CN104312213A - Multifunctional environment-friendly modified calcium carbonate and preparation method thereof - Google Patents
Multifunctional environment-friendly modified calcium carbonate and preparation method thereof Download PDFInfo
- Publication number
- CN104312213A CN104312213A CN201410507928.9A CN201410507928A CN104312213A CN 104312213 A CN104312213 A CN 104312213A CN 201410507928 A CN201410507928 A CN 201410507928A CN 104312213 A CN104312213 A CN 104312213A
- Authority
- CN
- China
- Prior art keywords
- calcium carbonate
- parts
- powder
- titanium dioxide
- added
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses multifunctional environment-friendly modified calcium carbonate which is characterized by being prepared from the following raw materials in parts by weight: 90-95 parts of calcium carbonate, 3-4 parts of waste hemp rope powder, 2-4 parts of silica fume, 2-3 parts of fly ash, 3-5 parts of gypsum powder, 1-2 parts of glutinous rice glue, 2-3 parts of bone meal, 1-1.2 parts of alkenyl succinic anhydride, 0.8-1 part of polyacrylamide, 6-8 parts of polyethylene powder and 3-4 parts of modified titanium dioxide. According to calcium carbonate disclosed by the invention, waste hemp ropes, coal ash, waste cloth pieces and the like are secondarily used and a macromolecular polymer is added for coating; therefore, calcium carbonate not only has good mechanical property, but also is safe, environment-friendly and energy-saving and consumption-reducing. Moreover, in the production process, modified titanium dioxide is added after wet-process grinding, so that waste of raw materials is avoided. The multifunctional environment-friendly modified calcium carbonate disclosed by the invention is suitable for producing auxiliaries such as plastic, coatings and rubber.
Description
Technical field
The present invention relates to industrial filler field, particularly a kind of multi-functional environment-protection modified calcium carbonate and preparation method thereof.
Background technology
Calcium carbonate is a kind of very important functional inorganic filling, is widely used in the industrial circles such as plastics, rubber, coating and papermaking.In the Application Areas of calcium carbonate, most products belongs to the category of polymkeric substance, such as plastics, rubber, tackiness agent, coating etc., and occupies the important market share.The performance and application of properties-correcting agent to nano-calcium carbonate serves vital role.Such as, dispersion agent add the reunion that can reduce nano particle, improve dispersed; Adding of surface-modifying agent can improve the consistency of nano-calcium carbonate in polymeric system.As can be seen here, dispersion agent and surface-modifying agent are vital for the application of nano-calcium carbonate.But, adding of dispersion agent and surface-modifying agent, make nano-calcium carbonate temperature use window greatly to diminish, reason is that conventional dispersion agent and coupling agent are at high temperature easy to decompose, cause bubble, cracking, defect, distortion etc., thus affect the outward appearance of material, resistance toheat and mechanical property.Change the performance of traditional calcium carbonate product, improving its application performance to meet the needs of novel material, development of new techniques, is calcium carbonate industry urgent problem.
Summary of the invention
The object of this invention is to provide a kind of multi-functional environment-protection modified calcium carbonate and preparation method thereof.
In order to realize object of the present invention, the present invention is by following scheme implementation:
A kind of multi-functional environment-protection modified calcium carbonate, is made up of the raw material of following weight part: calcium carbonate 90-95, useless rope made of hemp powder 3-4, silicon ash 2-4, flyash 2-3, gypsum powder 3-5, glutinous rice glue 1-2, bone meal 2-3, alkenyl succinic anhydride 1-1.2, polyacrylamide 0.8-1, polyethylene powder 6-8, modifying titanium dioxide 3-4;
Described modifying titanium dioxide is made up of the raw material of following weight part: nano titanium oxide 50-60, magnesium hydroxide 2-4, ethyl cellulose 4-6, n-butyl acrylate 5-7, silica powder 3-4, polyisobutene 3-4, Synolac 3-5, Terpineol 350 2-4, water 50-60; Preparation method be first add n-butyl acrylate, nano titanium oxide, magnesium hydroxide, ethyl cellulose, water stirs, form suspension, dry at 45-50 DEG C to water content 2-3%, then polyisobutene, Synolac mix and blend 25-35 minute is added immediately, then all the other remaining components are added, stir under 1200-1500 rev/min of condition, dry at 50-60 DEG C, be ground into ultrafine powder and get final product.
A kind of multi-functional environment-protection modified calcium carbonate of the present invention, be made up of following concrete steps:
(1) calcium carbonate, silicon ash, flyash, gypsum powder, polyethylene powder are added in high-speed kneading machine, be warming up between 70-80 DEG C, insulated and stirred half an hour, continue to add alkenyl succinic anhydride, polyacrylamide, continue to be warming up to 110-130 DEG C, be incubated and pour out after 15-20 minute;
(2) by adding appropriate deionized water and all the other remaining components except modifying titanium dioxide by pouring out material while hot, stirring and grinding 2-3 hour, forming suspension stand-by;
(3) suspension is mixed with modifying titanium dioxide, stir 10-15 minute under 800-1000 rev/min, dry, be ground into ultrafine powder and get final product.
