CN104176988A - Organic/inorganic composite material for rapidly repairing pit slots of bituminous pavement and preparation method thereof - Google Patents
Organic/inorganic composite material for rapidly repairing pit slots of bituminous pavement and preparation method thereof Download PDFInfo
- Publication number
- CN104176988A CN104176988A CN201410417601.2A CN201410417601A CN104176988A CN 104176988 A CN104176988 A CN 104176988A CN 201410417601 A CN201410417601 A CN 201410417601A CN 104176988 A CN104176988 A CN 104176988A
- Authority
- CN
- China
- Prior art keywords
- parts
- component
- preparation
- uniformly mixed
- composite material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses an organic/inorganic composite material for rapidly repairing pit slots of a bituminous pavement, which is prepared from the following main raw materials of polymethylene polyphenyl polyisocyanates, a polyurethane prepolymer, polyether polyol, petroleum asphalt, a catalyst, sodium silicate powder, carborundum and the like. The composition material comprises components A, B and C, wherein the components A and the component B are blended with the component C after being mixed, and can be quickly solidified after being cast into the pit slots at room temperature, so that the composite material has strong caking property and similar rigidity with an original bituminous pavement, and the travelling stationarity and comfortableness are achieved after restoration. The composite material is simple and convenient to construct, rapid, efficient and environmentally friendly, the setting time is smaller than or equal to 30 minutes, and the bituminous pavement can be opened after 90 minutes, so that the rapid repairing purpose is achieved, and the effect on traffic jam caused by pavement rehabilitation is greatly relieved. The composite material has excellent water tolerance, weather fastness, abrasive resistance and compressive shear resistance, is a novel green material for rapidly repairing pit slots of a pavement, and has positive promotion action and a good application effect on development of a preventive maintenance technology of highways.
Description
Technical field
The present invention relates to a kind of asphalt pavement pit repair materials and preparation method thereof, belong to highway material and applied technical field, relate in particular to organic/inorganic composite material of a kind of quick reparation asphalt pavement pit and preparation method thereof.
Technical background
Asphaltic road-mix surface course has the features such as construction speed is fast, maintenance simple, it is comfortable to drive a vehicle, surfacing, widely applies in China.But after bituminous pavement experience certain hour, due to high loading driving for a long time, extreme climate environment, temperature variation, rain erosion etc., all can damage bituminous pavement in various degree, cause cohesive force between pitch and base-material to reduce, under automotive wheel dynamic load repeated action, pitch comes off from base-material surface, pavement destruction is damaged to profound structure deteriorate development from shallow table gradually, destroys development from the local damage of small area to large-area monoblock.In order to ensure quick, safe, comfortable, the efficient Characteristics of Transportation of motorway, extend the work-ing life of motorway, make the economic and social benefit that its performance is larger, thereby need road pavement to carry out the maintenance and repair of normalization, the generation of the normal operation of guaranteeing highway to try to forestall traffic accidents.
Traditional repair materials is mainly hot-mix asphalt mixture, but this repair materials exists the defect that pollution is high, cost is large, and in addition, the impact of hot-mix asphalt mixture climate condition is larger,, should not construct because temperature is compared with low unsuitable compacting in cold season.Using in recent years more is asphalt cold repairing repair materials, as Emulsified Asphalt Mixture.Asphalt cold repairing repair materials has overcome the defect that hot-mix asphalt mixture low temperature should not be constructed, but in the time using cold repairing asphalt mixture redeck, after needing equal solvent to evaporate completely, just can play the effect of enhancing, so cold repairing asphalt mixture exist initial strength low, strengthen shortcoming slowly, can not reach the object that quick reparation is open to traffic fast, larger to traffic impact.Therefore novel material, new approaches, the novel process that proposes a kind of quick reparation asphalt pavement pit is very meaningful and is necessary.
Publication number is that CN101993222A discloses " a kind of pitch that is exclusively used in redeck and preparation method thereof ", mainly, taking plain asphalt, styrene-butadiene rubber(SBR), wilkinite, vibrin, gasoline, kerosene, talcum powder as raw material, prepare and be exclusively used in the pitch that redeck is used.This pitch is applicable to redeck and uses, can with the good combination of former pavement asphalt, extended work-ing life of highway.
Publication number is that CN102701787A discloses " a kind of bituminous pavement anti-freezing ice injury repairing material and preparation method thereof ", can solve existing maintenance and cannot resist the destruction problem that multigelation produces, its repair materials is made up of road oil hard pitch, coal-tar heavy oil and viscosity reduction permeate agent.
Publication number is that CN1970491A discloses " a kind of cement for quick reparing sill of Asphalt Pavement Semi-rigid Base ", its component is quick-setting and rapid-hardening cement, sand, stone, water reducer, fiber, specialist additive, water etc., can make foreshorten to 4 ~ 8h the repair time of bituminous pavement, alleviate to a certain extent road surface and repaired the impact on traffic congestion.
In addition, Zhang Wenjing, Wang Hui etc. are at " express highway pavement is repaired the research with polyurethane concrete fast " concrete, 2011(5), taking hard polyurethane foam as base mateiral, prepare polyurethane concrete material in conjunction with normal concrete technique, can realize the quick reparation of expressway surface in 2h.
Li Li, Wang Hongbin etc. " the synthetic and performance study of urethane/silicon carbide matrix material " New Chemical Materials, 2014, in 42 (3), with toluene diisocynate and the synthetic performed polymer of diphenylmethanediisocyanate, taking E300 as chainextender synthesis of polyurethane elastomerics, repair as base material road pavement hole groove, can realize the quick reparation of bituminous pavement in 2h.
