CN104277357A - Antibacterial PVC foaming sole material and manufacturing method thereof - Google Patents

Antibacterial PVC foaming sole material and manufacturing method thereof Download PDF

Info

Publication number
CN104277357A
CN104277357A CN201410449088.5A CN201410449088A CN104277357A CN 104277357 A CN104277357 A CN 104277357A CN 201410449088 A CN201410449088 A CN 201410449088A CN 104277357 A CN104277357 A CN 104277357A
Authority
CN
China
Prior art keywords
sole
foam material
pvc foam
antibacterial pvc
sheet stock
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410449088.5A
Other languages
Chinese (zh)
Inventor
黄超
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Jingro Technology Co Ltd
Original Assignee
Suzhou Jingro Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Jingro Technology Co Ltd filed Critical Suzhou Jingro Technology Co Ltd
Priority to CN201410449088.5A priority Critical patent/CN104277357A/en
Publication of CN104277357A publication Critical patent/CN104277357A/en
Pending legal-status Critical Current

Abstract

The invention provides an antibacterial PVC foaming sole material. The antibacterial PVC foaming sole material is prepared from the following components in parts by weight: 40-60 parts of PVC, 5-10 parts of nano titanium dioxide, 20-40 parts of plasticizer, 1-5 parts of foaming agent, 0.1-3 parts of coupling agent, 2-5 parts of ACR, 1-3 parts of stabilizer and 0.1-2 parts of lubricant. The invention also discloses a manufacturing method of the antibacterial PVC foaming sole material. The PVC foaming sole material is excellent in antibacterial property and capable of effectively removing peculiar smell and bacteria out of shoes.

