CN104177743A - 新型沥青路面雾封层养护材料及制备方法 - Google Patents

新型沥青路面雾封层养护材料及制备方法 Download PDF

Info

Publication number
CN104177743A
CN104177743A CN201410467946.9A CN201410467946A CN104177743A CN 104177743 A CN104177743 A CN 104177743A CN 201410467946 A CN201410467946 A CN 201410467946A CN 104177743 A CN104177743 A CN 104177743A
Authority
CN
China
Prior art keywords
parts
mist sealing
asphalt pavement
conserving material
new type
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410467946.9A
Other languages
English (en)
Inventor
张细贞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHONGQING LUOZI WOKE TRAFFIC TECHNOLOGY Co Ltd
Original Assignee
CHONGQING LUOZI WOKE TRAFFIC TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHONGQING LUOZI WOKE TRAFFIC TECHNOLOGY Co Ltd filed Critical CHONGQING LUOZI WOKE TRAFFIC TECHNOLOGY Co Ltd
Priority to CN201410467946.9A priority Critical patent/CN104177743A/zh
Publication of CN104177743A publication Critical patent/CN104177743A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种新型沥青路面雾封层养护材料,其成分及各种成分的质量份数比为:稠环芳烃油30份、聚异丁烯液体橡胶10份、丙烯酸树脂20份、湖沥青10份、二甲苯30份。本发明还公开了前述新型沥青路面雾封层养护材料的制备方法。本发明的有益技术效果是:提供了一种性能较好的沥青路面养护材料。

Description

新型沥青路面雾封层养护材料及制备方法
技术领域
本发明涉及一种沥青路面雾封层养护技术,尤其涉及一种新型沥青路面雾封层养护材料及制备方法。
背景技术
路面在使用过程中其性能不是直线下降的,在使用初期,其服务能力下降较缓慢,但当损坏状况超过某一限值时,路面的服务能力就开始急剧下降,病害急剧增多。若在此之前就采取预防性养护措施,则可及时阻止这种发展趋势,从而使路面始终维持较好的服务状况,可以有效地延长路面的寿命,本发明即是针对路面养护问题提出的一种新材料。
发明内容
本发明提出了一种新型沥青路面雾封层养护材料,所述新型沥青路面雾封层养护材料的成分及各种成分的质量份数比为:稠环芳烃油30份、聚异丁烯液体橡胶10份、丙烯酸树脂20份、湖沥青10份、二甲苯30份。
前述配方的原理是:沥青路面早期性能的下降主要是沥青在热、光、氧、水等环境因素的共同作用下其组成成分发生迁移和化学变化,逐渐变硬变脆,本发明的配方中含有聚异丁烯液体橡胶和稠环芳烃油,借助二甲苯的溶解和扩散渗透作用,能够为老化沥青补充油份和胶质,从而恢复老化沥青的性能,而耐候性能优良的丙烯酸树脂和湖沥青能封闭路表面,提高路面对热、光、氧、水等环境因素的抵抗能力,因而可以显著改善路面的服务水平,延长道路使用寿命。
优选地,所述稠环芳烃油中芳烃含量≥80%,稠环芳烃油的运动粘度为5~40mm2/s。
优选地,所述聚异丁烯液体橡胶的分子量为1000~30000。
优选地,所述丙烯酸树脂的玻璃化温度大于50℃。
优选地,所述湖沥青是软化点高于100℃的特立尼达湖沥青。
为了便于本领域技术人员实施,本发明还公开了前述新型沥青路面雾封层养护材料的制备方法,其具体步骤为:
1)按配方称取各种成分备用;
2)将二甲苯加入分散釜中,然后向二甲苯中缓慢加入湖沥青和丙烯酸树脂,加入湖沥青和丙烯酸树脂的同时,对混合物进行搅拌,直至湖沥青和丙烯酸树脂完全溶解,得到混合物A;
3)向混合物A中加入聚异丁烯液体橡胶和稠环芳烃油,搅拌至混合均匀,新型沥青路面雾封层养护材料制备完成。
本发明的有益技术效果是:提供了一种性能较好的沥青路面养护材料。
具体实施方式
一种新型沥青路面雾封层养护材料,其创新在于:所述新型沥青路面雾封层养护材料的成分及各种成分的质量份数比为:稠环芳烃油30份、聚异丁烯液体橡胶10份、丙烯酸树脂20份、湖沥青10份、二甲苯30份。
进一步地,所述稠环芳烃油中芳烃含量≥80%,稠环芳烃油的运动粘度为5~40mm2/s。
进一步地,所述聚异丁烯液体橡胶的分子量为1000~30000。
进一步地,所述丙烯酸树脂的玻璃化温度大于50℃。
进一步地,所述湖沥青是软化点高于100℃的特立尼达湖沥青。
一种新型沥青路面雾封层养护材料的制备方法,其创新在于:所述新型沥青路面雾封层养护材料的成分及各种成分的质量份数比为:稠环芳烃油30份、聚异丁烯液体橡胶10份、丙烯酸树脂20份、湖沥青10份、二甲苯30份;按如下方法制备新型沥青路面雾封层养护材料:
1)按配方称取各种成分备用;
2)将二甲苯加入分散釜中,然后向二甲苯中缓慢加入湖沥青和丙烯酸树脂,加入湖沥青和丙烯酸树脂的同时,对混合物进行搅拌,直至湖沥青和丙烯酸树脂完全溶解,得到混合物A;
3)向混合物A中加入聚异丁烯液体橡胶和稠环芳烃油,搅拌至混合均匀,新型沥青路面雾封层养护材料制备完成。
为说明本发明提供的沥青路面雾封层材料的有益效果,根据国家标准的试验方法,结合本发明方案的沥青路面雾封层材料与常用的雾封层材料乳化沥青进行比较,分别检测路面在养护前及施用养护材料一段时间后的渗水系数和抗滑系数,以评价材料对路面的养护效果。
选择已投入运营2年的沥青路面,在行车道上分别按照0.25Kg/m2的用量喷涂上本发明的沥青路面雾封层材料和乳化沥青,养护3h,检测渗水系数和抗滑系数后开放交通,6个月和18个月再检测路面的渗水系数和抗滑系数,结果如下表:
从上表可以看出,本发明提供的沥青路面雾封层养护材料,基本不降低路面的抗滑性,能够显著封闭沥青路面,增强路面对热、光、氧、水等环境因素的抵抗能力,从而提高路面的服务能力和延长道路的使用寿命。

