CN104326693A - Artificial light green quartz stone and preparation method thereof - Google Patents
Artificial light green quartz stone and preparation method thereof Download PDFInfo
- Publication number
- CN104326693A CN104326693A CN201310309869.XA CN201310309869A CN104326693A CN 104326693 A CN104326693 A CN 104326693A CN 201310309869 A CN201310309869 A CN 201310309869A CN 104326693 A CN104326693 A CN 104326693A
- Authority
- CN
- China
- Prior art keywords
- light green
- artificial light
- quartzite
- parts
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an artificial light green quartz stone comprising the following components by weight: 7-13 parts of glass sand of 2-3 mesh; 7-13 parts of quartz sand of 6-8 mesh; 15-25 parts of quartz sand of 26-40 mesh; 20-25 parts of quartz sand of 40-100 mesh; 20-25 parts of quartz sand of 325 mesh; 7-13 parts of resin; 0.15-0.2 part of a coupling agent; 0.05-0.15 part of a curing agent; 0.007-0.015 part of a promoting agent, 3-6 parts of titanium dioxide and 0.1-0.5 part of phthalocyanine green. The artificial light green quartz stone has the advantages of color stability, bright color, long service life, low cost, and convenient manufacture, fills the existing species of quartz stone patterns and colors, is novel in pattern and unique in color, and greatly satisfies the demand of people for artificial quartz stone in living and production.
Description
Technical field
The invention belongs to building materials technology field, relate to quartzite, especially a kind of artificial light green quartzite and preparation method thereof.
Background technology
Along with the develop rapidly of building material industry, all kinds of building material product grows with each passing day, and especially artificial quartz in lump is more and more subject to concern and the favor of people with its performance superior relative to lithotome.
Artificial quartz in lump, as the term suggests be the synthesis stone made by artificial method, is a kind of Novel decorative board that a kind of quartz crystal by more than 94% adds resin and a small amount of pigment synthetic.It is the large gauge sheet material by the vacuum vibration compacting under certain physics, electrochemical conditions of special machine.Its main raw composition is quartz.Its quality is harder, tight, has the characteristic such as wear-resisting, withstand voltage, high temperature resistant, anticorrosive, impermeable that other finishing material are incomparable.And the floral designs on its surface, color can manual controls, outward appearance can imitate marble, granite etc., the gracefulness of existing natural marble and granitic hard, has again the exquisiteness as timber and warming sense.
At present, along with artificial quartz in lump is subject to the favor of people day by day, therefore people to the pattern of artificial quartz in lump and the requirement of color also more and more higher, existing artificial quartz in lump can not meet the needs of people completely.
By retrieval, find the following patent publication us relevant to patent application of the present invention:
1, a kind of artificial quartz in lump and manufacturing process (CN101337805) thereof, disclose a kind of artificial quartz in lump, it contains quartzite 0 ~ 90%, silica powder 5 ~ 90%, fiber 1 ~ 25%, resin 0.1 ~ 20%, coupling agent 0.1 ~ 5%, solidifying agent 0.1 ~ 5%, glass cullet 0 ~ 70%, broken eyeglass 0 ~ 70%, pigment 0 ~ 5%, shell 0 ~ 5% and tinsel 0 ~ 5%, and per-cent is mass percent.The Resisting fractre intensity of artificial quartz in lump of the present invention, ultimate compression strength and flexural strength improve a lot compared to existing artificial quartz in lump.The invention still further relates to a kind of manufacturing process manufacturing artificial quartz stone plate or bulk and vessel.
2, a kind of artificial quartz in lump and preparation method thereof (CN102040349A), relate to rostone and preparation method thereof, expected to form by A material and B, wherein A material accounts for 70% of gross weight, B material accounts for 30% of gross weight, described A material is mixed by white glass, quartz, silica powder, resin, stock white, black slurry, red slurry, iron oxide yellow, promotor, solidifying agent and coupling agent, and described B material is mixed by black slurry, iron oxide yellow and red slurry.By above A material and B are expected fully to mix according to above-mentioned proportioning, strike off through stirring, extrusion molding, high bake, placement cooling, surrounding, after surface finish, carry out cutting into finished product.The artificial quartz in lump that beneficial effect is made is handsome in appearance, and pattern is distinct, and color is unique, great degree has been enriched kind and the style of artificial quartz in lump, and may be used for various decoration occasions, widely applicable.
3, a kind of artificial quartz in lump and preparation method thereof (CN102040350A), relate to rostone and preparation method thereof, expected to form by A material and B, it is characterized in that: described A material accounts for 50% of gross weight, B material accounts for 50% of gross weight, A material is mixed by mirror glass, white glass, quartz, silica powder, resin, stock white, black slurry, ultramarine, red slurry, promotor, solidifying agent and coupling agent, and B material is mixed by stock white, red slurry, yellow pulp and black slurry.By above A material and B are expected fully to mix according to above-mentioned proportioning, strike off through stirring, extrusion molding, high bake, placement cooling, surrounding, after surface finish, carry out cutting into finished product.The artificial quartz in lump that beneficial effect is made is handsome in appearance, and pattern is distinct, and color is unique, great degree has been enriched kind and the style of artificial quartz in lump, and may be used for various decoration occasions, widely applicable.
