CN104233307A - 链条零件淬火热处理后的防锈处理工艺 - Google Patents
链条零件淬火热处理后的防锈处理工艺 Download PDFInfo
- Publication number
- CN104233307A CN104233307A CN201410485025.5A CN201410485025A CN104233307A CN 104233307 A CN104233307 A CN 104233307A CN 201410485025 A CN201410485025 A CN 201410485025A CN 104233307 A CN104233307 A CN 104233307A
- Authority
- CN
- China
- Prior art keywords
- chain part
- soak solution
- water
- minutes
- naco
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种链条零件淬火热处理后的防锈处理工艺，就是采用防锈液浸泡的方式进行处理，浸泡液按下列成份与水的重量百分比配制：亚硝酸钠NaNO25%～12%,工业纯碱NaCO30.5%～1%。具体的处理方式，就是将链条零件静置于浸泡液中浸泡10～20分钟。这种工艺成本低，操作简单，防锈效果突出。
Description
技术领域
本发明涉及一种链条零件加工的中间工艺过程中的防锈处理工艺。
背景技术
链条各零件在淬火热处理过程中用水进行冷却。冷却后链条的链条轴、链条轴套、链片等在5到10分钟内就会生锈。生锈的产品影响其质量、外观、后期涂装及产品使用效果。链条零件淬火热处理后进行防锈处理，是生产实际中必须解决的一个技术课题。目前防锈处理的方法很多，但这些方法大多工艺复杂，成本较高。
发明内容
本发明的目的在于提供一种链条零件淬火热处理水冷却后的防锈处理工艺方法，经过防锈处理后的零件可以保持较长时间不生锈，且工艺操作简便，成本低廉。
为了达到上述目的，本发明技术解决方案是一种链条零件淬火热处理后的防锈处理工艺，就是采用防锈液浸泡的方式进行处理，浸泡液按下列成份与水的重量百分比配制：亚硝酸钠NaNO₂5%～12%,工业纯碱NaCO₃0.5%～1%。
浸泡液的优选配比是：亚硝酸钠NaNO₂8%～12%,工业纯碱NaCO₃0.8%～1%。
浸泡液的更优配比是：亚硝酸钠NaNO₂10%～12%,工业纯碱NaCO₃0.8%～1%。
具体处理方式是：将链条零件静置于浸泡液体中5～20分钟。
本发明与现有技术比，具有以下优点：
1、成本低。原料在市场容易得到，材料成本低，使用过程中防锈液损耗少，原液更换时间长，使用成本低。浸泡液配制简单，无需专业设备进行处理，无疑减少了成本支出。操作简单，无需增加人工成本。
2、防锈效果好。链条零件在浸泡液体中浸泡10～20分钟，可达45天以上直至3个月以上不生锈。
3、工艺过程简单，容易操作。零件在原工序淬火装框等待过程中同时静置于浸泡液中，无需额外增加工序时间和人工，即可达到防锈目的，无需加热、搅拌和专用的复杂设备。
具体实施方式
实施例1
亚硝酸钠NaNO₂6%，工业纯碱NaCO₃0.6%，用水配制成浸泡液，将链条零件侵泡15分钟，防锈时间可达45天以上。
实施例2
亚硝酸钠NaNO₂8%，工业纯碱NaCO₃0.8%，用水配制成浸泡液，将链条零件侵泡15分钟，防锈时间可达50天以上。
实施例3
亚硝酸钠NaNO₂10%，工业纯碱NaCO₃1%，用水配制成浸泡液，将链条零件侵泡15分钟，防锈时间可达65天以上。
实施例4
亚硝酸钠NaNO₂12%，工业纯碱NaCO₃1%，用水配制成浸泡液，将链条零件侵泡10分钟，防锈时间可达3个月以上。
Claims (8)
1.一种链条零件淬火热处理后的防锈处理工艺，就是采用防锈液浸泡的方式进行处理，其特征在于，浸泡液按下列成份与水的重量百分比配制：
亚硝酸钠NaNO₂5%～12%,工业纯碱NaCO₃0.5%～1%；
所述采用防锈液浸泡的方式进行处理，就是将链条零件静置于上述浸泡液中浸泡10～20分钟。
2.根据权利要求1所述的链条零件淬火热处理后的防锈处理工艺，其特征在于，浸泡液按下列成份与水的重量百分比配制：
亚硝酸钠NaNO₂8%～12%,工业纯碱NaCO₃0.8%～1%；
将链条零件静置于上述浸泡液中10～20分钟。
3.根据权利要求1或2所述的链条零件淬火热处理后的防锈处理工艺，其特征在于，浸泡液按下列成份与水的重量百分比配制：
亚硝酸钠NaNO₂10%～12%,工业纯碱NaCO₃0.8%～1%；
将链条零件静置于上述浸泡液中10～20分钟。
4.根据权利要求1所述的链条零件淬火热处理后的防锈处理工艺，其特征在于，浸泡液按下列成份与水的重量百分比配制：
亚硝酸钠NaNO₂6%，工业纯碱NaCO₃0.6%，用水配制成浸泡液；
将链条零件静置于上述浸泡液中侵泡15分钟。
5.根据权利要求1或2所述的链条零件淬火热处理后的防锈处理工艺，其特征在于，浸泡液按下列成份与水的重量百分比配制：
亚硝酸钠NaNO₂8%，工业纯碱NaCO₃0.8%；
将链条零件静置于上述浸泡液中侵泡15分钟。
6.根据权利要求1或2所述的链条零件淬火热处理后的防锈处理工艺，其特征在于，浸泡液按下列成份与水的重量百分比配制：
亚硝酸钠NaNO₂10%，工业纯碱NaCO₃0.8%；
将链条零件静置于上述浸泡液中侵泡15分钟。
7.根据权利要求1或2所述的链条零件淬火热处理后的防锈处理工艺，其特征在于，浸泡液按下列成份与水的重量百分比配制：
亚硝酸钠NaNO₂12%，工业纯碱NaCO₃1%；
将链条零件静置于上述浸泡液中侵泡10分钟。
8.根据权利要求3所述的链条零件淬火热处理后的防锈处理工艺，其特征在于，浸泡液按下列成份与水的重量百分比配制：
亚硝酸钠NaNO₂12%，工业纯碱NaCO₃1%；
将链条零件静置于上述浸泡液中侵泡10分钟。