CN104212284A - Reflective thermal insulation coating for car window - Google Patents
Reflective thermal insulation coating for car window Download PDFInfo
- Publication number
- CN104212284A CN104212284A CN201410522621.6A CN201410522621A CN104212284A CN 104212284 A CN104212284 A CN 104212284A CN 201410522621 A CN201410522621 A CN 201410522621A CN 104212284 A CN104212284 A CN 104212284A
- Authority
- CN
- China
- Prior art keywords
- parts
- thermal insulation
- insulation coating
- reflection type
- vehicle window
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a reflective thermal insulation coating for a car window. The reflective thermal insulation coating is made of raw materials including, by weight, 10-30 parts of acrylic emulsion, 1-5 parts of antifoaming agents, 1-5 parts of dispersing agents, 1-10 parts of thickening agents, 1-10 parts of flatting agents, 10-20 parts of titanium dioxide, 1-10 parts of ceramic micro-beads, 1-10 parts of coalescing agents and 20-50 parts of water. The reflective thermal insulation coating for the car window has a fine thermal insulation performance and a wide prospect in industrial application.
Description
Technical field
The present invention relates to automotive field, specifically, the present invention relates to a kind of vehicle window reflection type thermal insulation coating.
Background technology
Energy-saving heat-insulating coating has a lot of application in automobile industry.Such as, automobile will fully take into account heat insulation problem in manufacturing processed, otherwise summer automotive interior excess Temperature, turn on the aircondition can reduce temperature but can cause meaningless energy waste, in current gas price, continue the soaring age, the heat-insulating problem of automobile is also the problem that people relatively pay close attention to.So the research of the energy-saving heat-insulating coating on automobile is also the focus of current and future studies.At present, a kind of popular method is at vehicle window coating thermal insulating.
Summary of the invention
The object of the present invention is to provide a kind of vehicle window reflection type thermal insulation coating.
In order to realize object of the present invention, the invention provides a kind of vehicle window reflection type thermal insulation coating, by the raw material of following weight part, made: ACRYLIC EMULSION 10-30 part, defoamer 1-5 part, dispersion agent 1-5 part, thickening material 1-10 part, flow agent 1-10 part, titanium dioxide 10-20 part, ceramic fine bead 1-10 part, film coalescence aid 1-10 part and water 20-50 part.
Preferably, vehicle window of the present invention is made by the raw material of following weight part with reflection type thermal insulation coating: 45 parts, 25 parts of ACRYLIC EMULSION, 2.5 parts of defoamers, 1.5 parts of dispersion agents, 6 parts of thickening materials, 3 parts of flow agents, 16 parts of titanium dioxides, 7 parts of ceramic fine beads, 6 parts of film coalescence aid and water.
More preferably, described ACRYLIC EMULSION is HD1092 aqueous acrylic emulsion, for example can be purchased from U.S. Hua Jinsi company, and its detail file can reference: http://www.pthjs.com/products/HD1092.html.
More preferably, described defoamer is BYK-057, for example can be purchased from Shanghai great Pan Chemical Co., Ltd..
More preferably, described dispersion agent is EFKA6745, for example can be purchased from Changsha Tian Qi fine chemistry company limited.
More preferably, described thickening material is carboxymethyl cellulose.
More preferably, described flow agent is BD-3032, for example can be purchased from Hangzhou Bao Er get organosilicon company limited.
In the present invention, titanium dioxide (for example) can be purchased from Hebei titanium dioxide Manufacturing Co., Ltd.
In the present invention, ceramic fine bead (for example) can grind Science and Technology Ltd. purchased from Jiangsu tin sun, pulverizes in use 60 mesh sieves.
More preferably, described film coalescence aid be S-1-(2-ethoxyl phenenyl-4-[3-(1-benzotriazole oxygen base)-2-hydroxypropyl] piperazine.
Vehicle window of the present invention has good heat-proof quality with reflection type thermal insulation coating, in industrial application, has broad prospects.
Accompanying drawing explanation
Fig. 1 heat insulation test set of the present invention.
Embodiment
Below the invention will be further described for the description by embodiment, but this is not limitation of the present invention, those skilled in the art are according to basic thought of the present invention, can make various modifications or improvement, but only otherwise depart from basic thought of the present invention, all within the scope of the present invention.
