CN104263079B - UV curable white inkjet ink composition - Google Patents
UV curable white inkjet ink composition Download PDFInfo
- Publication number
- CN104263079B CN104263079B CN201410592715.0A CN201410592715A CN104263079B CN 104263079 B CN104263079 B CN 104263079B CN 201410592715 A CN201410592715 A CN 201410592715A CN 104263079 B CN104263079 B CN 104263079B
- Authority
- CN
- China
- Prior art keywords
- white inkjet
- ink
- white
- curable
- printing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to an UV (ultraviolet) curable white inkjet ink composition. According to the white inkjet ink composition, characters are spray-printed on an electronic circuit board base material in an inkjet printing manner; the characters formed by spray-printing the white inkjet ink composition can resist to tin bath with a temperature of 270 to 290 DEG C without being yellowed or falling off and have viscosities of 25 to 35cp at a normal temperature. Moreover, after inkjet printing, character images are clear, and the white inkjet ink composition has excellent covering power and printing smoothness and can meet the requirement for scale production of a PCB (Printed Circuit Board).
Description
Technical field
The present invention relates to a kind of composition for ink of employing ink-jetting style printing, a kind of specifically uV curable
White ink compositionss, the composition for ink can by way of inkjet printing printing mark symbol on circuit boards.
Background technology
Inkjet printing is a kind of non-contact type mode of printing, without the need for plate-making, word or image can be passed through computer controls
It is directly printed on base material, What You See Is What You Get, is a kind of efficient, high accurately mode of printing.With ink-jet printer and shower nozzle
High speed development, can adopt ink jet printing field expand to the industry using traditional printing mode such as ceramics, textile, and
Printed electronics field is just progressively becoming next ink-jet applications emphasis.Electronic circuit board be on pcb board would generally print character with
Just the mark for checking as subsequent installation or the labelling as maintenance, the character that tradition is printed in the circuit board is to adopt screen printing
The mode of brush, need to first prepare character half tone, then silk-screen is on board substrate, this mode of printing not only high cost, operation it is many,
Cycle is long, and the graph position dimensional discrepancy for being formed is big, and the character for often leading to print occurs that the handwriting is blurred, ghost image etc. lacks
Fall into.And be spray printing on demand using ink-jetting style print character, accurate positioning, a step complete, greatly shorten flow process, reduce
The discharge of energy consumption and waste water, while greatly improving the degree of accuracy of character.
The content of the invention
But, for for the character on printed electronic circuit board, either beaten using screen printing mode or ink-jet
India side formula, requires that formed white characters have the performance of high temperature yellowing-resistant, and this is a big technological difficulties, particularly with spray
Then difficulty is bigger for black printing white ink because ink-jet printing ink require to need to reach in terms of viscosity and surface tension it is special
Requirement could meet spray printing, and this just puts forward higher requirement to the ink-jet ink to develop high temperature yellowing-resistant.
To solve the above problems, a kind of bright white inkjet composition for ink for aiming to provide uV curable of we, institute
State white inkjet composition for ink by way of inkjet printing by character spray printing on electronic circuit board base material, it is described white spray
Black composition for ink Jing spray printings form character and are resistant to 270-290 DEG C of tin bath without xanthochromia, without coming off, and viscosity is in 25- at normal temperatures
35cp.In addition, Jing after inkjet printing, character picture is clear, while the white inkjet composition for ink has excellent covering power
With printing fluency, the needs of PCB large-scale productions can be met.
What the purpose of the present invention was realized particular by following technology path:
A kind of white inkjet composition for ink of uV curable, it include titanium dioxide, pigment dispersing agent, monomer and
Oligomer;The white inkjet composition for ink Jing spray printings formation character is resistant to 270-290 DEG C of tin bath and comes off without xanthochromia, nothing,
Under room temperature, viscosity is in 25-35cp.
Specifically, the monomer is selected from monofunctional monomer, bifunctional monomer and the polyfunctional monomer of UV-curable
Plant or numerous compositions, its consumption accounts for the 60-80% of the white inkjet combination of inks amount of substance.
Preferably, the monomer includes acryloyl morpholine (ACMO), and its consumption accounts for the white inkjet combination of inks material
The 1-20% of amount.Acryloyl morpholine is the thermostability function monomer of excellent performance, can improve the heat stability of system, in molecule
Nitrogen free radical can suppress the polyreaction that oxygen causes, and accelerate the curing rate of system.It has stable tensile property simultaneously, can
To reduce volume contraction during solidification, be conducive to increasing adhesive force.
