CN104057215B - Welding anti-spattering agent for galvanized steel plate and galvanized oil-coated steel plate - Google Patents
Welding anti-spattering agent for galvanized steel plate and galvanized oil-coated steel plate Download PDFInfo
- Publication number
- CN104057215B CN104057215B CN201310225956.7A CN201310225956A CN104057215B CN 104057215 B CN104057215 B CN 104057215B CN 201310225956 A CN201310225956 A CN 201310225956A CN 104057215 B CN104057215 B CN 104057215B
- Authority
- CN
- China
- Prior art keywords
- agent
- weight portion
- splash
- antioxidant
- oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention provides a welding anti-spattering agent for a galvanized steel plate and a galvanized oil-coated steel plate formed by coating of the welding anti-spattering agent on the galvanized steel plate. The welding anti-spattering agent contains 100 parts of machine oil, 0.2-5 parts of an anti-wear agent, 0.2-2 parts of an antioxidant, 0.5-2 parts of an antirust agent and 3-15 parts of Vaseline in parts by weight. The welding anti-spattering agent can form an antirust oil layer on the galvanized steel plate, so that the galvanized oil-coated steel plate has an anti-corrosion effect and an anti-welding-spattering effect.
Description
Technical field
The present invention relates to a kind of splash-proof welding agent for galvanized steel plain sheet, and described by being coated with galvanized steel plain sheet
Splash-proof welding agent and the zinc oiling steel plate that formed.
Background technology
Galvanized steel plain sheet a large amount of production and sellings in common iron and steel metallurgical production enterprise, it is mainly used in household electrical appliances and produces.
In order to reach improve corrosion proof purpose, galvanizing surface take Passivation Treatment or coating organic film, or take zinc-plated after
The production technology of electrostatic spraying antirust oil.Zinc-plated oiling steel plate is mainly used in household appliances enterprise and passes through to shape and welding production micro-wave oven
, during resistance salient point Welding, often welding spark splashing particle and is sticky in zinc-plated oiling surface of steel plate in cavity,
Clear up difficult on resistance salient point weldering flow production line by hand, the coating quality of impact micro-wave oven work chamber internal surface.
The anti-welding spark splashing agent product that existing market is sold is a lot, and it is anti-that such as CN1644302A discloses a kind of welding
Splashing agent, described preventing splash agent is made up of following raw materials according：Benzyl alcohol, titanium do, calcium nitrate, ferrovanadium aluminium, Zinc Oxide, mangaic acid iron, many
Base cellulose.CN1526509A discloses a kind of Water-based rustproof splash proof adherent for metal welding, and it is by following raw materials
Make：C12～185～9 parts of aliphatic acid polyethenoxy (9) ether, C3～90～18 part of alkylphenol-polyethenoxy (10) ether, C10～18Alkyl
2～20 parts of diglycollic amide, water add to 100 parts.CN102205471A discloses one kind and prevents splash agent, and it is mainly used in stainless steel
Prevent splash from sticking together during composite plate welding, be made up of following raw materials according：Benzyl alcohol 40～50%, titanium do 10～15%, micron order oxygen
Change calcium and magnesia mixture 15～20%, zinc oxide 5～8%, mangaic acid iron 6～8%, many bases cellulose 10～15%.
Anti- welding spark splashing agent product disclosed in above-mentioned document, is substantially all using spraying before welding or brushing in weldering
Near seam, play the purpose avoiding welding spark to splash.But above-mentioned document is all not directed on galvanized steel plain sheet can be formed anti-
Rust oil reservoir, is capable of the splash-proof welding agent of Anti-welding spatter again.
Content of the invention
It is an object of the invention to provide one kind can form antirust oil reservoir on galvanized steel plain sheet, so that zinc-plated oiling steel plate
Not only there is etch-proof effect, also there is the splash-proof welding agent of the effect of Anti-welding spatter, and by galvanized steel plain sheet
The upper zinc-plated oiling steel plate being coated with described splash-proof welding agent and being formed.
Present inventors discovered unexpectedly that, during zinc-plated oiling Plate Production, by conventional antirust oil
（Main component includes machinery oil, antiwear additive, antioxidant and antirust agent）The middle vaseline adding certain content, can be effectively
Solve the problems, such as that the welding spark splashing particle that conventional oil reservoir occurs is sticky in zinc-plated oiling surface of steel plate, obtain Anti-welding spatter
The zinc-plated oiling steel plate of function admirable.
