CN104332319A - Method for manufacturing dye-sensitized solar cell through full screen printing - Google Patents
Method for manufacturing dye-sensitized solar cell through full screen printing Download PDFInfo
- Publication number
- CN104332319A CN104332319A CN201410606019.0A CN201410606019A CN104332319A CN 104332319 A CN104332319 A CN 104332319A CN 201410606019 A CN201410606019 A CN 201410606019A CN 104332319 A CN104332319 A CN 104332319A
- Authority
- CN
- China
- Prior art keywords
- dye
- screen printing
- dyestuff
- silk screen
- slurry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a method for manufacturing a dye-sensitized solar cell (DSSC) through full screen printing. The method comprises the following steps: screen-printing TiO2 paste on conductive glass, sintering and annealing to form a TiO2 layer of a photo-anode; screen-printing paste which is prepared by mixing glass powder, terpilenol and ethyl cellulose around the TiO2 layer and sintering to form an insulating layer, and continuously immersing in dye-containing ethanol solution to form a dye layer; screen-printing paste which is prepared from gel, a pore forming agent and a liquid-state electrolyte on the dye material and heating to form a quasi-solid electrolyte layer; screen-printing carbon black paste on the quasi-solid electrolyte layer and volatizing to form a film so as to form a counter electrode. The new method for manufacturing the DSSC by performing all steps with the screen printing technology is simple and easy, is extremely low in cost and is suitable for large-scale production.
Description
Technical field
The present invention relates to DSSC technical field, be specifically related to a kind of method that full silk screen printing makes dye-sensitized cell (DSSC).
Background technology
DSSC (DSSC), the relatively advantage such as simple manufacture craft low, nontoxic with its abundant raw materials, cost, has attracted the extensive concern of educational circles, industrial circle.Its working mechanism and Mathematical Modeling are just furtherd investigate from that time, comprise electron injection, diffusion and multiple mechanism, and the physical model of whole solar cell.
have employed porous titanium dioxide thin-film, considerably increase the specific area of electrode and the ability of absorbing dye, through with after the bipyridyl ruthenium class dye sensitization of carboxyl, the maximum extinction efficiency of single wavelength can reach more than 98%, and the depth & wideth of DSSC research achieves breakthrough at this point.
Photoelectric efficiency at present based on the small size dye-sensitized cell of titanium deoxid film reaches 13%.But see with regard to the large-area efficiency of DSSC, stability, technical merit, industrialization, scale be realized, also there is the problems such as photoelectric conversion efficiency is not high, secular instability, complex process.
At present, TiO
2be most widely used smooth anode material in DSSC, other broad stopband oxide semiconductor materials are as ZnO, SnO in addition
2, Nb
2o
5deng also under study for action, but with TiO
2combination property best.Due to TiO
2abundance is cheap, nontoxic to be easy to absorbing dye and to become preferred material in dye-sensitized cell.TiO
2the porosity, specific area, particle size, crystal formation, degree of crystallinity etc. of film directly will have influence on Dye Adsorption, electric conductivity, extinction efficiency, the light scattering property of DSSC, thus affect the photoelectric conversion efficiency of DSSC.TiO
2layer must have specific area large as far as possible to adsorb more dye molecule promoting short circuit current to improve dyestuff to the absorption of light.Large specific area adds electron recombination probability simultaneously, and dark current increases.Both is conflict body, needs to reach optimum performance by process optimization.
The preparation method of nano-titanium dioxide film generally comprises Physical and the large class of chemical method two.Physical mainly comprises sputtering method, using vaporization condensation process and molecular beam epitaxy etc.The method preparing nano thin-film mainly chemical method conventional in DSSC research, common chemical method has sol-gel process (Sol-Gel method), predecessor crystalline solid is sublimed into embrane method, electrodeposition process, chemical vapour deposition technique, liquid phase deposition and hydro thermal method etc., and the existence form different according to reactant can be divided into vapor phase method, solid phase method and liquid phase method again.Vapor phase method can control particle size and the shape of product; Solid phase method prepares nano thin-film by the method such as pyrolysis, powdered reaction.Maximum methods is adopted to be liquid phase method, comprising solvent evaporated method, the precipitation method and sol-gel method etc. in current DSSC preparation.
