CN104342006A - Water-based fire protection finishing coat - Google Patents
Water-based fire protection finishing coat Download PDFInfo
- Publication number
- CN104342006A CN104342006A CN201410590562.6A CN201410590562A CN104342006A CN 104342006 A CN104342006 A CN 104342006A CN 201410590562 A CN201410590562 A CN 201410590562A CN 104342006 A CN104342006 A CN 104342006A
- Authority
- CN
- China
- Prior art keywords
- water
- finish paint
- filler
- based fireproof
- sanitas
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses water-based fire protection finishing coat. The water-based fire protection finishing coat is prepared from 30-40% of water-based polyurethane emulsion, 22-28% of a mixture of polymer-coated nanometer magnesium hydroxide and ammonium polyphosphate which are in a weight ratio of 1:1, 20-25% of deionized water, 8-12% of filler, 5-7% of aids, 0.2-0.5% of a defoaming agent, 0.1-0.5% of preservative and 0.5-0.9% of a thickening agent. The water-based fire protection finishing coat has good fire protection performance.
Description
Technical field
The present invention relates to water-based fireproof finish paint.
Background technology
In each field, widely, as on exterior wall, industrial warehouse, chemical industry, oil, food service industry class basin and pipe surface, the buildingss such as factory building, modernization plant, freezer, house owed by a citizen, office building are first-class in the application of coating.
Tradition is all the coating for organic solvent, and the contaminative of this coating is serious, therefore, now everybody big area bring into use water-borne coatings, and for exterior coating, need the wherein important technological problems solved to be fire prevention, but its fire resistance of existing water-borne coatings is all not good enough.
Summary of the invention
The object of this invention is to provide the water-based fireproof finish paint that a kind of fire resistance is good.
For achieving the above object, water-based fireproof finish paint, is made up of following raw material according to weight percent meter:
Aqueous polyurethane emulsion 30%-40%
Weight ratio is the nano-sized magnesium hydroxide of the polymer overmold of 1:1 and the mixture 22%-28% of ammonium polyphosphate
Deionized water 20%-25%
Filler 8%-12%
Auxiliary agent 5%-7%
Defoamer 0.2%-0.5%
Sanitas 0.1%-0.5%
Thickening material 0.5%-0.9%.
Further, the weight percent of each raw material is:
Aqueous polyurethane emulsion 35%
Weight ratio is the nano-sized magnesium hydroxide of the polymer overmold of 1:1 and the mixture 25% of ammonium polyphosphate
Deionized water 22.6%
Filler 10%
Auxiliary agent 6%
Defoamer 0.4%
Sanitas 0.3%
Thickening material 0.7%.
Further, filler is the one in talcum powder, dicalcium powder, kaolin, process white.
Further, described auxiliary agent is film coalescence aid, and described film coalescence aid is alcohol ether solvent or the cruel kind solvent of alcohol.
Further, described defoamer is polysiloxane-polyether copolymer, and described sanitas is nitrite, and described thickening material is one or both in association type polyurethane thickener.
The invention has the beneficial effects as follows: ammonium polyphosphate is nonpoisonous and tasteless, do not produce etchant gas, water absorbability is little, thermostability is high, there is good fire resistance, but when it uses together with the nano-sized magnesium hydroxide of polymer overmold, both create mutual synergy, thus further increase fire resistance; Meanwhile, coating of the present invention can form that sticking power is 0 grade, hardness is greater than 1H, the coating that water tolerance is greater than 250 hours on substrate surface.
Embodiment
Below in conjunction with specific embodiment, the present invention is further elaborated.
According to weight percent meter, water-based fireproof finish paint of the present invention by 30%-40% aqueous polyurethane emulsion, 22%-28% weight ratio be the mixture of the nano-sized magnesium hydroxide of the polymer overmold of 1:1 and ammonium polyphosphate, 20%-25% deionized water, 8%-12% filler, 5%-7% auxiliary agent, 0.2%-0.5% defoamer, 0.1%-0.5% sanitas, 0.5%-0.9% thickening material be prepared from.Filler is the one in talcum powder, dicalcium powder, kaolin, process white.Described auxiliary agent is film coalescence aid, and described film coalescence aid is alcohol ether solvent or the cruel kind solvent of alcohol.Described defoamer is polysiloxane-polyether copolymer, and described sanitas is nitrite, and described thickening material is one or both in association type polyurethane thickener.
Embodiment 1.
(1) take the mixture of nano-sized magnesium hydroxide that 250g weight ratio is the polymer overmold of 1:1 and ammonium polyphosphate, 226g deionized water, 100g filler and 60g auxiliary agent to stir under the rotating speed of the temperature 400 ~ 800r/min of 70-80 DEG C.
