CN104151643A - Rubber tube for automobile - Google Patents
Rubber tube for automobile Download PDFInfo
- Publication number
- CN104151643A CN104151643A CN201410339177.4A CN201410339177A CN104151643A CN 104151643 A CN104151643 A CN 104151643A CN 201410339177 A CN201410339177 A CN 201410339177A CN 104151643 A CN104151643 A CN 104151643A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber tube
- automobile
- raw material
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a rubber tube for an automobile. The rubber tube for the automobile is characterized by comprising the following raw materials in parts by weight: 80-120 parts of medium-high acrylonitrile NBR (nitrile-butadiene rubber), 3-7 parts of zinc oxide, 0.5-1.5 parts of stearic acid, 1-2 parts of sulfur, 60-140 parts of semi-reinforcing furnace black, 10-20 parts of a plasticizer DOS, 10-20 parts of a plasticizer DBP, 0.8-1.6 parts of a promoter DM and 0.2-0.8 part of an anti-aging agent NBC. Compared with the prior art, the rubber tube disclosed by the invention has the advantages as follows: (1) a product is cheap in price, relatively less in adopted raw material and simple in production process; (2) the rubber tube has a series of advantages of safety, environmental protection, excellent oil resistance, heat resistance and anti-aging performance and the like; (3) by integrally adopting NBR and PVC (polyvinyl chloride), the manufactured rubber tube has excellent bending and winding resistance and relatively high fatigue resistance.
Description
Technical field
The present invention relates to elastomeric material scientific domain, refer more particularly to a kind of automobile rubber pipe.
Background technology
Paracril (NBR) is made through emulsion polymerization by divinyl and vinyl cyanide, and paracril mainly adopts low temperature emulsion polymerization to produce, and oil-proofness is fabulous, and wear resistance is higher, and thermotolerance is better, and bonding force is strong.Its shortcoming is that lower temperature resistance is poor, ozone resistance is poor, and electrical property is inferior, and elasticity is slightly low.Paracril is mainly for the manufacture of oil resisting rubber goods.As contact sebific duct, rubber roll, seal washer, tub liner, fuel tanker lining and the large-scale oil sac etc. of oils.Utilize the good heat resistance of NBR, also can manufacture the conveying belt that transports thermal material (140 ℃ following).Take and PVC use, also can manufacture various difficult combustion goods.Based on this, existing by NBR with PVC also with manufacturing a kind of automobile rubber pipe, the fine shortcoming that has overcome NBR, is mainly used on the various component of automobile.
Summary of the invention
What technical problem to be solved by this invention was to provide a kind of safety and environmental protection and possessed good oil resistant, heat-resisting, ageing-resistant performance is applied to the sebific duct on the various component of automobile, i.e. a kind of automobile rubber pipe.
For solving the problems of the technologies described above, the present invention by the following technical solutions:
A kind of automobile rubber pipe, it is characterized in that, the raw material that comprises following weight part: middle high acrylonitrile NBR80-120 part, zinc oxide 3-7 part, stearic acid 0.5-1.5 part, Sulfur 1-2 part, semi-reinforcing furnace black 60-140 part, softening agent DOS10-20 part, Plasticizer DBP 10-20 part, altax 0.8-1.6 part, antioxidant NBC 0.2-0.8 part.
Preferably, the raw material of described each weight part is: middle high acrylonitrile NBR90-110 part, zinc oxide 4-6 part, stearic acid 0.75-1.25 part, Sulfur 1.2-1.8 part, semi-reinforcing furnace black 80-120 part, softening agent DOS12-18 part, Plasticizer DBP 12-18 part, altax 1-1.4 part, antioxidant NBC 0.4-0.6 part.
Preferably, the raw material of described each weight part is: middle high acrylonitrile NBR100 part, 5 parts, zinc oxide, 1 part of stearic acid, 1.5 parts of Sulfurs, 100 parts of semi-reinforcing furnace black, softening agent DOS15 part, 15 parts of Plasticizer DBP, 1.2 parts of altaxs, 0.5 part of antioxidant NBC.
The present invention compared with prior art, has the following advantages: product price that (1) the present invention produces is cheap, use raw material less, and production technique is simple; (2) the present invention has the series of advantages such as safety and environmental protection, good oil resistant, heat-resisting, ageing-resistant performance.(3) the present invention adopts NBR and PVC use, and the sebific duct producing not only has good resistance to circumnutating property but also has higher resistance to fatigue concurrently.
Embodiment
Below in conjunction with embodiment, technical scheme of the present invention is further described in detail.
Embodiment mono-:
An automobile rubber pipe, is characterized in that, comprises the raw material of following weight part: middle high acrylonitrile NBR80 part, 3 parts, zinc oxide, 0.5 part of stearic acid, 1 part of Sulfur, 60 parts of semi-reinforcing furnace black, softening agent DOS10 part, 10 parts of Plasticizer DBP, 0.8 part of altax, 0.2 part of antioxidant NBC.
The present invention compared with prior art, has the following advantages: product price that (1) the present invention produces is cheap, use raw material less, and production technique is simple; (2) the present invention has the series of advantages such as safety and environmental protection, good oil resistant, heat-resisting, ageing-resistant performance.(3) the present invention adopts NBR and PVC use, and the sebific duct producing not only has good resistance to circumnutating property but also has higher resistance to fatigue concurrently.