Thus, the present invention provides a kind of splash-proof welding agent for galvanized steel plain sheet, and wherein, described splash-proof welding agent contains
There are machinery oil, antiwear additive, antioxidant, antirust agent and vaseline；And the machinery oil with respect to 100 weight portions, described antiwear additive
For 0.2～5 weight portion, described antioxidant is 0.2～2 weight portion, and described antirust agent is 0.5～2 weight portion, described vaseline
For 3～15 weight portions.
The present invention also provides a kind of zinc-plated oiling steel plate, and wherein, this zinc-plated oiling steel plate passes through to be coated with galvanized steel plain sheet
Above-mentioned splash-proof welding agent and formed.
According to the present invention for galvanized steel plain sheet splash-proof welding agent, it has advantages below：
1）Do not change original galvanized steel plain sheet production technology, do not increase equipment.
2）Do not change corrosion resisting property and the mechanical property of zinc-plated oiling steel plate.
3）Reaching and no splashing viscous glutinous or dabbed with hand and wipe the purpose all coming off, to meet resistance salient point welding procedure quality
Requirement.
Additionally, other features and advantages of the present invention will be described in detail in subsequent specific embodiment part.
Specific embodiment
Hereinafter the specific embodiment of the present invention is described in detail.It should be appreciated that it is described herein concrete
Embodiment is merely to illustrate and explains the present invention, is not limited to the present invention.
Splash-proof welding agent provided by the present invention for galvanized steel plain sheet contains machinery oil, antiwear additive, antioxidant, antirust
Agent and vaseline；And the machinery oil with respect to 100 weight portions, described antiwear additive is 0.2～5 weight portion, and described antioxidant is
0.2～2 weight portion, described antirust agent is 0.5～2 weight portion, and described vaseline is 3～15 weight portions.
According to the present invention, the composition content of described splash-proof welding agent within the above range when, can be effectively zinc-plated
Antirust oil reservoir can be formed on steel plate, and the antirust oil reservoir of this formation not only has the function of anti-corrosion, and also can have
Effect prevents spatter, thus improving quality and the yield rate of zinc-plated oiling steel plate.In order to more effectively improve Anti-welding spatter
Effect, improves quality and the yield rate of zinc-plated oiling steel plate, preferably with respect to the machinery oil of 100 weight portions, described antiwear additive is
0.5～4 weight portion, described antioxidant is 0.5～1.5 weight portion, and described antirust agent is 1～2 weight portion, and described vaseline is
5～10 weight portions.
In the present invention, to described machinery oil, there is no particular limitation, can be the machinery in antirust oil commonly used in the art
Lubricating oil.Described machinery oil typically refers to petroleum oil fractions through dewaxing, solvent refining and general matter obtained by clay treatment
The lubricating oil of amount.This machinery oil is according to 50 DEG C of kinematic viscosity brands.Machinery oil used in the present invention is preferably in 50 DEG C of fortune
Kinetic viscosity is 7～13mm2·s-1, the more preferably kinematic viscosity at 50 DEG C is 10mm2·s-1Machinery oil.As such machine
The machinery oil that tool oil can be No. 10 with the trade mark known in the field, this No. 10 machinery oil known in this field is in 50 DEG C of motion
Viscosity is generally in 7～13mm2·s-1In the range of.
According to the present invention, described antiwear additive is various antiwear additives commonly used in this field.Under preferable case, described antiwear additive
For one or more of Type Phosphate Antiwear Additives and sulfuration three polybutene.Can be for example ability as described Type Phosphate Antiwear Additives
Low corrosion phosphate LYCO-P30 well known to domain.
According to the present invention, to consider in terms of reduction steel plate oxidation rate, preferably described antioxidant is di-t-butyl
Paracresol and/or fourth pentane phosphordithiic acid fat zinc salt.More preferably BHT.
According to the present invention, to consider in terms of anti-corrosion, preferably described antirust agent is petroleum sodium sulfonate and/or mahogany acid
Barium.More preferably petroleum sodium sulfonate.
According to the present invention, the surface tension preventing splash agent from reduction, preventing from preventing splash agent produces foam aspect to consider, excellent
Described splash-proof welding agent is selected also to contain defoamer.In the present invention, to described defoamer, there is no particular limitation, can be ability
The various defoamers that domain is commonly used.But under preferable case, described defoamer is dimethicone and/or methylbenzene silicone oil；More excellent
Elect dimethicone as.
