CN104223532A - Manufacturing method for light and thin warm-keeping fabric containing silk - Google Patents
Manufacturing method for light and thin warm-keeping fabric containing silk Download PDFInfo
- Publication number
- CN104223532A CN104223532A CN201410443720.5A CN201410443720A CN104223532A CN 104223532 A CN104223532 A CN 104223532A CN 201410443720 A CN201410443720 A CN 201410443720A CN 104223532 A CN104223532 A CN 104223532A
- Authority
- CN
- China
- Prior art keywords
- fabric
- silk
- warm
- layer
- plumage
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a manufacturing method for a light and thin warm-keeping fabric containing silk. The method comprises the following steps that (1) clean feather fabric stem and feather fabric are separated, the feather fabric is then disinfected and dried, the feather fabric is subjected to opening and is spread out to form a feather fabric warm-keeping layer; (2) a polyester staple fiber elastic layer is paved on the feather fabric warm-keeping layer, and the silk fabric is used as the fabric layer; (3) the silk fabric, the warm-keeping layer and the elastic layer are fixed through a quilting manner to form the light and thin and warm-keeping fabric. According to the manufacturing method for the light and thin warm-keeping fabric containing silk, the thickness and warm-keeping rate of the fabric are controlled by regulating the use amount of a flaky material and the density of quilting, the technology is simple, the prepared fabric is light and thin and warm-keeping, gentle in handfeel, good in breathability and has good wearability.
Description
Technical field:
The invention belongs to field of textiles, be specifically related to a kind of manufacture method of the frivolous thermal fabric containing silk.
Background technology:
Heat insulating material formed at present have natural heat insulating material formed and heat insulating material formed two kinds of chemistry.Naturally heat insulating material formedly be mainly the animal hairs such as eider down, the strings such as opal fiber, cotton such as silk.Chemistry is heat insulating material formed main based on oil extracts such as silk floss.
The strings such as cotton are as natural prodcuts, and its warming coefficient is lower, therefore often seem comparatively heavy for winter warming.And the animal hairs such as eider down, though for reaching certain coefficient during winter warming, but product is fluffy, and due to itself resource-constrained and complex process, price is higher and product is more too fat to move.Silk proteinoid fiber, tentacle soft comfortable, moisture absorption is fallen apart wet performance excellence, and warmth retention property is good, gives sensation cool in summer and warm in winter.Though the heat insulating material formed aboundresources of chemistry is cheap, also do not have the material of comparatively ideal warming coefficient at present.
Light and thin type is heat insulating material formed mainly reduces heat loss by blocking heat transfer, need to select thermal conductivity factor little and the frivolous material of quality as warming layer, while the guarantee of bamboo product one deck elastic intermediate is comfortable and easy to wear and durable, reduces the thermal conductivity of material, improve its thermal property.
Summary of the invention:
The object of this invention is to provide a kind of manufacture method of the frivolous thermal fabric containing silk, this method is by plumage silk as warming layer, and terylene short fiber is as elastic layer, and silk, as precoat, makes fabric both warming flexible, attractive in appearance comfortable again.
Object of the present invention is achieved through the following technical solutions:
Containing a manufacture method for the frivolous thermal fabric of silk, comprise the following steps:
(1) clean plumage screw mandrel is separated with plumage silk, plumage silk is sterilized, dry, after shredding, sprawl into loose plumage silk warming layer;
(2) on plumage silk warming layer, one deck terylene short fiber elastic layer is laid, using silk fabric as precoat;
(3) by quilting mode, fixing silk fabric and warming layer and elastic layer, form frivolous thermal fabric.
Preferred as technique scheme, the plumage silk in described step (1) can be the one in eider down, duck's down, goose down.
Preferred as technique scheme, the thickness of the plumage silk warming layer in described step (1) is 2-3mm, and density is 119-223g/cm
2.
Preferred as technique scheme, the line density of the terylene short fiber in described step (2) is 2.2dtex, and the thickness of elastic layer is 0.3-0.6mm.
Preferred as technique scheme, the graticule density of the silk fabric in described step (2) is 78 × 56/cm.
Preferred as technique scheme, the fabric thickness in described step (3) is 2.2-3.4mm.