Embodiment bis-:
An automobile rubber pipe, is characterized in that, comprises the raw material of following weight part: middle high acrylonitrile NBR120 part, 7 parts, zinc oxide, 1.5 parts of stearic acid, 2 parts of Sulfurs, 140 parts of semi-reinforcing furnace black, softening agent DOS20 part, 20 parts of Plasticizer DBP, 1.6 parts of altaxs, 0.8 part of antioxidant NBC.
The present invention compared with prior art, has the following advantages: product price that (1) the present invention produces is cheap, use raw material less, and production technique is simple; (2) the present invention has the series of advantages such as safety and environmental protection, good oil resistant, heat-resisting, ageing-resistant performance.(3) the present invention adopts NBR and PVC use, and the sebific duct producing not only has good resistance to circumnutating property but also has higher resistance to fatigue concurrently.
Embodiment tri-:
An automobile rubber pipe, is characterized in that, comprises the raw material of following weight part: middle high acrylonitrile NBR100 part, 5 parts, zinc oxide, 1 part of stearic acid, 1.5 parts of Sulfurs, 100 parts of semi-reinforcing furnace black, softening agent DOS15 part, 15 parts of Plasticizer DBP, 1.2 parts of altaxs, 0.5 part of antioxidant NBC.
The present invention compared with prior art, has the following advantages: product price that (1) the present invention produces is cheap, use raw material less, and production technique is simple; (2) the present invention has the series of advantages such as safety and environmental protection, good oil resistant, heat-resisting, ageing-resistant performance.(3) the present invention adopts NBR and PVC use, and the sebific duct producing not only has good resistance to circumnutating property but also has higher resistance to fatigue concurrently.
Embodiment tetra-:
An automobile rubber pipe, is characterized in that, comprises the raw material of following weight part: middle high acrylonitrile NBR90 part, 4 parts, zinc oxide, 0.75 part of stearic acid, 1.2 parts of Sulfurs, 80 parts of semi-reinforcing furnace black, softening agent DOS12 part, 12 parts of Plasticizer DBP, 1 part of altax, 0.4 part of antioxidant NBC.
The present invention compared with prior art, has the following advantages: product price that (1) the present invention produces is cheap, use raw material less, and production technique is simple; (2) the present invention has the series of advantages such as safety and environmental protection, good oil resistant, heat-resisting, ageing-resistant performance.(3) the present invention adopts NBR and PVC use, and the sebific duct producing not only has good resistance to circumnutating property but also has higher resistance to fatigue concurrently.
Embodiment five:
An automobile rubber pipe, is characterized in that, comprises the raw material of following weight part: middle high acrylonitrile NBR110 part, 6 parts, zinc oxide, 1.25 parts of stearic acid, 1.8 parts of Sulfurs, 120 parts of semi-reinforcing furnace black, softening agent DOS18 part, 18 parts of Plasticizer DBP, 1.4 parts of altaxs, 0.6 part of antioxidant NBC.
The present invention compared with prior art, has the following advantages: product price that (1) the present invention produces is cheap, use raw material less, and production technique is simple; (2) the present invention has the series of advantages such as safety and environmental protection, good oil resistant, heat-resisting, ageing-resistant performance.(3) the present invention adopts NBR and PVC use, and the sebific duct producing not only has good resistance to circumnutating property but also has higher resistance to fatigue concurrently.
It should be noted last that, above embodiment is only unrestricted in order to technical scheme of the present invention to be described, although the present invention is had been described in detail with reference to preferred embodiment, those of ordinary skill in the art is to be understood that, can modify or be equal to replacement technical scheme of the present invention, and not departing from the spirit and scope of technical solution of the present invention, it all should be encompassed in the middle of claim scope of the present invention.
Claims (3)
1. an automobile rubber pipe, it is characterized in that, the raw material that comprises following weight part: middle high acrylonitrile NBR80-120 part, zinc oxide 3-7 part, stearic acid 0.5-1.5 part, Sulfur 1-2 part, semi-reinforcing furnace black 60-140 part, softening agent DOS10-20 part, Plasticizer DBP 10-20 part, altax 0.8-1.6 part, antioxidant NBC 0.2-0.8 part.
2. automobile rubber pipe according to claim 1, it is characterized in that, the raw material of described each weight part is: middle high acrylonitrile NBR90-110 part, zinc oxide 4-6 part, stearic acid 0.75-1.25 part, Sulfur 1.2-1.8 part, semi-reinforcing furnace black 80-120 part, softening agent DOS12-18 part, Plasticizer DBP 12-18 part, altax 1-1.4 part, antioxidant NBC 0.4-0.6 part.
3. automobile rubber pipe according to claim 1 and 2, it is characterized in that, the raw material of described each weight part is: middle high acrylonitrile NBR100 part, 5 parts, zinc oxide, 1 part of stearic acid, 1.5 parts of Sulfurs, 100 parts of semi-reinforcing furnace black, softening agent DOS15 part, 15 parts of Plasticizer DBP, 1.2 parts of altaxs, 0.5 part of antioxidant NBC.