Although above-mentioned disclosed method, has accelerated the reparation of bituminous pavement to a certain extent, also has some problems, the one, contain organic solvent as gasoline, kerosene, coal tar wet goods, environment is had to pollution, affect operative employee's physical and mental health; The 2nd, the repair materials construction speed taking cement as main base material is slow, and setting rate is slow, and the road closure time is long; The 3rd, after repair materials sclerosis, does not mate with the rigidity of bituminous pavement, split away off from road surface after rolling through vehicle after a while.
Summary of the invention
The present invention is directed to asphalt pavement pit and repair problem, a kind of organic/inorganic composite material of quick reparation bituminous pavement is provided, this type material at normal temperatures just can fast setting, not only bituminous pavement is had to very strong cohesiveness, and do not contain low volatilization and poisonous organic solvent, be a kind of Cost of New Type Asphalt Pavement hole groove material for quickly repairing of environment-friendly type.This type material mixes after cast liquid mixture can flowing time≤10min, ambient cure time≤30min, and 90min has enough loading strengths to be open to traffic, and can guarantee the driving safety of vehicle, reaches the object of quick reparation.The present invention has not only solved the problems such as process complexity problem, curing speed that prior art repairs asphalt pavement pit be slow, and material after repairing has the performances such as good resistance to compression, anti-shearing, water erosion resistent, heat resistanceheat resistant be cold.
For achieving the above object, organic/inorganic composite material of a kind of quick reparation asphalt pavement pit of the present invention and preparation method thereof technical scheme is as follows:
An organic/inorganic composite material for quick reparation asphalt pavement pit, is characterized in that: described matrix material is made up of A, B and C component, and its composition and mass content thereof are as follows:
A component: 82~90 parts of poly methylene poly phenyl poly isocyanates;
10~5 parts of base polyurethane prepolymer for use as;
8~5 parts of propylene glycol carbonates;
B component: 4,450 66~80 parts of type polyether glycols
500 10~7 parts of type polyether glycols;
10~5 parts of dipropylene glycol dibenzoates;
3-chloro-3
'-ethyl-4,4
'2.5~1 parts of-diaminodiphenylmethane;
90
#5~3 parts, petroleum pitch;
1~0.5 part of catalyzer;
5~3 parts of instantly-soluble water glass micro mists;
0.5 part of BYK-A535 defoamer;
C component: 400 parts, silicon carbide;
0~700 part of stone chippings.
For a preparation method for the organic/inorganic composite material of a kind of quick reparation asphalt pavement pit described above, described in it, according to the mass fraction, step is as follows for preparation method:
The preparation of A component
Get 82~90 parts of poly methylene poly phenyl poly isocyanates and be placed in a band stirring mixer, then add 10~5 parts of base polyurethane prepolymer for use as, 8~5 parts of propylene glycol carbonates, are uniformly mixed under normal temperature, obtain A component, and inflated with nitrogen sealing is preserved;
The preparation of B component
By 90
#5~3 parts, petroleum pitch joins in 10~5 parts of dipropylene glycol dibenzoates, stand-by after heating for dissolving;
Get 66~80 parts of 4450 type polyether glycols and be placed in a band and be uniformly mixed container, then add successively 10~7 parts of 500 type polyether glycols, 3-chloro-3
'-ethyl-4,4
'2.5~1 parts of-diaminodiphenylmethane, 0.5 part of 1~0.5 part of catalyzer and BYK-A535 defoamer, after being uniformly mixed, add again petroleum pitch dipropylene glycol dibenzoate mixing solutions, further be uniformly mixed, and then 5~3 parts of instantly-soluble water glass micro mists are added to stir be dispersed in system, obtaining B component, sealing is preserved;
Above-mentioned A component and B component are mixed and stir rapidly after add again 300 parts, silicon carbide in C component, after being further uniformly mixed rapidly, be poured in the asphalt pavement pit that cleaned purging is clean, and strike off with scraper plate, then evenly sprinkle again 100 parts, silicon carbide on surface, if hole groove is darker, can in advance 0~700 part of stone chippings be laid on to bottom as aggregate, and then pour into a mould, according to hole groove depth and also graded cast of size, when graded casting, A component and B component are mixed with mass ratio 1:1.
The technical scheme of organic/inorganic composite material based on above-mentioned quick reparation asphalt pavement pit and preparation method thereof, technical scheme is as follows further:
According to the mass fraction, preparation method is as follows for the charging capacity of described base polyurethane prepolymer for use as:
100 parts of polyether glycol N220 that is 2000 by average molecular mass add in reactor at 120 DEG C, dewater 2 hours under 0.08Mpa vacuum condition, after dehydration, add 37.1 parts of tolylene diisocyanates to stir in reactor, temperature is controlled in 80 DEG C of reaction 2h, react rear deaeration to bright, obtain the Polyether-Polyol Polyurethane Prepolymer that 137.1 parts-NCO group mass content is 10%, performed polymer is packed to inflated with nitrogen and preserve.
Described poly methylene poly phenyl poly isocyanate-NCO group mass content is 30%~32%.
The modulus of described instantly-soluble water glass micro mist is 2.3~2.5, and fineness is 120 orders.
The hydroxyl value of described 4450 type polyether glycols is 350 ± 20mgKOH/g.
The hydroxyl value of described 500 type polyether glycols is 335 ± 20mgKOH/g.
