CN104341660A - High-elasticity film - Google Patents
High-elasticity film Download PDFInfo
- Publication number
- CN104341660A CN104341660A CN201410569685.1A CN201410569685A CN104341660A CN 104341660 A CN104341660 A CN 104341660A CN 201410569685 A CN201410569685 A CN 201410569685A CN 104341660 A CN104341660 A CN 104341660A
- Authority
- CN
- China
- Prior art keywords
- parts
- resin
- polyethylene
- film
- elasticity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a high-elasticity film which is prepared from the following raw materials in parts by weight: 9-14 parts of silicone resin, 6-8 parts of polybutylene terephthalate, 7-11 parts of glycerol, 3-7 parts of polyvinylidene fluoride resin, 2-6 parts of kaolin, 5-7 parts of polyvinyl alcohol, 4-11 parts of polytetrafluoroethylene resin, 4-10 parts of polyoxyethylene, 5-10 parts of dimethyldiethoxysilane, 4-7 parts of isocyanate, 5-8 parts of nano SiO2 powder, 1-5 parts of coupling agent, 14-20 parts of HDPE (high-density polyethylene), 5-7 parts of allyl siloxane and 9-14 parts of polyethylene. The high-elasticity film has the advantages of favorable elasticity, high tensile strength and favorable impact resistance.
Description
Technical field
The present invention relates to one and there is elastomeric film.
Background technology
One in the numerous main application of polyethylene is film application, and the liner of such as food bag, public catering or consumer's goods tank, shopping bag, shipment bag, food product packing film, many walls bag liner, product bag, cooked product parcel material, tension wrap up material and pyrocondensation parcel material.The crux physicals of polyethylene film comprises tearing strength, shock strength, tensile property, stiffness and transparency.But existing polyethylene film does not have comprehensive performance, can not meet user demand, therefore people expect a kind of high performance film, meet the use needs of people.
Summary of the invention
For the deficiencies in the prior art, the problem to be solved in the present invention is, provides one to have elastomeric film, has good elasticity, and tensile strength is high simultaneously, shock resistance good.
For solving prior art problem, technical scheme provided by the invention is, one has elastomeric film, and it is made up of the raw material of following parts by weight:
Silicone resin 9-14 part, polybutylene terephthalate 6-8 part, glycerol 7-11 part, polyvinylidene fluoride resin 3-7 part, kaolin 2-6 part, polyvinyl alcohol 5-7 part, teflon resin 4-11 part, polyoxyethylene 4-10 part, dimethyldiethoxysilane 5-10 part, isocyanic ester 4-7 part, nano level SiO2 powder 5-8 part, coupling agent 1-5 part, HDPE14-20 part, Allyl Siloxane 5-7 part, polyethylene 9-14 part.
The invention has the beneficial effects as follows: of the present invention have elastomeric film, has good elasticity, tensile strength is high simultaneously, shock resistance good.
Embodiment
embodiment 1
One has elastomeric film, and it is made up of the raw material of following parts by weight:
Silicone resin 9-14 part, polybutylene terephthalate 6-8 part, glycerol 7-11 part, polyvinylidene fluoride resin 3-7 part, kaolin 2-6 part, polyvinyl alcohol 5-7 part, teflon resin 4-11 part, polyoxyethylene 4-10 part, dimethyldiethoxysilane 5-10 part, isocyanic ester 4-7 part, nano level SiO2 powder 5-8 part, coupling agent 1-5 part, HDPE14-20 part, Allyl Siloxane 5-7 part, polyethylene 9-14 part.
Claims (1)
1. there is an elastomeric film, it is characterized in that: it is made up of the raw material of following parts by weight:
Silicone resin 9-14 part, polybutylene terephthalate 6-8 part, glycerol 7-11 part, polyvinylidene fluoride resin 3-7 part, kaolin 2-6 part, polyvinyl alcohol 5-7 part, teflon resin 4-11 part, polyoxyethylene 4-10 part, dimethyldiethoxysilane 5-10 part, isocyanic ester 4-7 part, nano level SiO2 powder 5-8 part, coupling agent 1-5 part, HDPE14-20 part, Allyl Siloxane 5-7 part, polyethylene 9-14 part.