CN104314454B - A kind of preparation method of functional window screening - Google Patents
A kind of preparation method of functional window screening Download PDFInfo
- Publication number
- CN104314454B CN104314454B CN201410425319.9A CN201410425319A CN104314454B CN 104314454 B CN104314454 B CN 104314454B CN 201410425319 A CN201410425319 A CN 201410425319A CN 104314454 B CN104314454 B CN 104314454B
- Authority
- CN
- China
- Prior art keywords
- functional
- yarn
- window screening
- preparation
- activity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention provides a kind of preparation method of functional window screening, the preparation method of this functional window screening, comprise the steps: with the germanium dioxide of hundred nano-scale for primary raw material, composite far-infrared functional auxiliary material, makes semiconductor yarn with fusion method; With the activity of bamboo charcoal charcoal of hundred nano-scale for primary raw material, composite oxide material, makes activity of bamboo charcoal yarn with fusion method; Semiconductor yarn and activity of bamboo charcoal yarn are mixed according to the ratio of 1:0.8, makes functional fibre; Take polyester monofilament as warp-wise yarn, functional fibre is broadwise yarn, forms functional window screening through braiding.The invention has the beneficial effects as follows that warp-wise yarn adopts polyester monofilament, make window screening have good light transmission and intensity, broadwise yarn adopts functional fibre, increases indoor negative ion amount and the Small molecular such as formaldehyde harmful in absorption chamber, benzene, is of value to health.
Description
Technical field
The invention belongs to textile fabrics field, especially relate to a kind of preparation method of functional window screening.
Background technology
Window screening refers generally to a kind of net made for raw material with chemical fibre etc., is widely used on door and window, corridor and prevents small insect from bothering, and generally supports the use with casement.Traditional window screening generally has most that daylighting is soft, the feature of air ventilation and mosquito-insect-proof, but along with expanding economy, the quality of life of people improves day by day, and the demand for the functional window screening that can improve IAQ (indoor air quality) gets more and more.
Summary of the invention
The object of this invention is to provide a kind of preparation method of functional window screening, this window screening has good light transmission and intensity, can improve indoor anion concentration, can also harmful Small molecular in absorption chamber, is of value to health.
For realizing above-mentioned goal of the invention, technical scheme of the present invention is as follows:
A kind of functional window screening, comprise warp-wise yarn and broadwise yarn, described warp-wise yarn is polyester monofilament, and described broadwise yarn is functional fibre, and described functional fibre comprises semiconductor yarn and activity of bamboo charcoal yarn.
Further, in described functional fibre, the mixed proportion of semiconductor yarn and activity of bamboo charcoal yarn is 1:0.8.
A preparation method for functional window screening, comprises the steps:
With the germanium dioxide of hundred nano-scale for primary raw material, composite far-infrared functional auxiliary material, makes semiconductor yarn with fusion method;
With the activity of bamboo charcoal charcoal of hundred nano-scale for primary raw material, composite oxide material, makes activity of bamboo charcoal yarn with fusion method;
Semiconductor yarn and activity of bamboo charcoal yarn are mixed according to the proportion of fibers of 1:0.8, makes functional fibre;
Take polyester monofilament as warp-wise yarn, functional fibre is broadwise yarn, forms functional window screening through braiding.
Further, described far-infrared functional auxiliary material is zirconium dioxide and titanium dioxide.
Further, described oxide material is alumina and quicklime.
Further, the activities of described fusion method comprises section, drying, melt extrudes, cooling forming, oil, drawing-off and winding.
Utilize semiconductor substance under the condition of light and heat, the characteristic of electro transfer can be produced, providing by electronics, negative aeroion under formation microenvironment, negative aeroion not only can improve the air quality with lift-off seal bedroom, strengthens the cohesion of dust, forms sedimentation, negative aeroion is also of value to lifting health simultaneously, and far-infrared functional auxiliary material can increase temperature rise effect of window screening.
