CN104047169B - A kind of synthetic leather solid polished finish agent of sheep Bagao and its preparation method - Google Patents
A kind of synthetic leather solid polished finish agent of sheep Bagao and its preparation method Download PDFInfo
- Publication number
- CN104047169B CN104047169B CN201410314115.8A CN201410314115A CN104047169B CN 104047169 B CN104047169 B CN 104047169B CN 201410314115 A CN201410314115 A CN 201410314115A CN 104047169 B CN104047169 B CN 104047169B
- Authority
- CN
- China
- Prior art keywords
- weight part
- bagao
- sheep
- synthetic leather
- polished finish
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to the solid polished finish agent of a kind of synthetic leather sheep Bagao and its preparation method, this treatment agent comprises following component: nitro-cotton, dimethyl formamide, second ester, silicon-dioxide flatting silica, epoxy soybean oil and amine hydroxybenzene. The solid polished finish agent of the sheep Bagao of the present invention is a kind of type material for the synthesis of leather last part technology, after this treatment agent polishing bright and oil wax effect good, feel is smooth, and the leather gloss nature made with this kind for the treatment of agent, color clarification net effect is good.
Description
Technical field
The present invention relates to synthetic leather surface treatment agent field, specifically, it relates to a kind of synthetic leather solid polished finish agent of sheep Bagao for the synthesis of leather last part technology, the present invention relates to the preparation method of the solid polished finish agent of this synthetic leather sheep Bagao simultaneously.
Background technology
Synthetic leather surface treatment agent can carry out surface daub on a wall according to the classification of product, and it can improve the brightness of synthetic leather, color and luster and feel, makes synthetic leather more close to corium. But, along with the color and luster of leather surface and feel are required more and more higher by human consumer, not only to be increased brightness and the feel of synthetic leather, require synthetic leather natural in color simultaneously, there is wax sense etc. And existing surface treatment agent can not meet the requirement that the aesthetic feeling of synthetic leather and feel are increased by human consumer day by day, therefore it is badly in need of one and can improve synthetic leather charcoal brightness, wax sense and the feel of synthetic leather can be improved again, the treatment agent of the net effects such as gloss.
Summary of the invention
In order to solve the problem and defect, it is an object of the invention to provide the solid polished finish agent of a kind of synthetic leather sheep Bagao.
The solid polished finish agent of sheep Bagao of the synthetic leather of the present invention is achieved through the following technical solutions:
The synthetic leather disclosed in this invention solid polished finish agent of sheep Bagao comprises following component: nitro-cotton, dimethyl formamide, second ester, silicon-dioxide flatting silica, epoxy soybean oil and amine hydroxybenzene.
Described synthetic leather is as follows by the proportioning of each component in the solid polished finish agent of sheep Bagao: nitro-cotton 18��20 weight part, dimethyl formamide 18��21 weight part, second ester 28��30 weight part, silicon-dioxide flatting silica 3��6 weight part, epoxy soybean oil 11��14 weight part, amine hydroxybenzene 3��4 weight part.
Further, described synthetic leather is as follows by the proportioning of each component in the solid polished finish agent of sheep Bagao: nitro-cotton 18��19 weight part, dimethyl formamide 19��20 weight part, second ester 28��29 weight part, silicon-dioxide flatting silica 4��5 weight part, epoxy soybean oil 12��13 weight part, amine hydroxybenzene 3��4 weight part.
Further, described synthetic leather is as follows by the proportioning of each component of the solid polished finish agent of sheep Bagao: nitro-cotton 19 weight part, dimethyl formamide 20 weight part, second ester 29 weight part, silicon-dioxide flatting silica 5 weight part, epoxy soybean oil 13 weight part, amine hydroxybenzene 3 weight part.
It is a further object of the present invention to provide the preparation method of the solid polished finish agent of a kind of above-mentioned synthetic leather sheep Bagao, the method includes the steps of:
1) taking each component materials in proportion, by the nitro-cotton of 1/2nd weight, and after the stirring of dimethyl formamide, second ester, silicon-dioxide flatting silica, grinding is filtered, and abandons filter residue;
2) in step 1) mixture of gained adds epoxy soybean oil, amine hydroxybenzene, stir evenly;
3) in step 2) mixture of gained adds the nitro-cotton of residue 1/2nd weight, stir evenly, obtain the solid polished finish agent of described synthetic leather sheep Bagao.
