CN104315790A - Glass fiber reinforced plastics liner for car refrigerator and preparation method thereof and car refrigerator - Google Patents
Glass fiber reinforced plastics liner for car refrigerator and preparation method thereof and car refrigerator Download PDFInfo
- Publication number
- CN104315790A CN104315790A CN201410629348.7A CN201410629348A CN104315790A CN 104315790 A CN104315790 A CN 104315790A CN 201410629348 A CN201410629348 A CN 201410629348A CN 104315790 A CN104315790 A CN 104315790A
- Authority
- CN
- China
- Prior art keywords
- inner bag
- casing
- glass fabric
- resin
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a glass fiber reinforced plastics liner for a car refrigerator. The glass fiber reinforced plastics liner for the car refrigerator comprises a piece of glass fiber cloth and resin composites, the resin composites are cured on the glass fiber cloth, the mass ratio between the resin composites and the glass fiber cloth is (0.5-0.6): 1, and the resin composites comprise, by mass, 56.5%-66.5% of resins, 30%-40% of aluminum powder, 0.8%-1.2% of accelerant, 1.6%-2.4% of a curing agent and 0.3%-0.7% of pigment. The glass fiber reinforced plastics liner is attractive in appearance, easy to clean, firm, free of deformation and damage and resistant to acid, alkali and corrosion. The period of starting and stopping of the refrigerator with the glass fiber reinforced plastics liner is long, the starting times of a compressor are reduced, and energy consumption is lowered.
Description
Technical field
The present invention relates to refrigerator technical field, particularly relate to a kind of car refrigerator fiberglass inner bag and preparation method thereof, and car refrigerator.
Background technology
The inner bag of car refrigerator has two kinds in the market: one is spliced with aluminium or stainless steel; One uses plastics forming.Front one is easily leaked, unsightly and hard object is run into yielding even damaged, not acid and alkali-resistance, is not easy to clean, and the time booty grown in gap can go bad and give off a peculiar smell.Though rear one is easy to clean, easily aging, impact strength is poor.
Summary of the invention
For solving problem existing in above-mentioned prior art, the invention provides a kind of car refrigerator fiberglass inner bag.
The present invention adopts following technical scheme to realize: a kind of car refrigerator fiberglass inner bag, comprise glass fabric and be solidificated in the resin combination on described glass fabric, the mass ratio of described resin combination and described glass fabric is (0.5 ~ 0.6): 1; Described resin combination comprises resin, aluminium powder, promoter and curing agent, in described resin combination, the mass percent of each component is: resin 56.5% ~ 66.5%, aluminium powder 30% ~ 40%, promoter 0.8% ~ 1.2%, curing agent 1.6% ~ 2.4%, pigment 0.3% ~ 0.7%.
Further, described aluminium powder is replaced by aluminium hydroxide or magnesium hydroxide or aluminium oxide.
The present invention also provides the preparation method of fiberglass inner bag described above, comprises the steps:
1) take described resin, aluminium powder, promoter, curing agent and pigment by formula, mixing and stirring, obtain resin compound;
2) by brush a layer thickness that brush is very thin on the mould scribbling releasing agent be the described resin compound of 0.25mm ~ 0.35mm, then put into baking oven heating, heating-up temperature is 65 DEG C ~ 75 DEG C, takes out after 10min ~ 15min;
3) layer of glass cloth is pasted above the mould after step 2 processes, then with spray gun by even for described resin compound spray attachment on described glass fabric, getting rid of bubble with cylinder roll extrusion again makes described resin compound infiltrate in described glass fabric, put into baking oven heating again, heating-up temperature is 65 DEG C ~ 75 DEG C, takes out after 10min ~ 15min; Afterwards, paste layer of glass cloth again, then with spray gun by even for described resin compound spray attachment on described glass fabric, getting rid of bubble with cylinder roll extrusion again makes described resin compound infiltrate in described glass fabric, put into baking oven heating again, heating-up temperature is 65 DEG C ~ 75 DEG C, takes out after 10min ~ 15min;
4) with cylinder step 3 process after mould above be coated with resin compound described in one deck, put into baking oven heating again, heating-up temperature is 65 DEG C ~ 75 DEG C, takes out after 50min ~ 75min, then uses the compressed air of 0.3MPa ~ 0.4MPa by the fiberglass inner bag demoulding of forming.
The present invention also provides a kind of car refrigerator, comprises fiberglass inner bag as above.
