CN104099097A - Thulium-and-holmium-codoped zirconium fluoride up-conversion luminescent material and preparation method thereof, and organic light-emitting diode - Google Patents

Thulium-and-holmium-codoped zirconium fluoride up-conversion luminescent material and preparation method thereof, and organic light-emitting diode Download PDF

Info

Publication number
CN104099097A
CN104099097A CN201310121305.3A CN201310121305A CN104099097A CN 104099097 A CN104099097 A CN 104099097A CN 201310121305 A CN201310121305 A CN 201310121305A CN 104099097 A CN104099097 A CN 104099097A
Authority
CN
China
Prior art keywords
luminescent material
conversion luminescent
codoped zirconium
zirconium tetrafluoride
thulium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310121305.3A
Other languages
Chinese (zh)
Inventor
周明杰
王平
陈吉星
钟铁涛
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Oceans King Lighting Science and Technology Co Ltd
Shenzhen Oceans King Lighting Science and Technology Co Ltd
Shenzhen Oceans King Lighting Engineering Co Ltd
Original Assignee
Oceans King Lighting Science and Technology Co Ltd
Shenzhen Oceans King Lighting Engineering Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Oceans King Lighting Science and Technology Co Ltd, Shenzhen Oceans King Lighting Engineering Co Ltd filed Critical Oceans King Lighting Science and Technology Co Ltd
Priority to CN201310121305.3A priority Critical patent/CN104099097A/en
Publication of CN104099097A publication Critical patent/CN104099097A/en
Pending legal-status Critical Current

Abstract

The invention provides a thulium-and-holmium-codoped zirconium fluoride up-conversion luminescent material. The general chemical formula of the luminescent material is ZrF4: xTm3+,yHo3+, wherein x is in a range of 0.002 to 0.06, and y is in a range of 0.002 to 0.04. In the photoluminescence spectrum of the thulium-and-holmium-codoped zirconium fluoride up-conversion luminescent material, the excitation wavelength of the thulium-and-holmium-codoped zirconium fluoride up-conversion luminescent material is 650 nm, and luminescence peaks at 454 nm and 476 nm are respectively formed by transition radiation of Tm3+ ions from 1D2 to 3H4 and from 1G4 to 3H6. The invention further provides a preparation method for the thulium-and-holmium-codoped zirconium fluoride up-conversion luminescent material and an organic light-emitting diode using the thulium-and-holmium-codoped zirconium fluoride up-conversion luminescent material.

Description

Thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material, preparation method and Organic Light Emitting Diode
Technical field
The present invention relates to a kind of thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material, preparation method and Organic Light Emitting Diode.
Background technology
Organic Light Emitting Diode (OLED) because unit construction is simple, the characteristic such as cheap, the luminous of production cost, reaction times be short, flexible, apply widely and obtained the utmost point.But owing to obtaining at present, the OLED blue light material of stability and high efficiency is more difficult, has limited greatly the development of white light OLED device and light source industry.
Upconverting fluorescent material can be launched visible ray under long wave (as infrared) radiation excitation, even UV-light, is with a wide range of applications in fields such as optical fiber communication technology, fibre amplifier, 3 D stereo demonstration, biomolecules fluorescence labelling, infrared detectives.But, can be by infrared, the long-wave radiations such as red-green glow inspire the thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material of blue emission, have not yet to see report.
Summary of the invention
Based on this, being necessary to provide a kind of can be inspired thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material, the preparation method of blue light and be used the Organic Light Emitting Diode of this thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material by long-wave radiation.
A kind of thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material, has following chemical formula ZrF 4: xTm 3+, yHo 3+, wherein, x is that 0.002～0.06, y is 0.002～0.04.
X is that 0.03, y is 0.01.
