CN104149445B - Bope哑白涂布膜 - Google Patents

Bope哑白涂布膜 Download PDF

Info

Publication number
CN104149445B
CN104149445B CN201410333946.XA CN201410333946A CN104149445B CN 104149445 B CN104149445 B CN 104149445B CN 201410333946 A CN201410333946 A CN 201410333946A CN 104149445 B CN104149445 B CN 104149445B
Authority
CN
China
Prior art keywords
layer
functional layer
subfunction
sandwich
polyethylene
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201410333946.XA
Other languages
English (en)
Other versions
CN104149445A (zh
Inventor
杨永胜
章栋
江四华
朱红卫
李红培
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HUBEI FIRSTA MATERIAL SCIENCE AND TECHNOLOGY GROUP Co Ltd
Original Assignee
HUBEI FIRSTA MATERIAL SCIENCE AND TECHNOLOGY GROUP Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HUBEI FIRSTA MATERIAL SCIENCE AND TECHNOLOGY GROUP Co Ltd filed Critical HUBEI FIRSTA MATERIAL SCIENCE AND TECHNOLOGY GROUP Co Ltd
Priority to CN201410333946.XA priority Critical patent/CN104149445B/zh
Publication of CN104149445A publication Critical patent/CN104149445A/zh
Application granted granted Critical
Publication of CN104149445B publication Critical patent/CN104149445B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种BOPE涂布膜。BOPE哑白涂布膜，其特征在于：它由功能层、次功能层、芯层和第三功能层组成，功能层、次功能层、芯层和第三功能层依次布置，功能层、次功能层、芯层和第三功能层采用共挤出后经双向拉伸而成一体；功能层、次功能层、芯层和第三功能层所占质量百分数为：功能层9～10％、次功能层3～5％、芯层80～82％、第三功能层6～7％；功能层的材料由高密度聚乙烯、乙烯丙烯共聚物、防粘剂组成，各原料所占质量百分数为：高密度聚乙烯20％、乙烯丙烯共聚物78％、防粘剂2％；次功能层的材料为TiO2；芯层的材料为聚乙烯；第三功能层的材料由聚乙烯、SiO2组成，各原料所占质量百分数为：聚乙烯98％、SiO2？2％。该膜哑白效果好。