Further, described car refrigerator also comprises casing, knocker, temperature display watch, knob, control panel, mechanical temperature-control, installation board of compressor, machine room cover, condenser, blower tray, fan, compressor assembly, handle, hinge and door body, described fiberglass inner bag is arranged in described casing, and described door body is connected with described casing by described hinge, and described hinge is arranged on the rear wall of described casing, described knocker is arranged on the front side wall of described casing, and described handle is arranged on a left side for described casing, on right side wall, described casing is provided with described control panel, described control panel is provided with described temperature display watch, knob and mechanical temperature-control, described casing bottom of right side is provided with machine room, and described wall box machine room upper place is provided with the described machine room cover covering machine room, is provided with described installation board of compressor, described installation board of compressor is fixed with described condenser bottom described machine room, blower tray and compressor assembly, described blower tray is fixed with described fan, described compressor assembly is connected with described condenser, and described condenser is connected by the evaporimeter being attached to described fiberglass inner bladder outer wall with described fiberglass inner bag, and described evaporimeter is connected with described compressor assembly.
Compared with prior art, the present invention has following beneficial effect: fiberglass inner bag is attractive in appearance, easy to clean, firm indeformable not damaged, goes back acid-fast alkali-proof corrosion-resistant.Adopt the cycle of the machine of stopping of the refrigerator of fiberglass inner bag longer, decrease the start number of times of compressor, reduce energy consumption.
Accompanying drawing explanation
Fig. 1 is the exploded perspective view of car refrigerator of the present invention.
Detailed description of the invention
Below in conjunction with specific embodiments and the drawings, the present invention is described in further detail.
Embodiment 1
As shown in Figure 1, a kind of car refrigerator, comprises casing 1, knocker 2, temperature display watch 3, knob 4, control panel 5, mechanical temperature-control 6, installation board of compressor 7, machine room cover 8, condenser 9, blower tray 10, fan 11, compressor assembly 12, fiberglass inner bag 13, handle 14, hinge 15 and door body 16, described fiberglass inner bag 13 is arranged in described casing 1, described door body 16 is connected with described casing 1 by described hinge 15, described hinge 15 is arranged on the rear wall of described casing 1, described knocker 2 is arranged on the front side wall of described casing 1, and described handle 14 is arranged on a left side for described casing 1, on right side wall, described casing 1 is provided with described control panel 5, described control panel 5 is provided with described temperature display watch 3, knob 4 and mechanical temperature-control 6, be provided with machine room bottom described casing 1, described casing 1 sidewall is provided with the described machine room cover 8 covering machine room, is provided with described installation board of compressor 7 in described machine room, described installation board of compressor 7 is fixed with described condenser 9, blower tray 10 and compressor assembly 12, described blower tray 10 is fixed with described fan 11, described compressor assembly 12 is connected with described condenser 9, described condenser 9 is connected by the evaporimeter being attached to described fiberglass inner bag 13 outer wall with described fiberglass inner bag 13, described evaporimeter is connected with described compressor assembly 12, and described fiberglass inner bag 13 has two storerooms.
Described fiberglass inner bag 13 is made up of glass fabric and the resin combination be solidificated on described glass fabric, and the mass ratio of described resin combination and described glass fabric is 0.5:1; Described resin combination comprises resin, aluminium powder, promoter and curing agent, and in described resin combination, the mass percent of each component is: resin 61.5%, aluminium powder 35%, promoter 1%, curing agent 2%, pigment 0.5%; Preparation method is as follows:
1) take described resin, aluminium powder, promoter, curing agent and pigment by formula, mixing and stirring, obtain resin compound;
2) by brush a layer thickness that brush is very thin on the mould scribbling releasing agent be the described resin compound of 0.3mm, then put into baking oven heating, heating-up temperature is 70 DEG C, takes out after 12min;
3) layer of glass cloth is pasted above the mould after step 2 processes, then with spray gun by even for described resin compound spray attachment on described glass fabric, getting rid of bubble with cylinder roll extrusion again makes described resin compound infiltrate in described glass fabric, put into baking oven heating again, heating-up temperature is 70 DEG C, takes out after 12min; Afterwards, paste layer of glass cloth again, then with spray gun by even for described resin compound spray attachment on described glass fabric, getting rid of bubble with cylinder roll extrusion again makes described resin compound infiltrate in described glass fabric, put into baking oven heating again, heating-up temperature is 70 DEG C, takes out after 12min;
4) with cylinder step 3 process after mould above be coated with resin compound described in one deck, then put into baking oven heating, heating-up temperature is 70 DEG C, takes out after 60min, then uses the compressed air of 0.4MPa by the fiberglass inner bag demoulding of forming.
