CN104069795A - Gas desulfurization and adsorption composition, preparation method thereof and method for desulfurizing sulfurous gases - Google Patents
Gas desulfurization and adsorption composition, preparation method thereof and method for desulfurizing sulfurous gases Download PDFInfo
- Publication number
- CN104069795A CN104069795A CN201310491618.8A CN201310491618A CN104069795A CN 104069795 A CN104069795 A CN 104069795A CN 201310491618 A CN201310491618 A CN 201310491618A CN 104069795 A CN104069795 A CN 104069795A
- Authority
- CN
- China
- Prior art keywords
- weight
- gas
- content
- adsorbing composition
- family metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a gas desulfurization and adsorption composition, a preparation method thereof and a method for desulfurizing sulfurous gases. The gas desulfurization and adsorption composition contains at least one of group VA metallic oxides, zinc oxide, oxysalt of calcium and at least one of group VIII metallic oxides. The gas desulfurization and adsorption composition disclosed by the invention has higher desulfurization activity.
Description
Technical field
The present invention relates to a kind of gas sweetening adsorbing composition, gas sweetening adsorbing composition prepared by a kind of preparation method of gas sweetening adsorbing composition and the method, and gas sweetening adsorbing composition is for the method for sulfurous gas desulfurization.
Background technology
Along with the pay attention to day by day of people to environmental protection, environmental regulation is day by day strict.In recent years, reduce sulphur emissions and be considered to one of most important measure improving air quality.On the one hand, the tail gas at present a lot of commercial plants, contains a large amount of sulfide in the flue gas of the large power plant that the coal of particularly take is fuel, and these sulfide must can reach emission request through removing.On the other hand, the sulfur content of the natural gas of exploiting out in the natural gas well is often higher, conventionally up to 10
4ppm, these natural gases must just can reach civilian requirement through deep desulfuration.
Gas absorption desulfur technology has that treating capacity is large, desulfurization depth is high and to advantages such as various sulfide adaptability height, has broad application prospects aspect the sulfur-containing compound in removing natural gas.
CN1559680A disclose a kind ofly under certain temperature, pressure condition, remove in natural gas, the solid desulphurization catalyst of the poisonous and harmful substance such as the sulfide in flue gas, oxysulfide, thioether, the percentage composition of catalyst weight of take is benchmark: ZnO content as 6.5% to 65%, NiO content as 0.5% to 2%, CaAl
2o
4content is 11% to 40%, TiO
2content is 0.5% to 2%, CoO content is 0.9% to 2%, MoO content is 0.7% to 3%, Al
2o
3content is 20% to 70%.The solid desulphurization catalyst of this patent application can be used for removing the poisonous and harmful substances such as sulfide in natural gas, in flue gas, oxysulfide, thioether.Yet this solid desulphurization catalyst is slightly poor for the desulphurizing ability of the higher sulfurous gas raw material of sulfur content.
CN101970106A discloses a kind of particle sulfur removal material, and it comprises one or more nickel compounds, zinc oxide carrier material and one or more alkali metal compounds, and wherein, the content of nickel is 0.3-10 % by weight, and alkali-metal content is 0.2-10 % by weight.The sulfur removal material of this patent application can make appropriate hydrocarbon gas material flow desulfurization for the hydrocarbon hydrogenolysis level to reduce.Yet the abrasion resistance properties of this sulfur removal material and compression strength are all poor, be unfavorable for using in industry.
CN101249440A discloses a kind of hydrogenation adsorption desulfurize catalyst containing aroamtic hydrocarbon raw material, and the weight percentage of this catalyst is: reduced state nickel content is 5-70%, and zinc oxide content is 30-95%, and alumina content is 0-50%.Yet the described catalyst of this patent application exists the difficulty of moulding aspect, limited its scope of application.
It is O composite metallic oxide catalyst that CN1868572A discloses a kind of iron, and this catalyst is for direct oxidation desulfurization.This catalyst forms by weight percentage: iron oxide content is 20-60%, and alumina content is 15-45%, and titanium oxide content is 15-45%, and zinc oxide content is 1-15%, and vanadium oxide content is 1-15%.This catalyst has higher activity and selective preferably, to H2S content range, be that sour gas between 1-85% can directly be processed, at normal pressure or low pressure (0.4MPa), 180 ℃, air speed, be under 1500-3000h-1 condition, the conversion ratio of H2S can reach more than 95.0%.This catalyst can efficiently be removed a large amount of hydrogen sulfide contained in gas, yet the desulfurization depth of this catalyst is lower slightly, cannot directly the sulfur content in conventional sulfurous gas be reduced to below 10ppm.
