CN104178276A - Nano-metal composite agent applied to turbine oil - Google Patents
Nano-metal composite agent applied to turbine oil Download PDFInfo
- Publication number
- CN104178276A CN104178276A CN201310205394.XA CN201310205394A CN104178276A CN 104178276 A CN104178276 A CN 104178276A CN 201310205394 A CN201310205394 A CN 201310205394A CN 104178276 A CN104178276 A CN 104178276A
- Authority
- CN
- China
- Prior art keywords
- metal
- powder
- oil
- oxidation
- base oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a nano-metal composite agent applied to turbine oil. The nano-metal composite agent consists of base oil, an antioxidant, a rusting inhibitor, a dispersant, a metal deactivator, an extreme pressure additive, a demulsification agent, metal molybdenum powder, metal rhenium powder and vitamin (E). The antioxidant is a mixture of diarylamine and tributyl phosphite; the rusting inhibitor is ethoxy phenol; the dispersant is ash-free phosphate ester; the metal deactivator is benzotriazole; the extreme pressure additive is a molybdenum salt of phosphate ester; and the demulsification agent is polyalkoxy polyol. The making method is simple, and the prepared product can effectively and comprehensively enhance various performance requirements of turbine lubricating oil. The service cycle of lubricating oil is extended, the anti-extreme pressure efficacy of lubricating oil is improved, and the oxidation tolerance, corrosion resistance, blistering resistance, oxidation resistance, oil sludge generation resistance and other efficacy of lubricating oil are comprehensively enhanced. And the comprehensive efficacy can be comprehensively improved.
Description
(1) technical field
The present invention relates to a kind of turbine oil nano metal composite additive, particularly a kind of preparation scheme and manufacture method that is applied in turbine oil nano metal recombiner.
(2) background technology
Current, because continuous lifting and the demand of the develop rapidly of automotive industry and human lives's condition, increasing people has bought automobile, and in big and medium-sized cities, automobile occupation rate is higher, almost one of each household, everyone one, family out of the ordinary.And along with the continuous progress of human civilization, the continuous renewal of all kinds of mechanical means, and the development of constantly bringing forth new ideas of the mechanical means of various new technologies and automotive industry, requirement with the lifting of human survival condition and to environment etc. is all had higher requirement to lube product, reaches upper limit (UL) and the most permanent drain period of energy-saving and emission-reduction from the phase.Therefore people have proposed higher performance requriements to turbine lube oil simultaneously too, and main effect of turbine lube oil must reach, anti-oxidant; Anticorrosive; Anti-greasy filth produces; Anti-foaming; Provide lubricated; Anti-extreme pressure; Wear-resistant changing; And good flowing.But the producer of the current turbine oil composite additive that can produce fine quality is few, the composite additive of property indices that can reach turbine is completely rare especially, and some lubricating oil processing is high has to the various composite additives of external import.But because turbine and constantly bringing forth new ideas of other various mechanical means require each class lubricating oil also will constantly bring forth new ideas to reach the requirement of all kinds of mechanical means and turbine.The manufacturer of existing turbine oil, is more to adopt several single doses to do physics blending, and product price is raise, and the manufacturer out of the ordinary who simultaneously has just thinks of profit, and the product life cycle of producing is short, various effect differences, and some emphasis are wear-resistant; The anti-extreme pressure of some emphasis; Some emphasis are anticorrosive; Some emphasis oil product colors, therefore the undesirable comprehensive effect of result of use is poor, causes the drain period short, wastes energy.Comprehensive good the price very expensive and complex manufacturing again of effect.
(3) summary of the invention
Main purpose of the present invention is the problem existing in above-mentioned technology, provides one to prepare scheme more scientific, and manufacture method is simpler, price is low, and quality is high, can reach higher environmental requirement simultaneously, anti-oxidant, anticorrosive, anti-greasy filth produces, anti-foaming, anti-extreme pressure, wear-resistant, good lubricating is provided, and can take away fast heat by circulating, and have good low temperature flowability, the one that can extend the drain period is applied in turbine oil nano metal recombiner.
