CN104194459A - 一种涂料用改性凹凸棒土填料及其制备方法 - Google Patents

一种涂料用改性凹凸棒土填料及其制备方法 Download PDF

Info

Publication number
CN104194459A
CN104194459A CN201410383584.5A CN201410383584A CN104194459A CN 104194459 A CN104194459 A CN 104194459A CN 201410383584 A CN201410383584 A CN 201410383584A CN 104194459 A CN104194459 A CN 104194459A
Authority
CN
China
Prior art keywords
parts
attapulgite
powder
coating
packing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410383584.5A
Other languages
English (en)
Inventor
李振国
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
MINGGUANG GUOXING ATTAPULGITE CLAY Co Ltd
Original Assignee
MINGGUANG GUOXING ATTAPULGITE CLAY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by MINGGUANG GUOXING ATTAPULGITE CLAY Co Ltd filed Critical MINGGUANG GUOXING ATTAPULGITE CLAY Co Ltd
Priority to CN201410383584.5A priority Critical patent/CN104194459A/zh
Publication of CN104194459A publication Critical patent/CN104194459A/zh
Pending legal-status Critical Current

Abstract

一种涂料用改性凹凸棒土填料,由下列重量份的原料制成：钛酸酯偶联剂1-2、聚丙烯酰胺3-5、醋酸丁酸纤维素2-3、乙二醇4-5、二甲基甲酰胺1-2、纳米氧化铝2-3、二乙基氨基乙基(甲基)丙烯酸酯1-2、甲基丙烯酸酯1-2、过硫酸铵0.2-0.4、凹凸棒土100-120、水适量、助剂5-10、3-5%盐酸溶液30-40；本发明改性凹凸棒土经过高分子聚合改性，表面亲油性增强，增加了涂料的悬浮性、触变性，而且增稠性好，漆膜更丰满，开罐效果更佳；通过添加纳米氧化铝，能够增加涂料的耐磨性能，在粉末涂料中助流动，提高上粉率。

Description

一种涂料用改性凹凸棒土填料及其制备方法
技术领域
本发明属于凹凸棒土加工领域，特别涉及一种涂料用改性凹凸棒土填料及其制备方法。
背景技术
凹凸棒石具有独特的分散、耐高温、抗盐碱等良好的胶体性质和较高的吸附脱色能力。并具有一定的可塑性及粘结力，吸水性强，湿时具粘性和可塑性，干燥后收缩小，不大显裂纹，水浸泡崩散，悬浮液遇电介质不絮凝沉淀。因此凹凸棒土被广泛用于污水处理、吸附净化、洗涤剂、橡胶、涂料、造纸、轻工、农业、化妆品等诸多领域，是一种重要的非金属矿产。
为了进一步提高凹凸棒土的使用效果，增强其整体的物化性能，通常在使用前对其进行改性处理，来提高凹凸棒土的分散性能，凝胶粘度，胶体率，流变性能。目前的改性凹凸棒土在很多性能上不能满足生产生活的需要，还需要进一步改进其性能。
发明内容
本发明的目的在于提供一种涂料用改性凹凸棒土填料及其制备方法，该凹凸棒土表面亲油性增强，增加了涂料的悬浮性、触变性，而且增稠性好，漆膜更丰满，开罐效果更佳，能够增加涂料的耐磨性能，在粉末涂料中助流动，提高上粉率。
本发明的技术方案如下：
一种涂料用改性凹凸棒土填料,其特征在于由下列重量份的原料制成：钛酸酯偶联剂1-2、聚丙烯酰胺3-5、醋酸丁酸纤维素2-3、乙二醇4-5、二甲基甲酰胺1-2、纳米氧化铝2-3、二乙基氨基乙基(甲基)丙烯酸酯1-2、甲基丙烯酸酯1-2、过硫酸铵0.2-0.4、凹凸棒土100-120、水适量、助剂5-10、3-5%盐酸溶液30-40；
所述助剂由下列重量份的原料制成：棕榈酸异辛酯0.2-0.3、多孔硅胶珠2-3、聚氨酯树脂0.4-0.6、乙二醇3-5、维生素E0.3-0.4、活性氧化铝0.3-0.5、亚麻油酸0.2-0.3、木质素磺酸钠0.3-0.4、珍珠粉1-1.5、竹纤维0.2-0.3、七水硫酸镁0.1-0.2、木炭粉2-3、琥珀酸0.2-0.3、双硬脂酸铝0.2-0.4、麦饭石粉3-5、硅烷偶联剂KH-5721-2；制备方法为：将多孔硅胶珠、珍珠粉、木炭粉、麦饭石粉、硅烷偶联剂KH-572混合研磨均匀，得到混合粉末；再将其他剩余成分混合搅拌均匀，与所得粉末混合研磨20-30分钟，再加热至60-70℃，研磨反应30-40分钟，即得。
所述的涂料用改性凹凸棒土填料的制备方法，其特征在于包括以下步骤：
（1）将凹凸棒土送入煅烧炉，在300-400℃下煅烧3-4小时,取出粉碎，过20目筛，加入340-360重量份的水中，在100-200转/分下搅拌10-12小时，得到凹凸棒土悬浮液，加入3-5%盐酸溶液，加热至50-60℃，搅拌1-2小时，过滤，水洗至PH值为6-8，再过滤，干燥，得到活化凹凸棒土粉末；
（2）将其他剩余成分研磨均匀，加入剩余水中，搅拌均匀，得到浆料；
（3）向凹凸棒土粉末吹50-60℃的热空气使其翻腾，再向翻腾的粉末中喷入雾状的第（2）步得到的浆料，使二者充分混合后，保持温度为50-60℃，继续翻腾30-40分钟；
(4)将第（3）步得到的混合物料烘干，研磨成5-80μm的颗粒，即得。
本发明的有益效果
本发明改性凹凸棒土经过高分子聚合改性，表面亲油性增强，增加了涂料的悬浮性、触变性，而且增稠性好，漆膜更丰满，开罐效果更佳；通过添加纳米氧化铝，能够增加涂料的耐磨性能，在粉末涂料中助流动，提高上粉率。
具体实施方式
一种涂料用改性凹凸棒土填料,由下列重量份（公斤）的原料制成：钛酸酯偶联剂1.5、聚丙烯酰胺4、醋酸丁酸纤维素2.5、乙二醇4.5、二甲基甲酰胺1.5、纳米氧化铝2.5、二乙基氨基乙基(甲基)丙烯酸酯1.5、甲基丙烯酸酯1.5、过硫酸铵0.3、凹凸棒土110、水适量、助剂7、4%盐酸溶液36；
所述助剂由下列重量份（公斤）的原料制成：棕榈酸异辛酯0.2、多孔硅胶珠2.5、聚氨酯树脂0.5、乙二醇4、维生素E0.4、活性氧化铝0.4、亚麻油酸0.3、木质素磺酸钠0.4、珍珠粉1.3、竹纤维0.2、七水硫酸镁0.2、木炭粉2.5、琥珀酸0.2、双硬脂酸铝0.3、麦饭石粉4、硅烷偶联剂KH-5721.5；制备方法为：将多孔硅胶珠、珍珠粉、木炭粉、麦饭石粉、硅烷偶联剂KH-572混合研磨均匀，得到混合粉末；再将其他剩余成分混合搅拌均匀，与所得粉末混合研磨25分钟，再加热至65℃，研磨反应35分钟，即得。
所述的涂料用改性凹凸棒土填料的制备方法，包括以下步骤：
（1）将凹凸棒土送入煅烧炉，在350℃下煅烧3.5小时,取出粉碎，过20目筛，加入350重量份的水中，在150转/分下搅拌12小时，得到凹凸棒土悬浮液，加入4%盐酸溶液，加热至55℃，搅拌1.5小时，过滤，水洗至PH值为6，再过滤，干燥，得到活化凹凸棒土粉末；
（2）将其他剩余成分研磨均匀，加入剩余水中，搅拌均匀，得到浆料；
（3）向凹凸棒土粉末吹55℃的热空气使其翻腾，再向翻腾的粉末中喷入雾状的第（2）步得到的浆料，使二者充分混合后，保持温度为55℃，继续翻腾35分钟；
(4)将第（3）步得到的混合物料烘干，研磨成5-80μm的颗粒，即得。
实验数据：
本实施例改性凹凸棒土比表面积为302㎡/g,按4%加入水中，测试粘度为9783mPa.s,用该凹凸棒土作为印花涂料填料，花型清晰，不粘网。