Embodiment 2
As shown in Figure 1, a kind of car refrigerator, comprises casing 1, knocker 2, temperature display watch 3, knob 4, control panel 5, mechanical temperature-control 6, installation board of compressor 7, machine room cover 8, condenser 9, blower tray 10, fan 11, compressor assembly 12, fiberglass inner bag 13, handle 14, hinge 15 and door body 16, described fiberglass inner bag 13 is arranged in described casing 1, described door body 16 is connected with described casing 1 by described hinge 15, described hinge 15 is arranged on the rear wall of described casing 1, described knocker 2 is arranged on the front side wall of described casing 1, and described handle 14 is arranged on a left side for described casing 1, on right side wall, described casing 1 is provided with described control panel 5, described control panel 5 is provided with described temperature display watch 3, knob 4 and mechanical temperature-control 6, be provided with machine room bottom described casing 1, described casing 1 sidewall is provided with the described machine room cover 8 covering machine room, is provided with described installation board of compressor 7 in described machine room, described installation board of compressor 7 is fixed with described condenser 9, blower tray 10 and compressor assembly 12, described blower tray 10 is fixed with described fan 11, described compressor assembly 12 is connected with described condenser 9, described condenser 9 is connected by the evaporimeter being attached to described fiberglass inner bag 13 outer wall with described fiberglass inner bag 13, described evaporimeter is connected with described compressor assembly 12, and described fiberglass inner bag 13 has two storerooms.
Described fiberglass inner bag 13 is made up of glass fabric and the resin combination be solidificated on described glass fabric, and the mass ratio of described resin combination and described glass fabric is 0.5:1; Described resin combination comprises polybutadiene epoxy resin, aluminium hydroxide, promoter and 590 curing agent, in described resin combination, the mass percent of each component is: polybutadiene epoxy resin 61.5%, aluminium hydroxide 35%, promoter 1%, 590 curing agent 2%, pigment 0.5%; Described promoter is made up of polyethylene polyamine and styrene, and polyethylene polyamine and cinnamic mass ratio are 1:1; Preparation method is as follows:
1) described polybutadiene epoxy resin, aluminium hydroxide, polyethylene polyamine, 590 curing agent and pigment is taken by formula, mixing and stirring, then the styrene adding formula ratio, stir, obtain resin compound;
2) by brush a layer thickness that brush is very thin on the mould scribbling releasing agent be the described resin compound of 0.3mm, then put into baking oven heating, heating-up temperature is 70 DEG C, takes out after 12min;
3) layer of glass cloth is pasted above the mould after step 2 processes, then with spray gun by even for described resin compound spray attachment on described glass fabric, getting rid of bubble with cylinder roll extrusion again makes described resin compound infiltrate in described glass fabric, put into baking oven heating again, heating-up temperature is 70 DEG C, takes out after 12min; Afterwards, paste layer of glass cloth again, then with spray gun by even for described resin compound spray attachment on described glass fabric, getting rid of bubble with cylinder roll extrusion again makes described resin compound infiltrate in described glass fabric, put into baking oven heating again, heating-up temperature is 70 DEG C, takes out after 12min;
4) with cylinder step 3 process after mould above be coated with resin compound described in one deck, then put into baking oven heating, heating-up temperature is 70 DEG C, takes out after 60min, then uses the compressed air of 0.4MPa by the fiberglass inner bag demoulding of forming.
Embodiment 3
As shown in Figure 1, a kind of car refrigerator, comprises casing 1, knocker 2, temperature display watch 3, knob 4, control panel 5, mechanical temperature-control 6, installation board of compressor 7, machine room cover 8, condenser 9, blower tray 10, fan 11, compressor assembly 12, fiberglass inner bag 13, handle 14, hinge 15 and door body 16, described fiberglass inner bag 13 is arranged in described casing 1, described door body 16 is connected with described casing 1 by described hinge 15, described hinge 15 is arranged on the rear wall of described casing 1, described knocker 2 is arranged on the front side wall of described casing 1, and described handle 14 is arranged on a left side for described casing 1, on right side wall, described casing 1 is provided with described control panel 5, described control panel 5 is provided with described temperature display watch 3, knob 4 and mechanical temperature-control 6, be provided with machine room bottom described casing 1, described casing 1 sidewall is provided with the described machine room cover 8 covering machine room, is provided with described installation board of compressor 7 in described machine room, described installation board of compressor 7 is fixed with described condenser 9, blower tray 10 and compressor assembly 12, described blower tray 10 is fixed with described fan 11, described compressor assembly 12 is connected with described condenser 9, described condenser 9 is connected by the evaporimeter being attached to described fiberglass inner bag 13 outer wall with described fiberglass inner bag 13, described evaporimeter is connected with described compressor assembly 12, and described fiberglass inner bag 13 has two storerooms.