CN1712500A discloses a kind of coal gas of high temperature composite oxide desulfurizing agent, the main active component of this desulfurizing agent is zinc oxide, less important active component is industrial cupric oxide, basic copper carbonate and natural manganese ore, and wherein the content of zinc oxide is that 33-50%, manganese oxide content are that 0-10% and cupric oxide content are 0-15%.Although this desulfurizing agent has good mechanical strength, close physical and chemical performance, can be applicable to fixed bed, fluid bed, air flow bed desulfurization reactor, this desulfurizing agent is inadequate to the adaptability of sulphur in raw material, lower slightly for the removal activity of sulfurous organic compound.
Therefore, in order to realize better gas absorption desulfur technology, need new gas sweetening adsorbent, overcome above-mentioned defect of the prior art.
Summary of the invention
The object of the invention is, in order to overcome the above-mentioned defect of existing gas sweetening adsorbent, provides the sulfur method of a kind of new gas sweetening adsorbing composition and preparation method thereof with sulfurous gas.
To achieve these goals, the invention provides a kind of gas sweetening adsorbing composition, wherein, the oxysalt that this gas sweetening adsorbing composition contains at least one VA family metal oxide, zinc oxide, calcium and at least one VIII family metal oxide.
The present invention also provides a kind of preparation method of gas sweetening adsorbing composition, and the method comprises the following steps:
(1) oxysalt of calcium, zinc oxide source, at least one VA family metal oxide source and acidic liquid are mixed and contacted, and the mixture obtaining is carried out to moulding, dry and roasting;
(2) product of roasting obtaining in step (1) is mixed and contacted with at least one VIII family metal oxide precursor, obtain adsorbent precursor, then described adsorbent precursor is carried out to roasting.
The present invention also provides the gas sweetening of being prepared by method provided by the invention adsorbing composition.
The invention provides a kind of sulfur method of sulfurous gas, the method comprises: after gas sweetening adsorbing composition is reduced under hydrogen atmosphere, contact with sulfurous gas, wherein, described gas sweetening adsorbing composition is gas sweetening adsorbing composition provided by the invention.
Gas sweetening adsorbing composition of the present invention has higher desulphurizing activated, can be used for the sulfurous gas raw material of various sulfur contents to carry out desulfurization, the sulfurous gas raw material that particularly sulfur content is higher, such as sulfur-containing tail gas (as flue gas) of natural gas, casing-head gas and various routines etc.; And, can obtain the sulfur content gas that meets the requirements after adopting described gas sweetening adsorbing composition of the present invention to process sulfurous gas.
And described gas sweetening adsorbing composition of the present invention has physical and chemical performance (as compression strength or abrasion strength resistance) and the longer service life of improvement, there is good practical application in industry and be worth.
In addition, described gas sweetening adsorbing composition of the present invention can, for desulfurization under low temperature and high temperature, be convenient to commercial Application.
In addition, the preparation method of described gas sweetening adsorbing composition of the present invention is simple, be easy to realize industrialization, and production cost is lower.
Other features and advantages of the present invention partly in detail are described the specific embodiment subsequently.
The specific embodiment
Below the specific embodiment of the present invention is elaborated.Should be understood that, the specific embodiment described herein only, for description and interpretation the present invention, is not limited to the present invention.
In the present invention, provide a kind of gas sweetening adsorbing composition, wherein, the oxysalt that this gas sweetening adsorbing composition contains at least one VA family metal oxide, zinc oxide, calcium and at least one VIII family metal oxide.
According to the present invention, in gas sweetening adsorbing composition, add VA family metal oxide can improve the desulfurized effect of gas sweetening adsorbing composition, make described gas sweetening adsorbing composition there is higher desulphurizing activated and service life.The consumption adding for VA family metal oxide can be selected in wider scope.Under preferable case, in order to make described gas sweetening adsorbing composition there is better desulfurized effect, the gross weight of described gas sweetening adsorbing composition of take is benchmark, the content of described VA family metal oxide is 3-30 % by weight, the content of preferred described VA family metal oxide is 5-20 % by weight, and further the content of preferred described VA family metal oxide is 8-18 % by weight.