Being prepared in the production of DSSC of titanium dioxide photo anode is a very crucial step, and the pattern of titanium dioxide and character will be directly connected to the photoelectric conversion efficiency of battery.At present conventional sol-gel process constant temperature a period of time and simultaneously add the growth that nitric acid or acetic acid suppresses titanium dioxide, then as hydro-thermal reaction in reactor at a certain temperature.The dispergation of this process need long period, carries out hydro-thermal reaction afterwards, occupies the plenty of time, and condition is not easy to control, and the performance of end product is not good, affects the application of DSSC.
Affecting a lot of because have of DSSC light conversion efficiency, except above-mentioned light anode, also having electrode, dye sensitizing agent, the preparation of redox electrolytes matter and the encapsulation etc. of battery.In traditional DSSC, light anode and to electrode between use liquid electrolyte, but its sealing and electrolyte inject be still a challenge.Usually, sarin film, a kind of hot melt diaphragm seal, is used as the encapsulant assembling battery.Electro-conductive glass bores two or more holes, liquid electrolyte to be filled in battery and to be sealed by epoxy resin with to electrode.Particularly along with the increase of area and the increase of module number, this problem becomes more complicated.
For overcoming liquid electrolyte easy-to-leak liquid and the low inferior weak point of solid electrolyte photoelectric conversion efficiency, people just propose this half-way house of quasi-solid electrolyte.Quasi-solid electrolyte is referred to be strapped in by liquid electrolyte drop in the three-dimensional crosslinked network that gel formed by the method for physics or chemistry and solidifies obtained gel state electrolyte, therefore is usually also referred to as gel electrolyte.The deficiency that quasi-solid electrolyte had not only had the ion mobility similar to liquid electrolyte but also overcome liquid electrolyte prevents the leakage of liquid electrolyte, reduce the vapour pressure of organic solvent, slow down the volatilization of organic solvent, thus improve useful life of dye-sensitized solar cells, therefore obtain and study very widely.In quasi-solid electrolyte, normally used gel has Low Molecular-Weight Gel agent, high molecular polymer gel and nano particle gel etc.
To electrode also known as photocathode.At light anode I
-reduced by the dye molecule of oxidation state, self changes I into
3 -, I
3 -ion is by diffusive migration to photocathode, and the electronics on photocathode is combined and is reduced to I
-be diffused into light anode again and participate in reaction, complete circulation.I
3 -/ I
-regeneration rate have appreciable impact to photronic performance, so to electrode in dye-sensitized cell except needing except good electronic conduction ability as electric negative electrode, another important effect is catalytic action, requires there is catalytic activity high as far as possible to electrode material, accelerates I
3 -/ I
-the switching rate of ion promotes the opto-electronic conversion performance of sensitized cells.Conventional base material does not have above-mentioned performance, experiment shows, simple fluoridizes electro-conductive glass as the photronic performance very low (fill factor, curve factor and photoelectric conversion efficiency are only 6% and 0.02% respectively) to electrode, therefore must modify substrate material surface, form one deck Catalytic Layer at conductive glass surface.
Pt is the material that current catalytic efficiency is the highest, and in experiment, the normal transparent conducting glass of platinum plating that uses is as to electrode.When photocell adopts incident light from the mode of light anode incidence, the Pt layer of light as reflector, can also promote photoelectric conversion efficiency.But be unfavorable for that large-scale promotion uses because Pt resource-constrained is expensive, researchers are just striving to find other suitable material and are carrying out alternative Pt.Material with carbon element enjoys favor and becomes the focus of research because abundance is with low cost, stable chemical nature, catalytic activity are high, have good development prospect.What current report was more is used as to mainly contain graphite, carbon black, carbon nano-tube, activated carbon etc. to the form of the carbon-based material of electrode.The adhesion of the glass of carbon nano-tube and conduction high polymer and conduction is more weak, is unfavorable for photronic long-time stability.Catalytic center due to material with carbon element is positioned on the border of material, and the carbon black material that therefore degree of crystallinity is low, specific area is large has higher catalytic activity than material with carbon element such as graphite, the carbon nano-tube of high-sequential.
The present invention utilizes screen printing technique, instead of the process of other complexity, manufactures DSSC.Screen printing technique is easy to realize a large amount of production, and do not require the production equipment of any costliness.Sinter alternative sarin film with glass dust preparation slurry again through silk screen printing; On dye coating, silk screen printing is by the formulated slurry of gel, pore creating material and liquid electrolyte, heating, forms quasi-solid electrolyte layer; Will by the silk screen printing of carbon black slurry on quasi-solid electrolyte layer, volatilization film forming, shape paired electrode.In addition, be only that carbon black does not need another block electro-conductive glass by silk screen printing on electrolyte to electrode, this will reduce costs to a great extent.