Description

A kind of antibacterial PVC foam material for sole of shoe and manufacture method thereof
Technical field:
The present invention relates to a kind of material for sole of shoe, particularly relate to a kind of antibacterial PVC foam material for sole of shoe and manufacture method thereof.
Background technology:
Peculiar smell in footwear, bacterium are the difficult problems perplexing people for a long time, and wherein, perspiring not easily distributes in footwear, causes bacterial reproduction, produce stink, form vicious cycle, even cause the generation of beriberi under the secretory product of the human sweat glands bacterial degradation in footwear.Beriberi not only affects the routine work life and work of self, but also can be transmitted to other people hidden danger.Existing material for sole of shoe mainly with for the purpose of raising comfort level, wear resisting property etc., seldom has the material for peculiar smell problem of bacteria in footwear greatly.
Summary of the invention:
The technical problem to be solved in the present invention is to provide a kind of antibacterial PVC foam material for sole of shoe, and its anti-microbial property is fine, effectively can remove peculiar smell and bacterium in footwear.
For solving the problems of the technologies described above, technical scheme of the present invention is:
An antibacterial PVC foam material for sole of shoe, its weight part consists of:
Preferably, softening agent of the present invention is dibenzyl sebacate, dioctyl sebacate or Octyl adipate.
Preferably, whipping agent of the present invention is AC whipping agent.
Preferably, coupling agent of the present invention is silane coupling agent.
Preferably, stablizer of the present invention is organic tin stablizer or complex lead salt stabilizer.
Preferably, lubricant of the present invention is oxidic polyethylene or fatty acid metal soap series lubricant agent.
Another technical problem that the present invention will solve is to provide the manufacture method of above-mentioned antibacterial PVC foam material for sole of shoe.
For solving the problems of the technologies described above, technical scheme is:
A manufacture method for antibacterial PVC foam material for sole of shoe, comprises the following steps:
(1) nano titanium oxide is configured to the suspension of 50g/l, regulates ph value to 4 with acetum, ultrasonic disperse 1 hour, add coupling agent, react 4 hours under the condition of high-speed stirring, filter, wash, at 100 DEG C, drying 10 hours, obtains modified nano-titanium dioxide after pulverizing;
(2) modified nano-titanium dioxide that other components and step (1) obtain is added kneader heating to mediate, mediate discharging after 2 hours;
(3) the complete compound of kneading is added twin-roll plastic mixing mill to plasticate pulling-on piece, plasticating temperature is 110 DEG C, obtains sheet stock;
(4) sheet stock is sent into thermocompressor heating plasticizing, foaming, cooling and shaping after foaming, obtains blank after the demoulding;
(5) blank to be sent in drying room foamable 40 minutes, temperature is 130 DEG C, and after obtaining foaming sheet stock, a few days is placed in cooling;
(6) foaming sheet stock stamping-out step (5) obtained is shaping, obtains antibacterial PVC foam material for sole of shoe.
Therefore compared with prior art, the present invention has following beneficial effect:
Nano titanium oxide is by its quantum size effect, produce electronics, hole pair, attack bacteria organism, play germicidal action, under action of ultraviolet radiation, bactericidal property is better, be a kind of antiseptic-germicide of permanent maintenance antibacterial effect, therefore the PVC foam material for sole of shoe adding nano titanium oxide has also possessed good anti-microbial property; Nano titanium oxide surfaces hydrophilic, be difficult to be dispersed in PVC matrix, therefore the present invention carries out surface modification by coupling agent to it, improves the hydrophobicity on its surface and the consistency in PVC matrix and dispersiveness, more can give full play to its anti-microbial property.
Embodiment:
Describe the present invention in detail below in conjunction with specific embodiment, be used for explaining the present invention in this illustrative examples of the present invention and explanation, but not as a limitation of the invention.
Embodiment 1
An antibacterial PVC foam material for sole of shoe, its weight part consists of:
Its manufacture method comprises the following steps:
(1) nano titanium oxide is configured to the suspension of 50g/l, regulates ph value to 4 with acetum, ultrasonic disperse 1 hour, add coupling agent, react 4 hours under the condition of high-speed stirring, filter, wash, at 100 DEG C, drying 10 hours, obtains modified nano-titanium dioxide after pulverizing;
(2) modified nano-titanium dioxide that other components and step (1) obtain is added kneader heating to mediate, mediate discharging after 2 hours;
(3) the complete compound of kneading is added twin-roll plastic mixing mill to plasticate pulling-on piece, plasticating temperature is 110 DEG C, obtains sheet stock;
(4) sheet stock is sent into thermocompressor heating plasticizing, foaming, cooling and shaping after foaming, obtains blank after the demoulding;
(5) blank to be sent in drying room foamable 40 minutes, temperature is 130 DEG C, and after obtaining foaming sheet stock, a few days is placed in cooling;
(6) foaming sheet stock stamping-out step (5) obtained is shaping, obtains antibacterial PVC foam material for sole of shoe.
Embodiment 2
An antibacterial PVC foam material for sole of shoe, its weight part consists of:
Its manufacture method comprises the following steps:
(1) nano titanium oxide is configured to the suspension of 50g/l, regulates ph value to 4 with acetum, ultrasonic disperse 1 hour, add coupling agent, react 4 hours under the condition of high-speed stirring, filter, wash, at 100 DEG C, drying 10 hours, obtains modified nano-titanium dioxide after pulverizing;
(2) modified nano-titanium dioxide that other components and step (1) obtain is added kneader heating to mediate, mediate discharging after 2 hours;
(3) the complete compound of kneading is added twin-roll plastic mixing mill to plasticate pulling-on piece, plasticating temperature is 110 DEG C, obtains sheet stock;
(4) sheet stock is sent into thermocompressor heating plasticizing, foaming, cooling and shaping after foaming, obtains blank after the demoulding;
(5) blank to be sent in drying room foamable 40 minutes, temperature is 130 DEG C, and after obtaining foaming sheet stock, a few days is placed in cooling;
(6) foaming sheet stock stamping-out step (5) obtained is shaping, obtains antibacterial PVC foam material for sole of shoe.
Embodiment 3
An antibacterial PVC foam material for sole of shoe, its weight part consists of:
Its manufacture method comprises the following steps:
(1) nano titanium oxide is configured to the suspension of 50g/l, regulates ph value to 4 with acetum, ultrasonic disperse 1 hour, add coupling agent, react 4 hours under the condition of high-speed stirring, filter, wash, at 100 DEG C, drying 10 hours, obtains modified nano-titanium dioxide after pulverizing;
(2) modified nano-titanium dioxide that other components and step (1) obtain is added kneader heating to mediate, mediate discharging after 2 hours;
(3) the complete compound of kneading is added twin-roll plastic mixing mill to plasticate pulling-on piece, plasticating temperature is 110 DEG C, obtains sheet stock;
(4) sheet stock is sent into thermocompressor heating plasticizing, foaming, cooling and shaping after foaming, obtains blank after the demoulding;
(5) blank to be sent in drying room foamable 40 minutes, temperature is 130 DEG C, and after obtaining foaming sheet stock, a few days is placed in cooling;
(6) foaming sheet stock stamping-out step (5) obtained is shaping, obtains antibacterial PVC foam material for sole of shoe.
Embodiment 4
An antibacterial PVC foam material for sole of shoe, its weight part consists of:
Its manufacture method comprises the following steps:
(1) nano titanium oxide is configured to the suspension of 50g/l, regulates ph value to 4 with acetum, ultrasonic disperse 1 hour, add coupling agent, react 4 hours under the condition of high-speed stirring, filter, wash, at 100 DEG C, drying 10 hours, obtains modified nano-titanium dioxide after pulverizing;
(2) modified nano-titanium dioxide that other components and step (1) obtain is added kneader heating to mediate, mediate discharging after 2 hours;
(3) the complete compound of kneading is added twin-roll plastic mixing mill to plasticate pulling-on piece, plasticating temperature is 110 DEG C, obtains sheet stock;
(4) sheet stock is sent into thermocompressor heating plasticizing, foaming, cooling and shaping after foaming, obtains blank after the demoulding;
(5) blank to be sent in drying room foamable 40 minutes, temperature is 130 DEG C, and after obtaining foaming sheet stock, a few days is placed in cooling;
(6) foaming sheet stock stamping-out step (5) obtained is shaping, obtains antibacterial PVC foam material for sole of shoe.
Embodiment 5
An antibacterial PVC foam material for sole of shoe, its weight part consists of:
Its manufacture method comprises the following steps:
(1) nano titanium oxide is configured to the suspension of 50g/l, regulates ph value to 4 with acetum, ultrasonic disperse 1 hour, add coupling agent, react 4 hours under the condition of high-speed stirring, filter, wash, at 100 DEG C, drying 10 hours, obtains modified nano-titanium dioxide after pulverizing;
(2) modified nano-titanium dioxide that other components and step (1) obtain is added kneader heating to mediate, mediate discharging after 2 hours;
(3) the complete compound of kneading is added twin-roll plastic mixing mill to plasticate pulling-on piece, plasticating temperature is 110 DEG C, obtains sheet stock;
(4) sheet stock is sent into thermocompressor heating plasticizing, foaming, cooling and shaping after foaming, obtains blank after the demoulding;
(5) blank to be sent in drying room foamable 40 minutes, temperature is 130 DEG C, and after obtaining foaming sheet stock, a few days is placed in cooling;
(6) foaming sheet stock stamping-out step (5) obtained is shaping, obtains antibacterial PVC foam material for sole of shoe.
Embodiment 6
An antibacterial PVC foam material for sole of shoe, its weight part consists of:
Its manufacture method comprises the following steps:
(1) nano titanium oxide is configured to the suspension of 50g/l, regulates ph value to 4 with acetum, ultrasonic disperse 1 hour, add coupling agent, react 4 hours under the condition of high-speed stirring, filter, wash, at 100 DEG C, drying 10 hours, obtains modified nano-titanium dioxide after pulverizing;
(2) modified nano-titanium dioxide that other components and step (1) obtain is added kneader heating to mediate, mediate discharging after 2 hours;
(3) the complete compound of kneading is added twin-roll plastic mixing mill to plasticate pulling-on piece, plasticating temperature is 110 DEG C, obtains sheet stock;
(4) sheet stock is sent into thermocompressor heating plasticizing, foaming, cooling and shaping after foaming, obtains blank after the demoulding;
(5) blank to be sent in drying room foamable 40 minutes, temperature is 130 DEG C, and after obtaining foaming sheet stock, a few days is placed in cooling;
(6) foaming sheet stock stamping-out step (5) obtained is shaping, obtains antibacterial PVC foam material for sole of shoe.
Above-described embodiment is illustrative principle of the present invention and effect thereof only, but not for limiting the present invention.Any person skilled in the art scholar all without prejudice under spirit of the present invention and category, can modify above-described embodiment or changes.Therefore, such as have in art usually know the knowledgeable do not depart from complete under disclosed spirit and technological thought all equivalence modify or change, must be contained by claim of the present invention.

