CN104057034A - Manufacturing process of integrated gas stove burner - Google Patents
Manufacturing process of integrated gas stove burner Download PDFInfo
- Publication number
- CN104057034A CN104057034A CN201410176195.5A CN201410176195A CN104057034A CN 104057034 A CN104057034 A CN 104057034A CN 201410176195 A CN201410176195 A CN 201410176195A CN 104057034 A CN104057034 A CN 104057034A
- Authority
- CN
- China
- Prior art keywords
- burner
- integrated gas
- manufacturing process
- finished product
- gas range
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a manufacturing process of an integrated gas stove burner and belongs to the technical field of gas stove burners. The integrated gas stove burner comprises a burner body and an upper burner cover, which are integrated. The manufacturing process comprises the following steps: performing gravity casting on liquid aluminum alloy to integrally form a semi-finished burner product; and performing after-treatment to obtain a finished integrated gas stove burner product. The integrated gas stove burner is high in yield, low in cost, not prone to rusting, stable in quality and long in life.
Description
Technical field
The invention belongs to the technical field of furnace end of gas cooker, particularly a kind of manufacturing process of integrated gas range burner.
Background technology
Along with the sustainable development of China's economy, people's growth in the living standard, the demand of home-use high-grade gas-cooker constantly increases.Burner is as the core component of gas-cooker, the performance of the whole gas-cooker of its quality influence
Common furnace end of gas cooker generally is split type, and its burner body for to separate manufacture, so just there will be sealing bad with burner upper cover, causes gas leakage; And burner body is iron casting manufacture; burner upper cover adopts aluminium alloy or copper alloy founding to manufacture; burner body usually there will be the phenomenon of getting rusty; cause not splitting with burner upper cover, and due to founding manufacturing process, the quality of burner body can not be guaranteed; may occur that there are sand or pore in inside; use may just there will be gas leakage for a long time, and serious may cause personal safety, and its processing cost is high.
Along with the improvement of technology, also there is the furnace end of gas cooker of integral type in this gas-cooker field, but its manufacturing process is founding manufacture, it there will be the drawback of founding manufacturing process equally, at the bottom of finished product rate, causes cost to improve, product quality can not be guaranteed simultaneously, and its life-span is not long.
Summary of the invention
The invention provides a kind of manufacturing process of integrated gas range burner, solved in prior art quality unstable, the problem that the life-span is not grown.Its technical scheme is as follows:
Integrated gas range burner, comprises burner body and burner upper cover, and is integrated, and its manufacturing process is: by liquid aluminium alloy by the semi-finished product of the one-body molded burner of gravity casting, then through the post processing formula furnace end of gas cooker finished product that becomes one.
In above-mentioned, concrete manufacturing technology steps is as follows:
A) manufacture loam core: the loam core of making burner internal cavity structures by core shooter;
B) casting semi-finished product: the correspondence position of loam core being put into the integrated gas range burner mould of gravity force casting machine, again aluminium alloy is melted to form temperature be that to be poured into mould temperature be in 200-400 DEG C of mould for the aluminium water of 650-800 DEG C, be incubated after 1-4 minute, the demoulding obtains integrated gas range burner semi-finished product;
C) post processing: after semi-finished product are naturally cooling, by the mode of beaing, inner loam core got, and clean out; By half-finished unnecessary waste material excision, through Overheating Treatment, then by polishing and ball blast, make its smooth surface clean again; Finally by being machined to as integral type furnace end of gas cooker finished product.
Aluminium coolant-temperature gage in above-mentioned steps b is preferably 700-720 DEG C.
Mould mould temperature in above-mentioned steps b is preferably 300-350 DEG C.
Temperature retention time in above-mentioned steps b is preferably 1.5-3 minute.
Adopt technique scheme, integrated gas range burner burner adopts aluminium alloy gravity casting to form, and its yield rate is high, and cost is low, and can not get rusty, steady quality, and the life-span is long.
Detailed description of the invention
To the technical scheme in the embodiment of the present invention be clearly and completely described below, obviously, described embodiment is only the present invention's part embodiment, instead of whole embodiment.Based on the embodiment in the present invention, those of ordinary skill in the art, not making the every other embodiment obtaining under creative work prerequisite, belong to the scope of protection of the invention.
Embodiment
Integrated gas range burner, comprises burner body and burner upper cover, and is integrated, and its manufacturing process is: by liquid aluminium alloy by the semi-finished product of the one-body molded burner of gravity casting, then through the post processing formula furnace end of gas cooker finished product that becomes one.Its yield rate is high, and cost is low, and can not get rusty, steady quality, and the life-span is long.
Its concrete manufacturing technology steps is as follows:
A) manufacture loam core: the loam core of making burner internal cavity structures by core shooter;
B) casting semi-finished product: the correspondence position of loam core being put into the integrated gas range burner mould of gravity force casting machine, again aluminium alloy thawing being formed to temperature is 650-800 DEG C, the aluminium water that is preferably 700-720 DEG C is poured into mould temperature for 200-400 DEG C, be preferably in the mould of 300-350 DEG C, insulation 1-4 minute, be preferably after 1.5-3 minute, the demoulding obtains integrated gas range burner semi-finished product;
C) post processing: after semi-finished product are naturally cooling, by the mode of beaing, inner loam core got, and clean out; By half-finished unnecessary waste material excision, through Overheating Treatment, then by polishing and ball blast, make its smooth surface clean again; Finally by being machined to as integral type furnace end of gas cooker finished product.
The foregoing is only preferred embodiment of the present invention, in order to limit the present invention, within the spirit and principles in the present invention not all, any amendment of doing, be equal to replacement, improvement etc., within all should being included in protection scope of the present invention.
Claims (5)
1. integrated gas range burner, comprises burner body and burner upper cover, and is integrated, and it is characterized in that, its manufacturing process is: by liquid aluminium alloy by the semi-finished product of the one-body molded burner of gravity casting, then through the post processing formula furnace end of gas cooker finished product that becomes one.
2. the manufacturing process of integrated gas range burner according to claim 1, is characterized in that, its concrete manufacturing technology steps is as follows:
A) manufacture loam core: the loam core of making burner internal cavity structures by core shooter;
B) casting semi-finished product: the correspondence position of loam core being put into the integrated gas range burner mould of gravity force casting machine, again aluminium alloy is melted to form temperature be that to be poured into mould temperature be in 200-400 DEG C of mould for the aluminium water of 650-800 DEG C, be incubated after 1-4 minute, the demoulding obtains integrated gas range burner semi-finished product;
C) post processing: after semi-finished product are naturally cooling, by the mode of beaing, inner loam core got, and clean out; By half-finished unnecessary waste material excision, through Overheating Treatment, then by polishing and ball blast, make its smooth surface clean again; Finally by being machined to as integral type furnace end of gas cooker finished product.
3. the manufacturing process of integrated gas range burner according to claim 2, is characterized in that, the aluminium coolant-temperature gage in above-mentioned steps b is preferably 700-720 DEG C.
4. the manufacturing process of integrated gas range burner according to claim 2, is characterized in that, the mould mould temperature in above-mentioned steps b is preferably 300-350 DEG C.
5. the manufacturing process of integrated gas range burner according to claim 2, is characterized in that, the temperature retention time in above-mentioned steps b is preferably 1.5-3 minute.