Technical scheme of the present invention:
One is applied in turbine oil nano metal recombiner, it is characterized in that: by base oil; Oxidation inhibitor; Rust oxidation; Dispersion agent; Metal passivator; Extreme-pressure additive; Demulsifying agent; Metal molybdenum powder; Rhenium metal powder; VITAMIN (E) composition.Described antioxidant is the mixture of diaryl-amine and tributyl phosphate; Described rust oxidation is oxyethyl group phenols; Described dispersion agent is ashless phosphoric acid ester; Described metal passivator is benzotriazole; Described extreme-pressure additive is the molybdenum salt of phosphoric acid ester; Described demulsifying agent is for having gathered oxygen Quito alcohol.The weight percent of each component is: oxidation inhibitor 5-27%; Rust oxidation 3-17%; Dispersion agent 2-22%; Metal passivator 4-18%; Extreme-pressure additive 2-11%; Demulsifying agent 5-15%; Metal molybdenum 0.5-6%; Rhenium metal 0.5-6%; VITAMIN (E) 1-6%, surplus is base oil.
One such application is at turbine oil nano metal recombiner, it is characterized in that: base oil is that the 500SN in any one component and the mineral base oil in synthetic base oil Poly alpha Olefins (PAO), polyethers, polyol ester and two fat, any one component subtracting in four lines, M14,32#, 46#, 68#, 5 centistokes, 10 centistokes combine, and the weight percent of two kinds of components is 1: 2.Also can be combined by 150BS and 500SN, any two kinds of components of subtracting in four lines, M14,32#, 46#, 68#, 5 centistokes, 10 centistokes, the weight quota of three kinds of components is 1: 1: 1.
One such application, at turbine oil nano metal recombiner, is characterized in that: metal molybdenum powder and rhenium metal powder are nanoscale powder material, and its grain graininess is 20-40nm.
One such application, at turbine oil nano metal recombiner, is characterized in that: oxidation inhibitor is that diaryl-amine and two kinds of components of tributyl phosphate combine, and the weight quota of two kinds of components is 3: 1.
One such application, at turbine oil nano metal recombiner, is characterized in that: by base oil; Oxidation inhibitor; Rust oxidation; Dispersion agent; Metal passivator; Extreme-pressure additive; Demulsifying agent; Metal molybdenum powder; Rhenium metal powder; VITAMIN (E) mixes, and heats and controls temperature in 55-85 DEG C, stirs 60-360 minute, goes out product of the present invention.
Advantage of the present invention: manufacture method of the present invention is simple, the product making is lower than other like product prices, and quality is high, effectively the properties requirement of General Promotion turbine lube oil.Extend the life cycle of lubricating oil, improve anti-extreme pressure effect of lubricating oil, the resistance to oxidation of General Promotion lubricating oil, anticorrosive, anti-foaming, the effects such as the generation of anti-oxidant and anti-greasy filth improve more.Comprehensive effect is able to comprehensive raising, and product of the present invention can 90% biological degradation, the environmental requirement that surmounts existing like product completely.
(4) embodiment
Embodiment 1
One is applied in turbine oil nano metal recombiner, by base oil; Oxidation inhibitor; Rust oxidation; Dispersion agent; Metal passivator; Extreme-pressure additive; Demulsifying agent; Metal molybdenum powder; Rhenium metal powder; VITAMIN (E) composition.Base oil is synthetic base oil Poly alpha Olefins (PAO) and two kinds of component compositions of 5 centistokes, and the weight quota of two kinds of components is 1: 2; Oxidation inhibitor is the mixture of diaryl-amine and tributyl phosphate; Rust oxidation is oxyethyl group phenols; Dispersion agent is ashless phosphoric acid ester; Metal passivator is benzotriazole; Extreme-pressure additive is the molybdenum salt of phosphoric acid ester; Demulsifying agent is for having gathered oxygen Quito alcohol; Metal molybdenum powder and metal magnesium powder are nanoscale powder material, and mean particle size is 20-40nm.The weight percent of each component is: base oil 15%; Oxidation inhibitor 24%; Rust oxidation 15%; Dispersion agent 16%; Metal passivator 12%; Extreme-pressure additive 8%; Demulsifying agent 5%; Metal molybdenum powder 2%; Rhenium metal powder 2%; VITAMIN (E) 1%.By base oil; Oxidation inhibitor; Rust oxidation; Dispersion agent; Metal passivator; Extreme-pressure additive; Demulsifying agent; Metal molybdenum powder; Rhenium metal powder; VITAMIN (E) should add weight percent metering by each component, then mixes, and heats and controls temperature between 50-70 DEG C, stirs 90 minutes, goes out this product.
This product is added in typical turbine machine oil by adding metering 5%, by practical application and comparison and detection, draws following result:
1. anti-oxidation efficacy promotes more than 70%.
2. corrosion inhibition effect promotes more than 85%.
3. anticorrosive effect promotes more than 90%.
4. anti-extreme pressure effect promotes more than 2 times.
5. wear-resistant effect promotes more than 1.5 times.
6. the drain period promotes more than 1 times.
