CN104046106A - Insulative coating - Google Patents
Insulative coating Download PDFInfo
- Publication number
- CN104046106A CN104046106A CN201410304134.2A CN201410304134A CN104046106A CN 104046106 A CN104046106 A CN 104046106A CN 201410304134 A CN201410304134 A CN 201410304134A CN 104046106 A CN104046106 A CN 104046106A
- Authority
- CN
- China
- Prior art keywords
- parts
- distilled water
- epoxy resin
- weight
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an insulative coating which is prepared from the following raw materials in parts by weight: 30-50 parts of epoxy resin, 6-10 parts of aluminum hydroxide, 3-6 parts of acrylic acid, 7-10 parts of thickener, 6-9 parts of titanium dioxide, 4-7 parts of hydroxyethyl cellulose, 20-30 parts of distilled water, 4-11 parts of a flame retardant, 2-4 parts of a dispersant and 9-15 parts of acrylate resin. The coating provided by the invention has the beneficial effects that the coating provided by the invention has an extremely strong insulating performance, is further good in thermal performance and mechanical performance and is very suitable for high-power electrical appliances and interior trim.
Description
Technical field
The present invention relates to a kind of insulation compound, belong to building material technical field.
Background technology
Insulation compound has the coating of good electric insulativity.There are good electrical property, thermal characteristics, mechanical property and chemical property.Mostly be varnish, also coloured enamel.Insulation compound heatproof, below 600 DEG C, adopts inorganic-organic polymer base-material, high, the hard-packed inorganic crystal material composition of volume specific resistance, and if aluminum oxide, silicon nitride etc. are filler, taking ceramic particle as high temperature film forming matter is as main, composition high-temperature-resistant insulating paint.Avoid stray ion, especially the introducing of basic metal or alkaline-earth metal ions; Reduce the content of glassy phase as far as possible, and be reduced to the electric conductivity of the glassy phase that improves processing performance and add as far as possible.
Summary of the invention
The deficiency existing for prior art, the technical problem to be solved in the present invention is, a kind of coating is provided, and has extremely strong insulating property, and thermal characteristics, mechanical property is also better, is very suitable for high-power electric appliance and interior decoration.
For solving the problems of the technologies described above, technical scheme of the present invention is, a kind of insulation compound, and its raw material by following parts by weight is made:
Epoxy resin 30-50 part, aluminium hydroxide 6-10 part, vinylformic acid 3-6 part, thickening material 7-10 part, titanium dioxide 6-9 part, Natvosol 4-7 part, distilled water 20-30 part, fire retardant 4-11 part, dispersion agent 2-4 part, acrylate resin 9-15 part.
The technical scheme of optimization of the present invention is, a kind of insulation compound, and its raw material by following parts by weight is made:
40 parts of epoxy resin, 8 parts, aluminium hydroxide, 4.5 parts, vinylformic acid, 8.5 parts of thickening materials, 7.5 parts of titanium dioxides, 6 parts of Natvosols, 25 parts of distilled water, 7 parts of fire retardants, 3 parts of dispersion agents, 12 parts of acrylate resins.
The invention has the beneficial effects as follows, coating of the present invention has extremely strong insulating property, and thermal characteristics, and mechanical property is also better, is very suitable for high-power electric appliance and interior decoration.
Embodiment
embodiment 1
A kind of insulation compound, its raw material by following parts by weight is made:
30 parts of epoxy resin, 6 parts, aluminium hydroxide, 3 parts, vinylformic acid, 7 parts of thickening materials, 6 parts of titanium dioxides, 4 parts of Natvosols, 20 parts of distilled water, 4 parts of fire retardants, 2 parts of dispersion agents, 9 parts of acrylate resins.
embodiment 2
A kind of insulation compound, its raw material by following parts by weight is made:
50 parts of epoxy resin, 10 parts, aluminium hydroxide, 6 parts, vinylformic acid, 10 parts of thickening materials, 9 parts of titanium dioxides, 7 parts of Natvosols, 30 parts of distilled water, 11 parts of fire retardants, 4 parts of dispersion agents, 15 parts of acrylate resins.
embodiment 3
A kind of insulation compound, its raw material by following parts by weight is made:
40 parts of epoxy resin, 8 parts, aluminium hydroxide, 4.5 parts, vinylformic acid, 8.5 parts of thickening materials, 7.5 parts of titanium dioxides, 6 parts of Natvosols, 25 parts of distilled water, 7 parts of fire retardants, 3 parts of dispersion agents, 12 parts of acrylate resins.
Claims (2)
1. an insulation compound, is characterized in that: its raw material by following parts by weight is made:
Epoxy resin 30-50 part, aluminium hydroxide 6-10 part, vinylformic acid 3-6 part, thickening material 7-10 part, titanium dioxide 6-9 part, Natvosol 4-7 part, distilled water 20-30 part, fire retardant 4-11 part, dispersion agent 2-4 part, acrylate resin 9-15 part.
2. coating according to claim 1, is characterized in that: its raw material by following parts by weight is made:
40 parts of epoxy resin, 8 parts, aluminium hydroxide, 4.5 parts, vinylformic acid, 8.5 parts of thickening materials, 7.5 parts of titanium dioxides, 6 parts of Natvosols, 25 parts of distilled water, 7 parts of fire retardants, 3 parts of dispersion agents, 12 parts of acrylate resins.