CN104139443B - A kind of manufacture craft of heavy bamboo carbonized floor - Google Patents
A kind of manufacture craft of heavy bamboo carbonized floor Download PDFInfo
- Publication number
- CN104139443B CN104139443B CN201410278759.6A CN201410278759A CN104139443B CN 104139443 B CN104139443 B CN 104139443B CN 201410278759 A CN201410278759 A CN 201410278759A CN 104139443 B CN104139443 B CN 104139443B
- Authority
- CN
- China
- Prior art keywords
- bamboo
- floor
- charing
- impregnation
- dry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of manufacture craft of heavy bamboo carbonized floor, comprise the following steps: choosing label, charing, drying, impregnation, drying, forging and stamping, cutting, burst, balance are standing, shipment.The present invention is existing carries out charing process by bamboo let, until moisture is carrying out dipping process after being down to 8%, the gap making glue pass through to carbonize bamboo let surface is carbonized bamboo let and is absorbed completely, bamboo let average moisture after impregnation forges and presses when dropping to 12%-18% again, make the ground board finished product crack resistence made, performance of damaging by worms good, environmental protection and floor light can be kept for a long time as new.
Description
Technical field
The present invention relates generally to heavy bamboo floor field, particularly relates to a kind of manufacture craft of heavy bamboo carbonized floor.
Background technology
Solid wooden floor board presents various form due to various wooden color patterns difference, deeply likes by consumer.But solid wooden floor board needs to consume a large amount of timber, timber resource shortage, become wooden growth cycle long, long-term a large amount of felling affects greatly environment.And mao bamboon because of its growth cycle short, aboundresources, recyclability is high, and it is more and more universal that mao bamboon applies to field, floor, praise highly wood substituted by bamboo, now even with bamboo victory wood.The bamboo wood tone of heavy bamboo floor mainly contains charing, true qualities, problems such as how improving the dimensional stability of heavy bamboo floor, prevent floor from ftractureing, damage by worms, is that heavy bamboo floor produces problems faced.
Summary of the invention
The object of the invention is exactly the defect in order to make up prior art, provides a kind of manufacture craft of heavy bamboo carbonized floor.
The present invention is achieved by the following technical solutions:
A manufacture craft for heavy bamboo carbonized floor, is characterized in that, comprise the following steps:
(1) choosing is signed: the bamboo let choosing length, width, consistency of thickness;
(2) carbonize: the bamboo let level chosen sent in hot press and carry out charing process, the parameter of hot press is: temperature remains on 120-140 DEG C, and air pressure is 3.6-3.8 atmospheric pressure, and carbonization time is 120-140 minute; Through charing process, the sugar of bamboo let is evaporated more than 80%;
(3) dry: the bamboo let after charing to be carried out drying process, bamboo let horizontal positioned on the ground, subsurface is provided with constant temperature heating device, surface temperature remains on 30-40 DEG C, drying time is 5-6 hour, move to standing on common ground depositing, until the average moisture content of bamboo let is down to less than 8% afterwards;
(4) impregnation: take out after dried bamboo let is sent into the abundant impregnation of Jiao Chi;
(5) dry: first bamboo let directly to be left standstill 1.5-2 hour, dry; Again the bamboo let dried is toasted 1-2 hour at the temperature of 60-80 DEG C; Move to standing on common ground depositing, until the average moisture content of bamboo let is down to 12%-18% afterwards;
(6) forge and press: all bamboo lets are longitudinally placed on forging press in batches, carry out forging forming; Large floor after shaping leaves standstill and deposits 30-40 days;
(7) cutting, burst: one piece of large floor is cut into the little floor meeting size needs, the little floor of every block is divided into the finished product floor of original thickness half;
(8) balance leaves standstill: finished product floor balance is left standstill 7-10 days, shipment.
Advantage of the present invention is:
The present invention is existing carries out charing process by bamboo let, until moisture carries out dipping process after being down to 8% again, the gap making glue pass through to carbonize bamboo let surface is carbonized bamboo let and is absorbed completely, bamboo let average moisture after impregnation forges and presses when dropping to 12%-18% again, make the ground board finished product crack resistence made, performance of damaging by worms good, environmental protection and floor light can be kept for a long time as new.
Detailed description of the invention
Embodiment
A manufacture craft for heavy bamboo carbonized floor, comprises the following steps:
(1) choosing is signed: the bamboo let choosing length, width, consistency of thickness;
(2) carbonize: the bamboo let level chosen sent in hot press and carry out charing process, the parameter of hot press is: temperature remains on 140 DEG C, and air pressure is 3.8 atmospheric pressure, and carbonization time is 140 minutes; Through charing process, the sugar of bamboo let is evaporated more than 80%;
(3) dry: the bamboo let after charing to be carried out drying process, bamboo let horizontal positioned on the ground, subsurface is provided with constant temperature heating device, surface temperature remains on 40 DEG C, drying time is 6 hours, move to standing on common ground depositing, until the average moisture content of bamboo let is down to less than 8% afterwards;
(4) impregnation: take out after dried bamboo let is sent into the abundant impregnation of Jiao Chi;
(5) dry: first bamboo let directly to be left standstill 2 hours, dry; Again the bamboo let dried is toasted 2 hours at the temperature of 80 DEG C; Move to standing on common ground depositing, until the average moisture content of bamboo let is down to 12% afterwards;
(6) forge and press: all bamboo lets are longitudinally placed on forging press in batches, carry out forging forming; Large floor after shaping leaves standstill and deposits 40 days;
(7) cutting, burst: one piece of large floor is cut into the little floor meeting size needs, the little floor of every block is divided into the finished product floor of original thickness half;
(8) balance leaves standstill: finished product floor balance is left standstill 10 days, shipment.
Claims (1)
1. a manufacture craft for heavy bamboo carbonized floor, is characterized in that, comprise the following steps:
(1) choosing is signed: the bamboo let choosing length, width, consistency of thickness;
(2) carbonize: the bamboo let level chosen sent in hot press and carry out charing process, the parameter of hot press is: temperature remains on 120-140 DEG C, and air pressure is 3.6-3.8 atmospheric pressure, and carbonization time is 120-140 minute; Through charing process, the sugar of bamboo let is evaporated more than 80%;
(3) dry: the bamboo let after charing to be carried out drying process, bamboo let horizontal positioned on the ground, subsurface is provided with constant temperature heating device, surface temperature remains on 30-40 DEG C, drying time is 5-6 hour, move to standing on common ground depositing, until the average moisture content of bamboo let is down to less than 8% afterwards;
(4) impregnation: take out after dried bamboo let is sent into the abundant impregnation of Jiao Chi;
(5) dry: first bamboo let directly to be left standstill 1.5-2 hour, dry; Again the bamboo let dried is toasted 1-2 hour at the temperature of 60-80 DEG C; Move to standing on common ground depositing, until the average moisture content of bamboo let is down to 12%-18% afterwards;
(6) forge and press: all bamboo lets are longitudinally placed on forging press in batches, carry out forging forming; Large floor after shaping leaves standstill and deposits 30-40 days;
(7) cutting, burst: one piece of large floor is cut into the little floor meeting size needs, the little floor of every block is divided into the finished product floor of original thickness half;
(8) balance leaves standstill: finished product floor balance is left standstill 7-10 days, shipment.