CN104212194A - Modified bentonite for thermoplastic elastomer wire/cable material and preparation method of modified bentonite - Google Patents
Modified bentonite for thermoplastic elastomer wire/cable material and preparation method of modified bentonite Download PDFInfo
- Publication number
- CN104212194A CN104212194A CN201410415276.6A CN201410415276A CN104212194A CN 104212194 A CN104212194 A CN 104212194A CN 201410415276 A CN201410415276 A CN 201410415276A CN 104212194 A CN104212194 A CN 104212194A
- Authority
- CN
- China
- Prior art keywords
- parts
- bentonite
- modified bentonite
- improved
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses modified bentonite for a thermoplastic elastomer wire/cable material and a preparation method of the modified bentonite. The modified bentonite is prepared from the following raw materials in parts by weight: 46-54 parts of bentonite, 4-8 parts of dimethyl fumarate, 15-20 parts of ketoaldehyde resin, 3-6 parts of candelilla wax, 5-10 parts of heavy calcium carbonate powder, 4-6 parts of nanometer magnesium titanate, 5-10 parts of petroleum coke powder, 3-5 parts of aluminium isopropoxide, 2-4 parts of antimony sulfide, 1.5-2.5 parts of diallyl bisphenol A, 1-2 parts of isoamyl p-methoxycinnamate, 2-3 parts of tetramethyl tetravinyl cyclotetrasiloxane, 1-2 parts of N,N'-diphenyl-1,3-propane diamine and 2-4 parts of an assistant. After the bentonite is subjected to modification treatment, the compatibility of inorganic particles and an organic polymer matrix is improved, phase separation is reduced, dispersion of the bentonite in the organic phase is facilitated, the filling performance and the reinforcing effect of bentonite are improved, the impact strength and the tensile strength of the composite material are greatly improved, the mechanical property of the composite material is improved, meanwhile, the heat resistance, the ageing resistance, the corrosion resistance, the oil resistance and the like of the composite material can be improved by virtue of filling of the modified bentonite.
Description
Technical field
The present invention relates to a kind of thermoplastic elastomer electric wire and cable material modified alta-mud and preparation method thereof, belong to mineral filler technical field.
Background technology
Wilkinite profit soil has another name called amargosite, otaylite, and sometimes also claim white clay, be that a kind of performance is very excellent, economic worth is higher, the clay resource that range of application is wider.Wilkinite to be a kind of with montmorillonite be main component moisture clay pit.Wilkinite, due to the mineral structure of uniqueness and crystal chemistry character, has many very excellent performances, is widely used in the mineral filler of the polymer composites materials such as plastics, rubber.But existing wilkinite poor compatibility not only and between organic polymer, and it is lower to fill function, makes bentonitic range of application have limitation.Therefore, certain modification must be carried out to it.
Summary of the invention
The object of the invention is to provide a kind of thermoplastic elastomer electric wire and cable material modified alta-mud and preparation method thereof, improves the consistency between wilkinite and organic polymer, improves bentonitic filling function.
For achieving the above object, the present invention adopts following technical scheme:
A kind of thermoplastic elastomer electric wire and cable material modified alta-mud, be made up of the raw material of following weight part: wilkinite 46-54, dimethyl fumarate 4-8, ketone resin 15-20, gama wax 3-6, dry powder 5-10, nano-sized magnesium titanate 4-6, petroleum coke powder 5-10, aluminum isopropylate 3-5, antimony sulfide 2-4, adjacent diallyl bisphenol 1.5-2.5, Neo Heliopan E1000 1-2, t etram-ethyltetravinylcyclotetrasiloxane 2-3, N, N'-phenylbenzene-1,3-propylene diamine 1-2, auxiliary agent 2-4;
Described auxiliary agent is mixed by the raw material of following weight part: diphenyl methane dimaleimide 3-4, two (t-butylperoxyisopropyl) benzene 2-3, pentalyn 4-5, zinc-ethylphenyl dithiocarbamate 2-3, tetra isopropyl two (dioctyl phosphito acyloxy) titanic acid ester 1-2, two Imidurea 2-4, N-phenyl-2-naphthylamine 1-2, two (the 6-tertiary butyl-3-methylphenol) 1.5-2.5, the stannous octoate 1-2 of 4,4'-butylidenes.
Thermoplastic elastomer electric wire and cable material method for preparing modified bentonite of the present invention, comprise the following steps: first bentonite in powder is broken to the fine powder that mean particle size is 2-5 μm, drop into again in high-speed mixer, add dry powder, nano-sized magnesium titanate, petroleum coke powder, gama wax, t etram-ethyltetravinylcyclotetrasiloxane, when 500-1000r/min high-speed mixing to material temperature reaches 60-70 DEG C, add ketone resin, dimethyl fumarate, aluminum isopropylate, antimony sulfide, when 1500-2000r/min high-speed mixing to material temperature reaches 80-90 DEG C, add remaining raw material, when 1000-1500r/min high-speed mixing to material temperature reaches 100-120 DEG C, then transport material in cold mixer, be cooled to 40-50 DEG C, discharging, dry, pulverize, sieve, pack.