In the synthetic leather provided by the present invention preparation method with the solid polished finish agent of sheep Bagao, the proportioning of each component is as follows: nitro-cotton 18��20 weight part, dimethyl formamide 18��21 weight part, second ester 28��30 weight part, silicon-dioxide flatting silica 3��6 weight part, epoxy soybean oil 11��14 weight part, amine hydroxybenzene 3��4 weight part.
In one embodiment of the invention, the synthetic leather institute of the preparation method of the solid polished finish agent of sheep Bagao carries out in steps all at normal temperatures and pressures.
Owing to adopting above technical scheme, the present invention compared with prior art tool have the following advantages:
Synthetic leather of the present invention is ep-type material with the solid polished finish agent of sheep Bagao, meets the environmental protection standard of European Union;
Synthetic leather of the present invention each component of the solid polished finish agent of sheep Bagao is coordinated mutually, acting in conjunction, after polishing bright and oil wax effect good, feel is smooth, the leather gloss nature made with this kind for the treatment of agent, color clarification, and net effect is good;
Synthetic leather of the present invention a kind of type material that the solid polished finish agent of sheep Bagao is the printing of rear section, it is possible to for existing synthetic leather production line, technique is simple, it is not necessary to changes production unit, can not increase production cost.
Embodiment
In order to make the object of the present invention, technical scheme and advantage clearly understand, below in conjunction with embodiment, the present invention is further elaborated. It is to be understood that specific embodiment described herein is only in order to explain the present invention, it is not intended to limit the present invention.
Embodiment 1
The synthetic leather solid polished finish agent of sheep Bagao is made up of the component of following proportioning: nitro-cotton 20 weight part, dimethyl formamide 19 weight part, second ester 28 weight part, silicon-dioxide flatting silica 4 weight part, epoxy soybean oil 11 weight part, amine hydroxybenzene 4 weight part.
The above-mentioned synthetic leather preparation method of the solid polished finish agent of sheep Bagao is: at normal temperatures and pressures, the silicon-dioxide flatting silica of the second ester of the dimethyl formamide of the nitro-cotton of 10 weight parts, 19 weight parts, 28 weight parts, 4 weight parts is mixed, stir and mix to mixture at least 30 minutes, mixture is filtered, abandons filter residue; The said mixture obtained adds the epoxy soybean oil of 11 weight parts and the amine hydroxybenzene of 4 weight parts, stirs and mix to mixture at least 30 minutes; The said mixture obtained adds the nitro-cotton of remaining 10 weight parts, stirs and mix to mixture at least 30 minutes, obtain the solid polished finish agent of synthetic leather sheep Bagao of the present invention. The synthetic leather obtained by the performance index of the solid polished finish agent of sheep Bagao in table 1.
The methods such as the stirring that adopts in above-mentioned preparation process, the filtration method that to be in this area usual.
Embodiment 2
The synthetic leather solid polished finish agent of sheep Bagao is made up of the component of following weight percent: nitro-cotton 19 weight part, dimethyl formamide 20 weight part, second ester 29 weight part, silicon-dioxide flatting silica 5 weight part, epoxy soybean oil 13 weight part, amine hydroxybenzene 3 weight part.
The above-mentioned synthetic leather preparation method of the solid polished finish agent of sheep Bagao is: at normal temperatures and pressures, the silicon-dioxide flatting silica of the second ester of the dimethyl formamide of the nitro-cotton of 9.5 weight parts, 20 weight parts, 29 weight parts, 5 weight parts is mixed, stir and mix to mixture at least 30 minutes, mixture is filtered, abandons filter residue; The said mixture obtained adds the epoxy soybean oil of 13 weight parts and the amine hydroxybenzene of 3 weight parts, stirs and mix to mixture at least 30 minutes; The said mixture obtained adds the nitro-cotton of remaining 9.5 weight parts, stirs and mix to mixture at least 30 minutes, obtain the solid polished finish agent of synthetic leather sheep Bagao of the present invention. The synthetic leather obtained by the performance index of the solid polished finish agent of sheep Bagao in table 1.
The methods such as the stirring that adopts in above-mentioned preparation process, the filtration method that to be in this area usual.
Embodiment 3
The synthetic leather solid polished finish agent of sheep Bagao is made up of the component of following weight percent: nitro-cotton 18 weight part, dimethyl formamide 21 weight part, second ester 30 weight part, silicon-dioxide flatting silica 3 weight part, epoxy soybean oil 12 weight part, amine hydroxybenzene 3 weight part.