Under preferable case, with respect to the machinery oil of 100 weight portions, the usage amount of described defoamer is 0.001～0.005 weight
Amount part；More preferably 0.002～0.005 weight portion.
According to the present invention, by adding the above-mentioned defoamer of specified volume in described splash-proof welding agent, enable to
To prevent splash agent and avoid bubbling, improve the coating performance that prevents splash agent.
According to the present invention, from reduce as far as possible the condensation point preventing splash agent, improve mobility, improve oil atomizing effect in terms of come
Consider, preferably described splash-proof welding agent also contains pour-point depressant.In the present invention, to described pour-point depressant, there is no particular limitation, permissible
For various pour-point depressants commonly used in this field.But under preferable case, described pour-point depressant is one of alkylnaphthalene and polyolefin etc.
Or it is multiple；Alkylnaphthalene T801 that for example can be well known in the art as described alkylnaphthalene.
Under preferable case, with respect to the machinery oil of 100 weight portions, the consumption of described pour-point depressant is 0.1～1.0 weight portion；
More preferably 0.4～1.0 weight portion.
According to the present invention, by adding the above-mentioned pour-point depressant of specified volume in described splash-proof welding agent, enable to
To prevent splash agent there is high mobility, and oil atomizing effect is good.
According to the present invention, from order that to consider in terms of easy the absorption on surface of steel plate that prevent splash agent, preferably described welding
Prevent splash agent and also contain adsorbent.In the present invention, to described adsorbent, there is no particular limitation, can be commonly used in this field
Various adsorbents.But under preferable case, described adsorbent is sulfuration oleic acid and/or sulfuration haco oil；More preferably sulfuration oleic acid.
Under preferable case, with respect to the machinery oil of 100 weight portions, consumption 0.1～0.5 weight portion of described adsorbent；More
It is preferably 0.2～0.5 weight portion.
According to the present invention, by adding the above-mentioned adsorbent of specified volume in described splash-proof welding agent, enable to
To the effect that there is easy absorption in surface of steel plate that prevents splash agent.
According to the present invention, for the preparation method of splash-proof welding agent of the present invention, there is no particular limitation, as long as will be upper
State each composition to be sufficiently mixed and be prepared into liquid.Under preferable case, after can first vaseline being melted, then enter with other compositions
Row mixing.
The present invention also provides a kind of zinc-plated oiling steel plate, and this zinc-plated oiling steel plate passes through to be coated with the present invention on galvanized steel plain sheet
Splash-proof welding agent and formed.
In the present invention, the not special restriction of method to above-mentioned coating, can be using various paintings commonly used in this field
The method of cloth, such as spin-coating method, electrostatic spray etc..For the condition being coated with, there is no particular limitation, as long as flying anti-for welding
The two-sided Weight control of coating oil film splashing agent is in 1～4g/m2?.
Hereinafter will be described the present invention by embodiment.
In following examples and comparative example, vaseline is purchased from packet header the Yellow River petrochemical industry Co., Ltd；No. 10 machinery oil purchases
From Changzhou Qin Bang lubricating oil Co., Ltd, model L-AN10,50 DEG C of kinematic viscosity is 10mm2/s.
Embodiment 1-6
According to the composition in table 1 and content, each composition is mixed, during mixing, after first vaseline being melted again with other
Composition is mixed, and so stirring 5 minutes, obtain splash-proof welding agent.
By in the oil groove of injection Electrostatic greasing unit, when zinc-plated coil of strip is when taking the lead to enter in Electrostatic greasing unit, start
The normal oiling of Electrostatic greasing unit, two-sided painting weight of oil reaches 1g/m to setup control galvanized steel plain sheet up and down2～4g/m2（Wherein, real
Applying example 1 is 1g/m2, embodiment 2 is 2g/m2, embodiment 3 is 3g/m2, embodiment 4 is 4g/m2, embodiment 5 is 2g/m2, embodiment
6 is 2g/m2）, galvanized steel strip volume press after setting speed passes through electrostatic spraying room and forms mixing of even application antirust oil and vaseline
Close oil film.Normally batched after Electrostatic greasing unit, obtain the zinc-plated oiling steel plate A1～A6 of anti-spatter.