Preferably, the monomer includes the acrylate of hydroxyl, and its consumption accounts for the white inkjet combination of inks material
The 3-10% of amount.The acrylate of the hydroxyl is selected from 2-(Acryloyloxy)ethanol (HEA), Hydroxypropyl acrylate (HPA), acrylic acid
Hydroxy butyl ester (HBA), caprolactone (CA), one or more mixing of pentaerythritol triacrylate (PETA).Third
Olefin(e) acid ester carries hydroxyl, can be reacted with the isocyanate group in pcb board solder mask, significantly improve the adhesive force of system.
The titanium dioxide accounts for the 6-12% of the white inkjet combination of inks amount of substance, titanium dioxide and pigment dispersing agent
Ratio be 10~15:1.Titanium dioxide grinding in sand mill in the presence of the components such as pigment dispersing agent prepares stable
Dispersible pigment dispersion, the titanium dioxide mean diameter after grinding is between 200-350nm.Titanium dioxide may be selected from rutile-type or
One or two mixture in Detitanium-ore-type.Rutile titanium dioxide pigment is selected from Dupont R-706, Dupont R-
900th, Dupont R-902+, Dupont R-960, Dupont R-931, Dupont R102, Dupont R-103, U.S.
Du Pont of state R104, Dupont R105, Dupont R108, Dupont R350;, U.S. gift connection TIONA595, U.S. gift connection R-
CL69, stone original TiO 2 pigment CR-90-2, stone original TiO 2 pigment CR-60-2, stone original TiO 2 pigment CR-57, spy
Promise TiO 2 pigment CR-828 or special promise TiO 2 pigment CR-826.The TiO 2 pigment of anatase titanium dioxide is selected from the former A- of stone
100 or the BA-01-01 of Landtek.
The pigment dispersing agent is selected from Lu Borun Solsperse32000, Lu Borun Solsperse32500, Lu Borun
Solsperse36000, Lu Borun Solsperse39000, EFKA EFKA Addities4310, EFKA EFKA
Addities4330, EFKA EFKA Addities4030, EFKA EFKA Addities7731, EFKA EFKA
Addities7732, EFKA EFKA Addities7701, Degussa Dispers710, Degussa Dispers685 or moral are solid
Sa Dispers655.
The oligomer is preferably Epoxy Phenolic Acrylates, and its consumption accounts for the white inkjet combination of inks amount of substance
5-20%.White characters ink requires very high adhesive force, acid-fast alkali-proof performance and resistance to elevated temperatures, so oligomer is first
Epoxy acrylate is selected, without selecting polyester propylene acid esters, polyethers propylene acid esters, urethane acrylate and pure acrylic acid
Ester.Solidifying the conventional epoxy acrylate in field in UV has four kinds, is respectively:Bisphenol-a epoxy acrylate, epoxy novolac third
Olefin(e) acid ester, epoxidized oil acrylate, sour and anhydride modified acrylate.The characteristics of they are total be good adhesive force and
Chemical-resistance, is the high temperature yellowing resistance energy for improving white characters ink, selects the primary standard of oligomer exactly have
Excellent resistance to elevated temperatures, the only epoxy novolac third having outstanding performance in this characteristic in four class epoxy acrylates more than
Olefin(e) acid ester.Therefore, the oligomer is preferably Epoxy Phenolic Acrylates, different manufacturers have different product grades and
Supply of material form, therefore not to repeat here.
Further, also including at least one auxiliary agent, which is surfactant, defoamer, storage stabilizer and/or rheology
Agent.
Specifically, the consumption of the surfactant accounts for the 0-2% of the white inkjet combination of inks amount of substance, and which is at this
Effect in the formula of invention is that the surface tension for controlling ink makes which meet spray printing requirement.The surfactant is selected from
BYK-333、BYK-377、BYK-358N、BYK-UV3500;TEGO RAD2100、TEGO RAD2250、TEGO RAD2200、
TEGO WET450, TEGO WET410 or TEGO WET245.
