CN104261772A - Cement foamed fireproof thermal-insulation board - Google Patents
Cement foamed fireproof thermal-insulation board Download PDFInfo
- Publication number
- CN104261772A CN104261772A CN201410476251.7A CN201410476251A CN104261772A CN 104261772 A CN104261772 A CN 104261772A CN 201410476251 A CN201410476251 A CN 201410476251A CN 104261772 A CN104261772 A CN 104261772A
- Authority
- CN
- China
- Prior art keywords
- parts
- insulation board
- sodium
- foam insulation
- potassium hydroxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a cement foamed fireproof thermal-insulation board which is composed of the following components in parts by weight: 2-3 parts of lauryl sodium sulfate, 1-2 parts of butyl sodium naphthalene sulfonate, 8-9 parts of water, 1-2 parts of sodium carbonate, 8-9 parts of fly ash, 1-2 parts of wood anti-cracking fiber, 1-2 parts of stearic acid, 1-2 parts of potassium hydroxide, 1-2 parts of calcium stearate, 1-2 parts of sulfamic acid and 65 parts of sulfoaluminate cement. The cement foamed fireproof thermal-insulation board has the advantages of favorable thermal-insulation effect and no flammability.
Description
Technical field
The present invention relates to Fireproof cement foam insulation board.
Background technology
Fireproof cement foam insulation board is the material of construction of widespread use, and the heat insulation effect of current Fireproof cement foam insulation board, Fire resistances are not very desirable.
Summary of the invention
The object of the present invention is to provide a kind of Fireproof cement foam insulation board, its high insulating effect, nonflammable.
For achieving the above object, technical scheme of the present invention is a kind of Fireproof cement foam insulation board of design, consists of the following composition by weight:
2 ~ 3 parts of sodium lauryl sulphate,
1 ~ 2 part of sodium butylnaphthalenesulfonate,
8 ~ 9 parts of water,
1 ~ 2 part of sodium carbonate,
8 ~ 9 parts of flyash,
1 ~ 2 part of wooden anti-crack fiber,
1 ~ 2 part of stearic acid,
1 ~ 2 part of potassium hydroxide,
1 ~ 2 part of calcium stearate,
1 ~ 2 part of thionamic acid,
65 parts of aluminosulfate cements.
Preferably, Fireproof cement foam insulation board, consists of the following composition by weight:
2.3 parts of sodium lauryl sulphate,
1.2 parts of sodium butylnaphthalenesulfonates,
8.9 parts of water,
1.2 parts of sodium carbonate,
8.9 parts of flyash,
1.2 parts of wooden anti-crack fibers,
1.2 parts of stearic acid,
1.2 parts of potassium hydroxide,
1.2 parts of calcium stearates,
1.2 parts of thionamic acids,
65 parts of aluminosulfate cements.
Preferably, Fireproof cement foam insulation board, consists of the following composition by weight:
3 parts of sodium lauryl sulphate,
2 parts of sodium butylnaphthalenesulfonates,
9 parts of water,
2 parts of sodium carbonate,
9 parts of flyash,
2 parts of wooden anti-crack fibers,
2 parts of stearic acid,
2 parts of potassium hydroxide,
2 parts of calcium stearates,
2 parts of thionamic acids,
65 parts of aluminosulfate cements.
Preferably, Fireproof cement foam insulation board, consists of the following composition by weight:
2 parts of sodium lauryl sulphate,
1 part of sodium butylnaphthalenesulfonate,
8 parts of water,
1 part of sodium carbonate,
8 parts of flyash,
1 part of wooden anti-crack fiber,
1 part of stearic acid,
1 part of potassium hydroxide,
1 part of calcium stearate,
1 part of thionamic acid,
65 parts of aluminosulfate cements.
Advantage of the present invention and beneficial effect are: provide a kind of Fireproof cement foam insulation board, and its high insulating effect is nonflammable.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
Fireproof cement foam insulation board, consists of the following composition by weight:
2.3 parts of sodium lauryl sulphate,
1.2 parts of sodium butylnaphthalenesulfonates,
8.9 parts of water,
1.2 parts of sodium carbonate,
8.9 parts of flyash,
1.2 parts of wooden anti-crack fibers,
1.2 parts of stearic acid,
1.2 parts of potassium hydroxide,
1.2 parts of calcium stearates,
1.2 parts of thionamic acids,
65 parts of aluminosulfate cements.
Embodiment 2
Fireproof cement foam insulation board, consists of the following composition by weight:
3 parts of sodium lauryl sulphate,
2 parts of sodium butylnaphthalenesulfonates,
9 parts of water,
2 parts of sodium carbonate,
9 parts of flyash,
2 parts of wooden anti-crack fibers,
2 parts of stearic acid,
2 parts of potassium hydroxide,
2 parts of calcium stearates,
2 parts of thionamic acids,
65 parts of aluminosulfate cements.
Embodiment 3
Fireproof cement foam insulation board, consists of the following composition by weight:
2 parts of sodium lauryl sulphate,
1 part of sodium butylnaphthalenesulfonate,
8 parts of water,
1 part of sodium carbonate,
8 parts of flyash,
1 part of wooden anti-crack fiber,
1 part of stearic acid,
1 part of potassium hydroxide,
1 part of calcium stearate,
1 part of thionamic acid,
65 parts of aluminosulfate cements.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (4)
1. Fireproof cement foam insulation board, is characterized in that, consists of the following composition by weight:
2 ~ 3 parts of sodium lauryl sulphate,
1 ~ 2 part of sodium butylnaphthalenesulfonate,
8 ~ 9 parts of water,
1 ~ 2 part of sodium carbonate,
8 ~ 9 parts of flyash,
1 ~ 2 part of wooden anti-crack fiber,
1 ~ 2 part of stearic acid,
1 ~ 2 part of potassium hydroxide,
1 ~ 2 part of calcium stearate,
1 ~ 2 part of thionamic acid,
65 parts of aluminosulfate cements.
2. Fireproof cement foam insulation board according to claim 1, is characterized in that, consists of the following composition by weight:
2.3 parts of sodium lauryl sulphate,
1.2 parts of sodium butylnaphthalenesulfonates,
8.9 parts of water,
1.2 parts of sodium carbonate,
8.9 parts of flyash,
1.2 parts of wooden anti-crack fibers,
1.2 parts of stearic acid,
1.2 parts of potassium hydroxide,
1.2 parts of calcium stearates,
1.2 parts of thionamic acids,
65 parts of aluminosulfate cements.
3. Fireproof cement foam insulation board according to claim 1, is characterized in that, consists of the following composition by weight:
3 parts of sodium lauryl sulphate,
2 parts of sodium butylnaphthalenesulfonates,
9 parts of water,
2 parts of sodium carbonate,
9 parts of flyash,
2 parts of wooden anti-crack fibers,
2 parts of stearic acid,
2 parts of potassium hydroxide,
2 parts of calcium stearates,
2 parts of thionamic acids,
65 parts of aluminosulfate cements.
4. Fireproof cement foam insulation board according to claim 1, is characterized in that, consists of the following composition by weight:
2 parts of sodium lauryl sulphate,
1 part of sodium butylnaphthalenesulfonate,
8 parts of water,
1 part of sodium carbonate,
8 parts of flyash,
1 part of wooden anti-crack fiber,
1 part of stearic acid,
1 part of potassium hydroxide,
1 part of calcium stearate,
1 part of thionamic acid,
65 parts of aluminosulfate cements.