Described catalyzer is PC-150 catalyzer, or organo-bismuth KRBi-A1.
In described C component: the particle diameter of stone chippings is 10~40mm; The particle diameter of silicon carbide is 0.5~2mm.
Realize organic/inorganic composite material of the above-mentioned a kind of quick reparation asphalt pavement pit of the present invention and preparation method thereof, compared with prior art, its advantage and positively effect are as follows.
This matrix material has raw material and is easy to get, and solidification process does not foam, and speed is fast, intensity is high, cold-curing operation at normal temperatures, and preparation of construction is simple, and operation renovation technique is easy, and reparation speed is fast, saves labor, pollution-free, clean environment firendly.
This matrix material short period after reparation can recover to be open to traffic, at 25 DEG C, recovery time≤the 90min that is open to traffic, can reduce the inconvenience impact that congestion in road brings, the original road surface of matrix material and pitch base material has good cohesiveness and rigidity similarity, after reparation, reach stationarity and the comfortableness of driving, also can not spend work-ing life soft or really up to the mark and after impact reparation because of matrix material.
This composite material by adopting poly methylene poly phenyl poly isocyanate and base polyurethane prepolymer for use as are used in conjunction with, and make matrix material have good cohesiveness, rigidity and toughness.Polyethers 4450 and polyethers 500 can be given desirable degree of crosslinking and the mechanical property of matrix material.The use of quick dissolved sodium silicate micro mist, that it is dispersed in polymerization system as mineral filler on the one hand, be conducive to the dispersion of counter stress, its carbonic acid gas discharging in can absorption system on the other hand, the defect foaming when this matrix material runs into micro-moisture in solidification process be can effectively overcome, planarization and aesthetic property after repairing strengthened.
Compare with hole, traditional road surface groove recovery technique there is quick, efficient, environmental protection, economic feature, right
The development of Preventive maintenance for highway technology has positive contribution and pushing effect.The present invention has not only solved the problems such as process complexity problem, curing speed that prior art repairs asphalt pavement pit be slow, and material after repairing has good resistance to compression, anti-shearing, water erosion resistent, weathering resistance, wear resistance.
This composite repair hole groove after fixing thing has higher frictional coefficient, has improved the adherence properties of tire, has guaranteed the security of driving.
A component described in the inventive method, 300 parts of mixing cured rear and A components of silicon carbide in B component and C component, B component is directly and after stone chippings mix, after 24 hours with reference to GB1040/92, HG2/167-65, JTJ052-2000, JTJ073.1-2001, GB/T10807-2006, the relevant test methods such as GB/T1843-2008, this matrix material and building stones cohesiveness can reach 5 grades, meet the requirement of motorway cohesiveness degree >=4 grade, tensile strength >=8 Mpa of matrix material, elongation at break is≤5%, tear strength >=10kN/m, compressive strength >=35Mpa, bending intensity >=6.2 Mpa, after progressive flooding 48h, record mechanical property and do not occur considerable change.Can meet quick reparation and the operating requirement of asphalt pavement of highway hole groove completely.
Embodiment
In order to make object, technical scheme and the advantage of invention clearer, below in conjunction with embodiment, the specific embodiment of the present invention is further illustrated.Should be appreciated that specific embodiment described herein is only in order to explain the present invention, and be not used in restriction invention.
Implement a kind of organic/inorganic composite material of quick reparation asphalt pavement pit, this matrix material is made up of A, B and C component, and its enforcement composition and mass content scope thereof are as follows.
A component: 82~90 parts of poly methylene poly phenyl poly isocyanates;
10~5 parts of base polyurethane prepolymer for use as;
8~5 parts of propylene glycol carbonates.
B component: 4,450 66~80 parts of type polyether glycols
500 10~7 parts of type polyether glycols;
10~5 parts of dipropylene glycol dibenzoates;
3-chloro-3
'-ethyl-4,4
'2.5~1 parts of-diaminodiphenylmethane;
90
#5~3 parts, petroleum pitch;
1~0.5 part of catalyzer;
5~3 parts of instantly-soluble water glass micro mists;
0.5 part of BYK-A535 defoamer.
C component: 400 parts, silicon carbide;
0~700 part of stone chippings.
Implement the preparation method of the organic/inorganic composite material of a kind of quick reparation asphalt pavement pit described above, the method is made up of A component, B component and C component, and it is as follows that its content and composition are all measured preparation process according to the mass fraction.
A component: get 82~90 parts of poly methylene poly phenyl poly isocyanates and be placed in a band stirring mixer, then add 10~5 parts of base polyurethane prepolymer for use as, 8~5 parts of propylene glycol carbonates, are uniformly mixed and obtain A component under normal temperature, inflated with nitrogen sealing is preserved.
B component: first by 90
#5~3 parts, petroleum pitch joins in 10~5 parts of dipropylene glycol dibenzoates, stand-by after heating for dissolving.
Get 66~80 parts of 4450 type polyether glycols and be placed in a band and be uniformly mixed container, then add successively 10~7 parts of 500 type polyether glycols, 3-chloro-3
'-ethyl-4,4
'2.5~1 parts of-diaminodiphenylmethane, 1~0.5 part of catalyzer, adds 90 after 0.5 part of BYK-A535 defoamer is uniformly mixed again
#petroleum pitch dipropylene glycol dibenzoate mixing solutions, is further uniformly mixed, and then 5~3 parts of instantly-soluble water glass micro mists are stirred and are dispersed in system, obtains B component, and sealing is preserved.