4, a kind of artificial quartz in lump and preparation method thereof (CN102040351A), relate to rostone and preparation method thereof, expected to form by A material and B, wherein A material accounts for 60% of gross weight, B material accounts for 40% of gross weight, A material is mixed by quartz, silica powder, resin, stock white, iron oxide yellow, black slurry, red slurry, promotor, solidifying agent and coupling agent, and B material is mixed by iron oxide yellow, black slurry, red slurry and yellow pulp.By above A material and B are expected fully to mix according to above-mentioned proportioning, strike off through stirring, extrusion molding, high bake, placement cooling, surrounding, after surface finish, carry out cutting into finished product.The artificial quartz in lump that beneficial effect is made is handsome in appearance, and pattern is distinct, and color is unique, great degree has been enriched kind and the style of artificial quartz in lump, and may be used for various decoration occasions, widely applicable.
By contrast, there are the different of essence in patent application of the present invention and above-mentioned patent publication us.
Summary of the invention
The object of the invention is to overcome the deficiencies in the prior art part, provide a kind of colour stable, bright, usage period long, and with low cost, artificial light green quartzite easy to make and preparation method thereof.
The technical scheme that the present invention realizes object is:
A kind of artificial light green quartzite, its moiety and parts by weight as follows:
And, described artificial light green quartzite, its moiety and parts by weight as follows:
The preparation method of artificial light green quartzite as above, step is as follows:
After above-mentioned raw materials mixing and stirring, through cloth, vacuum is jolt-squeezed, hot setting, surrounding strike off, fixed thick, grinding, surface finish, edges of boards repairing, the examination and test of products qualified after, monoblock quartzite is cut, obtains artificial light green quartzite finished product.
And the condition that described vacuum is jolt-squeezed is that 0.097 ~-0.1MPa vacuum is jolt-squeezed 180 ~ 220 seconds.
And the condition of described hot setting is the temperature of solidifying is 70 ~ 160 degree, and set time is 8 hours.
Advantage of the present invention and beneficial effect are:
1, the colour stable of artificial quartz in lump of the present invention, bright, usage period are long, and it is with low cost, easy to make, the pattern of existing quartzite and the kind of color are filled up, this artificial quartz in lump novel design, color are unique, greatly meet people in life and the demand to artificial quartz in lump in producing.
2, the inventive method preparation process is convenient and simple, simple to operate, raw material sources extensive, reduces production cost, improves the production efficiency of enterprise.
Embodiment
Below by specific embodiment, the invention will be further described, and following examples are descriptive, is not determinate, can not limit protection scope of the present invention with this.
If no special instructions, the reagent used in the present invention is conventional reagent; If no special instructions, the method used is ordinary method.
Embodiment 1
A kind of artificial light green quartzite, its moiety and parts by weight as follows:
The preparation method of above-mentioned artificial light green quartzite, step is as follows:
After above-mentioned raw materials mixing and stirring, jolt-squeeze (0.097 ~-0.1MPa vacuum is jolt-squeezed 180 ~ 220 seconds) through cloth, vacuum, (temperature of solidification is 70 ~ 160 degree to hot setting, set time is 8 hours), surrounding strikes off, fixed thick, grinding, surface finish, edges of boards repairing, the examination and test of products qualified after, monoblock quartzite is cut, obtains artificial light green quartzite finished product.
Embodiment 2
A kind of artificial light green quartzite, its moiety and parts by weight as follows:
The preparation method of above-mentioned artificial light green quartzite is with embodiment 1.
Embodiment 3
A kind of artificial light green quartzite, its moiety and parts by weight as follows:
The preparation method of above-mentioned artificial light green quartzite is with embodiment 1.
Claims (5)
1. an artificial light green quartzite, is characterized in that: its moiety and parts by weight as follows:
2. artificial light green quartzite according to claim 1, is characterized in that: its moiety and parts by weight as follows:
3. a preparation method for the artificial light green quartzite as described in any one of claim 1 or 2, is characterized in that: step is as follows:
After above-mentioned raw materials mixing and stirring, through cloth, vacuum is jolt-squeezed, hot setting, surrounding strike off, fixed thick, grinding, surface finish, edges of boards repairing, the examination and test of products qualified after, monoblock quartzite is cut, obtains artificial light green quartzite finished product.
4. the preparation method of described artificial light green quartzite according to claim 3, is characterized in that: the condition that described vacuum is jolt-squeezed is that 0.097 ~-0.1MPa vacuum is jolt-squeezed 180 ~ 220 seconds.
5. the preparation method of described artificial light green quartzite according to claim 3, is characterized in that: the condition of described hot setting is the temperature of solidifying is 70 ~ 160 degree, and set time is 8 hours.