Specifically, the consumption of the storage stabilizer accounts for the 0.1-0.5% of the white inkjet combination of inks amount of substance, its
Effect in the formula of the present invention is that polymerization occurs in storing process to prevent ink.The storage stabilizer is selected from
The GENORAD18 of GENORAD20, RAHN of RAHN, cyanogen spy S100, cyanogen spy S110, cyanogen spy S210 or cyanogen spy 130.
Specifically, the consumption of the rheological agent accounts for the 0-3% of the white inkjet combination of inks amount of substance, and which is in the present invention
Formula in effect be adjust rheological property of the ink on pcb board material.The rheological agent selected from BYK410, BYK411,
BYK415、BYK430;Lu Borun SOLTHIX250 or Lu Borun SOLTHIX200.
Specifically, the consumption of the defoamer accounts for the 0-0.5% of the white inkjet combination of inks amount of substance, and which is at this
It is to eliminate ink the harmful effect that the bubble of generation causes fluency is vibrated in pipeline that effect in bright formula is.Institute
Defoamer is stated selected from BYK-083, BYK-085 or BYK-088.
Compared with prior art, with following good effect:1st, the white inkjet ink of uV curable of the invention
Compositionss by way of inkjet printing by character spray printing on electronic circuit board base material, the composition for ink Jing spray printings are formed
Character is resistant to 270-290 DEG C of tin bath without xanthochromia, without coming off, and viscosity is in 25-35cp at normal temperatures.In addition, Jing after inkjet printing, word
Symbol image clearly, while the ink has excellent covering power and prints fluency, can meet the needs of PCB large-scale productions.
With reference to multiple embodiments, the invention will be further described.
Specific embodiment
Embodiment 1-4 and comparative example 1, the starting components of comparative example 2 and mass percent (%) are as shown in table 1.
Table 1
Each example tests white inkjet combination of inks physical performance as follows above:
1. II+PRO viscometers of Brookfield DV- are used, each embodiment is tested under the conditions of 25 DEG C and comparative example is viscous
Degree.
2. ink-jet printer spray printing character in PCB substrate, test printing fluency and observation character sharpness are used.
3. the character Jing 270-290 DEG C tin baths for spray printing solidification being completed 10s/3 time, observe character xanthochromia situation after cooling,
And character is clung with 3M600# adhesive tapes, and firmly to be pullled with 45 degree of angle directions, same position is pullled 3 times repeatedly, and observation character takes off
Fall situation.
Each example test result see the table below 2 above:
Table 2
Need illustratively, the viscosity in the application under room temperature refers to viscosity when 25 DEG C.
Above-mentioned embodiment is the invention is not limited in, if to various changes of the invention or modification without departing from the present invention
Spirit and scope, if these change and modification belong to the present invention claim and equivalent technologies within the scope of, then this
It is bright to be also intended to comprising these changes and modification.
Claims (5)
1. the white inkjet composition for ink of a kind of uV curable, it is characterised in that:Which includes titanium dioxide, pigment dispersion
Agent, monomer and oligomer;The white inkjet composition for ink Jing spray printings formed character be resistant to 270-290 DEG C of tin bath without xanthochromia,
Nothing comes off;The monomer includes the acrylate of acryloyl morpholine and hydroxyl, and the consumption of acryloyl morpholine accounts for the white spray
The 1-20% of black combination of inks amount of substance, the consumption of the acrylate of hydroxyl account for the white inkjet combination of inks amount of substance
3-10%;The oligomer is Epoxy Phenolic Acrylates, and its consumption accounts for the 5- of the white inkjet combination of inks amount of substance
20%.
2. the white inkjet composition for ink of uV curable as claimed in claim 1, it is characterised in that:The white inkjet
Under composition for ink room temperature, viscosity is between 25-35cP.
3. the white inkjet composition for ink of uV curable as claimed in claim 1, it is characterised in that:The titanium dioxide
Mix for rutile-type, Detitanium-ore-type or both.
4. the white inkjet composition for ink of uV curable as claimed in claim 1, it is characterised in that:The titanium dioxide
The 6-12% of the white inkjet combination of inks amount of substance is accounted for, the TiO 2 pigment of stable dispersion is made using the method for grinding
Dispersion liquid, after grinding, titanium dioxide mean diameter is between 200-350nm.
5. the white inkjet composition for ink of uV curable as claimed in claim 1, it is characterised in that:Also include at least one
Kind of auxiliary agent, its be surfactant, defoamer, storage stabilizer and or rheological agent.