Beneficial effect of the present invention is: its feather spending bar is made platy layer and made the fluffy softness of fabric, the cost of fabric and warming coefficient is regulated by selecting the raw material of feather, by regulating thickness and the density of the density domination fabric of plumage silk consumption and quilting, the warming coefficient of further adjustment fabric, by terylene short fiber as elastic layer, also the heat insulating ability of fabric can be improved increasing flexible while, by adopting silk fabric as precoat, the premium properties of silk fabric can be utilized, improve the skin-friendly of heat-preservation clothing material, the performances such as moisture retention, improve the comfort level that fabric is taken, adopt quilting mode compound, improve the gas permeability of whole material.It is high, frivolous warming that each interlayer of fabric prepared by the inventive method connects tight intensity, and feel is fine and smooth, and wearability is good.
Detailed description of the invention:
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the invention will be further described, and this embodiment only for explaining the present invention, does not form limiting the scope of the present invention.Embodiment 1:
Be separated with plumage silk by clean eider down screw mandrel, sterilized by plumage silk, dry, sprawling into thickness after shredding is 2mm, and density is 119g/cm
2plumage silk platy layer;
On plumage silk tablet, lay the terylene short fiber tablet that one deck line density is 2.2dtex, the thickness of tablet is 0.3mm, then is that the silk fabric of 78 × 56/cm is as precoat using graticule density;
By quilting mode, fixing silk fabric layer and platy layer, form the frivolous thermal fabric that thickness is 2.2mm, warming rate is 51.4%.
Embodiment 2:
Be separated with plumage silk by clean eider down plumage screw mandrel, sterilized by plumage silk, dry, sprawling into thickness after shredding is 3mm, and density is 223g/cm
2plumage silk platy layer;
On plumage silk tablet, lay the terylene short fiber tablet that one deck line density is 2.2dtex, the thickness of tablet is 0.6mm, then is that the silk fabric of 78 × 56/cm is as precoat using graticule density;
By quilting mode, fixing silk fabric layer and platy layer, form the frivolous thermal fabric that thickness is 3.4mm, warming rate is 61.7%.
Embodiment 3:
Be separated with plumage silk by clean Down In Ducks screw mandrel, sterilized by plumage silk, dry, sprawling into thickness after shredding is 2.4mm, and density is 146g/cm
2plumage silk platy layer;
On plumage silk tablet, lay the terylene short fiber tablet that one deck line density is 2.2dtex, the thickness of tablet is 0.5mm, then is that the silk fabric of 78 × 56/cm is as precoat using graticule density;
By quilting mode, fixing silk fabric layer and platy layer, form the frivolous thermal fabric that thickness is 3.0mm, warming rate is 54.6%.
Embodiment 4:
Be separated with plumage silk by clean goose down plumage screw mandrel, sterilized by plumage silk, dry, sprawling into thickness after shredding is 2.6mm, and density is 184g/cm
2plumage silk platy layer;
On plumage silk tablet, lay the terylene short fiber tablet that one deck line density is 2.2dtex, the thickness of tablet is 0.5mm, then is that the silk fabric of 78 × 56/cm is as precoat using graticule density;
By quilting mode, fixing silk fabric layer and platy layer, form the frivolous thermal fabric that thickness is 3.1mm, warming rate is 56.7%.
Claims (6)
1., containing a manufacture method for the frivolous thermal fabric of silk, it is characterized in that comprising the following steps:
(1) clean plumage screw mandrel is separated with plumage silk, plumage silk is sterilized, dry, after shredding, sprawl into loose plumage silk warming layer;
(2) on plumage silk warming layer, one deck terylene short fiber elastic layer is laid, using silk fabric as precoat;
(3) by quilting mode, fixing silk fabric and warming layer and elastic layer, form frivolous thermal fabric.
2. the manufacture method of a kind of frivolous thermal fabric containing silk according to claim 1, is characterized in that: the plumage silk in described step (1) can for the one in eider down, duck's down, goose down.
3. the manufacture method of a kind of frivolous thermal fabric containing silk according to claim 1, is characterized in that: the thickness of the plumage silk warming layer in described step (1) is 2-3mm, and density is 119-223g/cm
2.
4. the manufacture method of a kind of frivolous thermal fabric containing silk according to claim 1, it is characterized in that: the line density of the terylene short fiber in described step (2) is 2.2dtex, the thickness of elastic layer is 0.3-0.6mm.
5. the manufacture method of a kind of frivolous thermal fabric containing silk according to claim 1, is characterized in that: the graticule density of the silk fabric in described step (2) is 78 × 56/cm.
6. the manufacture method of a kind of frivolous thermal fabric containing silk according to claim 1, is characterized in that: the fabric thickness in described step (3) is 2.2-3.4mm.