Described fiberglass inner bag 13 is made up of glass fabric and the resin combination be solidificated on described glass fabric, and the mass ratio of described resin combination and described glass fabric is 0.55:1; Described resin combination comprises bisphenol A-type alkyd resin, magnesium hydroxide, promoter and pyromellitic acid anhydride, in described resin combination, the mass percent of each component is: bisphenol A-type alkyd resin 66.5%, magnesium hydroxide 30%, promoter 0.8%, pyromellitic acid anhydride 2.4%, pigment 0.3%; Described promoter is made up of methyl ethyl ketone peroxide and cobalt naphthenate, and the mass ratio of methyl ethyl ketone peroxide and cobalt naphthenate is 1:1; Preparation method is as follows:
1) take described bisphenol A-type alkyd resin, magnesium hydroxide, methyl ethyl ketone peroxide, pyromellitic acid anhydride and pigment by formula, then add the cobalt naphthenate of formula ratio, stir, obtain resin compound;
2) by brush a layer thickness that brush is very thin on the mould scribbling releasing agent be the described resin compound of 0.35mm, then put into baking oven heating, heating-up temperature is 75 DEG C, takes out after 10min;
3) layer of glass cloth is pasted above the mould after step 2 processes, then with spray gun by even for described resin compound spray attachment on described glass fabric, getting rid of bubble with cylinder roll extrusion again makes described resin compound infiltrate in described glass fabric, put into baking oven heating again, heating-up temperature is 75 DEG C, takes out after 10min; Afterwards, paste layer of glass cloth again, then with spray gun by even for described resin compound spray attachment on described glass fabric, getting rid of bubble with cylinder roll extrusion again makes described resin compound infiltrate in described glass fabric, put into baking oven heating again, heating-up temperature is 75 DEG C, takes out after 10min;
4) with cylinder step 3 process after mould above be coated with resin compound described in one deck, then put into baking oven heating, heating-up temperature is 75 DEG C, takes out after 50min, then uses the compressed air of 0.5MPa by the fiberglass inner bag demoulding of forming.
Embodiment 4
As shown in Figure 1, a kind of car refrigerator, comprises casing 1, knocker 2, temperature display watch 3, knob 4, control panel 5, mechanical temperature-control 6, installation board of compressor 7, machine room cover 8, condenser 9, blower tray 10, fan 11, compressor assembly 12, fiberglass inner bag 13, handle 14, hinge 15 and door body 16, described fiberglass inner bag 13 is arranged in described casing 1, described door body 16 is connected with described casing 1 by described hinge 15, described hinge 15 is arranged on the rear wall of described casing 1, described knocker 2 is arranged on the front side wall of described casing 1, and described handle 14 is arranged on a left side for described casing 1, on right side wall, described casing 1 is provided with described control panel 5, described control panel 5 is provided with described temperature display watch 3, knob 4 and mechanical temperature-control 6, be provided with machine room bottom described casing 1, described casing 1 sidewall is provided with the described machine room cover 8 covering machine room, is provided with described installation board of compressor 7 in described machine room, described installation board of compressor 7 is fixed with described condenser 9, blower tray 10 and compressor assembly 12, described blower tray 10 is fixed with described fan 11, described compressor assembly 12 is connected with described condenser 9, described condenser 9 is connected by the evaporimeter being attached to described fiberglass inner bag 13 outer wall with described fiberglass inner bag 13, described evaporimeter is connected with described compressor assembly 12, and described fiberglass inner bag 13 has two storerooms.
Described fiberglass inner bag 13 is made up of glass fabric and the resin combination be solidificated on described glass fabric, and the mass ratio of described resin combination and described glass fabric is 0.6:1; Described resin combination comprises S-739 gel coating resin, aluminium oxide, promoter and polyamide curing agent, in described resin combination, the mass percent of each component is: S-739 gel coating resin 56.5%, aluminium oxide 40%, promoter 1.2%, polyamide curing agent 1.6%, pigment 0.7%; Described promoter is made up of benzoperoxide and epoxyeicosatrienoic acid copper, and the mass ratio of benzoperoxide and epoxyeicosatrienoic acid copper is 1:1; Preparation method is as follows:
1) take described S-739 gel coating resin, aluminium oxide, benzoperoxide, polyamide curing agent and pigment by formula, then add the epoxyeicosatrienoic acid copper of formula ratio, stir, obtain resin compound;
2) by brush a layer thickness that brush is very thin on the mould scribbling releasing agent be the described resin compound of 0.25mm, then put into baking oven heating, heating-up temperature is 65 DEG C, takes out after 15min;
3) layer of glass cloth is pasted above the mould after step 2 processes, then with spray gun by even for described resin compound spray attachment on described glass fabric, getting rid of bubble with cylinder roll extrusion again makes described resin compound infiltrate in described glass fabric, put into baking oven heating again, heating-up temperature is 65 DEG C, takes out after 15min; Afterwards, paste layer of glass cloth again, then with spray gun by even for described resin compound spray attachment on described glass fabric, getting rid of bubble with cylinder roll extrusion again makes described resin compound infiltrate in described glass fabric, put into baking oven heating again, heating-up temperature is 65 DEG C, takes out after 15min;
4) with cylinder step 3 process after mould above be coated with resin compound described in one deck, then put into baking oven heating, heating-up temperature is 65 DEG C, takes out after 70min, then uses the compressed air of 0.35MPa by the fiberglass inner bag demoulding of forming.