Summary of the invention
The object of the invention is to the deficiency overcoming the existence of above-mentioned prior art, provide a kind of full silk screen printing to make the method for dye-sensitized cell (DSSC).
The object of the invention is to be achieved through the following technical solutions:
The present invention relates to a kind of method that full silk screen printing makes dye-sensitized cell, described method comprises the steps:
A, on electro-conductive glass silk screen printing TiO
2slurry, after 450 DEG C ~ 600 DEG C sintering, annealing in process, forms the TiO of light anode
2layer;
B, slurry glass dust mixing terpinol, ethyl cellulose made, silk screen printing is at described TiO
2the surrounding of layer, sinters under 450 DEG C ~ 600 DEG C conditions, forms insulating barrier;
C, containing dyestuff ethanolic solution in soak 16 ~ 24 hours, formed dye coating;
D, on dye coating, silk screen printing is by the formulated slurry of gel, pore creating material and liquid electrolyte, and 40 DEG C ~ 80 DEG C heating, form quasi-solid electrolyte layer;
E, will by the silk screen printing of carbon black slurry on quasi-solid electrolyte layer, volatilization film forming, shape paired electrode.
Preferably, in steps A, described TiO
2slurry is the business P25TiO purchased
2the slurry that powder is directly configured to.
Preferably, in steps A, after described sintering, annealing, also comprise TiCl
4the step of process, is specially the TiO by having light anode
2layer electro-conductive glass under the condition of 60 DEG C ~ 90 DEG C at the TiCl of 0.2M ~ 1M
430min ~ 90min is flooded, then at 450 DEG C ~ 600 DEG C sintering 30min ~ 90min in solution.
Preferably, described sintering time is 30min ~ 90min; Described sintering, annealing times are 1 ~ 3 time, all carry out TiCl after each annealing
4process.
Preferably, in step B, in described slurry, the consumption of glass dust, ethyl cellulose is 3: 1 ~ 10: 1, then dissolves with appropriate terpinol.
Preferably, in step B, described sintering time is 15min ~ 60min.
Preferably, in step C, described dyestuff is selected from one or more in C101 dyestuff, C106 dyestuff, D5 dyestuff, N1 dyestuff, N3 dyestuff, N719 dyestuff, Z4 dyestuff, black dyestuff, natural dye (as chlorophyll, anthocyanidin, curcumin, flavonoids).
Preferably, described dyestuff is N719 dyestuff, and described is 0.1mM ~ lmM containing the concentration of dyestuff in the ethanolic solution of dyestuff.
Preferably, in step D, in described dyestuff, the mass ratio of gel and pore creating material is 3: 1 ~ 1: 2, and the consumption (quality) of liquid electrolyte is identical with gel.
Preferably, the composition of described liquid electrolyte is selected from
redox couple, Br
-/ Br
2oxidation-reduction pair, SeCN
-/ (SeCN)
2, SCN
-/ (SCN)
2one in oxidation-reduction pair, Bipyridyl cobalt (II/III) oxidation-reduction pair.
Preferably, described gel is the ethanolic solution of the polyacrylic resin containing 0.1g/ml ~ 0.2g/ml, and described pore creating material is toluene.
Preferably, described liquid electrolyte is: in every 10ml methoxypropionitrile, dissolves 0.12g iodine, 0.67g lithium iodide, 1.345g 1,3-methylimidazole salt compounded of iodine, the described liquid electrolyte of 0.8ml 4-tert .-butylpyridine preparation formation.
Preferably, in step D, described heating time is 3min ~ 10min.
Preferably, in step e, in step e, described carbon black slurry is formulated by carbon black, pentyl acetate, ethyl acetate, polyvinyl butyral resin, ethyl cellulose, fluorographite; Every 2g carbon black, the consumption of all the other corresponding components is: 15ml pentyl acetate, 5ml ethyl acetate, 0.35g polyvinyl butyral resin, 1.3g ethyl cellulose and 0.3g fluorographite.
Preferably, the preparation of described carbon black slurry comprises: described pentyl acetate and ethyl acetate are mixed into solvent, more described polyvinyl butyral resin and ethyl cellulose is dissolved in solvent and increases viscosity; Until completely dissolved, described carbon black and fluorographite are added, stir 6 hours ~ 24 hours.