Embodiment 1
Take BYK-0572.5 kilogram, EFKA67451.5 kilogram, 6 kilograms of carboxymethyl celluloses, BD-30323 kilogram, S-1-(2-ethoxyl phenenyl-4-[3-(1-benzotriazole oxygen base)-2-hydroxypropyl] 45 kilograms, 6 kilograms of piperazines and water, under the condition of 200rpm, stir 10 minutes, then add 16 kilograms of titanium dioxides, under the condition of 1000rpm, stir 20 minutes, then add 7 kilograms of ceramic fine beads, under the condition of 50rpm, stir 10 minutes, then add 25 kilograms of HD1092 aqueous acrylic emulsions, under the condition of 200rpm, stir 30 minutes, then regulating pH value is 7.0, obtain reflection type thermal insulation coating of the present invention.
Embodiment 2
According to the mode identical with embodiment 1, prepare reflection type thermal insulation coating, difference is not use ceramic fine bead.
Experimental example
With the device of Fig. 1, carry out the heat-proof quality of the coating of test implementation example 1 and 2.The thermal insulating coating preparing is applied on the foursquare sheet glass of 15*15cm and (controls the consistency of thickness of at every turn filming), be positioned on the temperature measuring equipment shown in Fig. 1, open infrared lamp sample board is carried out to infrared radiation, temperature in sample board can raise gradually under the irradiation of infrared lamp, by moisture recorder (ZDR21J type, Hangzhou pool is large) record sample board internal temperature with the variation of infrared radiation time, thus can judge the effect of heat insulation of thermal insulating coating.Test is to carry out in thermostatic chamber, and the initial measurement temperature of holding plate inside is identical, reduces the interference of external environment to accuracy of measurement as far as possible.
Result
Coating for embodiment 1:
Coating for embodiment 2:
From result, can find out, the temperature in the test space, along with the prolongation of infrared radiation time raises, is finally tending towards a stable value.Irradiation due to infrared lamp, heat sees through glass or coating enters in thermometric space, temperature in thermometric space can raise gradually, but under infrared lamp irradiation, in temperature elevation process, can be diffused in air by some heat again, after both tend to balance, the hull-skin temperature of glass is elevated to maximum value and tends to be steady.Due to adding of ceramic fine bead, heat-proof quality is greatly strengthened.
Claims (8)
1. a vehicle window reflection type thermal insulation coating, it is characterized in that, by the raw material of following weight part, made: ACRYLIC EMULSION 10-30 part, defoamer 1-5 part, dispersion agent 1-5 part, thickening material 1-10 part, flow agent 1-10 part, titanium dioxide 10-20 part, ceramic fine bead 1-10 part, film coalescence aid 1-10 part and water 20-50 part.
2. vehicle window according to claim 1 reflection type thermal insulation coating, it is characterized in that, by the raw material of following weight part, made: 45 parts, 25 parts of ACRYLIC EMULSION, 2.5 parts of defoamers, 1.5 parts of dispersion agents, 6 parts of thickening materials, 3 parts of flow agents, 16 parts of titanium dioxides, 7 parts of ceramic fine beads, 6 parts of film coalescence aid and water.
3. vehicle window according to claim 2 reflection type thermal insulation coating, is characterized in that, described ACRYLIC EMULSION is HD 1092 aqueous acrylic emulsions.
4. vehicle window according to claim 2 reflection type thermal insulation coating, is characterized in that, described defoamer is BYK-057.
5. vehicle window according to claim 2 reflection type thermal insulation coating, is characterized in that, described dispersion agent is EFKA 6745.
6. vehicle window according to claim 2 reflection type thermal insulation coating, is characterized in that, described thickening material is carboxymethyl cellulose.
7. vehicle window according to claim 2 reflection type thermal insulation coating, is characterized in that, described flow agent is BD-3032.
8. vehicle window according to claim 2 reflection type thermal insulation coating, is characterized in that, described film coalescence aid be S-1-(2-ethoxyl phenenyl-4-[3-(1-benzotriazole oxygen base)-2-hydroxypropyl] piperazine.