Claims (6)

1.一种新型沥青路面雾封层养护材料,其特征在于:所述新型沥青路面雾封层养护材料的成分及各种成分的质量份数比为:稠环芳烃油30份、聚异丁烯液体橡胶10份、丙烯酸树脂20份、湖沥青10份、二甲苯30份。
2.根据权利要求1所述的沥青路面雾封层养护材料,其特征在于:所述稠环芳烃油中芳烃含量≥80%,稠环芳烃油的运动粘度为5~40mm2/s。
3.根据权利要求1所述的沥青路面雾封层养护材料,其特征在于:所述聚异丁烯液体橡胶的分子量为1000~30000。
4.根据权利要求1所述的沥青路面雾封层养护材料,其特征在于:所述丙烯酸树脂的玻璃化温度大于50℃。
5.根据权利要求1所述的沥青路面雾封层养护材料,其特征在于:所述湖沥青是软化点高于100℃的特立尼达湖沥青。
6.一种新型沥青路面雾封层养护材料的制备方法,其特征在于:所述新型沥青路面雾封层养护材料的成分及各种成分的质量份数比为:稠环芳烃油30份、聚异丁烯液体橡胶10份、丙烯酸树脂20份、湖沥青10份、二甲苯30份;按如下方法制备新型沥青路面雾封层养护材料:
1)按配方称取各种成分备用;
2)将二甲苯加入分散釜中,然后向二甲苯中缓慢加入湖沥青和丙烯酸树脂,加入湖沥青和丙烯酸树脂的同时,对混合物进行搅拌,直至湖沥青和丙烯酸树脂完全溶解,得到混合物A;
3)向混合物A中加入聚异丁烯液体橡胶和稠环芳烃油,搅拌至混合均匀,新型沥青路面雾封层养护材料制备完成。
CN201410467946.9A 2014-09-15 2014-09-15 新型沥青路面雾封层养护材料及制备方法 Pending CN104177743A (zh)