C component: 400 parts, silicon carbide, 0~700 part of stone chippings.
Above-mentioned A component and B component are mixed and stir rapidly after add again 300 parts, silicon carbide in C component, after being further uniformly mixed rapidly, be poured in the asphalt pavement pit that cleaned purging is clean, and strike off with scraper plate, then evenly sprinkle again 100 parts, silicon carbide on surface, if hole groove is darker, can in advance 0~700 part of stone chippings be laid on to bottom as aggregate, and then pour into a mould, according to hole groove depth and also graded cast of size, when graded casting, A component and B component are mixed with mass ratio 1:1, after mixing cast, liquid mixture can flowing time≤10min, ambient cure time≤30min, 90min can be open to traffic.
Base polyurethane prepolymer for use as preparation method described in A component following (charging capacity according to the mass fraction).
100 parts of polyether glycol N220 that is 2000 by average molecular mass add in reactor at 120 DEG C, dewater 2 hours under 0.08Mpa vacuum condition, after dehydration, add 37.1 parts of tolylene diisocyanates (TDI-80) to stir in reactor, temperature is controlled in 80 DEG C of reaction 2h, react rear deaeration to bright, obtain the Polyether-Polyol Polyurethane Prepolymer that 137.1 parts-NCO group mass content is 10%, performed polymer is packed to inflated with nitrogen and preserve.
Below by specific embodiment, the specific embodiment of the present invention is made and being further illustrated.
Embodiment 1
Implement a kind of preparation method of organic/inorganic composite material of quick reparation asphalt pavement pit, the method is made up of A component, B component and C component, and it is as follows that its content and composition are all measured preparation process according to the mass fraction.
A component: get 82 parts of poly methylene poly phenyl poly isocyanates and be placed in a band stirring mixer, then add 10 parts of base polyurethane prepolymer for use as, 8 parts of propylene glycol carbonates, are uniformly mixed and obtain A component under normal temperature, inflated with nitrogen sealing is preserved.
B component: first by 90
#5 parts, petroleum pitch joins in 10 parts of dipropylene glycol dibenzoates, stand-by after heating for dissolving.
Get 66 parts of 4450 type polyether glycols and be placed in a band and be uniformly mixed container, then add successively 10 parts of 500 type polyether glycols, 3-chloro-3
'-ethyl-4,4
'2.5 parts of-diaminodiphenylmethane, 1 part of PC-150 catalyzer, adds 90 after 0.5 part of BYK-A535 defoamer is uniformly mixed again
#petroleum pitch dipropylene glycol dibenzoate mixing solutions, is further uniformly mixed, and then adds wherein rapid stirring to be uniformly dispersed 5 parts of instantly-soluble water glass micro mists, obtains B component, and sealing is preserved.
C component: 400 parts, silicon carbide, 0 part of stone chippings.
Above-mentioned A component and B component are mixed and stir rapidly after add again 300 parts, silicon carbide in C component, after being further uniformly mixed rapidly, be poured in the asphalt pavement pit that cleaned purging is clean, and strike off with scraper plate, then evenly sprinkle again 100 parts, silicon carbide on surface, according to hole groove depth and also graded cast of size, when graded casting, A component and B component are mixed with mass ratio 1:1, after mixing cast, liquid mixture can flowing time≤10min, ambient cure time≤30min, 90min can be open to traffic.
Base polyurethane prepolymer for use as preparation method described in A component following (charging capacity is according to the mass fraction):
100 parts of polyether glycol N220 that is 2000 by average molecular mass add in reactor at 120 DEG C, dewater 2 hours under 0.08Mpa vacuum condition, after dehydration, add 37.1 parts of tolylene diisocyanates (TDI-80) to stir in reactor, temperature is controlled in 80 DEG C of reaction 2h, react rear deaeration to bright, obtain the Polyether-Polyol Polyurethane Prepolymer that 137.1 parts-NCO group mass content is 10%, performed polymer is packed to inflated with nitrogen and preserve.
Embodiment 2
Implement a kind of preparation method of organic/inorganic composite material of quick reparation asphalt pavement pit, the method is made up of A component, B component and C component, and it is as follows that its content and composition are all measured preparation process according to the mass fraction.
A component: get 90 parts of poly methylene poly phenyl poly isocyanates and be placed in a band stirring mixer, then add 5 parts of base polyurethane prepolymer for use as, 5 parts of propylene glycol carbonates, are uniformly mixed and obtain A component under normal temperature, inflated with nitrogen sealing is preserved.
B component: first by 90
#3 parts, petroleum pitch joins in 5 parts of dipropylene glycol dibenzoates, stand-by after heating for dissolving.
Get 80 parts of 4450 type polyether glycols and be placed in a band and be uniformly mixed container, then add successively 7 parts of 500 type polyether glycols, 3-chloro-3
'-ethyl-4,4
'1 part of-diaminodiphenylmethane, 0.5 part of organo-bismuth KRBi-A1 catalyzer, adds 90 after 0.5 part of BYK-A535 defoamer is uniformly mixed again
#petroleum pitch dipropylene glycol dibenzoate mixing solutions, is further uniformly mixed, and then adds wherein rapid stirring to be uniformly dispersed 3 parts of instantly-soluble water glass micro mists, obtains B component, and sealing is preserved.
C component: 400 parts, silicon carbide, 200 parts of stone chippings.