A preparation method for thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material, comprises the following steps:
According to ZrF 4: xTm 3+, yHo 3+the stoichiometric ratio of each element takes ZrF 4, Tm 2o 3and Ho 2o 3powder, wherein, x is that 0.002～0.06, y is 0.002～0.04;
The powder taking is dissolved in and in nitric acid, is mixed with the solution that the concentration of metallic cation is 0.5mol/L～3mol/L;
Described solution mist is changed into after mist to pass into temperature with carrier gas be that the silica tube of 150 DEG C～220 DEG C generates presoma, wherein, the diameter of silica tube is 30mm～150mm, and length is 0.5m～3m, and the flow of carrier gas is 1L/min～15L/min;
Described presoma is calcined at 600 DEG C～1300 DEG C and within 2 hours～5 hours, obtained chemical formula ZrF 4: xTm 3+, yHo 3+thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material.
Described x is that 0.03, y is 0.01.
Describedly the powder taking is dissolved in to the step that is mixed with solution in nitric acid also comprises: in described solution, add dispersion agent, the concentration of described dispersion agent is 0.005mol/L～0.05mol/L.
The step that described solution mist is changed into mist is, carrier gas and described solution are passed into together in spraying gun and makes described solution mist change into mist, and described carrier gas is rare gas element or reducing gas.
Described dispersion agent is oxalic acid, ethanol, trolamine, water soluble starch or polyoxyethylene glycol.
The flow of described carrier gas is 5L/min～8L/min.
A kind of Organic Light Emitting Diode, comprise the substrate, negative electrode, organic luminous layer, anode and the encapsulated layer that stack gradually, in described encapsulated layer, doped with thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material, the chemical general formula of this thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material is ZrF 4: xTm 3+, yHo 3+, wherein, x is that 0.002～0.06, y is 0.002～0.04.
Hydrothermal method mild condition, the synthesis temperature of above-mentioned thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material are low more easy to control, and granularity and the pattern of product are controlled, the powder complete crystallization of preparation, good dispersity, cost is lower, produces comparatively environmental protection in simultaneous reactions process without the three wastes; In the photoluminescence spectra of thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material of preparation, the excitation wavelength of thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material is 650nm, and corresponding respectively at the glow peak of 454nm and 476nm is Tm 3+ion 1d 2→ 3h 4with 1g 4→ 3h 6transition radiation form glow peak, can be used as blue light emitting material.
Brief description of the drawings
Fig. 1 is the structural representation of the Organic Light Emitting Diode of an embodiment;
Fig. 2 is the structural representation of the spray pyrolysis equipment of an embodiment;
Fig. 3 is the photoluminescence spectrogram of the thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material prepared of embodiment 1;
Fig. 4 is the XRD spectra of the thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material prepared of embodiment 1;
Fig. 5 is the spectrogram doped with the Organic Light Emitting Diode of thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material in the transparent encapsulated layer prepared of embodiment 1.
Embodiment
Below in conjunction with the drawings and specific embodiments, thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material and preparation method thereof is further illustrated.
The thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material of one embodiment, has following chemical general formula ZrF 4: xTm 3+, yHo 3+, wherein, x is that 0.002～0.06, y is 0.002～0.04.
Preferably, x is that 0.03, y is 0.01.
In the photoluminescence spectra of this thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material, the excitation wavelength of thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material is 650nm, and corresponding respectively at the glow peak of 454nm and 476nm is Tm 3+ion 1d 2→ 3h 4with 1g 4→ 3h 6, can be used as blue light emitting material.
The preparation method of above-mentioned thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material, comprises the following steps;
Step S101, according to ZrF 4: xTm 3+, yHo 3+the stoichiometric ratio of each element takes ZrF 4, Tm 2o 3and Ho 2o 3powder, wherein, x is that 0.002～0.06, y is 0.002～0.04.
Preferably, x is that 0.03, y is 0.01.
Being appreciated that in this step also can be according to mol ratio (0.996～0.9): (0.001～0.03): (0.001～0.02) takes ZrF 4, Tm 2o 3and Ho 2o 3powder.
Preferably, in this step, also can take ZrF according to mol ratio 0.96:0.015:0.005 4, Tm 2o 3and Ho 2o 3powder.
Step S102, the powder taking is dissolved in and in nitric acid, is mixed with the solution that the concentration of metallic cation is 0.5mol/L～3mol/L.