According to the present invention, under preferable case, described VA family metal oxide is Sb
2o
3and/or Bi
2o
3.
According to the present invention, under preferable case, the gross weight of described gas sweetening adsorbing composition of take is benchmark, and the content of described zinc oxide is 20-80 % by weight, the content of described VIII family metal oxide is 3-20 % by weight, and the content of the oxysalt of described calcium is 5-40 % by weight; Preferably, the content of described zinc oxide is 30-70 % by weight, and the content of described VIII family metal oxide is 5-15 % by weight, and the content of the oxysalt of described calcium is 15-35 % by weight; More preferably, the content of described zinc oxide is 38-65 % by weight, and the content of described VIII family metal oxide is 5-14 % by weight, and the content of the oxysalt of described calcium is 20-30 % by weight.
According to the present invention, under preferable case, the oxysalt of described calcium is selected from least one in calcium sulfate, calcium silicates, calcium phosphate and calcium aluminate, and the oxysalt of preferred described calcium is calcium sulfate.
According to the present invention, described VIII family metal oxide is used for promoting sulfurous gas sulfur-containing compound to react with zinc oxide, under preferable case, described VIII family metal oxide is the oxide that is selected from least one metal in cobalt, nickel, iron and manganese, more preferably cobalt oxide and/or nickel oxide, more preferably nickel oxide.When described VIII family metal oxide is nickel oxide, described gas sweetening adsorbing composition has higher desulphurizing activated and regenerability.
The present invention also provides a kind of preparation method of gas sweetening adsorbing composition, and the method comprises the following steps:
(1) oxysalt of calcium, zinc oxide source, at least one VA family metal oxide source and acidic liquid are mixed and contacted, and the mixture obtaining is carried out to moulding, dry and roasting;
(2) product of roasting obtaining in step (1) is mixed and contacted with at least one VIII family metal oxide precursor, obtain adsorbent precursor, then described adsorbent precursor is carried out to roasting.
According to preparation method provided by the invention, in step (1), obtain the mixture in oxysalt, zinc oxide source and the VA family metal oxide source of calcium.In the present invention, in the gas sweetening adsorbing composition of preparing by method of the present invention, add VA family metal oxide, can help to improve the desulfurized effect of the gas sweetening adsorbing composition of final acquisition.Tracing it to its cause may be in carrier, to have added VA family metal oxide, and this oxide and zinc oxide mix, and can increase the sulfur content that carries of zinc oxide.In the present invention, adding of described VA family metal oxide can be by adding the mode in VA family metal oxide source to introduce.Described VA family metal oxide source is for providing the material of VA family metal oxide.In the gas sweetening adsorbing composition that the addition in described VA family metal oxide source makes to prepare by method of the present invention, the gross weight of gas sweetening adsorbing composition of take is benchmark, the content of VA family metal oxide is 3-30 % by weight, preferably 5-20 % by weight, most preferably 8-18 % by weight.
In the present invention, under preferable case, described VA family metal oxide source is the trivalent of bismuth and/or antimony or the trivalent salt of antimony; Preferred described VA family metal oxide source is Sb
2o
3and/or Bi
2o
3or trichloride antimony.Described VA family metal oxide is identical with description above in the present invention.
In the present invention, under preferable case, in the gas sweetening adsorbing composition that the addition of the oxysalt of described calcium makes to prepare by method of the present invention, the gross weight of gas sweetening adsorbing composition of take is benchmark, the content of the oxysalt of calcium is 5-40 % by weight, preferred 15-35 % by weight, most preferably 20-30 % by weight.The oxysalt of described calcium is identical with description above in the present invention.
In the present invention, under preferable case, in the gas sweetening adsorbing composition that the addition of described zinc oxide source makes to prepare by method of the present invention, the gross weight of gas sweetening adsorbing composition of take is benchmark, the content of zinc oxide is 20-80 % by weight, preferred 30-70 % by weight, most preferably 38-65 % by weight.
In the present invention, described zinc oxide source can and/or can be converted into the zinc oxide precursor of zinc oxide for zinc oxide under the condition of the described roasting of step (1).Described zinc oxide precursor can be at least one in zinc sulphide, zinc sulfate, zinc hydroxide, zinc carbonate, zinc acetate and zinc nitrate.