Above-mentioned A component and B component are mixed and stir rapidly after add again 300 parts, silicon carbide in C component, after being further uniformly mixed rapidly, be poured in the asphalt pavement pit that cleaned purging is clean, and strike off with scraper plate, then evenly sprinkle again 100 parts, silicon carbide on surface, if hole groove is darker, can in advance 200 parts of stone chippings be laid on to bottom as aggregate, and then pour into a mould, according to hole groove depth and also graded cast of size, when graded casting, A component and B component are mixed with mass ratio 1:1, after mixing cast, liquid mixture can flowing time≤10min, ambient cure time≤30min, 90min can be open to traffic.
Base polyurethane prepolymer for use as preparation method described in A component is with specific embodiment 1.
Embodiment 3.
Implement a kind of preparation method of organic/inorganic composite material of quick reparation asphalt pavement pit, the method is made up of A component, B component and C component, and it is as follows that its content and composition are all measured preparation process according to the mass fraction.
A component: get 86 parts of poly methylene poly phenyl poly isocyanates and be placed in a band stirring mixer, then add 7 parts of base polyurethane prepolymer for use as, 7 parts of propylene glycol carbonates, are uniformly mixed and obtain A component under normal temperature, inflated with nitrogen sealing is preserved.
B component: first by 90
#3.5 parts, petroleum pitch joins in 8 parts of dipropylene glycol dibenzoates, stand-by after heating for dissolving.
Get 74 parts of 4450 type polyether glycols and be placed in a band and be uniformly mixed container, then add successively 8 parts of 500 type polyether glycols, 3-chloro-3
'-ethyl-4,4
'2 parts of-diaminodiphenylmethane, 1 part of catalyst P C-150, after being uniformly mixed, 0.5 part of BYK-A535 defoamer adds again petroleum pitch dipropylene glycol dibenzoate mixing solutions, further be uniformly mixed, and then 3 parts of instantly-soluble water glass micro mists are stirred and are dispersed in system, obtain B component, sealing is preserved.
C component: 400 parts, silicon carbide, 400 parts of stone chippings.
Above-mentioned A component and B component are mixed and stir rapidly after add again 300 parts, silicon carbide in C component, after being further uniformly mixed rapidly, be poured in the asphalt pavement pit that cleaned purging is clean, and strike off with scraper plate, then evenly sprinkle again 100 parts, silicon carbide on surface, if hole groove is darker, can in advance 400 parts of stone chippings be laid on to bottom as aggregate, and then pour into a mould, according to hole groove depth and also graded cast of size, when graded casting, A component and B component are mixed with mass ratio 1:1, after mixing cast, liquid mixture can flowing time≤10min, ambient cure time≤30min, 90min can be open to traffic.
Base polyurethane prepolymer for use as preparation method specific embodiment 1 described in A component.
Embodiment 4
Implement a kind of preparation method of organic/inorganic composite material of quick reparation asphalt pavement pit, the method is made up of A component, B component and C component, and it is as follows that its content and composition are all measured preparation process according to the mass fraction.
A component: get 85 parts of poly methylene poly phenyl poly isocyanates and be placed in a band stirring mixer, then add 10 parts of base polyurethane prepolymer for use as, 5 parts of propylene glycol carbonates, are uniformly mixed and obtain A component under normal temperature, inflated with nitrogen sealing is preserved.
B component: first by 90
#3.5 parts, petroleum pitch joins in 10 parts of dipropylene glycol dibenzoates, stand-by after heating for dissolving.
Get 70 parts of 4450 type polyether glycols and be placed in a band and be uniformly mixed container, then add successively 9 parts of 500 type polyether glycols, 3-chloro-3
'-ethyl-4,4
'2.5 parts of-diaminodiphenylmethane, 0.5 part of PC-150 catalyzer, after being uniformly mixed, 0.5 part of BYK-A535 defoamer adds again petroleum pitch dipropylene glycol dibenzoate mixing solutions, further be uniformly mixed, and then 4 parts of instantly-soluble water glass micro mists are stirred and are dispersed in system, obtain B component, sealing is preserved.
C component: 400 parts of stone chippings, 500 parts, silicon carbide.
Above-mentioned A component and B component are mixed and stir rapidly after add again 300 parts, silicon carbide in C component, after being further uniformly mixed rapidly, be poured in the asphalt pavement pit that cleaned purging is clean, and strike off with scraper plate, then evenly sprinkle again 100 parts, silicon carbide on surface, if hole groove is darker, can in advance 500 parts of stone chippings be laid on to bottom as aggregate, and then pour into a mould, according to hole groove depth and also graded cast of size, when graded casting, A component and B component are mixed with mass ratio 1:1, after mixing cast, liquid mixture can flowing time≤10min, ambient cure time≤30min, 90min can be open to traffic.
Base polyurethane prepolymer for use as preparation method specific embodiment 1 described in A component.
Embodiment 5
Implement a kind of preparation method of organic/inorganic composite material of quick reparation asphalt pavement pit, the method is made up of A component, B component and C component, and it is as follows that its content and composition are all measured preparation process according to the mass fraction.
A component: get 88 parts of poly methylene poly phenyl poly isocyanates and be placed in a band stirring mixer, then add 6 parts of base polyurethane prepolymer for use as, 6 parts of propylene glycol carbonates, are uniformly mixed and obtain A component under normal temperature, inflated with nitrogen sealing is preserved.
B component: first by 90
#3 parts, petroleum pitch joins in 8 parts of dipropylene glycol dibenzoates, stand-by after heating for dissolving.