Claims (7)

1. an antibacterial PVC foam material for sole of shoe, is characterized in that: its weight part consists of:
2. a kind of antibacterial PVC foam material for sole of shoe according to claim 1, is characterized in that: described softening agent is dibenzyl sebacate, dioctyl sebacate or Octyl adipate.
3. a kind of antibacterial PVC foam material for sole of shoe according to claim 1, is characterized in that: described whipping agent is AC whipping agent.
4. a kind of antibacterial PVC foam material for sole of shoe according to claim 1, is characterized in that: described coupling agent is silane coupling agent.
5. a kind of antibacterial PVC foam material for sole of shoe according to claim 1, is characterized in that: described stablizer is organic tin stablizer or complex lead salt stabilizer.
6. a kind of antibacterial PVC foam material for sole of shoe according to claim 1, is characterized in that: described lubricant is oxidic polyethylene or fatty acid metal soap series lubricant agent.
7. the manufacture method of a kind of antibacterial PVC foam material for sole of shoe according to claim 1 ~ 6 any one, is characterized in that: comprise the following steps:
(1) nano titanium oxide is configured to the suspension of 50g/l, regulates ph value to 4 with acetum, ultrasonic disperse 1 hour, add coupling agent, react 4 hours under the condition of high-speed stirring, filter, wash, at 100 DEG C, drying 10 hours, obtains modified nano-titanium dioxide after pulverizing;
(2) modified nano-titanium dioxide that other components and step (1) obtain is added kneader heating to mediate, mediate discharging after 2 hours;
(3) the complete compound of kneading is added twin-roll plastic mixing mill to plasticate pulling-on piece, plasticating temperature is 110 DEG C, obtains sheet stock;
(4) sheet stock is sent into thermocompressor heating plasticizing, foaming, cooling and shaping after foaming, obtains blank after the demoulding;
(5) blank to be sent in drying room foamable 40 minutes, temperature is 130 DEG C, and after obtaining foaming sheet stock, a few days is placed in cooling;
(6) foaming sheet stock stamping-out step (5) obtained is shaping, obtains antibacterial PVC foam material for sole of shoe.
CN201410449088.5A 2014-09-04 2014-09-04 Antibacterial PVC foaming sole material and manufacturing method thereof Pending CN104277357A (en)