CN104250448A - Antistatic modified plastic raw material - Google Patents
Antistatic modified plastic raw material Download PDFInfo
- Publication number
- CN104250448A CN104250448A CN201410472070.7A CN201410472070A CN104250448A CN 104250448 A CN104250448 A CN 104250448A CN 201410472070 A CN201410472070 A CN 201410472070A CN 104250448 A CN104250448 A CN 104250448A
- Authority
- CN
- China
- Prior art keywords
- mixture
- parts
- plastic
- polyetherimide
- conductive agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an antistatic modified plastic raw material which comprises components as follows: 80-120 parts of plastic waste, 20-40 parts of a mixture of polyether sulfone and polyetherimide in a weight ratio of 4:1, 10-20 parts of ABS, 5-10 parts of brucite powder, 3-8 parts of chloromethane, 1-3 parts of graphite, 0.5-1 part of a non-ionic surface active agent, 0.5-1 part of benzophenone, and 0.5-1 part of a conductive agent. The antistatic modified plastic raw material solves the problem that plastic recycling is not enough in the prior art; the plastic waste is mixed with the mixture of polyether sulfone and polyetherimide in the weight ratio of 4:1, and the new recycled material is obtained under the combined action of the conductive agent and the non-ionic surface active agent, so that the use ratio is improved by 12.1% and the antistatic performance is improved by 9.2% in comparison with the traditional method which uses plastic waste only.
Description
technical field
The present invention relates to plastic raw materials technical field.Particularly relate to a kind of antistatic modified plastic raw materials.
background technology
In daily life, use various plastics, these plastics, after discarding, are not easily degraded, are arbitrarily abandoned generation pollution problem, so the regeneration for these discarded plastics is the technical issues that need to address.At present, comprise the application of a series of plastics such as polyethylene, polypropylene, polyvinyl chloride, polystyrene and polyester, throughout all respects of industrial and agricultural production and people's daily life.But along with extensive, a large amount of application of plastics casing plastics, various plastic waste and discarded plastics also produce in a large number, and these plastic waste are difficult to degraded under physical environment, can only process by burning or burying.But, when burning, a lot of obnoxious flavoures such as hydrogenchloride can be produced due to high-temp combustion, great harm caused to environment.And bury in process, the toxic substance in plastics can ooze out, and causes secondary pollution, affects the utility value in soil.Therefore, need to adopt new technique to obtain process and the regeneration of plastic waste.
Summary of the invention:
The object of the invention is to, the problem of plastic reclaimed underutilization in a kind of prior art is provided, provide a kind of proportioning simple, easy to use, a kind of antistatic modified plastic raw materials that waste utilization rate is high.
For solving the problems of the technologies described above, the invention provides a kind of antistatic modified plastic raw materials, wherein, comprising following component:
Plastic waste 80-120 part, polyethersulfone and polyetherimide according to mixture 20-40 part of mass ratio 4:1 mixture, ABS10-20 part, brucite powder 5-10 part, methyl chloride 3-8 part, graphite 1-3 part, nonionogenic tenside 0.5-1 part, benzophenone 0.5-1 part, conductive agent 0.5-1 part.
Or, comprise following component: plastic waste 80-100 part, polyethersulfone and polyetherimide are according to mixture 20-30 part of mass ratio 4:1 mixture, ABS10-15 part, brucite powder 5-8 part, methyl chloride 3-7 part, graphite 1-2 part, nonionogenic tenside 0.5-0.8 part, benzophenone 0.5-0.8 part, conductive agent 0.5-0.8 part.
Or, comprise following component: plastic waste 100-120 part, polyethersulfone and polyetherimide are according to mixture 30-40 part of mass ratio 4:1 mixture, ABS15-20 part, brucite powder 8-10 part, methyl chloride 5-8 part, graphite 2-3 part, nonionogenic tenside 0.8-1 part, benzophenone 0.8-1 part, conductive agent 0.8-1 part.
The preparation method of above-mentioned materials
The cleaning of A, waste material: plastic waste and polyethersulfone and polyetherimide are put in pickling tub according to the mixture of mass ratio 4:1 mixture and soaks 2 days, then pull out, dry.
