer;
(2) outer weathering layer, the weather-proof adhesive linkage of middle pet layer and inner side to be joined lamination by viscose glue, obtain laminar films structural material;
(3) above-mentioned laminar films structural material is carried out vacuum to cold pressing, prepare flame retardant solar cell panel notacoria.
Embodiment 2:
A kind of flame retardant solar cell panel notacoria, for inside and outside two-layer and intermediate layer sandwich diaphragm structure, skin is weathering layer, intermediate layer is pet layer, internal layer is weather-proof adhesive linkage, skin is connected by gluing with intermediate layer and between intermediate layer with internal layer, and weathering layer is made up of each component of following mass fraction: modified organic silicone resin 70 parts, fire retardant 10 parts, silicon nitride nano ceramic particle 8 parts, silane coupler 8 parts, asbestos fibre 6 parts, diethylenetriamine 10 parts and dimethylbenzene 25 parts.
A preparation method for flame retardant solar cell panel notacoria, preparation process is as follows:
(1) prepare weathering layer: joined by organic siliconresin in solvent, after mixing, add fire retardant, nano-ceramic particle, asbestos fibre successively, after ultrasonic agitation is even, adds silane coupler and curing agent, constantly stir, after mixing, pour mould into, hot pressing is weathering layer;
(2) outer weathering layer, the weather-proof adhesive linkage of middle pet layer and inner side to be joined lamination by viscose glue, obtain laminar films structural material;
(3) above-mentioned laminar films structural material is carried out vacuum to cold pressing, prepare flame retardant solar cell panel notacoria.
Embodiment 3:
A kind of flame retardant solar cell panel notacoria, for inside and outside two-layer and intermediate layer sandwich diaphragm structure, skin is weathering layer, intermediate layer is pet layer, internal layer is weather-proof adhesive linkage, skin is connected by gluing with intermediate layer and between intermediate layer with internal layer, and weathering layer is made up of each component of following mass fraction: modified organic silicone resin 55 parts, melamine cyanurate 6 parts, nanometer silicon carbide ceramic particle 5 parts, silane coupler 5 parts, asbestos fibre 3 parts, triethylene tetramine 6 parts and 17 parts, acetone.
A preparation method for flame retardant solar cell panel notacoria, preparation process is as follows:
(1) prepare weathering layer: joined by organic siliconresin in solvent, after mixing, add fire retardant, nano-ceramic particle, asbestos fibre successively, after ultrasonic agitation is even, adds silane coupler and curing agent, constantly stir, after mixing, pour mould into, hot pressing is weathering layer;
(2) outer weathering layer, the weather-proof adhesive linkage of middle pet layer and inner side to be joined lamination by viscose glue, obtain laminar films structural material;
(3) above-mentioned laminar films structural material is carried out vacuum to cold pressing, prepare flame retardant solar cell panel notacoria.
Embodiment 4:
A kind of flame retardant solar cell panel notacoria, for inside and outside two-layer and intermediate layer sandwich diaphragm structure, skin is weathering layer, intermediate layer is pet layer, internal layer is weather-proof adhesive linkage, skin is connected by gluing with intermediate layer and between intermediate layer with internal layer, and weathering layer is made up of each component of following mass fraction: modified organic silicone resin 60 parts, fire retardant 7 parts, nanometer silicon carbide ceramic particle 6 parts, silane coupler 6 parts, asbestos fibre 4 parts, triethylene tetramine 8 parts and 19 parts, acetone.
A preparation method for flame retardant solar cell panel notacoria, preparation process is as follows:
(1) prepare weathering layer: joined by organic siliconresin in solvent, after mixing, add fire retardant, nano-ceramic particle, asbestos fibre successively, after ultrasonic agitation is even, adds silane coupler and curing agent, constantly stir, after mixing, pour mould into, hot pressing is weathering layer;
(2) outer weathering layer, the weather-proof adhesive linkage of middle pet layer and inner side to be joined lamination by viscose glue, obtain laminar films structural material;
(3) above-mentioned laminar films structural material is carried out vacuum to cold pressing, prepare flame retardant solar cell panel notacoria.
Embodiment 5:
A kind of flame retardant solar cell panel notacoria, for inside and outside two-layer and intermediate layer sandwich diaphragm structure, skin is weathering layer, intermediate layer is pet layer, internal layer is weather-proof adhesive linkage, skin is connected by gluing with intermediate layer and between intermediate layer with internal layer, and weathering layer is made up of each component of following mass fraction: modified organic silicone resin 65 parts, melamine cyanurate 9 parts, nanometer silicon carbide ceramic particle 7 parts, silane coupler 7 parts, asbestos fibre 5 parts, diethylenetriamine 9 parts and 21 parts, acetone.
