CN104087779A - Fragrant metal - Google Patents
Fragrant metal Download PDFInfo
- Publication number
- CN104087779A CN104087779A CN201410313700.6A CN201410313700A CN104087779A CN 104087779 A CN104087779 A CN 104087779A CN 201410313700 A CN201410313700 A CN 201410313700A CN 104087779 A CN104087779 A CN 104087779A
- Authority
- CN
- China
- Prior art keywords
- aluminium powder
- minutes
- fragrance
- metal
- foaming agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a fragrant metal. A manufacturing process of the fragrant metal comprises the following steps: (1) preparing aluminium ingots into aluminium powder with the fineness of 100-150 meshes; (2) putting the aluminium powder obtained in the step (1) into a grinding machine and grinding for 15 minutes at a high speed; (3) adding a foaming agent into the aluminium powder and grinding for 20 minutes at a medium speed; (4) adding fragrance into the mixture of the aluminium powder and the foaming agent, which is obtained in the step (3), and grinding for 10 minutes at a low speed; (5) heating the mixture obtained in the step (4) to 680 DEG C and stirring at a high speed for 2 minutes after the mixture is molten; (6) pouring the melt of the mixture, which is obtained in the step (5), into a mould, forming and rapidly cooling; (7) opening the mould after the melt is solidified and cooled, taking out and polishing to obtain a finished product, wherein the foaming agent is magnesium carbonate; the using amount of the foaming agent accounts for 3-5wt% of the aluminium powder; the using amount of the fragrance accounts for 2-5wt% of the aluminium powder. The fragrant metal disclosed by the invention has the beneficial effects that cars made from the fragrant metal can release fragrance with no need for placing perfume and the fragrance never fades; crafts made from the fragrant metal can release fragrance which never disappears; the fragrant metal is simple in manufacturing process, low in manufacturing cost and suitable for popularization and application.
Description
Technical field
The present invention relates to fragrance Metal Production technical field, especially a kind of fragrance metal.
Background technology
Along with developing rapidly of world economy, people's standard of living improves day by day, people are also more and more higher to the requirement of quality of life, and a lot of people have automobile, in automobile, all can place perfume, common perfume is all liquid, have certain work-ing life, somebody likes collecting artwork, and it is all dulcet having a lot of artworks, but metal handicrafts can exist fragrance seldom, being therefore badly in need of a kind of new technology solves above-mentioned technological deficiency.
Summary of the invention
The invention provides a kind of fragrance metal.
The present invention is directed to the technical scheme that above-mentioned technological deficiency proposes is:
A fragrance metal, its manufacturing process steps is:
(1) aluminium ingot is made to aluminium powder, aluminium powder fineness is 100-150 order;
(2) aluminium powder of gained in step 1 is put into shredder, speed lapping 15 minutes;
(3) in aluminium powder, add whipping agent, middling speed is ground 20 minutes;
(4) in the aluminium powder blowing agent blends of step 3 gained, add spices, low speed grinds 10 minutes;
(5) heating steps 4 gained mixtures are put 680 degrees Celsius, and after thing fusing to be mixed, high-speed stirring is 2 minutes;
(6) pour gained mixture melt thing in step 5 into die for molding, and cooling rapidly;
(7) until melt solidify cooling after die sinking take out, and polishing, obtains finished product.
Described whipping agent is magnesiumcarbonate.
Described foaming agent consumption is the 3%-5% of aluminium powder weight.
Described spices consumption is the 2%-5% of aluminium powder weight.
The invention has the beneficial effects as follows: the automobile that adopts fragrance metal to make, without placing perfume, automotive interior be can do by myself and given out fragrance, and never take off, the artwork that adopts fragrance metal to make, can oneself give out fragrance, fragrance never disappears, fragrance metal manufacture craft is simple, and cost of manufacture is little, is applicable to promoting the use of.
Embodiment
A fragrance metal, its manufacturing process steps is: (1) makes aluminium powder by aluminium ingot, aluminium powder fineness is 100-150 order; (2) aluminium powder of gained in step 1 is put into shredder, speed lapping 15 minutes; (3) in aluminium powder, add whipping agent, middling speed is ground 20 minutes; (4) in the aluminium powder blowing agent blends of step 3 gained, add spices, low speed grinds 10 minutes; (5) heating steps 4 gained mixtures are put 680 degrees Celsius, and after thing fusing to be mixed, high-speed stirring is 2 minutes; (6) pour gained mixture melt thing in step 5 into die for molding, and cooling rapidly.(7) until melt solidify cooling after die sinking take out, and polishing, obtains finished product; Described whipping agent is magnesiumcarbonate, and described foaming agent consumption is the 3%-5% of aluminium powder weight, and described spices consumption is the 2%-5% of aluminium powder weight, the automobile that adopts fragrance metal to make, without placing perfume, automotive interior be can do by myself and given out fragrance, and never takes off, the artwork that adopts fragrance metal to make, can oneself give out fragrance, fragrance never disappears, and fragrance metal manufacture craft is simple, cost of manufacture is little, is applicable to promoting the use of.
Claims (4)
1. a fragrance metal, is characterized in that: its manufacturing process steps is:
(1) aluminium ingot is made to aluminium powder, aluminium powder fineness is 100-150 order;
(2) aluminium powder of gained in step 1 is put into shredder, speed lapping 15 minutes;
(3) in aluminium powder, add whipping agent, middling speed is ground 20 minutes;
(4) in the aluminium powder blowing agent blends of step 3 gained, add spices, low speed grinds 10 minutes;
(5) heating steps 4 gained mixtures are put 680 degrees Celsius, and after thing fusing to be mixed, high-speed stirring is 2 minutes;
(6) pour gained mixture melt thing in step 5 into die for molding, and cooling rapidly;
(7) until melt solidify cooling after die sinking take out, and polishing, obtains finished product.
2. a kind of fragrance metal according to claim 1, is characterized in that: described whipping agent is magnesiumcarbonate.
3. a kind of fragrance metal according to claim 1, is characterized in that: described foaming agent consumption is the 3%-5% of aluminium powder weight.
4. a kind of fragrance metal according to claim 1, is characterized in that: described spices consumption is the 2%-5% of aluminium powder weight.