Comparative example 1
Method according to embodiment 1 is carried out, and does not except for the difference that add vaseline in splash-proof welding agent, obtain coating fluid and
Zinc-plated oiling steel plate B1.Additionally, the concrete composition of coating fluid and content are shown in Table 1.
Comparative example 2
Method according to embodiment 4 is carried out, and does not except for the difference that add vaseline in splash-proof welding agent, obtain coating fluid and
Zinc-plated oiling steel plate B2.Additionally, the concrete composition of coating fluid and content are shown in Table 1.
Table 1
Note：（）Interior numerical value represents used weight portion.
- expression does not use
Embodiment 7
The corrosion resistance of zinc-plated oiling steel plate A1～A6 and B1～B2 obtained above is checked according to GB/T10125-1997
《Artificial atmosphere corrosion test-salt spray test》Neutral salt spray test carry out.
Its concrete grammar is：Zinc-plated oiling steel plate A1～A6 and B1～B2 is respectively cut as 150mm × 75mm × 1.0mm
Size after, use adhesive tape edge sealing, obtain style.Sample is put in salt spray test chamber, and test face and vertical direction be in 15 °～
30 ° of angles.Test temperature is 35 ± 2 DEG C, and test(ing) medium is the NaCl aqueous solution of concentration 50g/L, pH value 6.5, salt fog settling amount：1
～2ml/h.80cm2.Open within every 2 hours chamber taking-up sample to be observed, control sample corrosion situation of change.By contrast
The corrosion understanding zinc-plated oiling steel plate A1～A6, considerably less than zinc-plated oiling steel plate B1～B2, illustrates zinc-plated oiling steel plate A1～A6
There is good corrosion resistance.
Embodiment 8
Welding splash-proof test is carried out to zinc-plated oiling steel plate A1～A6 and B1～B2 obtained above.
Anti- spatter test is using the serious CO of spatter2Protection weldering is tested（Carbon dioxide gas arc welding
Be welding method the most serious of splashing, molten metal particles splashing amount is big, splash and stick to weldment surface, in addition with weldment table
Metallurgical binding in face).Concrete process of the test：Zinc-plated oiling steel plate is placed on CO2On the welding bead side of protection weldering test plate (panel)（Level
Distance about 10mm）, it is observed that molten metal particles are rolled after being splashed on zinc-plated oiling steel plate A1～A6 in welding process
Dynamic do not glue glutinous, and molten metal particles be splashed to zinc-plated oiling steel plate B1～B2 upper after stopping immediately being sticky in together, and postwelding
Also cannot be scratched using hand and remove.
In addition, welding to zinc-plated oiling steel plate A1～A6 and B1～B2 using energy storage salient point welding machine, test anti-splashing
Performance, deliberately improves the charging voltage of energy storage salient point welding machine, artificially causes the experimental condition of aggravation that splashes, and result displays that melting
Metallic particles be splashed to zinc-plated oiling steel plate A1～A6 upper after do not glue glutinous, anti-spatter is respond well, and molten metal particles
Be splashed to zinc-plated oiling steel plate B1～B2 upper after stop immediately being sticky in together, and postwelding also cannot be scratched using hand and remove.
By above-described embodiment and comparative example, it is coated with the zinc-plated oiling steel plate of splash-proof welding agent of the present invention not
Only can have good etch-proof effect, also there is the effect of good Anti-welding spatter.
The preferred embodiment of the present invention described in detail above, but, the present invention is not limited in above-mentioned embodiment
Detail, in the range of the technology design of the present invention, multiple simple variant can be carried out to technical scheme, this
A little simple variant belong to protection scope of the present invention.It is further to note that described in above-mentioned specific embodiment
Each particular technique feature, in the case of reconcilable, can be combined by any suitable means, in order to avoid not
Necessary repetition, the present invention no longer separately illustrates to various possible combinations.
Additionally, can also be combined between the various different embodiment of the present invention, as long as it is without prejudice to this
The thought of invention, it equally should be considered as content disclosed in this invention.
Claims (8)
1. a kind of splash-proof welding agent for galvanized steel plain sheet is it is characterised in that described splash-proof welding agent is by machinery oil, wear-resistant
Agent, antioxidant, antirust agent and vaseline composition；And the machinery oil with respect to 100 weight portions, described antiwear additive is 0.2～5 weight
Amount part, described antioxidant is 0.2～2 weight portion, and described antirust agent is 0.5～2 weight portion, and described vaseline is 3～15 weights
Amount part；
Wherein, described antiwear additive is sulfuration three polybutene, and described antioxidant is BHT, and described antirust agent is stone
Oily sodium sulfonate and/or barium mahogany sulfonate.
