CN104046030A - High temperature-resistant oil-resistant rubber - Google Patents
High temperature-resistant oil-resistant rubber Download PDFInfo
- Publication number
- CN104046030A CN104046030A CN201410287790.6A CN201410287790A CN104046030A CN 104046030 A CN104046030 A CN 104046030A CN 201410287790 A CN201410287790 A CN 201410287790A CN 104046030 A CN104046030 A CN 104046030A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- high temperature
- resistant
- oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses high temperature-resistant oil-resistant rubber. The high temperature-resistant oil-resistant rubber is characterized by consisting of the following components in parts by weight: 50 parts of silicon rubber, 35 parts of natural rubber, 27 parts of nitrile rubber, 15 parts of fluororubber, 4 parts of zinc oxide, 1.8 parts of stearic acid, 2.6 parts of accelerant CZ, 35 parts of carbon black, 3.4 parts of anti-ageing agent RD, 5 parts of paraffin, 3 parts of 2,2 '- dithiobisbenzothiazole and 30 parts of flame retardant. The silicon rubber and the fluororubber are combined, so that mechanical performance, thermal stability and oil resistance of the silicon rubber are effectively improved; the flame retardant is added, so that the high temperature-resistant oil-resistant rubber has oil temperature resistance and flame resistance. The rubber disclosed by the invention has high temperature resistance of the silicon rubber, and oil resistance of the nitrile rubber; the natural rubber is added, so that production cost is lowered; and the rubber disclosed by the invention has excellent high temperature resistance and oil resistance.
Description
Technical field
The invention belongs to rubber materials, specifically a kind of high temperature resistant oil resisting rubber.
Background technology
Silicon rubber is a kind of macromolecular material of excellent combination property, there is high and low temperature resistance, excellent resistance to ozone ageing, thermo-oxidative ageing, photoaging and weather aging resistance, good electrical insulation capability and special surface property, good ventilation property and excellent physiology inertia.Make it of many uses, except automobile, electrical equipment and electronics, office apparatus three large field application, also in a large number for high-tech areas such as building, medical treatment, foodstuffs industry and Aeronautics and Astronautics, but there is certain deficiency at aspects such as physical strength, oil resistant, resistance to solvent, acidproof, alkaline-resisting and resistance to steam in silicon rubber, has greatly limited its application.
Rubber blending also claims elastomerics use, is a kind of technology that starts for a long time application in rubber industry, and rubber blending can meet its required application, can solve again some problem existing in single rubber compound in the past, and production cost is corresponding reduction also.But different sorts rubber and with needs, consider compatibility problem, prior art is not also by the example of silicon rubber, natural rubber, paracril and viton use.
Summary of the invention
The object of the invention is to prior art defect, a kind of high temperature resistant oil resisting rubber is provided.
Object of the present invention can be achieved through the following technical solutions:
A kind of high temperature resistant oil resisting rubber, it is characterized in that, described high temperature resistant oil resisting rubber is comprised of the component of following weight part: 5 parts, 50 parts, silicon rubber, 35 parts of natural rubbers, 27 parts of paracrils, 15 parts of viton, 4 parts, zinc oxide, 1.8 parts of stearic acid, 2.6 parts of accelerant CZs, 35 parts of carbon blacks, 3.4 parts of anti-aging agent RDs, paraffin, 2,3 parts of 2'-dithio-bis-benzothiazoles, 30 parts of fire retardants.
Described fire retardant is that magnesium hydroxide, ammonium polyphosphate, zinc borate are with the mixing of 1:1:1 ratio.
The present invention also comprises 0.7 part, sulphur.
Beneficial effect of the present invention: silicon rubber and viton are also used and effectively improved the mechanical property of silicon rubber, thermostability and oil-proofness, add fire retardant, there is high temperature resistant and flame retardant properties, rubber of the present invention has the high thermal resistance of silicon rubber, the oil-proofness of paracril, adds natural rubber, reduces production costs; Rubber of the present invention has excellent high thermal resistance and oil-proofness, and its mechanical property is improved.
Embodiment
Embodiment
A high temperature resistant oil resisting rubber, described high temperature resistant oil resisting rubber is comprised of the component of following weight part: 50 parts, silicon rubber, 35 parts of natural rubbers, 27 parts of paracrils, 15 parts of viton, 4 parts, zinc oxide, 1.8 parts of stearic acid, 2.6 parts of accelerant CZs, 35 parts of carbon blacks, 3.4 parts of anti-aging agent RDs, 5 parts, paraffin,, 0.7 part, sulphur, 2,3 parts of 2'-dithio-bis-benzothiazoles, 10 parts of magnesium hydroxides, 10 parts of ammonium polyphosphates, 10 parts of zinc borates.
Above content is only to structure example of the present invention and explanation; affiliated those skilled in the art make various modifications to described specific embodiment or supplement or adopt similar mode to substitute; only otherwise depart from the structure of invention or surmount this scope as defined in the claims, all should belong to protection scope of the present invention.
Claims (3)
1. a high temperature resistant oil resisting rubber, it is characterized in that, described high temperature resistant oil resisting rubber is comprised of the component of following weight part: 5 parts, 50 parts, silicon rubber, 35 parts of natural rubbers, 27 parts of paracrils, 15 parts of viton, 4 parts, zinc oxide, 1.8 parts of stearic acid, 2.6 parts of accelerant CZs, 35 parts of carbon blacks, 3.4 parts of anti-aging agent RDs, paraffin, 2,3 parts of 2'-dithio-bis-benzothiazoles, 30 parts of fire retardants.
2. high temperature resistant oil resisting rubber according to claim 1, is characterized in that, described fire retardant is that magnesium hydroxide, ammonium polyphosphate, zinc borate are with the mixing of 1:1:1 ratio.
3. high temperature resistant oil resisting rubber according to claim 1, is characterized in that, also comprises 0.7 part, sulphur.