CN104046344A - Movable gel plugging agent for oilfield water injection - Google Patents
Movable gel plugging agent for oilfield water injection Download PDFInfo
- Publication number
- CN104046344A CN104046344A CN201310078645.2A CN201310078645A CN104046344A CN 104046344 A CN104046344 A CN 104046344A CN 201310078645 A CN201310078645 A CN 201310078645A CN 104046344 A CN104046344 A CN 104046344A
- Authority
- CN
- China
- Prior art keywords
- linking agent
- mass ratio
- polyacrylamide
- aqueous solution
- resene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A movable gel profile control agent for oilfield flooding is characterized in that a heterocyclic resin cross-linking agent accounting for 0.15-0.3% of the mass ratio of the heterocyclic resin cross-linking agent to a polyacrylamide aqueous solution accounting for 0.15-0.3% of the mass ratio of the polyacrylamide aqueous solution, an organic chromium cross-linking agent accounting for 0.3-0.4% of the mass ratio of the heterocyclic resin cross-linking agent to the polyacrylamide aqueous solution, and a hexamethylenetetramine-thiourea stabilizer accounting for 0.1-0.15% of the mass ratio of the heterocyclic resin cross. The invention is used for water injection profile control of oil fields, and the heterocyclic resin cross-linking agent with lower cost and the nonhazardous organic chromium cross-linking agent are added into the aqueous solution of polyacrylamide, so the economic benefit and the environmental protection level of large-scale application are improved.
Description
Technical field: the present invention relates to a kind of oil extraction in oil field Chemicals, especially for the movable gel plugging agent of a kind of oil-field flooding of Profile Control in Injection Well.
Background technology: before the present invention, each oil field, for the polyacrylamide plugging agent of water injectivity profile modification, adopts chromium metal system or the stronger phenolic aldehyde cross-linking system of toxic that cost is higher more, thereby affected economic benefit or the Environmental Protection Level of large-scale application.
Summary of the invention: the object of the invention is: for oil-field flooding profile control provides a kind of oil-field flooding movable gel plugging agent, because this product is the organic chromium linking agent that adds heterocycle resene linking agent and toxicological harmless in the aqueous solution of polyacrylamide, thereby economic benefit and the Environmental Protection Level of large-scale application are improved.
The object of the invention is to realize by following measures: the movable gel plugging agent of a kind of oil-field flooding, comprise polyacrylamide, heterocycle resene linking agent, organic chromium linking agent, vulkacit H-thiocarbamide stablizer, it is characterized in that in the aqueous solution of mass content 0.15%-0.3% polyacrylamide, add and the heterocycle resene linking agent of its mass ratio 0.15%-0.3%, the organic chromium linking agent of 0.3%-0.4%, vulkacit H-thiocarbamide stablizer of 0.1%-0.15%; Wherein heterocycle resene linking agent is by phenol and the furans ring system derivative of mol ratio 1:1 and forms with sodium hydroxide, 17% ethanol of its mass ratio 10%.
The present invention is for oil-field flooding profile control, owing to being the organic chromium linking agent that adds lower-cost heterocycle resene linking agent and toxicological harmless in the aqueous solution of polyacrylamide, thereby improved economic benefit and the Environmental Protection Level of large-scale application.
Embodiment: the movable gel plugging agent of oil-field flooding, be in the aqueous solution of mass content 0.15%-0.3% polyacrylamide, add and the heterocycle resene linking agent of its mass ratio 0.15%-0.3%, the organic chromium linking agent of 0.3%-0.4%, vulkacit H-thiocarbamide stablizer of 0.1%-0.15%; Wherein heterocycle resene linking agent is by phenol and the furans ring system derivative of mol ratio 1:1 and forms with sodium hydroxide, 17% ethanol of its mass ratio 10%.
Embodiment is:
1, the preparation of heterocycle resene linking agent:
1.1 get phenol and the furans ring system derivative (pure substance mol ratio 1:1) of aequum, then by the mass ratio of this total amount 10% get sodium hydroxide, to get ethanol by 17% for subsequent use;
1.2 pour got phenol into reactor passes into steam and heats to 50 DEG C, adds 70% amount of got sodium hydroxide after being melt into liquid, keeps 50 DEG C of temperature of reaction kettle, stirring reaction 20 minutes;
80% amount of got furans ring system derivative is added this reactor by 1.3, keeps 50 DEG C of temperature of reaction kettle, stirring reaction 50 minutes;
1.4 add this reactor, stirring reaction 20 minutes by 30% amount of got sodium hydroxide remainder;
20% amount of got furans ring system derivative remainder is added this reactor by 1.5, keeps 50 DEG C of temperature of reaction kettle, stirring reaction 3 hours;
1.6 by got ethanol all amount add this reactor, obtain bright red-brown, can be completely water-soluble solution finished product.
2, the scene of the movable gel plugging agent of oil-field flooding preparation:
2.1 prepare the aqueous solution of slaking mass content 0.15%-0.3% polyacrylamide in the desired amount;
2.2 add the heterocycle resene linking agent that 0.15%-0.3% made, the organic chromium linking agent of 0.3%-0.4%, vulkacit H-thiocarbamide stablizer of 0.1%-0.15% by its mass ratio of the polyacrylamide solution after slaking;
After 2.3 cooperations, fully stir, make the methylolphenol of polyacrylamide and organic chromium linking agent carry out condensation reaction (reaction formula one), carry out condensation reaction (reaction formula two) with heterocycle resene linking agent;
Reaction formula one:
Reaction formula two:
2.4 question responses complete under direct Injection Well, and closing well 5 days.
Claims (1)
1. the movable gel plugging agent of oil-field flooding, comprise polyacrylamide, heterocycle resene linking agent, organic chromium linking agent, vulkacit H-thiocarbamide stablizer, it is characterized in that: in the aqueous solution of mass content 0.15%-0.3% polyacrylamide, add and the heterocycle resene linking agent of its mass ratio 0.15%-0.3%, the organic chromium linking agent of 0.3%-0.4%, vulkacit H-thiocarbamide stablizer of 0.1%-0.15%; Wherein heterocycle resene linking agent is by phenol and the furans ring system derivative of mol ratio 1:1 and forms with sodium hydroxide, 17% ethanol of its mass ratio 10%.