B, the fertilizer pulverizing of will dry, after melting of heating, add ABS, brucite powder, methyl chloride, graphite, nonionogenic tenside, benzophenone, conductive agent, make it become thick,
C, use forcing machine, raw material thick in step B is extruded slivering, and forcing machine front arranges cutting knife, and every 1mm cutting once, is little strip after cutting and drops on water-cooled travelling belt,
The cooling of little bar given by D, water-cooled travelling belt in transmitting procedure, the plastic raw materials particle packing antistatic modified to end.
Advantage of the present invention is: the problem of plastic reclaimed underutilization in prior art, by plastics fertilizer and polyethersulfone and the polyetherimide mixture mixture according to mass ratio 4:1 mixture, by conductive agent and nonionogenic tenside acting in conjunction, obtain new reworked material, the simple use plastic waste that utilization ratio is more traditional improves 12.1%, and antistatic property improves 9.2%.
embodiment:
Example 1:
Plastic waste 80 parts, polyethersulfone and polyetherimide according to 20 parts, the mixture of mass ratio 4:1 mixture, ABS10 part, brucite powder 5 parts, methyl chloride 3 parts, 1 part, graphite, nonionogenic tenside 0.5 part, benzophenone 0.5 part, conductive agent 0.5 part.
Example 2
Plastic waste 100 parts, polyethersulfone and polyetherimide according to 30 parts, the mixture of mass ratio 4:1 mixture, ABS15 part, brucite powder 8 parts, methyl chloride 7 parts, 2 parts, graphite, nonionogenic tenside 0.8 part, benzophenone 0.8 part, conductive agent 0.8 part.
Example 3
Plastic waste 120 parts, polyethersulfone and polyetherimide according to 40 parts, the mixture of mass ratio 4:1 mixture, ABS20 part, brucite powder 10 parts, methyl chloride 8 parts, 3 parts, graphite, nonionogenic tenside 1 part, benzophenone 1 part, conductive agent 1 part.
The preparation method of above-mentioned materials
The cleaning of waste material: plastic waste and polyethersulfone and polyetherimide are put in pickling tub according to the mixture of mass ratio 4:1 mixture and soaks 2 days, then pull out, dry.
The fertilizer dried is pulverized, after melting of heating, adds ABS, brucite powder, methyl chloride, graphite, nonionogenic tenside, benzophenone, conductive agent, make it become thick, use forcing machine,
Raw material thick in step B is extruded slivering, and forcing machine front arranges cutting knife, and every 1mm cutting once, is little strip after cutting and drops on water-cooled travelling belt,
The cooling of little bar given by water-cooled travelling belt in transmitting procedure, the plastic raw materials particle packing antistatic modified to end.
Advantage of the present invention is: the problem of plastic reclaimed underutilization in prior art, by plastics fertilizer and polyethersulfone and the polyetherimide mixture mixture according to mass ratio 4:1 mixture, by conductive agent and nonionogenic tenside acting in conjunction, obtain new reworked material, the simple use plastic waste that utilization ratio is more traditional improves 12.1%, and antistatic property improves 9.2%.
Claims (3)
1. an antistatic modified plastic raw materials, is characterized in that, comprises following component:
Plastic waste 80-120 part, polyethersulfone and polyetherimide according to mixture 20-40 part of mass ratio 4:1 mixture, ABS10-20 part, brucite powder 5-10 part, methyl chloride 3-8 part, graphite 1-3 part, nonionogenic tenside 0.5-1 part, benzophenone 0.5-1 part, conductive agent 0.5-1 part.
2. plastic raw materials antistatic modified according to claim 1, it is characterized in that, comprise following component: plastic waste 80-100 part, polyethersulfone and polyetherimide according to mixture 20-30 part of mass ratio 4:1 mixture, ABS10-15 part, brucite powder 5-8 part, methyl chloride 3-7 part, graphite 1-2 part, nonionogenic tenside 0.5-0.8 part, benzophenone 0.5-0.8 part, conductive agent 0.5-0.8 part.
3. plastic raw materials antistatic modified according to claim 1, it is characterized in that, comprise following component: plastic waste 100-120 part, polyethersulfone and polyetherimide according to mixture 30-40 part of mass ratio 4:1 mixture, ABS15-20 part, brucite powder 8-10 part, methyl chloride 5-8 part, graphite 2-3 part, nonionogenic tenside 0.8-1 part, benzophenone 0.8-1 part, conductive agent 0.8-1 part.