The foregoing is only preferred embodiment of the present invention, not in order to limit the present invention, all any amendments done within the spirit and principles in the present invention, equivalent replacement and improvement etc., all should be included within protection scope of the present invention.
Claims (5)
1. a car refrigerator fiberglass inner bag, is characterized in that, comprise glass fabric and be solidificated in the resin combination on described glass fabric, the mass ratio of described resin combination and described glass fabric is (0.5 ~ 0.6): 1; Described resin combination comprises resin, aluminium powder, promoter and curing agent, in described resin combination, the mass percent of each component is: resin 56.5% ~ 66.5%, aluminium powder 30% ~ 40%, promoter 0.8% ~ 1.2%, curing agent 1.6% ~ 2.4%, pigment 0.3% ~ 0.7%.
2. car refrigerator fiberglass inner bag as claimed in claim 1, is characterized in that, described aluminium powder is replaced by aluminium hydroxide or magnesium hydroxide or aluminium oxide.
3. the preparation method of fiberglass inner bag as claimed in claim 1, is characterized in that, comprise the steps:
1) take described resin, aluminium powder, promoter, curing agent and pigment by formula, mixing and stirring, obtain resin compound;
2) by brush a layer thickness that brush is very thin on the mould scribbling releasing agent be the described resin compound of 0.25mm ~ 0.35mm, then put into baking oven heating, heating-up temperature is 65 DEG C ~ 75 DEG C, takes out after 10min ~ 15min;
3) layer of glass cloth is pasted above the mould after step 2 processes, then with spray gun by even for described resin compound spray attachment on described glass fabric, getting rid of bubble with cylinder roll extrusion again makes described resin compound infiltrate in described glass fabric, put into baking oven heating again, heating-up temperature is 65 DEG C ~ 75 DEG C, takes out after 10min ~ 15min; Afterwards, paste layer of glass cloth again, then with spray gun by even for described resin compound spray attachment on described glass fabric, getting rid of bubble with cylinder roll extrusion again makes described resin compound infiltrate in described glass fabric, put into baking oven heating again, heating-up temperature is 65 DEG C ~ 75 DEG C, takes out after 10min ~ 15min;
4) with cylinder step 3 process after mould above be coated with resin compound described in one deck, put into baking oven heating again, heating-up temperature is 65 DEG C ~ 75 DEG C, takes out after 50min ~ 75min, then uses the compressed air of 0.3MPa ~ 0.6MPa by the fiberglass inner bag demoulding of forming.
4. a car refrigerator, is characterized in that, comprises fiberglass inner bag as claimed in claim 1 or 2.
5. car refrigerator as claimed in claim 4, is characterized in that, also comprise casing, knocker, temperature display watch, knob, control panel, mechanical temperature-control, installation board of compressor, machine room cover, condenser, blower tray, fan, compressor assembly, handle, hinge and door body, described fiberglass inner bag is arranged in described casing, and described door body is connected with described casing by described hinge, and described hinge is arranged on the rear wall of described casing, described knocker is arranged on the front side wall of described casing, and described handle is arranged on a left side for described casing, on right side wall, described casing is provided with described control panel, described control panel is provided with described temperature display watch, knob and mechanical temperature-control, described casing bottom of right side is provided with machine room, described wall box machine room upper place is provided with the described machine room cover covering machine room, and described machine room inner bottom part is provided with described installation board of compressor, and described installation board of compressor is fixed with described condenser, blower tray and compressor assembly, described blower tray is fixed with described fan, described compressor assembly is connected with described condenser, and described condenser is connected by the evaporimeter being attached to described fiberglass inner bladder outer wall with described fiberglass inner bag, and described evaporimeter is connected with described compressor assembly.