Metallic cation in solution is Zr 4+, Tm 3+, Ho 3+.
Preferably, the powder taking being dissolved in to the step that is mixed with solution in nitric acid also comprises: in solution, add dispersion agent, the concentration of dispersion agent is 0.005mol/L～0.05mol/L.
Preferred dispersion agent can comprise oxalic acid, ethanol, trolamine, water soluble starch or polyoxyethylene glycol.
In present embodiment, dispersion agent is polyoxyethylene glycol.
Refer to Fig. 2, the spray pyrolysis equipment 100 shown in Fig. 2 comprises container for storing liquid 10, gas-holder 20, spraying gun 30, silica tube 40 and collector 50.
In present embodiment, solution prepared by step S102 is deposited in container for storing liquid 10.
S103, solution mist is changed into after mist to pass into temperature with carrier gas be that the silica tube 40 of 150 DEG C～220 DEG C generates presoma, wherein the diameter of silica tube 40 is 30mm～150mm, and length is 0.5m～3m, and the flow of carrier gas is 1L/min～15L/min.
Preferably, the diameter of silica tube is 95mm, and length is 1.4m.
In present embodiment, use spraying gun 30 by solution atomization, spraying gun 30 is compression atomizing device.Concrete, the solution of the carrier gas of gas-holder 20 interior storages and container for storing liquid 10 interior storages is together passed into spraying gun 30 and make solution mist change into mist.Carrier gas is rare gas element or reducing gas, as: at least one in nitrogen, argon gas and hydrogen, the flow of carrier gas is 5L/min～8L/min.
Silica tube 40 outer walls are being wound around resistance wire 42.
Solution mist passes into from one end of silica tube 40 after changing into mist, and at the interior generation presoma of silica tube 40, presoma is trickle powder, and pulverous presoma is the other end ejection from silica tube with carrier gas.Further, presoma uses collector 50 to collect after silica tube 40 flows out.In present embodiment, collector 50 is the acidproof filtration funnel of micropore.
S104, presoma is calcined at 600 DEG C～1300 DEG C within 2 hours～5 hours, to obtain chemical formula be ZrF 4: xTm 3+, yHo 3+thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material.
Preferably, presoma is placed in the calcination 3 hours at 800 DEG C of temperature programmed control stove.
The preparation method of above-mentioned thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material is spray pyrolysis, and raw material mixes under solution state, can ensure uniform component distribution, and technological process is simple, component loss is few, can accurately control stoichiometric ratio, is especially applicable to preparing polycomponent composite powder; Micro mist is by being suspended in airborne droplet drying, and particle is generally the spherical of rule, and few reunion, grinds without follow-up washing, ensures the high purity of product, high reactivity; Whole process completed rapidly in short several seconds, and therefore drop has little time to occur solute segregation in reaction process, further ensured the homogeneity that component distributes; Reaction process is simple, and a step obtains finished product, and without filtration, washing, dry, crushing process, simple to operation, production process is continuous, and production capacity is large, and production efficiency is high, is very beneficial for large suitability for industrialized production; In the photoluminescence spectra of thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material of preparation, the excitation wavelength of thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material is 650nm, and corresponding respectively at the glow peak of 454nm and 476nm is Tm 3+ion 1d 2→ 3h 4and 1G 4→ 3h 6transition radiation form glow peak, realized that to inspire blue light shortwave by the infrared long-wave radiation to green glow luminous.
Refer to Fig. 1, the Organic Light Emitting Diode 100 of an embodiment, this Organic Light Emitting Diode 100 comprises the substrate 1, negative electrode 2, organic luminous layer 3, transparent anode 4 and the encapsulated layer 5 that stack gradually.In encapsulated layer 5, be dispersed with thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material 6, the chemical general formula of thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material is ZrF 4: xTm 3+, yHo 3+, wherein, x is that 0.002～0.06, y is 0.002～0.04.