Beneficial effect of the present invention:
Wilkinite of the present invention is after modification, improve the consistency of inorganic particulate and organic polymer matrix, reduce and be separated, more be conducive to the dispersion of wilkinite in organic phase, improve bentonitic filling properties and reinforcing effect, significantly improve shock strength and the tensile strength of matrix material, improve the mechanical property of matrix material.Meanwhile, the filling of modified alta-mud can improve the performance such as thermotolerance, resistance to deterioration, erosion resistance, oil-proofness of matrix material, has a extensive future.
Embodiment
A kind of thermoplastic elastomer electric wire and cable material modified alta-mud, be made up of the raw material of following weight (kg): wilkinite 48, dimethyl fumarate 6, ketone resin 18, gama wax 4.5, dry powder 7, nano-sized magnesium titanate 5, petroleum coke powder 8, aluminum isopropylate 4, antimony sulfide 3, adjacent diallyl bisphenol 2, Neo Heliopan E1000 1.5, t etram-ethyltetravinylcyclotetrasiloxane 2.5, N, N'-phenylbenzene-1,3-propylene diamine 1.5, auxiliary agent 3;
Described auxiliary agent is mixed by the raw material of following weight (kg): diphenyl methane dimaleimide 4, two (t-butylperoxyisopropyl) benzene 3, pentalyn 5, zinc-ethylphenyl dithiocarbamate 3, tetra isopropyl two (dioctyl phosphito acyloxy) titanic acid ester 2, two Imidurea 4, N-phenyl-2-naphthylamine 2,4,4'-butylidene two (the 6-tertiary butyl-3-methylphenol) 2.5, stannous octoate 2.
Thermoplastic elastomer electric wire and cable material method for preparing modified bentonite, comprise the following steps: first bentonite in powder is broken to the fine powder that mean particle size is 2-5 μm, drop into again in high-speed mixer, add dry powder, nano-sized magnesium titanate, petroleum coke powder, gama wax, t etram-ethyltetravinylcyclotetrasiloxane, when 500-1000r/min high-speed mixing to material temperature reaches 60-70 DEG C, add ketone resin, dimethyl fumarate, aluminum isopropylate, antimony sulfide, when 1500-2000r/min high-speed mixing to material temperature reaches 80-90 DEG C, add remaining raw material, when 1000-1500r/min high-speed mixing to material temperature reaches 100-120 DEG C, then transport material in cold mixer, be cooled to 40-50 DEG C, discharging, dry, pulverize, sieve, pack.
The modified alta-mud that above-described embodiment obtains is as shown in the table for the performance test results of filling thermoplastic elastomer electric wire and cable material:
The performance test results of the filling-modified bentonitic thermoplastic elastomer electric wire and cable material of table 1
Claims (2)
1. a thermoplastic elastomer electric wire and cable material modified alta-mud, it is characterized in that, be made up of the raw material of following weight part: wilkinite 46-54, dimethyl fumarate 4-8, ketone resin 15-20, gama wax 3-6, dry powder 5-10, nano-sized magnesium titanate 4-6, petroleum coke powder 5-10, aluminum isopropylate 3-5, antimony sulfide 2-4, adjacent diallyl bisphenol 1.5-2.5, Neo Heliopan E1000 1-2, t etram-ethyltetravinylcyclotetrasiloxane 2-3, N, N'-phenylbenzene-1,3-propylene diamine 1-2, auxiliary agent 2-4;
Described auxiliary agent is mixed by the raw material of following weight part: diphenyl methane dimaleimide 3-4, two (t-butylperoxyisopropyl) benzene 2-3, pentalyn 4-5, zinc-ethylphenyl dithiocarbamate 2-3, tetra isopropyl two (dioctyl phosphito acyloxy) titanic acid ester 1-2, two Imidurea 2-4, N-phenyl-2-naphthylamine 1-2, two (the 6-tertiary butyl-3-methylphenol) 1.5-2.5, the stannous octoate 1-2 of 4,4'-butylidenes.
2. a thermoplastic elastomer electric wire and cable material method for preparing modified bentonite as claimed in claim 1, it is characterized in that comprising the following steps: first bentonite in powder is broken to the fine powder that mean particle size is 2-5 μm, drop into again in high-speed mixer, add dry powder, nano-sized magnesium titanate, petroleum coke powder, gama wax, t etram-ethyltetravinylcyclotetrasiloxane, when 500-1000r/min high-speed mixing to material temperature reaches 60-70 DEG C, add ketone resin, dimethyl fumarate, aluminum isopropylate, antimony sulfide, when 1500-2000r/min high-speed mixing to material temperature reaches 80-90 DEG C, add remaining raw material, when 1000-1500r/min high-speed mixing to material temperature reaches 100-120 DEG C, then transport material in cold mixer, be cooled to 40-50 DEG C, discharging, dry, pulverize, sieve, pack.