The above-mentioned synthetic leather preparation method of the solid polished finish agent of sheep Bagao is: at normal temperatures and pressures, the silicon-dioxide flatting silica of the second ester of the dimethyl formamide of the nitro-cotton of 9 weight parts, 21 weight parts, 30 weight parts, 3 weight parts is mixed, stir and mix to mixture at least 30 minutes, mixture is filtered, abandons filter residue; The said mixture obtained adds the epoxy soybean oil of 12 weight parts and the amine hydroxybenzene of 3 weight parts, stirs and mix to mixture at least 30 minutes; The said mixture obtained adds the nitro-cotton of remaining 9 weight parts, stirs and mix to mixture at least 30 minutes, obtain the solid polished finish agent of synthetic leather sheep Bagao of the present invention. The synthetic leather obtained by the performance index of the solid polished finish agent of sheep Bagao in table 1.
Embodiment 4
The synthetic leather solid polished finish agent of sheep Bagao is made up of the component of following weight percent: nitro-cotton 19 weight part, dimethyl formamide 18 weight part, second ester 29 weight part, silicon-dioxide flatting silica 6 weight part, epoxy soybean oil 14 weight part, amine hydroxybenzene 4 weight part.
The above-mentioned synthetic leather preparation method of the solid polished finish agent of sheep Bagao is: at normal temperatures and pressures, the silicon-dioxide flatting silica of the second ester of the dimethyl formamide of the nitro-cotton of 9.5 weight parts, 18 weight parts, 29 weight parts, 6 weight parts is mixed, stir and mix to mixture at least 30 minutes, mixture is filtered, abandons filter residue; The said mixture obtained adds the epoxy soybean oil of 14 weight parts and the amine hydroxybenzene of 4 weight parts, stirs and mix to mixture at least 30 minutes; The said mixture obtained adds the nitro-cotton of remaining 9.5 weight parts, stirs and mix to mixture at least 30 minutes, obtain the solid polished finish agent of synthetic leather sheep Bagao of the present invention. The synthetic leather obtained by the performance index of the solid polished finish agent of sheep Bagao in table 1.
The methods such as the stirring that adopts in above-mentioned preparation process, the filtration method that to be in this area usual.
Table 1
The foregoing is only the better embodiment of the present invention, not it is used for limiting the practical range of the present invention; If not departing from the spirit and scope of the present invention, the present invention being modified or equivalent replacement, all should be encompassed in the middle of the protection domain of the claims in the present invention.
Claims (5)
1. the synthetic leather solid polished finish agent of sheep Bagao, it is for the synthesis of the last part technology of leather, it is characterized in that, it is made up of each component of following proportioning: nitro-cotton 18��20 weight part, dimethyl formamide 18��21 weight part, second ester 28��30 weight part, silicon-dioxide flatting silica 3��6 weight part, epoxy soybean oil 11��14 weight part, amine hydroxybenzene 3��4 weight part.
2. the synthetic leather according to claim 1 solid polished finish agent of sheep Bagao, it is characterized in that, the proportioning of described each component is as follows: nitro-cotton 18��19 weight part, dimethyl formamide 19��20 weight part, second ester 28��29 weight part, silicon-dioxide flatting silica 4��5 weight part, epoxy soybean oil 12��13 weight part, amine hydroxybenzene 3��4 weight part.
3. the synthetic leather according to claim 1 solid polished finish agent of sheep Bagao, it is characterized in that, the proportioning of described each component is as follows: nitro-cotton 19 weight part, dimethyl formamide 20 weight part, second ester 29 weight part, silicon-dioxide flatting silica 5 weight part, epoxy soybean oil 13 weight part, amine hydroxybenzene 3 weight part.
4. synthetic leather according to any one of the claims 1-3 preparation method of the solid polished finish agent of sheep Bagao, it is characterised in that, comprise following step:
1) taking each component materials in proportion, by the nitro-cotton of 1/2nd weight, and after the stirring of dimethyl formamide, second ester, silicon-dioxide flatting silica, grinding is filtered, and abandons filter residue;
2) in step 1) mixture of gained adds epoxy soybean oil, amine hydroxybenzene, stir evenly;
3) in step 2) mixture of gained adds the nitro-cotton of residue 1/2nd weight, stir evenly, obtain the solid polished finish agent of described synthetic leather sheep Bagao.
5. the synthetic leather according to claim 4 preparation method of the solid polished finish agent of sheep Bagao, it is characterised in that, institute carries out in steps all at normal temperatures and pressures.