In the encapsulated layer 5 of Organic Light Emitting Diode 100, be dispersed with thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material 6, the excitation wavelength of thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material is 650nm, and corresponding respectively at the glow peak of 454nm and 476nm is Tm 3+ion 1d 2→ 3h 4with 1g 4→ 3h 6transition radiation form glow peak, excite and can launch blue light by red-green glow, blue light mixes the Organic Light Emitting Diode that afterwards formation emits white light with red-green glow.
Be specific embodiment below.
Embodiment 1
Take ZrF 4, Tm 2o 3and Ho 2o 3the mole number of powder is respectively 0.96mmol, 0.015mmol, and 0.005mmol, is dissolved in the solution that is mixed with 1.5mol/L in nitric acid, and adds the polyoxyethylene glycol additive of 0.01mol/L.Then solution is put into atomisation unit, pass into afterwards the argon gas of 5L/min to atomisation unit.Solution presoma with argon carrier enter temperature be 110 DEG C silica tube generate presoma, wherein the diameter of silica tube is 95mm, length is 1.4m.Then fluorescent material enters condenser with air-flow, finally collected by the acidproof filtration funnel of micropore.The presoma of collecting fluorescent material, is placed in temperature programmed control stove and calcines 3 hours, and 1100 DEG C of calcining temperatures, obtain ZrF 4: 0.03Tm 3+, 0.01Ho 3+up-conversion phosphor.
The substrate 1 stacking gradually use soda-lime glass, negative electrode 2 use metal A g layer, organic luminous layer 3 use Ir (piq) 2 (acac) Chinese name two (1-phenyl-isoquinoline 99.9) (methyl ethyl diketones) close iridium (III), transparent anode 4 uses tin indium oxide ITO, and transparent encapsulated layer 5 tetrafluoroethylene.In transparent encapsulated layer 5, be dispersed with thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material 6, the chemical formula of thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material is ZrF 4: 0.03Tm 3+, 0.01Ho 3+.
Refer to Fig. 3, Figure 3 shows that the thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material chemical general formula that this enforcement obtains is ZrF 4: 0.03Tm 3+, 0.01Ho 3+photoluminescence spectra figure.As seen from Figure 3, the excitation wavelength of the thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material that curve 2 the present embodiment obtain is 650nm, and corresponding respectively at the glow peak of 454nm and 476nm is Tm 3+ion 1d 2→ 3h 4with 1g 4→ 3h 6transition radiation form glow peak, this thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material can be used as blue light emitting material, curve 1 is the Ho that undopes 3+glow peak, can find out and increase Ho 3+the sample of element codoped can obtain better luminous efficiency.
Refer to Fig. 4, in Fig. 4, curve is the XRD curve of implementing the thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material of 1 preparation, test comparison standard P DF card.Contrast PDF card, can find out that diffraction peak is depicted as the crystal orientation of Zirconium tetrafluoride.There is not the peak of impurity, do not occur the peak of rare earth ion yet.Illustrate that ion is the lattice that doping has entered Zirconium tetrafluoride.
Fig. 5 is the spectrogram that has the Organic Light Emitting Diode that thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material forms in the transparent encapsulated layer prepared of embodiment 1, and curve 2 is not for adding the contrast of fluorescent material.In figure, can find out, fluorescent material can, by the red light of long wave, inspire the blue light of shortwave, blendes together white light.
Embodiment 2
Take ZrF 4, Tm 2o 3and Ho 2o 3the mole number of powder is respectively 0.95mmol, 0.03mmol, and 0.02mmol, is dissolved in the solution that is mixed with 3mol/L in nitric acid, and adds the polyoxyethylene glycol additive of 0.05mol/L.Then solution is put into atomisation unit, pass into afterwards the argon gas of 1L/min to atomisation unit.Solution presoma with argon carrier enter temperature be 220 DEG C silica tube generate presoma, wherein the diameter of silica tube is 150mm, length is 3m.Then fluorescent material enters condenser with air-flow, finally collected by the acidproof filtration funnel of micropore.The presoma of collecting fluorescent material, is placed in temperature programmed control stove and calcines 5 hours, and 1300 DEG C of calcining temperatures, obtain ZrF 4: 0.06Tm 3+, 0.04Ho 3+up-conversion phosphor.