In the present invention, for described acidic liquid, the consumption of acidic liquid preferably makes the pH value of mixture of oxysalt, zinc oxide source, VA family metal oxide source and acidic liquid of described calcium for 2-7, more preferably 3-6.
In the present invention, described acidic liquid can be acid or aqueous acid.Described acid can be water-soluble inorganic acid and/or water-soluble organic acid, for example, can be a kind of or industrial acid water of direct employing in hydrochloric acid, nitric acid, phosphoric acid and acetic acid.Described industrial acid water is the acidic liquid that in Catalyst Production, the conventional pH value of using is 3-5.
In the present invention, according to the preparation method of described gas sweetening adsorbing composition, in step (1), the oxysalt of described calcium, zinc oxide, VA family metal oxide source and acidic liquid are being mixed in the process contacting, there is no particular limitation for the feeding sequence of various materials.In one embodiment, first the oxysalt of described calcium, described VA family metal oxide source can be contacted with described acidic liquid and form slurries, and carry out aging; Then, the slurries that obtain after aging are mixed and contacted with the slurries of described zinc oxide, obtain carrier pulp, be the mixture obtaining in step (1).
The mixture obtaining in step of the present invention (1) can contain oxysalt, zinc oxide source, VA family metal oxide source and the acidic liquid of described calcium, and this mixture can be the forms such as wet mixture, paste mixture, dough or slurries.By described moulding, described mixture is shaped to extrudate, sheet, pill, ball or micro-spherical particle.For example, when described mixture is dough or paste mixture, can make this mixture moulding (preferably extrusion molding) is particle, and preferably diameter is 1.0-8.0mm, length is the cylindrical extrudate of 2.0-5.0mm, then makes the extrudate of gained be dried, roasting; When described mixture is wet mixture, can make this mixture multiviscosisty, through super-dry aftershaping; When described mixture is slurries, by the dry formation granularity of spraying, be the microballoon of 20-200 micron, reach the object of moulding, dry for the ease of spraying, the solid content of dry front slurries is preferably 10-50 % by weight, more preferably 20-50 % by weight.
In the present invention, in step (1), described dry method and condition have been conventionally known to one of skill in the art, for example, dry method can be dry, oven dry, forced air drying etc.Described dry temperature can be room temperature to 400 ℃, is preferably 100-350 ℃.
In the present invention, in step (1), the condition of described roasting is also conventionally known to one of skill in the art, and in general, the temperature of roasting can be 400-700 ℃, is preferably 450-650 ℃; The time of roasting at least can, for 0.5 hour, be preferably 0.5-100 hour, more preferably 0.5-10 hour.
In the present invention, according to the preparation method of described gas sweetening adsorbing composition, the object of step (2) is in order to introduce VIII family metal oxide in the gas sweetening adsorbing composition to final preparation.
In step of the present invention (2), it is also in order to introduce VIII family metal oxide precursor on described product of roasting that the product of roasting obtaining in step (1) is mixed to the object contacting with at least one VIII family metal oxide precursor.Concrete method of operating can adopt and well known to a person skilled in the art dipping method or intermediate processing realization.Described dipping method is with product of roasting described in the solution of VIII family metal oxide precursor or suspension impregnation.Described intermediate processing is that the solution of VIII family metal oxide precursor or suspension are mixed with described product of roasting, then adds ammoniacal liquor that VIII family metal oxide precursor is deposited on described product of roasting.
In the present invention, according to the preparation method of described gas sweetening adsorbing composition, in the gas sweetening adsorbing composition that the consumption of the described VIII family metal oxide precursor in step (2) makes to prepare by method of the present invention, the gross weight of gas sweetening adsorbing composition of take is benchmark, the content of VIII family metal oxide is 3-20 % by weight, preferred 5-15 % by weight, most preferably 5-14 % by weight.
In the present invention, according to the preparation method of described gas sweetening adsorbing composition, the described VIII family metal oxide precursor in step (2) can be identical or different.Described VIII family metal oxide precursor in step (2) is preferably at least one in acetate, carbonate, nitrate, sulfate, rhodanate and the oxide that is selected from VIII family metal separately, is preferably at least one in acetate, carbonate, nitrate, sulfate, rhodanate and the oxide of cobalt and/or nickel.Described VIII family metal oxide precursor can be to contain or not use containing the form of the crystallization water.