A preparation method for flame retardant solar cell panel notacoria, preparation process is as follows:
(1) prepare weathering layer: joined by organic siliconresin in solvent, after mixing, add fire retardant, nano-ceramic particle, asbestos fibre successively, after ultrasonic agitation is even, adds silane coupler and curing agent, constantly stir, after mixing, pour mould into, hot pressing is weathering layer;
(2) outer weathering layer, the weather-proof adhesive linkage of middle pet layer and inner side to be joined lamination by viscose glue, obtain laminar films structural material;
(3) above-mentioned laminar films structural material is carried out vacuum to cold pressing, prepare flame retardant solar cell panel notacoria.
Application number be 201310392515.6 the disclosed technical scheme of patent document " a kind of flame retardant solar battery back film " prepare solar battery back film, be control group; Measure the performance of above-mentioned detailed description of the invention and control group notacoria.
(1) two eight or five degradations
Carry out two eight or five degradations to embodiment 1-5 and control group, result is as shown in table 1:
The weatherability test of table 1 back film of solar cell
| Project | Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Embodiment 5 | Control group |
| Two eight or five aging/h | ≥2000 | ≥2000 | ≥2000 | ≥2000 | ≥2000 | ≥1800 |
As seen from the above table, two eight or five senile experiments of embodiment 1-5 are all more than 2000h, and control group is more than 1800h, and embodiment 1-5 is higher than control group, and therefore, the excellent weather resistance and hard of embodiment 1-5 is in control group.
(2) fire resistance
Measure the burning grade (UL94 standard) of embodiment 1-5 and control group, result is as shown in table 2:
The fire resistance test of table 2 back film of solar cell
| Project | Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Embodiment 5 | Control group |
| Burning grade | V-1 | V-1 | V-1 | V-1 | V-1 | V-0 |
As seen from the above table, the burning grade of embodiment 1-5 is higher than control group, and therefore the fire resistance of embodiment 1-5 is better than control group.
In sum, flame retardant solar cell panel notacoria provided by the invention has excellent weather resistance and fire resistance.
To the above-mentioned explanation of the disclosed embodiments, professional and technical personnel in the field are realized or uses the present invention.To be apparent for those skilled in the art to the multiple amendment of these embodiments, General Principle as defined herein can without departing from the spirit or scope of the present invention, realize in other embodiments.Therefore, the present invention can not be restricted to these embodiments shown in this article, but will meet the widest scope consistent with principle disclosed herein and features of novelty.
Claims (8)
1. a flame retardant solar cell panel notacoria, for inside and outside two-layer and intermediate layer sandwich diaphragm structure, skin is weathering layer, intermediate layer is pet layer, internal layer is weather-proof adhesive linkage, skin is connected by gluing with intermediate layer and between intermediate layer with internal layer, it is characterized in that, weathering layer is made up of each component of following mass fraction: modified organic silicone resin 45-70 part, fire retardant 5-10 part, nano-ceramic particle 3-8 part, silane coupler 4-8 part, asbestos fibre 2-6 part, curing agent 5-10 part and solvent 15-25 part.
2. flame retardant solar cell panel notacoria according to claim 1, is characterized in that: described fire retardant is at least one of phosphotriester, APP, Firebrake ZB, melamine cyanurate and Noryl.
3. flame retardant solar cell panel notacoria according to claim 2, is characterized in that: described fire retardant is APP, Firebrake ZB or melamine cyanurate.
4. flame retardant solar cell panel notacoria according to claim 3, is characterized in that: described fire retardant is melamine cyanurate.
5. flame retardant solar cell panel notacoria according to claim 1, is characterized in that: described nano-ceramic particle is silicon nitride or nanometer silicon carbide ceramic particle.
6. flame retardant solar cell panel notacoria according to claim 1, is characterized in that: described curing agent is diethylenetriamine or triethylene tetramine.
7. flame retardant solar cell panel notacoria according to claim 1, is characterized in that: described solvent is dimethylbenzene or acetone.
8. a preparation method for flame retardant solar cell panel notacoria according to claim 1, it is characterized in that, preparation process is as follows:
(1) prepare weathering layer: joined by organic siliconresin in solvent, after mixing, add fire retardant, nano-ceramic particle, asbestos fibre successively, after ultrasonic agitation is even, adds silane coupler and curing agent, constantly stir, after mixing, pour mould into, hot pressing is weathering layer;
(2) outer weathering layer, the weather-proof adhesive linkage of middle pet layer and inner side to be joined lamination by viscose glue, obtain laminar films structural material;
(3) above-mentioned laminar films structural material is carried out vacuum to cold pressing, prepare flame retardant solar cell panel notacoria.