CN104295805A - Rapid transport pipeline for concrete - Google Patents
Rapid transport pipeline for concrete Download PDFInfo
- Publication number
- CN104295805A CN104295805A CN201410407228.2A CN201410407228A CN104295805A CN 104295805 A CN104295805 A CN 104295805A CN 201410407228 A CN201410407228 A CN 201410407228A CN 104295805 A CN104295805 A CN 104295805A
- Authority
- CN
- China
- Prior art keywords
- minute
- concrete
- percent
- transportation pipeline
- shaping
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of transport equipment manufacturing, in particular to a rapid transport pipeline for concrete. The rapid transport pipeline is characterized by comprising 41 percent of cast iron, 10 percent of antioxygen, 15 percent of silicone oil, seven percent of graphite, seven percent of boric acid, seven percent of calcium oxide, 10 percent of rubber liquid and three percent of curing agents. A method of the rapid transport pipeline is reasonable, the ratio is clear, and manufacturing is convenient and fast.
Description
Technical field:
The present invention relates to haulage device manufacturing technology field, be specifically related to a kind of concrete fast transportation pipeline.
Background technique:
Concrete, referred to as " concrete (t ó ng) ": refer to the general designation being cemented to overall engineered composite material by gelatinization material by gathering materials.Usually concrete one word said refers to makes gelatinization material with cement, and sand, masonry gather materials; Coordinate by a certain percentage with water (can contain admixture and admixture), the cement concrete obtained through stirring, also claims normal concrete, and it is widely used in civil engineering.
And concrete is entering stirrer or when pouring out from stirrer, or enter some other place and all need to use delivery pipe, but because concrete weight ratio is larger, long conveying may cause delivery pipe to occur displacement or fracture, so just brings many unnecessary troubles.
Summary of the invention:
Technical problem to be solved by this invention is to overcome existing technological deficiency and provides that a kind of method is reasonable, proportioning is clear, a kind of concrete fast transportation pipeline of easy making process.
Technical problem to be solved by this invention adopts following technological scheme to realize:
A kind of concrete fast transportation pipeline, is characterized in that: comprise following composition,
Present invention also offers a kind of preparation method of concrete fast transportation pipeline, comprise the following steps,
Step one, by the pig iron in the melting furnace of the high temperature of 780-860 DEG C, fusing 30-47 minute, then take out liquid, be placed in the constant temperature oven of 650-740 DEG C and keep temperature;
Step 2, to be placed in shredder by graphite and to pulverize 5-12 minute, pulverizing limit, limit is stirred, and is ground into Powdered;
Step 3, rubber liquid to be placed in clean glass container, inwardly to add curing agent, and stir mixing in 2-4 minute;
Step 4, successively the blending agent of step 3, pig iron liquid, silicone oil, calcium oxide, silicone oil, plumbago, boric acid, antioxidant are put into shaping box successively and carried out shaping;
Step 5, after shaping 20-30 minute, carry out the cold cooling of air, lower the temperature after 10-18 minute and take out;
In environment that is clean, that ventilate, place 5-10 minute after step 6, taking-up, then carry out polishing, polishing.
Beneficial effect of the present invention is: the proportioning of above-mentioned material is clear, and step for temperature, the time require clear and definite description, operate so very convenient.
Embodiment:
The technological means realized to make the present invention, creation characteristic, reaching object and effect is easy to understand, setting forth the present invention further below.
A kind of concrete fast transportation pipeline, is characterized in that: comprise following composition,
Present invention also offers a kind of preparation method of concrete fast transportation pipeline, comprise the following steps,
Step one, by the pig iron in the melting furnace of the high temperature of 780-860 DEG C, fusing 30-47 minute, then take out liquid, be placed in the constant temperature oven of 650-740 DEG C and keep temperature;
Step 2, to be placed in shredder by graphite and to pulverize 5-12 minute, pulverizing limit, limit is stirred, and is ground into Powdered;
Step 3, rubber liquid to be placed in clean glass container, inwardly to add curing agent, and stir mixing in 2-4 minute;
Step 4, successively the blending agent of step 3, pig iron liquid, silicone oil, calcium oxide, silicone oil, plumbago, boric acid, antioxidant are put into shaping box successively and carried out shaping;
Step 5, after shaping 20-30 minute, carry out the cold cooling of air, lower the temperature after 10-18 minute and take out;
In environment that is clean, that ventilate, place 5-10 minute after step 6, taking-up, then carry out polishing, polishing.
More than show and describe basic principle of the present invention and major character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (2)
1. a concrete fast transportation pipeline, is characterized in that: comprise following composition,
2. a kind of concrete fast transportation pipeline according to claim 1, is characterized in that: the preparation method that present invention also offers a kind of concrete fast transportation pipeline, comprises the following steps,
Step one, by the pig iron in the melting furnace of the high temperature of 780-860 DEG C, fusing 30-47 minute, then take out liquid, be placed in the constant temperature oven of 650-740 DEG C and keep temperature;
Step 2, to be placed in shredder by graphite and to pulverize 5-12 minute, pulverizing limit, limit is stirred, and is ground into Powdered;
Step 3, rubber liquid to be placed in clean glass container, inwardly to add curing agent, and stir mixing in 2-4 minute;
Step 4, successively the blending agent of step 3, pig iron liquid, silicone oil, calcium oxide, silicone oil, plumbago, boric acid, antioxidant are put into shaping box successively and carried out shaping;
Step 5, after shaping 20-30 minute, carry out the cold cooling of air, lower the temperature after 10-18 minute and take out;
In environment that is clean, that ventilate, place 5-10 minute after step 6, taking-up, then carry out polishing, polishing.