In the present invention, according to the preparation method of described gas sweetening adsorbing composition, in step (2), the temperature of described roasting can be 300-800 ℃, and the time of described roasting can be 0.5-100 hour.
The present invention also provides the gas sweetening of being prepared by method provided by the invention adsorbing composition.
The present invention also provides a kind of sulfur method of sulfurous gas, the method comprises: after gas sweetening adsorbing composition is reduced under hydrogen atmosphere, contact with sulfurous gas, wherein, described gas sweetening adsorbing composition is gas sweetening adsorbing composition provided by the invention.
According to sulfur method of the present invention, before carrying out gas sweetening, can also comprise gas sweetening adsorbing composition is reduced under hydrogen atmosphere.The condition of for example gas sweetening adsorbing composition being reduced under hydrogen atmosphere comprises: hydrogen content is 10-60 volume %, and the temperature of reduction is 300-600 ℃, and the time of reduction is 0.5-6 hour; Preferably the temperature of reduction is 400-500 ℃, and the time of reduction is 1-3 hour.Gas sweetening adsorbing composition is reduced, the metal of VIII family metal oxide is existed with reduction-state substantially.
According to sulfur method of the present invention, the temperature that described sulfurous gas contacts with gas sweetening adsorbing composition can be 250-800 ℃, is preferably 350-450 ℃.The present invention goes for any suitable pressure, and the pressure of processed raw material does not have large impact for sweetening process, and generally, from the viewpoint of easy to operate and cost, contact is preferably 0.1-0.2MPa.
The sulfur method of sulfurous gas of the present invention can carry out in fluid bed, fixed bed or moving bed, and reaction is carried out under normal pressure, non-oxidizing atmosphere.
According to sulfur method of the present invention, described sulfurous gas can be the various suitable gas that contains sulfur-containing compound, and the example of this type of suitable gas comprises that light hydrocarbon is as methane, ethane and natural gas; Gas such as hydrogen and nitrogen; The gas oxygen compound of carbon is as carbon monoxide, carbon dioxide; Steam and inert gas etc., and the gas obtaining from oil product and extraction and/or liquefaction coal and brown coal products obtained therefrom; The gas obtaining from Tar sands and shale oil; Synthesis gas obtaining from coal etc.Described sulfurous gas is natural gas, casing-head gas and various sulfur-containing tail gas for example.Described sulfurous gas is not suitable for containing oxidizing substance, such as oxygen, halogen and nitrogen oxide etc.
According to sulfur method of the present invention, the sulfur-containing compound in described sulfurous gas can exist in a variety of forms, as hydrogen sulfide, sulfur dioxide, carbonyl sulfide (COS), carbon disulfide (CS2), thioether etc.The mass concentration of the sulphur in described sulfurous gas is 200ppm to 5%, is preferably 1000ppm to 4%.
According to sulfur method of the present invention, after described contact finishes, preferably also comprise the gas sweetening adsorbing composition after contact is regenerated.The method of regeneration can comprise: first use inert gas (as nitrogen) to purge, then pass into oxygen-containing gas (oxygen content can be 30-60 volume %) and carry out oxidation regeneration, regeneration temperature is 450-600 ℃, is preferably 480-520 ℃, preferably under normal pressure, regenerates.
The pressure relating in the present invention is gauge pressure.
The invention will be further described by the following examples.
In the following Examples and Comparative Examples, the composition of gas sweetening adsorbing composition adopts XRD(X x ray diffraction) method analysis.
Embodiment 1
The present embodiment is used for illustrating described gas sweetening adsorbing composition of the present invention and preparation method thereof.
3.81 kilograms of Zinc oxide powders (Headhorse company, purity is not less than 99.7 % by weight) and 4.12 kilograms of deionized waters are mixed, stir and after 30 minutes, obtain the slurries of zinc oxide.
Get 3.06 kilograms, calcium sulfate (traditional Chinese medicines chemical reagents corporation, purity is not less than 98 % by weight), antimony oxide and 5.9 kilograms of industrial acid waters (pH value is 4) of 1.8 kilograms under agitation mix, and continue to stir to carry out aging in 1 hour.Then add the slurries of zinc oxide and stir 0.5 hour, obtaining pH value and be 4.7 carrier pulp.