The advantage that the present invention has and good effect as follows:
1, adopt the germanium dioxide of hundred nano-scale to be major ingredient, and composite other has the auxiliary material of far-infrared functional, makes functional filament with fusion method, adopt hundred nano-scale raw material both can the function of improving product, particulate can not be caused again the infringement of human body;
2, the bamboo carbon active carbon adopting hundred nano-scale is major ingredient, and other oxide material fusion method composite makes fiber, formaldehyde harmful in Absorbable rod bedroom, the subset materials such as benzene, and utilize can effect of moisture absorption with semiconductor fiber is comprehensively auxiliary joins, promote the initial condition of anion generation;
3, the global design of window screening is light and thin type, warp-wise yarn adopts polyester monofilament, terylene brute force is high, UV resistant performance is good, the photoconductivity of window screening can be increased and ensure the intensity of window screening, broadwise yarn adopts the functional fibre of semiconductor and the mixing of activity of bamboo charcoal yarn, give full play to luminous effect and fuel factor, increase negative aeroion generation, do not affect indoor lighting simultaneously.
Detailed description of the invention
Below in conjunction with specific embodiment, the invention will be further described, but do not limit protection scope of the present invention.
Embodiment
A kind of functional window screening, comprise warp-wise yarn and broadwise yarn, described warp-wise yarn is polyester monofilament, and described broadwise yarn is functional fibre, described functional fibre comprises semiconductor yarn and activity of bamboo charcoal yarn, and in described functional fibre, the mixed proportion of semiconductor yarn and activity of bamboo charcoal yarn is 1:0.8.
A preparation method for functional window screening, comprises the steps:
With the germanium dioxide of hundred nano-scale for primary raw material, composite zirconium dioxide and titanium dioxide, make semiconductor yarn through fusion method;
With the activity of bamboo charcoal charcoal of hundred nano-scale for primary raw material, composite alumina and quicklime, make activity of bamboo charcoal yarn through fusion method;
Semiconductor yarn and activity of bamboo charcoal yarn are mixed according to the proportion of fibers of 1:0.8, makes functional fibre;
Take polyester monofilament as warp-wise yarn, functional fibre is broadwise yarn, forms functional window screening through braiding.
The activities of fusion method is as follows: first through section; Then dry removing moisture, improves the uniformity that section is moisture, cleanliness factor and softening point; Melt extrude, in extrusion, screw rod completes the supply of section again, the melting of section and extruding of melt, makes the effect that material plays mixing and melts simultaneously; Cooling forming afterwards; And with food tray, dewing is carried out to strand and oil; Then carry out drawing-off with drawing godet to strand, drawing godet temperature general control is within the scope of vitrification point 10-20 DEG C; Functional filament is made finally by winding process.
By the functional window screening that above step is made, it is 4000-6000/m under room temperature condition that anion produces concentration
2, the grammes per square metre of integral fabric is 30-50g/m
2, after once using, adsorption rate reaches more than 85%, and color fastness is washable (variable color/staining) 3-4 level, and the 3-4 of resistance to unlubricated friction level, moisture-proof rubs 3 grades, fast light 4 grades, and ultimate strength is 300/N.
Above embodiments of the invention have been described in detail, but described content being only preferred embodiment of the present invention, can not being considered to for limiting practical range of the present invention.All equalizations done according to the present patent application scope change and improve, and all should still belong within patent covering scope of the present invention.
Claims (4)
1. a preparation method for functional window screening, comprises the steps:
With the germanium dioxide of hundred nano-scale for primary raw material, composite far-infrared functional auxiliary material, makes semiconductor fiber with fusion method;
With the activity of bamboo charcoal charcoal of hundred nano-scale for primary raw material, composite oxide material, makes activity of bamboo charcoal fiber with fusion method;
Semiconductor fiber and activity of bamboo charcoal fiber are mixed according to the proportion of fibers of 1:0.8, makes functional fibre;
Take polyester monofilament as warp-wise yarn, functional fibre is broadwise yarn, forms functional window screening through braiding.
2. the preparation method of a kind of functional window screening according to claim 1, is characterized in that: described far-infrared functional auxiliary material is zirconium dioxide and titanium dioxide.
3. the preparation method of a kind of functional window screening according to claim 1, is characterized in that: described oxide material is alumina and quicklime.
4. the preparation method of a kind of functional window screening according to claim 1, is characterized in that: described fusion method comprises following activities: section, dry, melt extrude, cooling forming, oil, drawing-off and winding.