Embodiment 2
One is applied in turbine oil nano metal recombiner, by base oil; Oxidation inhibitor; Rust oxidation; Dispersion agent; Metal passivator; Extreme-pressure additive; Demulsifying agent; Metal molybdenum powder; Rhenium metal powder; VITAMIN (E) composition.Base oil is mineral base oil, 150BS and 32# and subtracts three kinds of components of four lines and combine, and the weight quota of three kinds of components is 1: 1: 1; Oxidation inhibitor is the mixture of diaryl-amine and tributyl phosphate; Rust oxidation is oxyethyl group phenols; Dispersion agent is ashless phosphoric acid ester; Metal passivator is benzotriazole; Extreme-pressure additive is the molybdenum salt of phosphoric acid ester; Demulsifying agent is for having gathered oxygen Quito alcohol; Metal molybdenum powder and metal magnesium powder are nanoscale powder material, and mean particle size is 20-40nm.The weight percent of each component is: base oil 13%; Oxidation inhibitor 21%; Rust oxidation 16%; Dispersion agent 15%; Metal passivator 15%; Extreme-pressure additive 9%; Demulsifying agent 5%; Metal molybdenum powder 2.5%; Rhenium metal powder 2.5%; VITAMIN (E) 1%.By base oil; Oxidation inhibitor; Rust oxidation; Dispersion agent; Metal passivator; Extreme-pressure additive; Demulsifying agent; Metal molybdenum powder; Rhenium metal powder; VITAMIN (E) should add weight percent metering by each component, then mixes, and heats and controls temperature between 50-70 DEG C, stirs 360 minutes, goes out this product.
This product is added in typical turbine machine oil by adding metering 6%, by practical application and comparison and detection, draws following result:
1. anti-oxidation efficacy promotes more than 85%.
2. corrosion inhibition effect promotes more than 95%.
3. anticorrosive effect promotes more than 1.3 times.
4. anti-extreme pressure effect promotes more than 3 times.
5. wear-resistant effect promotes more than 2 times.
6. the drain period promotes more than 1.2 times.
Claims (5)
1. be applied in a turbine oil nano metal recombiner, it is characterized in that: by base oil; Oxidation inhibitor; Rust oxidation; Dispersion agent; Metal passivator; Extreme-pressure additive; Demulsifying agent; Metal molybdenum powder; Rhenium metal powder; VITAMIN (E) composition.Described antioxidant is the mixture of diaryl-amine and tributyl phosphate; Described rust oxidation is oxyethyl group phenols; Described dispersion agent is ashless phosphoric acid ester; Described metal passivator is benzotriazole; Described extreme-pressure additive is the molybdenum salt of phosphoric acid ester; Described demulsifying agent is for having gathered oxygen Quito alcohol.The weight percent of each component is: oxidation inhibitor 5-27%; Rust oxidation 3-17%; Dispersion agent 2-22%; Metal passivator 4-18%; Extreme-pressure additive 2-11%; Demulsifying agent 5-15%; Metal molybdenum 0.5-6%; Rhenium metal 0.5-6%; VITAMIN (E) 1-6%, surplus is base oil.
2. one according to claim 1 is applied in turbine oil nano metal recombiner, it is characterized in that: base oil is that the 500SN in any one component and the mineral base oil in synthetic base oil Poly alpha Olefins (PAO), polyethers, polyol ester and two fat, any one component subtracting in four lines, M14,32#, 46#, 68#, 5 centistokes, 10 centistokes combine, and the weight percent of two kinds of components is 1: 2.Also can be combined by 150BS and 500SN, any two kinds of components of subtracting in four lines, M14,32#, 46#, 68#, 5 centistokes, 10 centistokes, the weight quota of three kinds of components is 1: 1: 1.
3. one according to claim 1 is applied in turbine oil nano metal recombiner, it is characterized in that: metal molybdenum powder and rhenium metal powder are nanoscale powder material, and its grain graininess is 20-40nm.
4. one according to claim 1 is applied in turbine oil nano metal recombiner, it is characterized in that: oxidation inhibitor is that diaryl-amine and two kinds of components of tributyl phosphate combine, and the weight quota of two kinds of components is 3: 1.
5. one according to claim 1 is applied in turbine oil nano metal recombiner, it is characterized in that: by base oil; Oxidation inhibitor; Rust oxidation; Dispersion agent; Metal passivator; Extreme-pressure additive; Demulsifying agent; Metal molybdenum powder; Rhenium metal powder; VITAMIN (E) mixes, and heats and controls temperature in 55-85 DEG C, stirs 60-360 minute, goes out product of the present invention.