Described carrier pulp adopts Niro Bowen Nozzle Tower
tMit is dry that the spray dryer of model is sprayed, and spraying drying pressure is 6.0 to 6.5MPa, and inlet temperature is below 340 ℃, and outlet temperature is about 120 ℃.By the dry microballoon roasting at 550 ℃ obtaining of spraying, within 1 hour, obtain adsorbing agent carrier.
By 2.8 kilograms of Nickelous nitrate hexahydrate (Beijing chemical reagents corporations for the adsorbing agent carrier of 4.3 kilograms, purity is greater than 98.5 % by weight) and the aqueous solution dipping of 0.8 kilogram of deionized water, obtain mixture after 180 ℃ are dried 2 hours, 550 ℃ of roastings of air atmosphere 1 hour, obtain gas sweetening adsorbing composition A1.
The chemical composition of this gas sweetening adsorbing composition A1 is: zinc oxide content is 38 % by weight, and nickel oxide content is 14 % by weight, calcium sulfate 30 % by weight, Sb
2o
3content is 18 % by weight.
Embodiment 2
The present embodiment is used for illustrating described gas sweetening adsorbing composition of the present invention and preparation method thereof.
4.81 kilograms of Zinc oxide powders (Headhorse company, purity is not less than 99.7 % by weight) and 4.12 kilograms of deionized waters are mixed, stir and after 30 minutes, obtain the slurries of zinc oxide.
Get 2.86 kilograms of (traditional Chinese medicines chemical reagents corporations of calcium sulfate, purity is not less than 98 % by weight), trichloride antimony (the traditional Chinese medicines chemical reagents corporation of 0.956 kilogram, purity is not less than 98 % by weight) and 5.5 kilograms of acid waters under agitation mix, and continue to stir and to carry out aging in 1 hour.Then add the slurries of zinc oxide and stir 0.5 hour, obtaining pH value and be 5.0 carrier pulp.
With reference to the method for embodiment 1, carry out the spray drying forming of carrier and introduce nickel oxide, obtaining gas sweetening adsorbing composition A2.
The chemical composition of this gas sweetening adsorbing composition A2 is: zinc oxide content is 48 % by weight, and nickel oxide content is 12 % by weight, and calcium sulphate content is 28 % by weight, Sb
2o
3content is 12 % by weight.
Embodiment 3
The present embodiment is used for illustrating described gas sweetening adsorbing composition of the present invention and preparation method thereof.
6.52 kilograms of Zinc oxide powders (Headhorse company, purity is not less than 99.7 % by weight) and 7.50 kilograms of deionized waters are mixed, stir and after 30 minutes, obtain the slurries of zinc oxide.
Get 2.14 kilograms, calcium sulfate (traditional Chinese medicines chemical reagents corporation, purity is not less than 98 % by weight), bismuth oxide and 3.6 kilograms of acid waters of 0.8 kilogram under agitation mix, and continue to stir to carry out aging in 1 hour.Then the slurry agitation 1 hour that adds zinc oxide, obtains pH value and is 5.2 carrier pulp.
With reference to the method for embodiment 1, carry out the spray drying forming of carrier and introduce nickel oxide, obtaining gas sweetening adsorbing composition A3.
The chemical composition of this gas sweetening adsorbing composition A3 is: zinc oxide content is 65 % by weight, and nickel oxide content is 6 % by weight, calcium sulfate 21 % by weight, Bi
2o
3content is 8 % by weight.
Comparative example 1
3.81 kilograms of Zinc oxide powders (Headhorse company, purity is not less than 99.7 % by weight) and 4.12 kilograms of deionized waters are mixed, stir and after 30 minutes, obtain the slurries of zinc oxide.
Get 3.06 kilograms, calcium sulfate (traditional Chinese medicines chemical reagents corporation, purity is not less than 98 % by weight), diatomite (Nanjing catalyst branch company, containing butt 1.80 kilograms) and 5.9 kilograms of acid waters of 1.86 kilograms under agitation mix, and continue stirring 1 hour.Then add the slurries of zinc oxide and stir 0.5 hour, obtaining pH value and be 4.7 carrier pulp.
With reference to the method for embodiment 1, carry out the spray drying forming of carrier and introduce nickel oxide, obtaining gas sweetening adsorbing composition B1.