Get 75 parts of 4450 polyether glycols and be placed in a band and be uniformly mixed container, then add successively 8 parts of 500 polyether glycols, 3-chloro-3
'-ethyl-4,4
'1 part of-diaminodiphenylmethane, 0.5 part of organo-bismuth KRBi-A1 catalyzer, after being uniformly mixed, 0.5 part of BYK-A535 defoamer adds again petroleum pitch dipropylene glycol dibenzoate mixing solutions, further be uniformly mixed, and then 4 parts of instantly-soluble water glass micro mists are stirred and are dispersed in system, obtain B component, sealing is preserved.
C component: 400 parts of stone chippings, 700 parts, silicon carbide.
Above-mentioned A component and B component are mixed and stir rapidly after add again 300 parts, silicon carbide in C component, after being further uniformly mixed rapidly, be poured in the asphalt pavement pit that cleaned purging is clean, and strike off with scraper plate, then evenly sprinkle again 100 parts, silicon carbide on surface, if hole groove is darker, can in advance 700 parts of stone chippings be laid on to bottom as aggregate, and then pour into a mould, according to hole groove depth and also graded cast of size, when graded casting, A component and B component are mixed with mass ratio 1:1, after mixing cast, liquid mixture can flowing time≤10min, ambient cure time≤30min, 90min can be open to traffic.
Base polyurethane prepolymer for use as preparation method specific embodiment 1 described in A component.
Embodiment 6
Implement a kind of preparation method of organic/inorganic composite material of quick reparation asphalt pavement pit, the method is made up of A component, B component and C component, and it is as follows that its content and composition are all measured preparation process according to the mass fraction.
A component: get 86 parts of poly methylene poly phenyl poly isocyanates and be placed in a band stirring mixer, then add 9 parts of base polyurethane prepolymer for use as, 5 parts of propylene glycol carbonates, are uniformly mixed and obtain A component under normal temperature, inflated with nitrogen sealing is preserved.
B component: first by 90
#4 parts, petroleum pitch joins in 10 parts of dipropylene glycol dibenzoates, stand-by after heating for dissolving.
Get 70 parts of 4450 polyether glycols and be placed in a band and be uniformly mixed container, then add successively 10 parts of 500 polyether glycols, 3-chloro-3
'-ethyl-4,4
'1.5 parts of-diaminodiphenylmethane, 1 part of organo-bismuth KRBi-A1 catalyzer, after being uniformly mixed, 0.5 part of BYK-A535 defoamer adds again petroleum pitch dipropylene glycol dibenzoate mixing solutions, further be uniformly mixed, and then 3 parts of instantly-soluble water glass micro mists are stirred and are dispersed in system, obtain B component, sealing is preserved.
C component: 400 parts of stone chippings, 100 parts, silicon carbide.
Above-mentioned A component and B component are mixed and stir rapidly after add again 300 parts, silicon carbide in C component, after being further uniformly mixed rapidly, be poured in the asphalt pavement pit that cleaned purging is clean, and strike off with scraper plate, then evenly sprinkle again 100 parts, silicon carbide on surface, can in advance 100 parts of stone chippings be laid on to bottom as aggregate, and then pour into a mould, according to hole groove depth and also graded cast of size, when graded casting, A component and B component are mixed with mass ratio 1:1, after mixing cast, liquid mixture can flowing time≤10min, ambient cure time≤30min, 90min can be open to traffic.
Base polyurethane prepolymer for use as preparation method described in A component following (charging capacity is according to the mass fraction):
100 parts of polyether glycol N220 that is 2000 by average molecular mass add in reactor at 120 DEG C, dewater 2 hours under 0.08Mpa vacuum condition, after dehydration, add 37.1 parts of tolylene diisocyanates (TDI-80) to stir in reactor, temperature is controlled in 80 DEG C of reaction 2h, react rear deaeration to bright, obtain the Polyether-Polyol Polyurethane Prepolymer that 137.1 parts-NCO group mass content is 10%, performed polymer is packed to inflated with nitrogen and preserve.
Embodiment 7
Implement a kind of preparation method of organic/inorganic composite material of quick reparation asphalt pavement pit, the method is made up of A component, B component and C component, and it is as follows that its content and composition are all measured preparation process according to the mass fraction.
A component: get 82 parts of poly methylene poly phenyl poly isocyanates and be placed in a band stirring mixer, then add 10 parts of base polyurethane prepolymer for use as, 8 parts of propylene glycol carbonates, are uniformly mixed and obtain A component under normal temperature, inflated with nitrogen sealing is preserved.
B component: first by 90
#3.5 parts, petroleum pitch joins in 9 parts of dipropylene glycol dibenzoates, stand-by after heating for dissolving.
Get 75 parts of 4450 polyether glycols and be placed in a band and be uniformly mixed container, then add successively 7 parts of 500 polyether glycols, 3-chloro-3
'-ethyl-4,4
'1 part of-diaminodiphenylmethane, 1 part of PC-150 catalyzer, after being uniformly mixed, 0.5 part of BYK-A535 defoamer adds again petroleum pitch dipropylene glycol dibenzoate mixing solutions, further be uniformly mixed, and then 3 parts of instantly-soluble water glass micro mists are stirred and are dispersed in system, obtain B component, sealing is preserved.
C component: 400 parts of stone chippings, 300 parts, silicon carbide.