Description

BOPE哑白涂布膜
技术领域
本发明属于包装材料技术领域，具体涉及一种BOPE涂布膜。
背景技术
BOPE涂布膜本身既有的一些特性使得它广泛使用于软包装行业，如烟标、镭射、食品包装等等。现有的BOPE涂布膜存在着如下不足：哑白效果差。
发明内容
本发明的目的在于提供一种BOPE哑白涂布膜，该膜哑白效果好。
为了实现上述目的，本发明所采取的技术方案是：BOPE哑白涂布膜，其特征在于：它由功能层、次功能层、芯层和第三功能层组成，功能层、次功能层、芯层和第三功能层依次布置，功能层、次功能层、芯层和第三功能层采用共挤出后经双向拉伸而成一体；功能层、次功能层、芯层和第三功能层所占质量百分数为：功能层9～10％、次功能层3～5％、芯层80～82％、第三功能层6～7％；
功能层的材料由高密度聚乙烯(高密度聚乙烯的密度为0.925g/cm3以上)、乙烯丙烯共聚物、防粘剂(如硅藻土、滑石粉或碳酸钙或SiO2)组成，各原料所占质量百分数为：高密度聚乙烯20％、乙烯丙烯共聚物78％、防粘剂2％；
次功能层的材料为TiO2；
芯层的材料为聚乙烯(PE)；
第三功能层的材料由聚乙烯(PE)、SiO2组成，各原料所占质量百分数为：聚乙烯(PE)98％、SiO22％。
本发明的有益效果是：本发明的原料采用特定的配比量，并且采用次功能层；使本发明膜的哑白效果显著的好。
附图说明
图1是本发明的结构示意图。
图中：1-功能层，2-次功能层，3-芯层，4-第三功能层。
具体实施方式
实施例1：
如图1所示，BOPE哑白涂布膜，它由功能层1、次功能层2、芯层3和第三功能层4组成，功能层、次功能层、芯层和第三功能层依次布置，功能层、次功能层、芯层和第三功能层采用共挤出后经双向拉伸而成一体；功能层、次功能层、芯层和第三功能层所占质量百分数为：功能层9％、次功能层3％、芯层82％、第三功能层6％；
功能层的材料由高密度聚乙烯(高密度聚乙烯的密度为0.925g/cm3以上)、乙烯丙烯共聚物、防粘剂(如硅藻土、滑石粉或碳酸钙或SiO2)组成，各原料所占质量百分数为：高密度聚乙烯20％、乙烯丙烯共聚物78％、防粘剂2％；
次功能层的材料为TiO2；
芯层的材料为聚乙烯(PE)；
第三功能层的材料由聚乙烯(PE)、SiO2组成，各原料所占质量百分数为：聚乙烯(PE)98％、SiO22％。
本发明的制备方法是：将选配的原料送入挤出机加工成熔体，熔体通过流延铸片共挤成厚片(挤出温度为200-260℃)，厚片经双向拉伸成薄膜，薄膜经电晕处理或火焰处理成母膜，母卷经时效处理，最后分切成BOPE哑白涂布膜成品。
本发明的BOPE哑白涂布膜成品与现有的BOPE涂布膜进行比较，本发明的哑白效果显著的好。
实施例2：
如图1所示，BOPE哑白涂布膜，它由功能层1、次功能层2、芯层3和第三功能层4组成，功能层、次功能层、芯层和第三功能层依次布置，功能层、次功能层、芯层和第三功能层采用共挤出后经双向拉伸而成一体；功能层、次功能层、芯层和第三功能层所占质量百分数为：功能层10％、次功能层3％、芯层80％、第三功能层7％；
功能层的材料由高密度聚乙烯(高密度聚乙烯的密度为0.925g/cm3以上)、乙烯丙烯共聚物、防粘剂(如硅藻土、滑石粉或碳酸钙或SiO2)组成，各原料所占质量百分数为：高密度聚乙烯20％、乙烯丙烯共聚物78％、防粘剂2％；
次功能层的材料为TiO2；
芯层的材料为聚乙烯(PE)；
第三功能层的材料由聚乙烯(PE)、SiO2组成，各原料所占质量百分数为：聚乙烯(PE)98％、SiO22％。
本发明的制备方法是：将选配的原料送入挤出机加工成熔体，熔体通过流延铸片共挤成厚片(挤出温度为200-260℃)，厚片经双向拉伸成薄膜，薄膜经电晕处理或火焰处理成母膜，母卷经时效处理，最后分切成BOPE哑白涂布膜成品。
本发明的BOPE哑白涂布膜成品与现有的BOPE涂布膜进行比较，本发明的哑白效果显著的好。
实施例3：
如图1所示，BOPE哑白涂布膜，它由功能层1、次功能层2、芯层3和第三功能层4组成，功能层、次功能层、芯层和第三功能层依次布置，功能层、次功能层、芯层和第三功能层采用共挤出后经双向拉伸而成一体；功能层、次功能层、芯层和第三功能层所占质量百分数为：功能层9％、次功能层5％、芯层80％、第三功能层6％；
功能层的材料由高密度聚乙烯(高密度聚乙烯的密度为0.925g/cm3以上)、乙烯丙烯共聚物、防粘剂(如硅藻土、滑石粉或碳酸钙或SiO2)组成，各原料所占质量百分数为：高密度聚乙烯20％、乙烯丙烯共聚物78％、防粘剂2％；
次功能层的材料为TiO2；
芯层的材料为聚乙烯(PE)；
第三功能层的材料由聚乙烯(PE)、SiO2组成，各原料所占质量百分数为：聚乙烯(PE)98％、SiO22％。
本发明的制备方法是：将选配的原料送入挤出机加工成熔体，熔体通过流延铸片共挤成厚片(挤出温度为200-260℃)，厚片经双向拉伸成薄膜，薄膜经电晕处理或火焰处理成母膜，母卷经时效处理，最后分切成BOPE哑白涂布膜成品。
本发明的BOPE哑白涂布膜成品与现有的BOPE涂布膜进行比较，本发明的哑白效果显著的好。
本发明所列举的各原料(包含不同分子量的、不同生产厂家的)都能实现本发明，在此不一一列举实施例。

Claims (2)

1.BOPE哑白涂布膜，其特征在于：它由功能层、次功能层、芯层和第三功能层组成，功能层、次功能层、芯层和第三功能层依次布置，功能层、次功能层、芯层和第三功能层采用共挤出后经双向拉伸而成一体；功能层、次功能层、芯层和第三功能层所占质量百分数为：功能层9～10％、次功能层3～5％、芯层80～82％、第三功能层6～7％；
功能层的材料由高密度聚乙烯、乙烯丙烯共聚物、防粘剂组成，各原料所占质量百分数为：高密度聚乙烯20％、乙烯丙烯共聚物78％、防粘剂2％；高密度聚乙烯的密度为0.925g/cm3以上；
次功能层的材料主要为TiO2；
芯层的材料为聚乙烯；
第三功能层的材料由聚乙烯、SiO2组成，各原料所占质量百分数为：聚乙烯98％、SiO22％。
2.根据权利要求1所述的BOPE哑白涂布膜，其特征在于：防粘剂为硅藻土、滑石粉、碳酸钙或SiO2。
CN201410333946.XA 2014-07-14 2014-07-14 Bope哑白涂布膜 Expired - Fee Related CN104149445B (zh)