The chemical composition of this gas sweetening adsorbing composition B1 is: zinc oxide content is 38 % by weight, and nickel oxide content is 14 % by weight, and calcium sulphate content is 30 % by weight, and diatomite content is 18 % by weight.
Comparative example 2
4.81 kilograms of Zinc oxide powders (Headhorse company, purity is not less than 99.7 % by weight) and 4.12 kilograms of deionized waters are mixed, stir and after 30 minutes, obtain the slurries of zinc oxide.
Get 2.86 kilograms, calcium sulfate (traditional Chinese medicines chemical reagents corporation, purity is not less than 98 % by weight), kaolin (Nanjing catalyst branch company, containing butt 1.20 kilograms) and 5.5 kilograms of acid waters of 1.50 kilograms under agitation mix, and continue stirring 1 hour.Then add the slurries of zinc oxide and stir 0.5 hour, obtaining pH value and be 5.0 carrier pulp.
With reference to the method for embodiment 1, carry out the spray drying forming of carrier and introduce nickel oxide, obtaining gas sweetening adsorbing composition B2.
The chemical composition of this gas sweetening adsorbing composition B2 is: zinc oxide content is 48 % by weight, and nickel oxide content is 12 % by weight, and calcium sulphate content is 28 % by weight, and kaolin content is 12 % by weight.
Comparative example 3
6.52 kilograms of Zinc oxide powders (Headhorse company, purity is not less than 99.7 % by weight) and 7.5 kilograms of deionized waters are mixed, stir and after 30 minutes, obtain the slurries of zinc oxide.
Get 2.14 kilograms, calcium sulfate (traditional Chinese medicines chemical reagents corporation, purity is not less than 98 % by weight), carclazyte (Nanjing catalyst branch company, containing butt 0.8 kilogram) and 3.6 kilograms of acid waters of 1.00 kilograms under agitation mix, and continue stirring 1 hour.Then the slurry agitation 1 hour that adds zinc oxide, obtains pH value and is 5.2 carrier pulp.
With reference to the method for embodiment 1, carry out the spray drying forming of carrier and introduce nickel oxide, obtaining gas sweetening adsorbing composition B3.
The chemical composition of this gas sweetening adsorbing composition B3 is: zinc oxide content is 65 % by weight, and nickel oxide content is 6 % by weight, and calcium sulphate content is 21 % by weight, and carclazyte content is 8 % by weight.
Test case 1
(1) specific area of gas sweetening adsorbing composition A1-A3 and B1-B3 adopts nitrogen physical absorption method, on the 2020ASSP of Merck & Co., Inc adsorption instrument, carries out;
(2) intensity of gas sweetening adsorbing composition A1-A3 and B1-B3 adopts straight tube wearing and tearing method to evaluate, its evaluation method (is shown in the volumes such as < < Petrochemical Engineering Analysis method > > (RIPP test method) Yang Cuiding with reference to the standard method of RIPP29-90, Science Press, nineteen ninety publishes), wherein, abrasion index is less, shows that abrasion strength resistance is higher.The test result of gas with various desulfurization adsorbing composition is as shown in table 1 below.
Table 1
| Composition | A1 | B1 | A2 | B2 | A3 | B3 |
| Specific area (m 2/g） | 68 | 47 | 61 | 39 | 57 | 34 |
| Abrasion index | 4.9 | 5.3 | 5.4 | 5.6 | 5.5 | 6.1 |
Data by table 1 can find out, prepared according to the methods of the invention gas sweetening adsorbing composition has higher specific area and abrasion strength resistance.
Embodiment 4
The present embodiment is for illustrating the sulfur method of described sulfurous gas of the present invention.
Gas sweetening adsorbing composition A1 is reduced 1 hour at hydrogen content is 10 volume %, 400 ℃, and being then seated in internal diameter is in 30mm fixed bed reactors, and sample-loading amount is 30 grams.
Then, first under argon gas atmosphere, the gas sweetening adsorbing composition in middle reactor is heated to 400 ℃.Then, in reactor, inject simulation sulfurous gas (2.8 volume %H
2s, 0.2 volume %SO
2, 0.2 volume %COS, 47 volume % methane, 5%H
2, 45%N
2), the volume space velocity of injection is 1200h
-1.
