CN104293034A - Relief sculpture top coating - Google Patents
Relief sculpture top coating Download PDFInfo
- Publication number
- CN104293034A CN104293034A CN201410501385.XA CN201410501385A CN104293034A CN 104293034 A CN104293034 A CN 104293034A CN 201410501385 A CN201410501385 A CN 201410501385A CN 104293034 A CN104293034 A CN 104293034A
- Authority
- CN
- China
- Prior art keywords
- parts
- top coating
- embossment
- coating
- pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a relief sculpture top coating which comprises the following components in parts by weight: 40-50 parts of organosilicone modified acrylic resin (50% of solid), 1-3 parts of a dispersing agent, 1-2 parts of a flatting agent, 15-25 parts of titanium dioxide, 3-8 parts of pigment, 15-25 parts of methylbenzene and 0.2-1 part of organic silicon oil. The relief sculpture top coating provided by the invention is good in decoration effect, resistant to low temperature, good in adhesion property and easy to construct.
Description
Technical field
The present invention relates to a kind of coating, specifically refer to a kind of embossment overlay coating.
Background technology
Textured coating also claims plastic-blasting coating, concavo-convex coated coating belongs to complex layer coating kind.Be widely used in inside and outside wall decoration, texture is stronger.Be made up of the closed end, undercoat, main coating and Lacquer finish coating.Main coating is to provide the main coating of decorative pattern texture, divides polymer cement class, silicates, synthetic resin emulsion class and reflection curing synthetic resin emulsion class by filmogen kind.Textured coating belongs to rigidity mastic coatings, and its viscosity scope is greatly between 3-20Pa, s.The similar mastic coatings of the mode of production, FAQs also similar mastic coatings in production and construction.
Summary of the invention
For the deficiency that prior art exists, technical problem to be solved by this invention is, provides a kind of embossment overlay coating, good decorating effect, and low temperature resistant, tack is good, is easy to construction.
For solving the problems of the technologies described above, the technical solution used in the present invention is, a kind of embossment overlay coating, comprises the component of following weight proportion: organosilicon modified crylic acid resin (50% solid), 40-50 part; Dispersion agent, 1-3 part; Flow agent, 1-2 part; Titanium dioxide, 15-25 part; Pigment, 3-8 part; Toluene, 15-25 part; Organic silicone oil, 0.2-1 part.
Above-mentioned embossment overlay coating, comprises the component of following weight proportion: organosilicon modified crylic acid resin (50% solid), 45 parts; Dispersion agent, 2 parts; Flow agent, 1 part; Titanium dioxide, 20 parts; Pigment, 5 parts; Toluene, 20 parts; Organic silicone oil, 0.5 part.
Tool of the present invention has the following advantages and beneficial effect:
A kind of embossment overlay coating provided by the invention, good decorating effect, low temperature resistant, tack is good, is easy to construction.
embodiment
embodiment 1
The embossment overlay coating of the present embodiment, comprises the component of following weight proportion: organosilicon modified crylic acid resin (50% solid), 45 parts; Dispersion agent, 2 parts; Flow agent, 1 part; Titanium dioxide, 20 parts; Pigment, 5 parts; Toluene, 20 parts; Organic silicone oil, 0.5 part.
embodiment 2
The technical solution used in the present invention is, a kind of embossment overlay coating, comprises the component of following weight proportion: organosilicon modified crylic acid resin (50% solid), 40 parts; Dispersion agent, 1 part; Flow agent, 1 part; Titanium dioxide, 15 parts; Pigment, 3 parts; Toluene, 15 parts; Organic silicone oil, 0.2 part.
embodiment 3
The technical solution used in the present invention is, a kind of embossment overlay coating, comprises the component of following weight proportion: organosilicon modified crylic acid resin (50% solid), 50 parts; Dispersion agent, 3 parts; Flow agent, 2 parts; Titanium dioxide, 25 parts; Pigment, 8 parts; Toluene, 25 parts; Organic silicone oil, 1 part.
The above is only to preferred embodiment of the present invention, and be not do other forms of restriction to the present invention, any those skilled in the art may utilize the technology contents of above-mentioned announcement to be changed or be modified as the Equivalent embodiments of equivalent variations.But, everyly do not depart from technical solution of the present invention content, according to technical spirit of the present invention to any simple modification made for any of the above embodiments, equivalent variations and remodeling, still belong to the protection domain of technical solution of the present invention.
Claims (2)
1. an embossment overlay coating, is characterized in that: the component comprising following weight proportion: organosilicon modified crylic acid resin (50% solid), 40-50 part; Dispersion agent, 1-3 part; Flow agent, 1-2 part; Titanium dioxide, 15-25 part; Pigment, 3-8 part; Toluene, 15-25 part; Organic silicone oil, 0.2-1 part.
2. embossment overlay coating according to claim 1, is characterized in that: the component comprising following weight proportion: organosilicon modified crylic acid resin (50% solid), 45 parts; Dispersion agent, 2 parts; Flow agent, 1 part; Titanium dioxide, 20 parts; Pigment, 5 parts; Toluene, 20 parts; Organic silicone oil, 0.5 part.