Embodiment 3
Take ZrF 4, Tm 2o 3and Ho 2o 3the mole number of powder is respectively 0.996mmol, 0.001mmol, and 0.001mmol, is dissolved in the solution that is mixed with 0.5mol/L in nitric acid, and adds the polyoxyethylene glycol additive of 0.005mol/L.Then solution is put into atomisation unit, pass into afterwards the argon gas of 15L/min to atomisation unit.Solution presoma with argon carrier enter temperature be 150 DEG C silica tube generate presoma, wherein the diameter of silica tube is 30mm, length is 3m.Then fluorescent material enters condenser with air-flow, finally collected by the acidproof filtration funnel of micropore.The presoma of collecting fluorescent material, is placed in temperature programmed control stove and calcines 2 hours, and 600 DEG C of calcining temperatures, obtain ZrF 4: 0.002Tm 3+, 0.002Ho 3+up-conversion phosphor.
Embodiment 4
Take ZrF 4, Tm 2o 3and Ho 2o 3the mole number of powder is respectively 0.97mmol, 0.005mmol, and 0.01mmol, is dissolved in the solution that is mixed with 1mol/L in nitric acid, and adds the polyoxyethylene glycol additive of 0.008mol/L.Then solution is put into atomisation unit, pass into afterwards the argon gas of 5L/min to atomisation unit.Solution presoma with argon carrier enter temperature be 180 DEG C silica tube generate presoma, wherein the diameter of silica tube is 95mm, length is 1.4m.Then fluorescent material enters condenser with air-flow, finally collected by the acidproof filtration funnel of micropore.The presoma of collecting fluorescent material, is placed in temperature programmed control stove and calcines 3 hours, and 1100 DEG C of calcining temperatures, obtain ZrF 4: 0.01Tm 3+, 0.02Ho 3+up-conversion phosphor.
Embodiment 5
Take ZrF 4, Tm 2o 3and Ho 2o 3the mole number of powder is respectively 0.92mmol, 0.01mmol, and 0.02mmol, is dissolved in the solution that is mixed with 1.5mol/L in nitric acid, and adds the polyoxyethylene glycol additive of 0.01mol/L.Then solution is put into atomisation unit, pass into afterwards the argon gas of 5L/min to atomisation unit.Solution presoma with argon carrier enter temperature be 180 DEG C silica tube generate presoma, wherein the diameter of silica tube is 95mm, length is 1.4m.Then fluorescent material enters condenser with air-flow, finally collected by the acidproof filtration funnel of micropore.The presoma of collecting fluorescent material, is placed in temperature programmed control stove and calcines 3 hours, and 1100 DEG C of calcining temperatures, obtain ZrF 4: 0.02Tm 3+, 0.04Ho 3+up-conversion phosphor.
Embodiment 6
Take ZrF 4, Tm 2o 3and Ho 2o 3the mole number of powder is respectively 0.93mmol, 0.025mmol, and 0.01mmol, is dissolved in the solution that is mixed with 2.5mol/L in nitric acid, and adds the polyoxyethylene glycol additive of 0.016mol/L.Then solution is put into atomisation unit, pass into afterwards the argon gas of 5L/min to atomisation unit.Solution presoma with argon carrier enter temperature be 180 DEG C silica tube generate presoma, wherein the diameter of silica tube is 95mm, length is 1.4m.Then fluorescent material enters condenser with air-flow, finally collected by the acidproof filtration funnel of micropore.The presoma of collecting fluorescent material, is placed in temperature programmed control stove and calcines 3 hours, and 1100 DEG C of calcining temperatures, obtain ZrF 4: 0.05Tm 3+, 0.02Ho 3+up-conversion phosphor.