Preferably, described method also comprises: to silk screen printing one deck conductive copper paste on electrode, as the extraction electrode of battery.
Compared with prior art, the present invention has following beneficial effect:
The present invention proposes and use screen printing technique to complete the new method manufacturing DSSC in steps, make method simple, easy and there is extremely low cost, being suitable for large-scale production.Glass dust does form slurry through allotment, can be used for silk screen printing to prepare the insulating barrier of battery.Polyacrylic resin (being now widely used as coating material, capsule shell) is adopted as gel rubber material, add a small amount of toluene as pore creating material after, polyacrylic resin easily can form three-dimensional network and the gel that goes on well thus silk screen printing can prepare quasi-solid electrolyte.Ethyl acetate and pentyl acetate are selected as the solvent of carbon black slurry, and the insoluble solution polyacrylic resin of described solvent makes carbon black slurry silk screen printing can do paired electrode on quasi-solid electrolyte; In addition, described solvent is volatile, and can at room temperature remove without the need to any heating process.
Accompanying drawing explanation
By reading the detailed description done non-limiting example with reference to the following drawings, the other features, objects and advantages of patent of the present invention will become more obvious:
Fig. 1 is that full silk screen printing makes DSSC process chart;
Fig. 2 is the J-V curve of DSSC.
Embodiment
Below in conjunction with the drawings and specific embodiments, the present invention is described in detail.Following examples will contribute to those skilled in the art and understand the present invention further, but not limit the present invention in any form.It should be pointed out that to those skilled in the art, without departing from the inventive concept of the premise, some distortion and improvement can also be made.These all belong to protection scope of the present invention.
embodiment 1
The present embodiment relates to a kind of method of novel making dye-sensitized cell (DSSC), it is characterized in that nearly all step can both have been come by silk screen printing, and without the need to the equipment and process of other complexity, thus can reduce cost of manufacture.As shown in Figure 1, concrete preparation process is as follows for its processing step and process chart:
Step 1: by 3 " silk screen printing TiO on FTO glass (fluoridizing electro-conductive glass)
2slurry one sinters an annealing " to form the TiO of light anode
2(Muffle furnace sintering temperature is 450 DEG C to layer, and the time is 30 minutes, cools with stove.This sintering temperature can be arbitrary value in 450 DEG C ~ 600 DEG C, and sintering time can be arbitrary value in 30min ~ 90min).
Herein, the TiO finally obtained
2light anode can use TiCl
4process, to obtain higher electricity conversion.The concrete steps of process are: get 150ml deionized water, tighten after bottleneck puts into low temperature thermostat bath-6 DEG C maintenance 30min take out with preservative film.Get 1.8ml titanium tetrachloride solution with 2ml syringe, dropwise add freezing after deionized water in, do not stop to stir the TiCl obtaining 0.5mol/L
4solution.The electro-conductive glass containing titanium dioxide semiconductor film of having annealed vertically is put into and fills TiCl
4in the beaker of solution, beaker is put into constant temperature blender with magnetic force, be heated to 65 DEG C, take out electro-conductive glass deionized water rinsing after insulation 30min clean.Above-mentioned gained is put into Muffle furnace again with the electro-conductive glass of titanium dioxide semiconductor film, is heated to 450 DEG C, sintering 30min, closes Muffle furnace power supply, electro-conductive glass is cooled with stove.
Wherein, TiCl
4the concentration of solution is not limited to 0.5mol/L, the arbitrary value in desirable 0.2M ~ 1M.There is the TiO of light anode
2the electro-conductive glass of layer is at TiCl
4dipping temperature in solution can be arbitrary value in 60 DEG C ~ 90 DEG C, and dip time can be arbitrary value in 30min ~ 90min.The sintering temperature of electro-conductive glass after dipping in Muffle furnace can be arbitrary value in 450 DEG C ~ 600 DEG C, and sintering time can be arbitrary value in 30min ~ 90min.
Step 2: 10g glass dust (fusing point 380 DEG C) mixing 1.2g ethyl cellulose is dissolved in the slurry made in 15ml terpinol and is printed on TiO by screen printing technique second version
2the surrounding of layer, and sinter to form insulating barrier under 450 DEG C of conditions.For guaranteeing that insulation is reliable, printing, sintering, annealing process are repeated; Then soak 16 ~ 24 hours in the ethanolic solution of the N719 dyestuff of 0.3mM.