(2) taken 350g aqueous polyurethane emulsion to join in step (1), and reacted 20-40min while stirring in the water-bath of 80-100 DEG C.
(3) take 4g defoamer, 3g sanitas, 7g thickening material join in step (2), under 400 ~ 800r/min speed conditions, stir 5 ~ 10 minutes; Obtain water-based fireproof finish paint after filtration.
Embodiment 2.
(1) take the mixture of nano-sized magnesium hydroxide that 238g weight ratio is the polymer overmold of 1:1 and ammonium polyphosphate, 250g deionized water, 120g filler and 70g auxiliary agent to stir under the rotating speed of the temperature 400 ~ 800r/min of 70-80 DEG C.
(2) taken 300g aqueous polyurethane emulsion to join in step (1), and reacted 20-40min while stirring in the water-bath of 80-100 DEG C.
(3) take 5g defoamer, 8g sanitas, 9g thickening material join in step (2), under 400 ~ 800r/min speed conditions, stir 5 ~ 10 minutes; Obtain water-based fireproof finish paint after filtration.
Embodiment 3.
(1) take the mixture of nano-sized magnesium hydroxide that 220g weight ratio is the polymer overmold of 1:1 and ammonium polyphosphate, 242g deionized water, 80g filler and 50g auxiliary agent to stir under the rotating speed of the temperature 400 ~ 800r/min of 70-80 DEG C.
(2) taken 400g aqueous polyurethane emulsion to join in step (1), and reacted 20-40min while stirring in the water-bath of 80-100 DEG C.
(3) take 2g defoamer, 1g sanitas, 5g thickening material join in step (2), under 400 ~ 800r/min speed conditions, stir 5 ~ 10 minutes; Obtain water-based fireproof finish paint after filtration.
Embodiment 4.
(1) take the mixture of nano-sized magnesium hydroxide that 280g weight ratio is the polymer overmold of 1:1 and ammonium polyphosphate, 200g deionized water, 100g filler and 60g auxiliary agent to stir under the rotating speed of the temperature 400 ~ 800r/min of 70-80 DEG C.
(2) taken 347g aqueous polyurethane emulsion to join in step (1), and reacted 20-40min while stirring in the water-bath of 80-100 DEG C.
(3) take 3g defoamer, 4g sanitas, 5g thickening material join in step (2), under 400 ~ 800r/min speed conditions, stir 5 ~ 10 minutes; Obtain water-based fireproof finish paint after filtration.
Ammonium polyphosphate is nonpoisonous and tasteless, does not produce etchant gas, and water absorbability is little, thermostability is high, has good fire resistance, but when it uses together with the nano-sized magnesium hydroxide of polymer overmold, both create mutual synergy, thus further increase fire resistance; Meanwhile, coating of the present invention can form that sticking power is 0 grade, hardness is greater than 1H, the coating that water tolerance is greater than 250 hours on substrate surface.
Claims (5)
1. water-based fireproof finish paint, is characterized in that, is made up of following raw material according to weight percent meter:
Aqueous polyurethane emulsion 30%-40%
Weight ratio is the nano-sized magnesium hydroxide of the polymer overmold of 1:1 and the mixture 22%-28% of ammonium polyphosphate
Deionized water 20%-25%
Filler 8%-12%
Auxiliary agent 5%-7%
Defoamer 0.2%-0.5%
Sanitas 0.1%-0.5%
Thickening material 0.5%-0.9%.
2. water-based fireproof finish paint according to claim 1, is characterized in that: the weight percent of each raw material is:
Aqueous polyurethane emulsion 35%
Weight ratio is the nano-sized magnesium hydroxide of the polymer overmold of 1:1 and the mixture 25% of ammonium polyphosphate
Deionized water 22.6%
Filler 10%
Auxiliary agent 6%
Defoamer 0.4%
Sanitas 0.3%
Thickening material 0.7%.
3. water-based fireproof finish paint according to claim 1, is characterized in that: filler is the one in talcum powder, dicalcium powder, kaolin, process white.
4. require the water-based fireproof finish paint described in 1 as requested, it is characterized in that: described auxiliary agent is film coalescence aid, described film coalescence aid is alcohol ether solvent or the cruel kind solvent of alcohol.
5. water-based fireproof finish paint according to claim 1, is characterized in that: described defoamer is polysiloxane-polyether copolymer, and described sanitas is nitrite, and described thickening material is one or both in association type polyurethane thickener.