Embodiment 7
Take ZrF 4, Tm 2o 3and Ho 2o 3the mole number of powder is respectively 0.92mmol, 0.02mmol, and 0.02mmol, is dissolved in the solution that is mixed with 0.8mol/L in nitric acid, and adds the polyoxyethylene glycol additive of 0.033mol/L.Then solution is put into atomisation unit, pass into afterwards the argon gas of 5L/min to atomisation unit.Solution presoma with argon carrier enter temperature be 180 DEG C silica tube generate presoma, wherein the diameter of silica tube is 95mm, length is 1.4m.Then fluorescent material enters condenser with air-flow, finally collected by the acidproof filtration funnel of micropore.The presoma of collecting fluorescent material, is placed in temperature programmed control stove and calcines 3 hours, and 1100 DEG C of calcining temperatures, obtain ZrF 4: 0.04Tm 3+, 0.04Ho 3+up-conversion phosphor.
The above embodiment has only expressed several embodiment of the present invention, and it describes comparatively concrete and detailed, but can not therefore be interpreted as the restriction to the scope of the claims of the present invention.It should be pointed out that for the person of ordinary skill of the art, without departing from the inventive concept of the premise, can also make some distortion and improvement, these all belong to protection scope of the present invention.Therefore, the protection domain of patent of the present invention should be as the criterion with claims.

Claims (10)

1. a thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material, is characterized in that: have following chemical general formula ZrF 4: xTm 3+, yHo 3+, wherein, x is that 0.002～0.06, y is 0.002～0.04.
2. thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material according to claim 1, is characterized in that, described x is that 0.03, y is 0.01.
3. a preparation method for thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material, is characterized in that, comprises the following steps:
According to ZrF 4: xTm 3+, yHo 3+the stoichiometric ratio of each element takes ZrF 4, Tm 2o 3and Ho 2o 3powder, wherein, x is that 0.002～0.06, y is 0.002～0.04;
The powder taking is dissolved in and in nitric acid, is mixed with the solution that the concentration of metallic cation is 0.5mol/L～3mol/L;
Described solution mist is changed into after mist to pass into temperature with carrier gas be that the silica tube of 150 DEG C～220 DEG C generates presoma, wherein, the diameter of silica tube is 30mm～150mm, and length is 0.5m～3m, and the flow of carrier gas is 1L/min～15L/min;
Described presoma is calcined at 600 DEG C～1300 DEG C and within 2 hours～5 hours, obtained chemical formula ZrF 4: xTm 3+, yHo 3+thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material.
4. the preparation method of thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material according to claim 3, is characterized in that, described x is that 0.03, y is 0.01.
5. the preparation method of thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material according to claim 3, it is characterized in that, describedly the powder taking is dissolved in to the step that is mixed with solution in nitric acid also comprises: in described solution, add dispersion agent, the concentration of described dispersion agent is 0.005mol/L～0.05mol/L.
6. the preparation method of thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material according to claim 3, is characterized in that, described dispersion agent is oxalic acid, ethanol, trolamine, water soluble starch or polyoxyethylene glycol.
7. the preparation method of thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material according to claim 3, it is characterized in that, the step that described solution mist is changed into mist is, carrier gas and described solution are passed into together in spraying gun and makes described solution mist change into mist, and described carrier gas is rare gas element or reducing gas.
8. the preparation method of thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material according to claim 3, is characterized in that, the flow of described carrier gas is 5L/min～8L/min.
9. an Organic Light Emitting Diode, comprise the substrate, negative electrode, organic luminous layer, anode and the transparent encapsulated layer that stack gradually, it is characterized in that, in described transparent encapsulated layer, doped with thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material, the chemical general formula of described thulium holmium codoped Zirconium tetrafluoride up-conversion luminescent material is ZrF 4: xTm 3+, yHo 3+, wherein, x is that 0.002～0.06, y is 0.002～0.04.
10. Organic Light Emitting Diode according to claim 9, is characterized in that, described x is that 0.03, y is 0.01.
CN201310121305.3A 2013-04-09 2013-04-09 Thulium-and-holmium-codoped zirconium fluoride up-conversion luminescent material and preparation method thereof, and organic light-emitting diode Pending CN104099097A (en)