Herein, it is N719 dyestuff that dyestuff can not limit, and also can be N3 dyestuff, Z4 dyestuff, N1 dyestuff, C106 dyestuff, can be even natural dye, and as chlorophyll, anthocyanidin, curcumin, but the efficiency comparison of present stage N719 dyestuff is high.The concentration of the ethanolic solution of N719 dyestuff is also not limited to 0.3mM, can for being selected from the arbitrary value in 0.1mM ~ 1mM.In above-mentioned slurry, the amount ratio of glass dust, ethyl cellulose can be arbitrary value in 10: 1 ~ 3: 1, then dissolves glass dust, ethyl cellulose with appropriate terpinol.Above-mentioned sintering temperature can be arbitrary value in 450 DEG C ~ 600 DEG C; Sintering time can be arbitrary value in 15min ~ 60min.
Step 3: by selecting special gel and pore creating material, then add liquid electrolyte.Concrete steps are: be placed on by 1ml ethanol in a beaker, then in beaker, put into 0.14g polyacrylic resin, seal up beaker with preservative film, be heated to 70 DEG C, until polyacrylic resin dissolves completely.Get 1ml liquid electrolyte and add beaker, stir.Add 0.6g toluene again, then stir.Then gained slurry is printed on dye coating by the 3rd version and (is specially TiO
2layer is not containing the dye coating of the part correspondence of insulating barrier) on, be heated to 40 DEG C (this heating time can be arbitrary value in 40 DEG C ~ 80 DEG C) and keep 4 minutes to prepare quasi-solid electrolyte layer.(gel is that polyacrylic resin is dissolved in ethanol, pore creating material is toluene, the composition of liquid electrolyte is: the mixture of 0.12g iodine, 0.67g lithium iodide, 1.345g 1,3-methylimidazole salt compounded of iodine, 0.8ml 4-tert .-butylpyridine, 10ml methoxypropionitrile.
Herein, the composition of liquid electrolyte also not only for based on
redox couple can also be Br
-/ Br
2oxidation-reduction pair, SeCN
-/ (SeCN)
2, SCN
-/ (SCN)
2oxidation-reduction pair, Bipyridyl cobalt (II/III) oxidation-reduction pair.In dyestuff, the mass ratio of gel and pore creating material can be arbitrary value in 3: 1 ~ 1: 2, and the quality of described liquid electrolyte is identical with gel.In gel (ethanolic solution of polyacrylic resin), the concentration of polyacrylic resin can be arbitrary value in 0.1g/ml ~ 0.2g/ml.
Step 4: with the carbon black slurry made (composition: carbon black, pentyl acetate, ethyl acetate, polyvinyl butyral resin, ethyl cellulose, fluorographite) the 4th version silk screen printing on whole quasi-solid electrolyte layer, this slurry can volatilization film forming in a few minutes at normal temperatures, shape paired electrode.This process repeats 5 times.
The concrete steps of slurry configuration are: first 15ml pentyl acetate and 5ml ethyl acetate are mixed into solvent, then 0.35g polyvinyl butyral resin and 1.3g ethyl cellulose are dissolved in solvent and increase viscosity.After above-mentioned substance dissolves completely, 2g carbon black and 0.3g fluorographite are added mixed slurry, and by magnetic stirrer 12 hours.
Step 5: to silk screen printing one deck conductive copper paste on electrode, as the extraction electrode of battery.
A sun (100mW/cm is simulated as light source with the xenon lamp of the 500W having added AMl.5G filter
2) luminous intensity.Density of photocurrent-the voltage characteristic of solar cell is measured, as the index evaluating this technology with CHI660D electrochemical workstation.When the effective area of DSSC be 0.36 square centimeter (6mm × 6mm square), open circuit voltage is 0.66V as can be seen from Figure 2, short circuit current is 1.39mA (current density, J=3.86mA/cm
2), activity coefficient (FF) is 0.42 as calculated.Therefore, the conversion efficiency obtained is 1.08%, consider this just without the result optimized and use the method cost cheap (the electro-conductive glass price of fluoridizing of the every sheet 12mm × 18mm platinum plating of tradition is approximately 20 yuans, and with carbon black slurry make respective area to electrode cost less than 0.2 yuan; The heat-sealing film price 2 yuans of the every sheet 7mm × 7mm of tradition, and mix insulating barrier cost that slurry prepared by ethyl cellulose prepared by silk screen printing less than 0.1 yuan with glass dust), this conversion efficiency or satisfactory.