The invention has the beneficial effects as follows: the present invention carries out second stage employ to the useless rope made of hemp, flyash etc., adding high molecular polymer carries out coated, not only there is good mechanical property, and safety and environmental protection, energy-saving and cost-reducing, and in production technique, after wet grinding, add modifying titanium dioxide, do not cause the waste of raw material, the present invention is applicable to producing the auxiliary agents such as plastics, coating, rubber.
Specific embodiments
Below by specific examples, the present invention is described in detail.
A kind of multi-functional environment-protection modified calcium carbonate, is made up of the raw material of following weight part (kilogram): calcium carbonate 90, useless rope made of hemp powder 3, silicon ash 2, flyash 2, gypsum powder 3, glutinous rice glue 1, bone meal 2, alkenyl succinic anhydride 1, polyacrylamide 0.8, polyethylene powder 6, modifying titanium dioxide 3;
Described modifying titanium dioxide is made up of the raw material of following weight part (kilogram): nano titanium oxide 50, magnesium hydroxide 2, ethyl cellulose 4, n-butyl acrylate 5, silica powder 3, polyisobutene 3, Synolac 3, Terpineol 350 2, water 50; Preparation method be first add n-butyl acrylate, nano titanium oxide, magnesium hydroxide, ethyl cellulose, water stirs, form suspension, dry at 45-50 DEG C to water content 2-3%, then polyisobutene, Synolac mix and blend 25-35 minute is added immediately, then all the other remaining components are added, stir under 1200-1500 rev/min of condition, dry at 50-60 DEG C, be ground into ultrafine powder and get final product.
A kind of multi-functional environment-protection modified calcium carbonate of the present invention, be made up of following concrete steps:
(1) calcium carbonate, silicon ash, flyash, gypsum powder, polyethylene powder are added in high-speed kneading machine, be warming up between 70-80 DEG C, insulated and stirred half an hour, continue to add alkenyl succinic anhydride, polyacrylamide, continue to be warming up to 110-130 DEG C, be incubated and pour out after 15-20 minute;
(2) by adding appropriate deionized water and all the other remaining components except modifying titanium dioxide by pouring out material while hot, stirring and grinding 2-3 hour, forming suspension stand-by;
(3) suspension is mixed with modifying titanium dioxide, stir 10-15 minute under 800-1000 rev/min, dry, be ground into ultrafine powder and get final product.
The Performance Detection of modified calcium carbonate of the present invention and ordinary calcium carbonate is compared as follows:
First measure the tap density of the forward and backward calcium carbonate of modification, then join in polyvinyl chloride resin in the ratio of 15% respectively by calcium carbonate good for modification and unmodified water-ground limestone, make sample, the mechanical property respectively both test, comparing result sees the following form:
As can be seen from the above table, the loose bulk density of modified calcium carbonate diminishes, and illustrates that calcium carbonate split fully disperses, and it can also be seen that every mechanical property of modified calcium carbonate is all improved.
Claims (2)
1. a multi-functional environment-protection modified calcium carbonate, it is characterized in that, be made up of the raw material of following weight part: calcium carbonate 90-95, useless rope made of hemp powder 3-4, silicon ash 2-4, flyash 2-3, gypsum powder 3-5, glutinous rice glue 1-2, bone meal 2-3, alkenyl succinic anhydride 1-1.2, polyacrylamide 0.8-1, polyethylene powder 6-8, modifying titanium dioxide 3-4;
Described modifying titanium dioxide is made up of the raw material of following weight part: nano titanium oxide 50-60, magnesium hydroxide 2-4, ethyl cellulose 4-6, n-butyl acrylate 5-7, silica powder 3-4, polyisobutene 3-4, Synolac 3-5, Terpineol 350 2-4, water 50-60; Preparation method be first add n-butyl acrylate, nano titanium oxide, magnesium hydroxide, ethyl cellulose, water stirs, form suspension, dry at 45-50 DEG C to water content 2-3%, then polyisobutene, Synolac mix and blend 25-35 minute is added immediately, then all the other remaining components are added, stir under 1200-1500 rev/min of condition, dry at 50-60 DEG C, be ground into ultrafine powder and get final product.
2. a kind of multi-functional environment-protection modified calcium carbonate according to claim 1, is characterized in that, be made up of following concrete steps:
(1) calcium carbonate, silicon ash, flyash, gypsum powder, polyethylene powder are added in high-speed kneading machine, be warming up between 70-80 DEG C, insulated and stirred half an hour, continue to add alkenyl succinic anhydride, polyacrylamide, continue to be warming up to 110-130 DEG C, be incubated and pour out after 15-20 minute;
(2) by adding appropriate deionized water and all the other remaining components except modifying titanium dioxide by pouring out material while hot, stirring and grinding 2-3 hour, forming suspension stand-by;
(3) suspension is mixed with modifying titanium dioxide, stir 10-15 minute under 800-1000 rev/min, dry, be ground into ultrafine powder and get final product.