Sulphur storage capacity by measure from reactor out gas the content of sulfur-containing compound judge.Employing on-line mass spectroscopy is detector, measures the content of sulfur-containing compound in the gas of discharging from reactor.When the concentration of hydrogen sulfide reaches 20ppm in tail gas, think that gas sweetening adsorbing composition absorbs saturated, now the sulfur content in gas sweetening adsorbing composition is considered to the sulfur content that carries of this gas sweetening adsorbing composition.Carry sulfur content higher, show the desulphurizing activated higher of gas sweetening adsorbing composition.
Absorb saturated after, first adopt nitrogen to purge 30 minutes to gas sweetening adsorbing composition in reactor, and temperature be raised to 500 ℃; Then pass into 50 volume % air and 50 volume % nitrogen mixtures, carry out oxidation regeneration, gaseous mixture flow velocity is 160ml/min, and the recovery time is 2 hours.
After having regenerated, pass into High Purity Nitrogen and purge, and be cooled to reaction temperature, again adopt described simulation sulfurous gas to carry out the evaluation of a new circulation, carry out altogether 6 circulations and evaluate.Year sulfur content of the gas sweetening adsorbing composition that each circulation is measured is as shown in table 2 below.
Embodiment 5-6 and comparative example 4-6
According to the method circulation of embodiment 4, evaluate the sulfur content that carries of gas sweetening adsorbing composition A2-A3 and B1-B3.Evaluation result is as shown in table 2 below.
Table 2
From table 2, for identical appreciation condition with containing gas body, gas sweetening adsorbing composition provided by the invention has better sulphur absorbability, desulphurizing activated height, and the sulfur content that carries after 6 circulations is all much higher than contrast medium.
Claims (10)
1. a gas sweetening adsorbing composition, is characterized in that, the oxysalt that this gas sweetening adsorbing composition contains at least one VA family metal oxide, zinc oxide, calcium and at least one VIII family metal oxide.
2. composition according to claim 1, wherein, the gross weight of gas sweetening adsorbing composition of take is benchmark, the content of described zinc oxide is 20-80 % by weight, the content of described VIII family metal oxide is 3-20 % by weight, the content of described VA family metal oxide is 3-30 % by weight, and the content of the oxysalt of described calcium is 5-40 % by weight.
3. composition according to claim 1 and 2, wherein, the oxysalt of described calcium is selected from least one in calcium sulfate, calcium silicates, calcium phosphate and calcium aluminate.
4. a preparation method for gas sweetening adsorbing composition, the method comprises the following steps:
(1) oxysalt of calcium, zinc oxide source, at least one VA family metal oxide source and acidic liquid are mixed and contacted, and the mixture obtaining is carried out to moulding, dry and roasting;
(2) product of roasting obtaining in step (1) is mixed and contacted with at least one VIII family metal oxide precursor, obtain adsorbent precursor, then described adsorbent precursor is carried out to roasting.
5. method according to claim 4, wherein, in step (1), in the gas sweetening adsorbing composition that the addition in the oxysalt of described calcium, zinc oxide source and VA family metal oxide source makes to obtain, the gross weight of gas sweetening adsorbing composition of take is benchmark, the content of described zinc oxide is 20-80 % by weight, and the content of described VA family metal oxide is 3-30 % by weight, and the content of the oxysalt of described calcium is 5-40 % by weight; It is 2-7 that the consumption of acidic liquid makes the pH value of described mixture.
6. according to the method described in claim 4 or 5, wherein, described zinc oxide source is zinc oxide and/or the zinc oxide precursor that can be converted into zinc oxide under the condition of the described roasting of step (1).
7. method according to claim 4, wherein, in the gas sweetening adsorbing composition that the consumption of the described VIII family metal oxide precursor in step (2) makes to obtain, the gross weight of gas sweetening adsorbing composition of take is benchmark, and the content of VIII family metal oxide is 3-20 % by weight.
8. according to the method described in claim 4 or 7, wherein, described VIII family metal oxide precursor is at least one in acetate, carbonate, nitrate, sulfate, rhodanate and the oxide that is selected from VIII family metal.
9. the gas sweetening adsorbing composition that in claim 4-8 prepared by the method described in any one.
10. the sulfur method of a sulfurous gas, the method comprises: after gas sweetening adsorbing composition is reduced under hydrogen atmosphere, contact with sulfurous gas, it is characterized in that, described gas sweetening adsorbing composition is the gas sweetening adsorbing composition described in any one in claim 1-3 and 9.