CN104343013A - 带有果冻效果的柔软且有垂感人造革 - Google Patents

带有果冻效果的柔软且有垂感人造革 Download PDF

Info

Publication number
CN104343013A
CN104343013A CN201310339511.1A CN201310339511A CN104343013A CN 104343013 A CN104343013 A CN 104343013A CN 201310339511 A CN201310339511 A CN 201310339511A CN 104343013 A CN104343013 A CN 104343013A
Authority
CN
China
Prior art keywords
warp thread
artificial leather
fabric
warp yarn
sense
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310339511.1A
Other languages
English (en)
Inventor
冯爱华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WUXI TEBO ELECTRONIC TECHNOLOGY Co Ltd
Original Assignee
WUXI TEBO ELECTRONIC TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WUXI TEBO ELECTRONIC TECHNOLOGY Co Ltd filed Critical WUXI TEBO ELECTRONIC TECHNOLOGY Co Ltd
Priority to CN201310339511.1A priority Critical patent/CN104343013A/zh
Publication of CN104343013A publication Critical patent/CN104343013A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种带有果冻效果的柔软且有垂感人造革。它包括相互粘合的面层（3）和基层（4），还包括复合压制而成的透明膜（1）和彩色膜（2），所述面层（3）上粘合有彩色膜（2）；所述基层（4）采用织物制成，所述织物由经纱一、经纱二和纬纱交叉编织构成，所述经纱一为75D涤棉复合丝，经纱二为麻纤维，所述纬纱为32S棉，所述经纱一和经纱二交替排列。本发明由于透明膜的高透光率和高表面光度，因此表面看上去像果冻般的凝胶效果，满足了人们的需要。本发明所采用的织物柔软且有垂感。

Description

带有果冻效果的柔软且有垂感人造革
技术领域
本发明涉及一种人造革。
背景技术
普通的人造革由基层和面层构成，基层为普通的织物，面层为PVC 塑料层，这样的人造革表面看上去颜色效果单一，满足不了人们的需要。另外，基层存在织物不细腻、不柔软且无有垂感，贴身等不足。
发明内容
本发明的目的在于克服上述不足，提供了一种表面像果冻般凝胶效果的人造革。
本发明的目的是这样实现的：
一种带有果冻效果的柔软且有垂感人造革，其特点是：所述人造革包括相互粘合的面层和基层，还包括复合压制而成的透明膜和彩色膜，所述面层上粘合有彩色膜；所述基层采用织物制成，所述织物由经纱一、经纱二和纬纱交叉编织构成，所述经纱一为75D涤棉复合丝，经纱二为麻纤维，所述纬纱为32S棉，所述经纱一和经纱二交替排列。
本发明一种带有果冻效果的柔软且有垂感人造革，其透明膜的厚度＞0.3mm，透光率≥90%，表面光度在60°角＞80。
本发明的有益效果是：
1、本发明一种带有果冻效果的柔软且有垂感人造革，由于透明膜的高透光率和高表面光度，因此本发明的表面看上去像果冻般的凝胶效果，满足了人们的需要。
2、本发明具有织物细腻、柔软且有垂感，麻纤维的存在使织物不贴身等优点。
附图说明
图1为本发明一种带有果冻效果的柔软且有垂感人造革的结构示意图。
图中：
透明膜1，
彩色膜2，
面层3，
基层4。
具体实施方式
参见图1，本发明一种带有果冻效果的柔软且有垂感人造革，它包括相互粘合的面层3和基层4，还包括复合压制而成的透明膜1和彩色膜2，所述面层3上粘合有彩色膜2。
其中透明膜1的厚度＞0.3mm，透光率≥90%，表面光度在60°角＞80。
所述基层4采用织物制成，所述织物由经纱一、经纱二和纬纱交叉编织构成，所述经纱一为75D涤棉复合丝，经纱二为麻纤维，所述纬纱为32S棉，所述经纱一和经纱二交替排列。

Claims (2)

1.一种带有果冻效果的柔软且有垂感人造革，其特征在于：所述人造革包括相互粘合的面层（3）和基层（4），还包括复合压制而成的透明膜（1）和彩色膜（2），所述彩色膜（2）粘合在面层（3）上；所述基层（4）采用织物制成，所述织物由经纱一、经纱二和纬纱交叉编织构成，所述经纱一为75D涤棉复合丝，经纱二为麻纤维，所述纬纱为32S棉，所述经纱一和经纱二交替排列。
2.根据权利要求1所述的一种带有果冻效果的柔软且有垂感人造革，其特征在于：所述透明膜（1）的厚度＞0.3mm，透光率≥90%，表面光度在60°角＞80。
CN201310339511.1A 2013-08-07 2013-08-07 带有果冻效果的柔软且有垂感人造革 Pending CN104343013A (zh)