2. splash-proof welding agent according to claim 1, wherein, with respect to the machinery oil of 100 weight portions, described antiwear additive
For 0.5～4 weight portion, described antioxidant is 0.5～1.5 weight portion, and described antirust agent is 1～2 weight portion, described vaseline
For 5～10 weight portions.
3. splash-proof welding agent according to claim 1 and 2, wherein, described machinery oil 50 DEG C kinematic viscosity be 7～
13mm2·s-1.
4. a kind of splash-proof welding agent for galvanized steel plain sheet is it is characterised in that described splash-proof welding agent is by machinery oil, wear-resistant
Agent, antioxidant, antirust agent, defoamer and vaseline composition；And the machinery oil with respect to 100 weight portions, described antiwear additive is
0.2～5 weight portion, described antioxidant is 0.2～2 weight portion, and described antirust agent is 0.5～2 weight portion, and described vaseline is
3～15 weight portions, described defoamer is 0.001～0.005 weight portion；
Wherein, described antiwear additive is sulfuration three polybutene, and described antioxidant is BHT, and described antirust agent is stone
Oily sodium sulfonate and/or barium mahogany sulfonate, described defoamer is dimethicone and/or methylbenzene silicone oil.
5. a kind of splash-proof welding agent for galvanized steel plain sheet is it is characterised in that described splash-proof welding agent is by machinery oil, wear-resistant
Agent, antioxidant, antirust agent, pour-point depressant and vaseline composition；And the machinery oil with respect to 100 weight portions, described antiwear additive is
0.2～5 weight portion, described antioxidant is 0.2～2 weight portion, and described antirust agent is 0.5～2 weight portion, and described vaseline is
3～15 weight portions, described pour-point depressant is 0.1～1.0 weight portion；
Wherein, described antiwear additive is sulfuration three polybutene, and described antioxidant is BHT, and described antirust agent is stone
Oily sodium sulfonate and/or barium mahogany sulfonate, described pour-point depressant is one or more of alkylnaphthalene and polyolefin.
6. a kind of splash-proof welding agent for galvanized steel plain sheet is it is characterised in that described splash-proof welding agent is by machinery oil, wear-resistant
Agent, antioxidant, antirust agent, adsorbent and vaseline composition；And the machinery oil with respect to 100 weight portions, described antiwear additive is
0.2～5 weight portion, described antioxidant is 0.2～2 weight portion, and described antirust agent is 0.5～2 weight portion, and described vaseline is
3～15 weight portions, described adsorbent is 0.1～0.5 weight portion；
Wherein, described antiwear additive is sulfuration three polybutene, and described antioxidant is BHT, and described antirust agent is stone
Oily sodium sulfonate and/or barium mahogany sulfonate, described adsorbent is sulfuration oleic acid and/or sulfuration haco oil.
7. a kind of splash-proof welding agent for galvanized steel plain sheet is it is characterised in that described splash-proof welding agent is by machinery oil, wear-resistant
Agent, antioxidant, antirust agent, defoamer, pour-point depressant, adsorbent and vaseline composition；And the machinery with respect to 100 weight portions
Oil, described antiwear additive is 0.2～5 weight portion, and described antioxidant is 0.2～2 weight portion, and described antirust agent is 0.5～2 weight
Part, described vaseline be 3～15 weight portions, described defoamer be 0.001～0.005 weight portion, described pour-point depressant be 0.1～
1.0 weight portions, described adsorbent is 0.1～0.5 weight portion；
Wherein, described antiwear additive is sulfuration three polybutene, and described antioxidant is BHT, and described antirust agent is stone
Oily sodium sulfonate and/or barium mahogany sulfonate, described defoamer is dimethicone and/or methylbenzene silicone oil, and described pour-point depressant is alkane
One or more of base naphthalene and polyolefin, described adsorbent is sulfuration oleic acid and/or sulfuration haco oil.
8. a kind of zinc-plated oiling steel plate is it is characterised in that this zinc-plated oiling steel plate passes through to be coated with claim on galvanized steel plain sheet
Splash-proof welding agent described in any one in 1-7 and formed.