Above specific embodiments of the invention are described.It is to be appreciated that the present invention is not limited to above-mentioned particular implementation, those skilled in the art can make various distortion or amendment within the scope of the claims, and this does not affect flesh and blood of the present invention.
Claims (10)
1. full silk screen printing makes a method for dye-sensitized cell, and it is characterized in that, described method comprises the steps:
A, on electro-conductive glass silk screen printing TiO
2slurry, after sintering, annealing in process, forms the TiO of light anode
2layer; Described sintering temperature is 450 DEG C ~ 600 DEG C;
B, slurry glass dust mixing terpinol, ethyl cellulose made, silk screen printing is at described TiO
2the surrounding of layer, sinters under 450 DEG C ~ 600 DEG C conditions, forms insulating barrier;
C, containing dyestuff ethanolic solution in soak 16 ~ 24 hours, formed dye coating;
D, on dye coating, silk screen printing is by the formulated slurry of gel, pore creating material and liquid electrolyte, and 40 DEG C ~ 80 DEG C heating, form quasi-solid electrolyte layer;
E, will by the silk screen printing of carbon black slurry on quasi-solid electrolyte layer, volatilization film forming, shape paired electrode.
2. full silk screen printing according to claim 1 makes the method for dye-sensitized cell, it is characterized in that, in steps A, also comprises TiCl after described sintering, annealing
4the step of process, is specially the TiO by having light anode
2layer electro-conductive glass under the condition of 60 DEG C ~ 90 DEG C at the TiCl of 0.2M ~ 1M
430min ~ 90min is flooded, then at 450 DEG C ~ 600 DEG C sintering 30min ~ 90min in solution.
3. full silk screen printing according to claim 1 makes the method for dye-sensitized cell, and it is characterized in that, in step B, in described slurry, the mass ratio of glass dust, ethyl cellulose is 3: 1 ~ 10: 1; Described sintering time is 15min ~ 60min.
4. full silk screen printing according to claim 1 makes the method for dye-sensitized cell, it is characterized in that, in step C, described dyestuff is selected from one or more in C101 dyestuff, C106 dyestuff, D5 dyestuff, N1 dyestuff, N3 dyestuff, N719 dyestuff, Z4 dyestuff, black dyestuff, natural dye.
5. full silk screen printing according to claim 4 makes the method for dye-sensitized cell, and it is characterized in that, described dyestuff is N719 dyestuff, and described is 0.1mM ~ 1mM containing the concentration of N719 dyestuff in the ethanolic solution of dyestuff.
6. full silk screen printing according to claim 1 makes the method for dye-sensitized cell, and it is characterized in that, in step D, in described dyestuff, the mass ratio of gel and pore creating material is 3: 1 ~ 1: 2, and the quality of described liquid electrolyte is identical with gel.
7. full silk screen printing according to claim 6 makes the method for dye-sensitized cell, it is characterized in that, described gel is the ethanolic solution of the polyacrylic resin containing 0.1g/ml ~ 0.2g/ml; Described pore creating material is toluene.
8. full silk screen printing according to claim 6 makes the method for dye-sensitized cell, it is characterized in that, described liquid electrolyte is: in every 10ml methoxypropionitrile, dissolve 0.12g iodine, 0.67g lithium iodide, 1.345g 1,3-methylimidazole salt compounded of iodine, the described liquid electrolyte of 0.8ml 4-tert .-butylpyridine preparation formation.
9. full silk screen printing according to claim 1 makes the method for dye-sensitized cell, it is characterized in that, in step e, described carbon black slurry is formulated by carbon black, pentyl acetate, ethyl acetate, polyvinyl butyral resin, ethyl cellulose, fluorographite; Every 2g carbon black, corresponding 15ml pentyl acetate, 5ml ethyl acetate, 0.35g polyvinyl butyral resin, 1.3g ethyl cellulose and 0.3g fluorographite.
10. full silk screen printing according to claim 9 makes the method for dye-sensitized cell, it is characterized in that, the preparation of described carbon black slurry comprises: described pentyl acetate and ethyl acetate are mixed into solvent, more described polyvinyl butyral resin and ethyl cellulose is dissolved in solvent and increases viscosity; Until completely dissolved, described carbon black and fluorographite are added, stir 6 hours ~ 24 hours.