Claims (2)

1.一种涂料用改性凹凸棒土填料,其特征在于由下列重量份的原料制成：钛酸酯偶联剂1-2、聚丙烯酰胺3-5、醋酸丁酸纤维素2-3、乙二醇4-5、二甲基甲酰胺1-2、纳米氧化铝2-3、二乙基氨基乙基(甲基)丙烯酸酯1-2、甲基丙烯酸酯1-2、过硫酸铵0.2-0.4、凹凸棒土100-120、水适量、助剂5-10、3-5%盐酸溶液30-40；
所述助剂由下列重量份的原料制成：棕榈酸异辛酯0.2-0.3、多孔硅胶珠2-3、聚氨酯树脂0.4-0.6、乙二醇3-5、维生素E0.3-0.4、活性氧化铝0.3-0.5、亚麻油酸0.2-0.3、木质素磺酸钠0.3-0.4、珍珠粉1-1.5、竹纤维0.2-0.3、七水硫酸镁0.1-0.2、木炭粉2-3、琥珀酸0.2-0.3、双硬脂酸铝0.2-0.4、麦饭石粉3-5、硅烷偶联剂KH-5721-2；制备方法为：将多孔硅胶珠、珍珠粉、木炭粉、麦饭石粉、硅烷偶联剂KH-572混合研磨均匀，得到混合粉末；再将其他剩余成分混合搅拌均匀，与所得粉末混合研磨20-30分钟，再加热至60-70℃，研磨反应30-40分钟，即得。
2.根据权利要求1所述的涂料用改性凹凸棒土填料的制备方法，其特征在于包括以下步骤：
（1）将凹凸棒土送入煅烧炉，在300-400℃下煅烧3-4小时,取出粉碎，过20目筛，加入340-360重量份的水中，在100-200转/分下搅拌10-12小时，得到凹凸棒土悬浮液，加入3-5%盐酸溶液，加热至50-60℃，搅拌1-2小时，过滤，水洗至PH值为6-8，再过滤，干燥，得到活化凹凸棒土粉末；
（2）将其他剩余成分研磨均匀，加入剩余水中，搅拌均匀，得到浆料；
（3）向凹凸棒土粉末吹50-60℃的热空气使其翻腾，再向翻腾的粉末中喷入雾状的第（2）步得到的浆料，使二者充分混合后，保持温度为50-60℃，继续翻腾30-40分钟；
(4)将第（3）步得到的混合物料烘干，研磨成5-80μm的颗粒，即得。
CN201410383584.5A 2014-08-06 2014-08-06 一种涂料用改性凹凸棒土填料及其制备方法 Pending CN104194459A (zh)