CN104292907A - Anti-photolysis anti-corrosive acrylic coating - Google Patents
Anti-photolysis anti-corrosive acrylic coating Download PDFInfo
- Publication number
- CN104292907A CN104292907A CN201410622136.6A CN201410622136A CN104292907A CN 104292907 A CN104292907 A CN 104292907A CN 201410622136 A CN201410622136 A CN 201410622136A CN 104292907 A CN104292907 A CN 104292907A
- Authority
- CN
- China
- Prior art keywords
- acrylic coating
- anticorrosion
- water
- coating
- titanium dioxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anti-photolysis anti-corrosive acrylic coating which comprises the following components in percentage by weight: 32%-48% of an acrylate composition, 25%-31% of epoxy resin, 1%-5% of a curing agent, 12%-28% of talcum powder, 2%-10% of nano zinc, 10%-25% of titanium dioxide and the balance of water. By adding titanium dioxide and the talcum powder, the coating has a very good overall reflection effect, generates a small amount of volatile gas in light, and is not irritating.
Description
Technical field
The present invention relates to marine finish field, relate in particular to a kind of marine finish of antiseptic power brilliance.
Background technology
Existing protective system mostly is acrylate paint, decomposes under sunlight and high temperature, and after decomposing, resistance to corrosion will decline.And take into account anti-light decomposition and possess the coating of antiseptic power, meet also not having of ship domain at present.
Summary of the invention
Goal of the invention: the object of this invention is to provide a kind of a kind of coating of slow, the effective rot-resistant of decomposition rate being specially adapted for ship domain.
Technical scheme: in order to realize foregoing invention object, the anticorrosion acrylic coating of the anti-light decomposition of one of the present invention, comprises following component by mass percentage: acrylate composition 32 ~ 48%; Epoxy resin 25 ~ 31%; Solidifying agent 1 ~ 5%; Talcum powder 12 ~ 28%; Nano-Zinc 2 ~ 10%; Titanium dioxide 10 ~ 25%; All the other are water.
As preferred version of the present invention, described coating comprises by mass percentage: acrylate composition 36%; Epoxy resin 28%; Solidifying agent 3%; Talcum powder 18%; Nano-Zinc 4%; Titanium dioxide 15%; All the other are water.
Described acrylate composition is made up of by the mixing of 2:1:1 mass ratio methoxy poly (ethylene glycol) mono acrylic ester, Triethylene glycol diacrylate, Rocryl 410.
The particle diameter of described Nano-Zinc is not more than 100 nanometers.
Described water is deionized water.
Acrylate composition of the present invention includes but not limited to any three kinds or more combination in tetrahydrofuran methyl acrylate, phenoxyethyl methacrylate, methoxy poly (ethylene glycol) mono acrylic ester, lauryl methacrylate, methacrylic acid tetradecyl ester, methacrylic acid cetyl ester, polyethyleneglycol diacrylate, Triethylene glycol diacrylate, Propenoic acid, 2-methyl, isobutyl ester, hydroxyethyl methylacrylate, Rocryl 410.
Beneficial effect: the anticorrosion acrylic coating of the anti-light decomposition of one of the present invention is by adding titanium dioxide, and talcum powder, make integral inverted light effect very outstanding, body of getting angry under illumination is few, and is not pungent.
Embodiment
Technical scheme: in order to realize foregoing invention object, the anticorrosion acrylic coating of the anti-light decomposition of one of the present invention, comprises following component by mass percentage: acrylate composition 32 ~ 48%; Epoxy resin 25 ~ 31%; Solidifying agent 1 ~ 5%; Talcum powder 12 ~ 28%; Nano-Zinc 2 ~ 10%; Titanium dioxide 10 ~ 25%; All the other are water.As preferred version of the present invention, described coating comprises by mass percentage: acrylate composition 36%; Epoxy resin 28%; Solidifying agent 3%; Talcum powder 18%; Nano-Zinc 4%; Titanium dioxide 15%; All the other are water.Described acrylate composition is made up of by the mixing of 2:1:1 mass ratio methoxy poly (ethylene glycol) mono acrylic ester, Triethylene glycol diacrylate, Rocryl 410.The particle diameter of described Nano-Zinc is not more than 100 nanometers.Described water is deionized water.
The above is only the preferred embodiment of the present invention; be noted that for those skilled in the art; under the premise without departing from the principles of the invention, can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (4)
1. the anticorrosion acrylic coating of anti-light decomposition, is characterized in that, comprises following component by mass percentage:
Acrylate composition 32 ~ 48%;
Epoxy resin 25 ~ 31%;
Solidifying agent 1 ~ 5%;
Talcum powder 12 ~ 28%;
Nano-Zinc 2 ~ 10%;
Titanium dioxide 10 ~ 25%;
All the other are water.
2. the anticorrosion acrylic coating of the anti-light decomposition of one according to claim 1, is characterized in that: described acrylate composition is made up of by the mixing of 2:1:1 mass ratio methoxy poly (ethylene glycol) mono acrylic ester, Triethylene glycol diacrylate, Rocryl 410.
3. the anticorrosion acrylic coating of the anti-light decomposition of one according to claim 1, is characterized in that: the particle diameter of described Nano-Zinc is not more than 100 nanometers.
4. the anticorrosion acrylic coating of the anti-light decomposition of one according to claim 1, is characterized in that: described water is deionized water.