CN104277752A - Wood adhesive - Google Patents
Wood adhesive Download PDFInfo
- Publication number
- CN104277752A CN104277752A CN201410552514.8A CN201410552514A CN104277752A CN 104277752 A CN104277752 A CN 104277752A CN 201410552514 A CN201410552514 A CN 201410552514A CN 104277752 A CN104277752 A CN 104277752A
- Authority
- CN
- China
- Prior art keywords
- parts
- epoxy resin
- maleic anhydride
- weight
- modified polyethylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a wood adhesive, comprising the following components in parts by weight: 1-2 parts of iso-tridecanol polyoxyethylene ether, 8-9 parts of sodium hexametaphosphate, 2-3 parts of dibutyl phthalate, 8-9 parts of epoxy resin emulsion, 2-3 parts of hydroxyethyl saponin gum, 1-2 parts of potassium peroxodisulfate, 1-2 parts of maleic anhydride-modified polyethylene, 1-2 parts of caprolactam, 5-6 parts of polyether polyol and 2-3 parts of hydroxy propyl cellulose. The wood adhesive disclosed by the invention is strong in binding power, not easy to fall off, available in raw materials, and good in weather fastness.
Description
Technical field
The present invention relates to Wood industry adhesive.
Background technology
Solid wooden floor board in use, can use tackiness agent, but existing tackiness agent, cohesive force is not strong, easily come off, and weathering resistance is poor.
Summary of the invention
The object of the present invention is to provide a kind of Wood industry adhesive, its cohesive force is strong, be not easy to come off, and raw material is easy to get, and good weatherability.
For achieving the above object, technical scheme of the present invention is a kind of Wood industry adhesive of design, consists of the following composition by weight:
1 ~ 2 part of isomerous tridecanol polyoxyethylene ether,
8 ~ 9 parts of Sodium hexametaphosphate 99s,
2 ~ 3 parts of dibutyl phthalates,
8 ~ 9 parts of epoxy resin latexes,
2 ~ 3 parts of hydroxyethyl saponin gums,
1 ~ 2 part of Potassium Persulphate,
1 ~ 2 part of maleic anhydride modified polyethylene,
1 ~ 2 part of hexanolactam,
5 ~ 6 parts of polyether glycols,
2 ~ 3 parts of hydroxypropylcelluloses.
Preferably, Wood industry adhesive, consists of the following composition by weight:
1.2 parts of isomerous tridecanol polyoxyethylene ethers,
8.9 parts of Sodium hexametaphosphate 99s,
2.3 parts of dibutyl phthalates,
8.9 parts of epoxy resin latexes,
2.3 parts of hydroxyethyl saponin gums,
1.2 parts of Potassium Persulphates,
1.2 parts of maleic anhydride modified polyethylene,
1.2 parts of hexanolactams,
5.6 parts of polyether glycols,
2.3 parts of hydroxypropylcelluloses.
Preferably, Wood industry adhesive, consists of the following composition by weight:
1 part of isomerous tridecanol polyoxyethylene ether,
8 parts of Sodium hexametaphosphate 99s,
2 parts of dibutyl phthalates,
8 parts of epoxy resin latexes,
2 parts of hydroxyethyl saponin gums,
1 part of Potassium Persulphate,
1 part of maleic anhydride modified polyethylene,
1 part of hexanolactam,
5 parts of polyether glycols,
2 parts of hydroxypropylcelluloses.
Preferably, Wood industry adhesive, consists of the following composition by weight:
2 parts of isomerous tridecanol polyoxyethylene ethers,
9 parts of Sodium hexametaphosphate 99s,
3 parts of dibutyl phthalates,
9 parts of epoxy resin latexes,
3 parts of hydroxyethyl saponin gums,
2 parts of Potassium Persulphates,
2 parts of maleic anhydride modified polyethylene,
2 parts of hexanolactams,
6 parts of polyether glycols,
3 parts of hydroxypropylcelluloses.
