CN104230361A - High-temperature reinforcing agent for refractory materials and preparation method of high-temperature reinforcing agent - Google Patents
High-temperature reinforcing agent for refractory materials and preparation method of high-temperature reinforcing agent Download PDFInfo
- Publication number
- CN104230361A CN104230361A CN201410488950.3A CN201410488950A CN104230361A CN 104230361 A CN104230361 A CN 104230361A CN 201410488950 A CN201410488950 A CN 201410488950A CN 104230361 A CN104230361 A CN 104230361A
- Authority
- CN
- China
- Prior art keywords
- reinforcing agent
- temperature
- high temperature
- particle size
- temperature reinforcing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the technical field of refractory materials and discloses a high-temperature reinforcing agent for refractory materials and a preparation method of the high-temperature reinforcing agent. The high-temperature reinforcing agent is prepared from the following raw materials in percentage by weight: 15-20 percent of synthetic mullite of which the particle size is smaller than 0.045 mm, 55-60 percent of alumina micro-powder of which the particle size is smaller than 0.045 mm, 15-20 percent of silica micro-powder of which the particle size is smaller than 0.045mm and 5-10 percent of a special additive, wherein the special additive is sodium carboxymethyl cellulose or sodium lignin sulfonate. The preparation method comprises the following steps: taking the raw materials in proportion, mixing and grinding to the average particle size of being smaller than 0.002mm. After the high-temperature reinforcing agent is added in a refractory product, the normal-temperature and high-temperature mechanical properties of the product can be greatly improved, and the high-temperature erosion resistance is superior.
Description
Technical field
The invention belongs to technical field of refractory materials, be specifically related to a kind of high temperature toughener used for refractory material and preparation method thereof.
Background technology
The bonding agent of most of aluminium silicon based article produced in the market generally uses soft clay, soft clay has certain plasticity-, adobe can be made to have certain intensity when drying, under high temperature, forming section liquid phase makes goods produce liquid phase sintering, a large amount of glassy phase is filled between goods internal particle, goods have beautiful and charming normal temperature strength, but mechanical behavior under high temperature is poor, as soft in lotus, thermal shock, the anti-folding of high temperature etc.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind of high temperature toughener used for refractory material and preparation method thereof, after this high temperature toughener is added to refractory product, overcomes the problem that there is side effect when existing bonding agent uses.
For solving the problems of the technologies described above, the technical scheme that the present invention takes is as follows:
A kind of high temperature toughener used for refractory material, is made up of the raw material of following mass percent: the mullite synthesizing 15-20% of granularity < 0.045mm, the alumina powder 55-60% of granularity < 0.045mm, the silicon powder 15-20% of granularity < 0.045mm, specialist additive 5-10%; Described specialist additive is Xylo-Mucine or sodium lignosulfonate.
In mass percentage, in mullite synthesizing: mullite phase 80-90%, Fe
2o
3< 0.8%, K
2o+Na
2o < 0.3%, Al in alumina powder
2o
3> 99%, SiO in silicon powder
2> 92%.
The preparation method of high temperature toughener used for refractory material: feeding in proportion, mixing is milled to mean particle size < 0.002mm altogether.
After product of the present invention is added to refractory product, sintering reaction can be completed under original sintering temperature, do not need improve firing temperature and cause energy dissipation and cost to raise, the high temperature toughener added at high temperature self can react in-situ preparation part mullite phase, the part mullite crystal under a small amount of liquid phase effect of high temperature added constantly is grown and is grown up, be interconnected with one another around product grain, connect mutually mainly through mullite between goods internal particle, normal temperature and the mechanical behavior under high temperature of goods can be increased substantially, and high-temperature anti-corrosion performance is more superior.Simultaneously because this high temperature toughener at high temperature generates mullite meeting with certain volumetric expansion, so this high temperature toughener can regulate add-on to control the rate of expansion of goods.
Embodiment
Embodiment 1
Raw material (mass percent): the mullite synthesizing 15% of granularity < 0.045mm, the alumina powder 55% of granularity < 0.045mm, the silicon powder 20% of granularity < 0.045mm, Xylo-Mucine 10%.Wherein, in mass percentage, in mullite synthesizing: mullite phase 80-90%, Fe
2o
3< 0.8%, K
2o+Na
2o < 0.3%, Al in alumina powder
2o
3> 99%, SiO in silicon powder
2> 92%.
Make: grinding placing after above-mentioned raw materials in proportion precise to close in grinding machine, when taking out precise pack after mean particle size < 0.002mm, obtaining high temperature toughener used for refractory material.
Embodiment 2
Raw material (mass percent): the mullite synthesizing 20% of granularity < 0.045mm, the alumina powder 60% of granularity < 0.045mm, the silicon powder 15% of granularity < 0.045mm, sodium lignosulfonate 5%.Wherein, in mass percentage, in mullite synthesizing: mullite phase 80-90%, Fe
2o
3< 0.8%, K
2o+Na
2o < 0.3%, Al in alumina powder
2o
3> 99%, SiO in silicon powder
2> 92%.
Make: grinding placing after above-mentioned raw materials in proportion precise to close in grinding machine, when taking out precise pack after mean particle size < 0.002mm, obtaining high temperature toughener used for refractory material.
effect example
Test example 1:
(1) add: prepare in the raw material of siliceous mullite brick by weighing high temperature toughener prepared by embodiment 1 accurately in joining outside 5wt% ratio (accounting for the per-cent of siliceous mullite brick raw material gross weight), mixing, shaping adobe; The raw material of described siliceous mullite brick consists of: the 97# silicon carbide 15wt% of the 80# bauxite 10wt% of the 80# bauxite 10wt% of granularity 5-3mm, the 80# bauxite 35wt% of granularity 3-1mm, granularity 1-0mm, the 80# bauxite 25wt% of granularity < 0.088mm, granularity < 0.088mm, the Suzhou soil 5wt% of granularity < 0.045mm, wherein 80# bauxite refers to Al wherein
2o
3>=80wt%, 97# silicon carbide refers to SiC>=97wt% wherein.
(2) burn till: after drying 24 hours through 110 DEG C after the adobe after shaping being taken out, loading of kiln, in 1500 DEG C of insulations cooling after 5 hours, namely obtains the siliceous mullite brick goods containing high temperature toughener.
Test example 2: be to add high temperature toughener prepared by embodiment 2 with the difference of test example 1, other is all with test example 1.
Reference examples: be not add high temperature toughener with the difference of test example 1, other is all with test example 1.
Implementation result:
As can be seen from the above table: after same goods add product of the present invention, indices all increases, for high-performance refractory goods from now on provide the desirable raw material of high-quality.
Claims (3)
1. a high temperature toughener used for refractory material, is characterized in that being made up of the raw material of following mass percent: the mullite synthesizing 15-20% of granularity < 0.045mm, the alumina powder 55-60% of granularity < 0.045mm, the silicon powder 15-20% of granularity < 0.045mm, specialist additive 5-10%; Described specialist additive is Xylo-Mucine or sodium lignosulfonate.
2. high temperature toughener used for refractory material as claimed in claim 1, is characterized in that in mass percentage, in mullite synthesizing: mullite phase 80-90%, Fe
2o
3< 0.8%, K
2o+Na
2o < 0.3%, Al in alumina powder
2o
3> 99%, SiO in silicon powder
2> 92%.
3. prepare a method for high temperature toughener used for refractory material as claimed in claim 1 or 2, it is characterized in that: feeding in proportion, mixing is milled to mean particle size < 0.002mm altogether.