Above-mentioned A component and B component are mixed and stir rapidly after add again 300 parts, silicon carbide in C component, after being further uniformly mixed rapidly, be poured in the asphalt pavement pit that cleaned purging is clean, and strike off with scraper plate, then evenly sprinkle again 100 parts, silicon carbide on surface, if hole groove is darker, can in advance 300 parts of stone chippings be laid on to bottom as aggregate, and then pour into a mould, according to hole groove depth and also graded cast of size, when graded casting, A component and B component are mixed with mass ratio 1:1, after mixing cast, liquid mixture can flowing time≤10min, ambient cure time≤30min, 90min can be open to traffic.
Base polyurethane prepolymer for use as preparation method specific embodiment 1 described in A component.
Embodiment 8
Implement a kind of preparation method of organic/inorganic composite material of quick reparation asphalt pavement pit, the method is made up of A component, B component and C component, and it is as follows that its content and composition are all measured preparation process according to the mass fraction.
A component: get 84 parts of poly methylene poly phenyl poly isocyanates and be placed in a band stirring mixer, then add 9 parts of base polyurethane prepolymer for use as, 7 parts of propylene glycol carbonates, are uniformly mixed and obtain A component under normal temperature, inflated with nitrogen sealing is preserved.
B component: first by 90
#3 parts, petroleum pitch joins in 9 parts of dipropylene glycol dibenzoates, stand-by after heating for dissolving.
Get 72 parts of 4450 polyether glycols and be placed in a band and be uniformly mixed container, then add successively 8 parts of 500 polyether glycols, 3-chloro-3
'-ethyl-4,4
'2 parts of-diaminodiphenylmethane, 0.5 part of PC-150 catalyzer, after being uniformly mixed, 0.5 part of BYK-A535 defoamer adds again petroleum pitch dipropylene glycol dibenzoate mixing solutions, further be uniformly mixed, and then 5 parts of instantly-soluble water glass micro mists are stirred and are dispersed in system, obtain B component, sealing is preserved.
C component: 400 parts of stone chippings, 600 parts, silicon carbide.
Above-mentioned A component and B component are mixed and stir rapidly after add again 300 parts, silicon carbide in C component, after being further uniformly mixed rapidly, be poured in the asphalt pavement pit that cleaned purging is clean, and strike off with scraper plate, then evenly sprinkle again 100 parts, silicon carbide on surface, if hole groove is darker, can in advance 600 parts of stone chippings be laid on to bottom as aggregate, and then pour into a mould, according to hole groove depth and also graded cast of size, when graded casting, A component and B component are mixed with mass ratio 1:1, after mixing cast, liquid mixture can flowing time≤10min, ambient cure time≤30min, 90min can be open to traffic.
Base polyurethane prepolymer for use as preparation method specific embodiment 1 described in A component.
Embodiment 9
Implement a kind of preparation method of organic/inorganic composite material of quick reparation asphalt pavement pit, the method is made up of A component, B component and C component, and it is as follows that its content and composition are all measured preparation process according to the mass fraction.
A component: get 87 parts of poly methylene poly phenyl poly isocyanates and be placed in a band stirring mixer, then add 7 parts of base polyurethane prepolymer for use as, 6 parts of propylene glycol carbonates, are uniformly mixed and obtain A component under normal temperature, inflated with nitrogen sealing is preserved.
B component: first by 90
#4 parts, petroleum pitch joins in 10 parts of dipropylene glycol dibenzoates, stand-by after heating for dissolving.
Get 71 parts of 4450 polyether glycols and be placed in a band and be uniformly mixed container, then add successively 8 parts of 500 polyether glycols, 3-chloro-3
'-ethyl-4,4
'1 part of-diaminodiphenylmethane, 0.5 part of PC-150 catalyzer, after being uniformly mixed, 0.5 part of BYK-A535 defoamer adds again petroleum pitch dipropylene glycol dibenzoate mixing solutions, further be uniformly mixed, and then 5 parts of instantly-soluble water glass micro mists are stirred and are dispersed in system, obtain B component, sealing is preserved.
C component: 400 parts of stone chippings, 0 part, silicon carbide.
Above-mentioned A component and B component are mixed and stir rapidly after add again 300 parts, silicon carbide in C component, after being further uniformly mixed rapidly, be poured in the asphalt pavement pit that cleaned purging is clean, and strike off with scraper plate, then evenly sprinkle again 100 parts, silicon carbide on surface, according to hole groove depth and also graded cast of size, when graded casting, A component and B component are mixed with mass ratio 1:1, after mixing cast, liquid mixture can flowing time≤10min, ambient cure time≤30min, 90min can be open to traffic.
Base polyurethane prepolymer for use as preparation method specific embodiment 1 described in A component.
Embodiment 10
Implement a kind of preparation method of organic/inorganic composite material of quick reparation asphalt pavement pit, the method is made up of A component, B component and C component, and it is as follows that its content and composition are all measured preparation process according to the mass fraction.
A component: get 89 parts of poly methylene poly phenyl poly isocyanates and be placed in a band stirring mixer, then add 6 parts of base polyurethane prepolymer for use as, 5 parts of propylene glycol carbonates, are uniformly mixed and obtain A component under normal temperature, inflated with nitrogen sealing is preserved.
B component: first by 90
#4.5 parts, petroleum pitch joins in 10 parts of dipropylene glycol dibenzoates, stand-by after heating for dissolving.