Advantage of the present invention and beneficial effect are: provide a kind of Wood industry adhesive, and its cohesive force is strong, be not easy to come off, and raw material is easy to get, and good weatherability.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
Wood industry adhesive, consists of the following composition by weight:
1.2 parts of isomerous tridecanol polyoxyethylene ethers,
8.9 parts of Sodium hexametaphosphate 99s,
2.3 parts of dibutyl phthalates,
8.9 parts of epoxy resin latexes,
2.3 parts of hydroxyethyl saponin gums,
1.2 parts of Potassium Persulphates,
1.2 parts of maleic anhydride modified polyethylene,
1.2 parts of hexanolactams,
5.6 parts of polyether glycols,
2.3 parts of hydroxypropylcelluloses.
Embodiment 2
Wood industry adhesive, consists of the following composition by weight:
1 part of isomerous tridecanol polyoxyethylene ether,
8 parts of Sodium hexametaphosphate 99s,
2 parts of dibutyl phthalates,
8 parts of epoxy resin latexes,
2 parts of hydroxyethyl saponin gums,
1 part of Potassium Persulphate,
1 part of maleic anhydride modified polyethylene,
1 part of hexanolactam,
5 parts of polyether glycols,
2 parts of hydroxypropylcelluloses.
Embodiment 3
Wood industry adhesive, consists of the following composition by weight:
2 parts of isomerous tridecanol polyoxyethylene ethers,
9 parts of Sodium hexametaphosphate 99s,
3 parts of dibutyl phthalates,
9 parts of epoxy resin latexes,
3 parts of hydroxyethyl saponin gums,
2 parts of Potassium Persulphates,
2 parts of maleic anhydride modified polyethylene,
2 parts of hexanolactams,
6 parts of polyether glycols,
3 parts of hydroxypropylcelluloses.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (4)
1. Wood industry adhesive, is characterized in that, consists of the following composition by weight:
1 ~ 2 part of isomerous tridecanol polyoxyethylene ether,
8 ~ 9 parts of Sodium hexametaphosphate 99s,
2 ~ 3 parts of dibutyl phthalates,
8 ~ 9 parts of epoxy resin latexes,
2 ~ 3 parts of hydroxyethyl saponin gums,
1 ~ 2 part of Potassium Persulphate,
1 ~ 2 part of maleic anhydride modified polyethylene,
1 ~ 2 part of hexanolactam,
5 ~ 6 parts of polyether glycols,
2 ~ 3 parts of hydroxypropylcelluloses.
2. Wood industry adhesive according to claim 1, is characterized in that, consists of the following composition by weight:
1.2 parts of isomerous tridecanol polyoxyethylene ethers,
8.9 parts of Sodium hexametaphosphate 99s,
2.3 parts of dibutyl phthalates,
8.9 parts of epoxy resin latexes,
2.3 parts of hydroxyethyl saponin gums,
1.2 parts of Potassium Persulphates,
1.2 parts of maleic anhydride modified polyethylene,
1.2 parts of hexanolactams,
5.6 parts of polyether glycols,
2.3 parts of hydroxypropylcelluloses.
3. Wood industry adhesive according to claim 1, is characterized in that, consists of the following composition by weight:
1 part of isomerous tridecanol polyoxyethylene ether,
8 parts of Sodium hexametaphosphate 99s,
2 parts of dibutyl phthalates,
8 parts of epoxy resin latexes,
2 parts of hydroxyethyl saponin gums,
1 part of Potassium Persulphate,
1 part of maleic anhydride modified polyethylene,
1 part of hexanolactam,
5 parts of polyether glycols,
2 parts of hydroxypropylcelluloses.
4. Wood industry adhesive according to claim 1, is characterized in that, consists of the following composition by weight:
2 parts of isomerous tridecanol polyoxyethylene ethers,
9 parts of Sodium hexametaphosphate 99s,
3 parts of dibutyl phthalates,
9 parts of epoxy resin latexes,
3 parts of hydroxyethyl saponin gums,
2 parts of Potassium Persulphates,
2 parts of maleic anhydride modified polyethylene,
2 parts of hexanolactams,
6 parts of polyether glycols,
3 parts of hydroxypropylcelluloses.