Get 68 parts of 4450 type polyether glycols and be placed in a band and be uniformly mixed container, then add successively 10 parts of 500 type polyether glycols, 3-chloro-3
'-ethyl-4,4
'2.5 parts of-diaminodiphenylmethane, 0.5 part of organo-bismuth KRBi-A1 catalyzer, after being uniformly mixed, 0.5 part of BYK-A535 defoamer adds again petroleum pitch dipropylene glycol dibenzoate mixing solutions, further be uniformly mixed, and then 4 parts of instantly-soluble water glass micro mists are stirred and are dispersed in system, obtain B component, sealing is preserved.
C component: 400 parts of stone chippings, 300 parts, silicon carbide.
Above-mentioned A component and B component are mixed and stir rapidly after add again 300 parts, silicon carbide in C component, after being further uniformly mixed rapidly, be poured in the asphalt pavement pit that cleaned purging is clean, and strike off with scraper plate, then evenly sprinkle again 100 parts, silicon carbide on surface, if hole groove is darker, can in advance 300 parts of stone chippings be laid on to bottom as aggregate, and then pour into a mould, according to hole groove depth and also graded cast of size, when graded casting, A component and B component are mixed with mass ratio 1:1, after mixing cast, liquid mixture can flowing time≤10min, ambient cure time≤30min, 90min can be open to traffic.
Base polyurethane prepolymer for use as preparation method specific embodiment 1 described in A component.
Claims (9)
1. an organic/inorganic composite material of repairing fast asphalt pavement pit, is characterized in that: described matrix material is made up of A, B and C component, and its composition and mass content thereof are as follows:
A component: 82~90 parts of poly methylene poly phenyl poly isocyanates;
10~5 parts of base polyurethane prepolymer for use as;
8~5 parts of propylene glycol carbonates;
B component: 4,450 66~80 parts of type polyether glycols
500 10~7 parts of type polyether glycols;
10~5 parts of dipropylene glycol dibenzoates;
3-chloro-3
'-ethyl-4,4
'2.5~1 parts of-diaminodiphenylmethane;
90
#5~3 parts, petroleum pitch;
1~0.5 part of catalyzer;
5~3 parts of instantly-soluble water glass micro mists;
0.5 part of BYK-A535 defoamer;
C component: 400 parts, silicon carbide;
0~700 part of stone chippings.
2. for a preparation method for the organic/inorganic composite material of a kind of quick reparation asphalt pavement pit claimed in claim 1, described in it, according to the mass fraction, step is as follows for preparation method:
The preparation of A component
Get 82~90 parts of poly methylene poly phenyl poly isocyanates and be placed in a band stirring mixer, then add 10~5 parts of base polyurethane prepolymer for use as, 8~5 parts of propylene glycol carbonates, are uniformly mixed under normal temperature, obtain A component, and inflated with nitrogen sealing is preserved;
The preparation of B component
By 90
#5~3 parts, petroleum pitch joins in 10~5 parts of dipropylene glycol dibenzoates, stand-by after heating for dissolving;
Get 66~80 parts of 4450 type polyether glycols and be placed in a band and be uniformly mixed container, then add successively 10~7 parts of 500 type polyether glycols, 3-chloro-3
'-ethyl-4,4
'2.5~1 parts of-diaminodiphenylmethane, 0.5 part of 1~0.5 part of catalyzer and BYK-A535 defoamer, after being uniformly mixed, add again petroleum pitch dipropylene glycol dibenzoate mixing solutions, further be uniformly mixed, and then 5~3 parts of instantly-soluble water glass micro mists are added to stir be dispersed in system, obtaining B component, sealing is preserved;
Above-mentioned A component and B component are mixed and stir rapidly after add again 300 parts, silicon carbide in C component, after being further uniformly mixed rapidly, be poured in the asphalt pavement pit that cleaned purging is clean, and strike off with scraper plate, then evenly sprinkle again 100 parts, silicon carbide on surface, if hole groove is darker, can in advance 0~700 part of stone chippings be laid on to bottom as aggregate, and then pour into a mould, according to hole groove depth and also graded cast of size, when graded casting, A component and B component are mixed with mass ratio 1:1.
3. preparation method as claimed in claim 2, described in it, according to the mass fraction, preparation method is as follows for the charging capacity of base polyurethane prepolymer for use as:
100 parts of polyether glycol N220 that is 2000 by average molecular mass add in reactor at 120 DEG C, dewater 2 hours under 0.08Mpa vacuum condition, after dehydration, add 37.1 parts of tolylene diisocyanates to stir in reactor, temperature is controlled in 80 DEG C of reaction 2h, react rear deaeration to bright, obtain the Polyether-Polyol Polyurethane Prepolymer that 137.1 parts-NCO group mass content is 10%, performed polymer is packed to inflated with nitrogen and preserve.
4. preparation method as claimed in claim 2, described in it poly methylene poly phenyl poly isocyanate-NCO group mass content is 30%~32%.
5. preparation method as claimed in claim 2, described in it, the modulus of instantly-soluble water glass micro mist is 2.3~2.5, fineness is 120 orders.
6. preparation method as claimed in claim 2, described in it, the hydroxyl value of 4450 type polyether glycols is 350 ± 20mgKOH/g.
7. preparation method as claimed in claim 2, described in it, the hydroxyl value of 500 type polyether glycols is 335 ± 20mgKOH/g.
8. as right is wanted the preparation method as described in 2, described in it, catalyzer is PC-150 catalyzer, or organo-bismuth KRBi-A1.
9. preparation method as claimed in claim 2, described in it in C component: the particle diameter of stone chippings is 10~40mm; The particle diameter of silicon carbide is 0.5~2mm.