CN104045462A - 桐油包膜缓释肥及其制备方法 - Google Patents
桐油包膜缓释肥及其制备方法 Download PDFInfo
- Publication number
- CN104045462A CN104045462A CN201410314684.2A CN201410314684A CN104045462A CN 104045462 A CN104045462 A CN 104045462A CN 201410314684 A CN201410314684 A CN 201410314684A CN 104045462 A CN104045462 A CN 104045462A
- Authority
- CN
- China
- Prior art keywords
- fertilizer
- tung oil
- coated
- film
- slow release
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种桐油包膜缓释肥及其制备方法。它的包膜物为桐油,在空气中吸收氧气的能力强,干燥快,被称为干性油,具有很好的成膜性。制备方法包括加热,控温,拌和,干燥。制成的包膜肥料不吸湿,强度和耐磨性好,能减缓尿素分解,阻止氮素挥发,减少磷和钾的流失,有效延长肥力期,肥料利用率高;包膜物含植物营养素丰富,能向作物提供多种有机养分,且具有改良土壤,增强地力,防治病虫害的复合作用。本发明简化了包膜工艺,降低了生产成本,合理有效地解决了一般植物油包涂化肥不密封、不干燥、不结膜的“三不”工艺技术难题。
Description
技术领域
本发明涉及包膜型缓释肥料技术领域,具体涉及一种桐油包膜缓释肥。
背景技术
一般不饱和油肥料包膜,如亚麻籽油、葵花籽油、红花油、大豆油等形成的肥料包膜,比硫磺等无机物形成的包膜的防水性能和释放效果要好一些,但这些有机包膜肥料的制备相对复杂,一般在肥料颗粒上要涂两层涂层:第一层是具高黏性不饱和油,第二层是起密封作用的低黏性不饱和油;在进行包膜前,还要往油中掺和催干剂。因此制备费用增高,加大了生产投入。有些包膜还招引地下害虫,可能对环境和农业产生负面影响。
发明内容
本发明的目的在于提供一种桐油包膜缓释肥及其制备方法,克服上述技术中存在的缺陷。
本发明这样实现上述目的:
1.一种桐油包膜缓释肥,其包括颗粒肥料和包覆该颗粒肥料的包膜,所述包膜由桐油形成。
2.以上1的桐油包膜缓释肥,其中颗粒肥料选自氮肥、钾肥、磷肥、复混肥料、掺混肥料中的一种或多种。
3.以上1或2的桐油包膜缓释肥,其中包覆该颗粒肥料的包膜的厚度为1μm~200μm,优选10μm~100μm,更优选10μm~50μm。
4.以上1~3任一项的桐油包膜缓释肥的制备方法,其特征在于,制备工艺的具体步骤如下:
(1)将桐油加热到65~100℃,优选70-80℃,更优选71℃,使其溶解熟化;
(2)将步骤(1)熟桐油的温度控制在45~50℃,优选48℃左右;
(3)按照1:15~35,优选1:20~30,更优选1:23~27的比例,将步骤(2)的熟桐油喷洒到化肥颗粒料上,再采用搅拌机拌和(例如3分钟以上,例如3~5min),使桐油在颗粒料表面涂抹均匀;
(4)将步骤(3)得到的涂油颗粒料干燥结膜,形成包衣,即得成品。
5.以上1~3任一项的桐油包膜缓释肥的制备方法,其特征在于,制备工艺的具体步骤如下:
(1)按照1:20~30的比例,将生桐油喷洒到选好的化肥颗粒料上,再采用搅拌拌和(例如3分钟以上,例如3~5min),使桐油在颗粒料表面涂抹均匀。
(2)将涂油颗粒料置于通风处,干燥结膜,形成包衣,即得成品。
以上5的方法适用于夏天气温高的情况下例如气温达到30~40℃的情况下。
在以上步骤(1)中,通过将将桐油加热到65~100℃,优选70-80℃,更优选71℃,使其溶解熟化,增强其自行聚合力。
在以上步骤(2)中,通过将步骤(1)熟桐油的温度控制在45~50℃,优选48℃左右,避免骤热骤冷,防止变型和痴化。
本发明采用的缓释肥的包膜物桐油,从油桐子热压所得,一种干性植物油,我国特产。其特有的成膜性适宜做缓释肥包膜。《辞海》中记载,桐油的主要成分是桐油酸,简称“桐酸”,一种具有三个双键互成共轭体系的三烯酸。有多种顺反异构体存在,最主要的a-桐酸,熔点48~49℃;β-桐酸,溶点71℃。桐酸易聚合及被氧化。将桐油涂成薄片,在空气中能干燥结膜;高温加热,可自行聚合而成凝胶,这是其它干性油所未有的特性。
发明人将上述桐油用作包膜物,它特有的成膜性使其在肥料表面形成包衣,减少了磷和钾的流失以及氮的流失和挥发,提高肥料利用率,减少对环境造成的污染。此外,它还具有一些其它缓释肥包膜所没有的优点:供肥培肥,防治病虫害,发挥复合作用。
本发明的有益效果是:
1、桐油是我国特产,货源广泛,其价格比当地其它不饱和油平均价低30%左右,可减少原材料支出。
2、本品制备方法简单,工艺流程短,减少了不饱和油包膜肥料通常的重复涂层环节,免去了添加催干剂,节省了人力物力,降低了生产成本。
3、本品具有杀虫、杀菌、抑制细菌生长的作用。
4、本品不吸湿,强度和耐磨性好,便于运输和贮存。
5、本品宜做基肥和种肥,施于种子斜下方和两穴种子之间,深度8-12cm,也可作追肥,追施的时间要适当提前。本品能有效减缓尿素分解,阻止氮素挥发,减少有效磷、钾的流失,延长肥效期一倍以上,提高肥料利用率。
6、本品的包膜物能向作物提供蛋白质、糖类、脂肪、维生素等多种有机养分,等肥量施肥可增产14%以上,同等产量可节肥20%-30%,还具有改良土壤、增强地力的作用。
7、本品具有杀虫、杀菌、抑制细菌生长的作用,防治病原线虫和地下害虫危害的效果突出。
具体实施方式
实施例1
本实施例所采用的一种桐油包膜缓释肥的制备方法,其特征在于,制备工艺的具体步骤如下:
(1)加热 取所用桐油,加热至71℃,使其熔解熟化,增强自行聚合力。
(2)控温 将步骤(1)熟桐油的温度控制在48℃左右,避免骤热骤冷,防止变型和痴化。
(3)拌和 按照1:20的比例,将步骤(2)的熟桐油喷洒到选好的氮肥尿素颗粒料上,再采用搅拌机拌和3~5min,使桐油在颗粒料表面涂抹均匀。
(4)干燥 将步骤(3)得到的涂油颗粒料置于通风处,干燥结膜,膜厚度一般为40~50μm左右,形成包衣,即得成品。
实施例2
本实施例所采用的一种桐油包膜缓释肥的制备方法,其特征在于,制备工艺的具体步骤如下:
(1)加热 取所用桐油,加热至71℃,使其熔解熟化,增强自行聚合力。
(2)控温 将步骤(1)熟桐油的温度控制在48℃左右,避免骤热骤冷,防止变型和痴化。
(3)拌和 按照1:25的比例,将步骤(2)的熟桐油喷洒到选好的氮磷复合肥磷酸二铵颗粒料上,再采用搅拌机拌和3~5min,使桐油在颗粒料表面涂抹均匀。
(4)干燥 将步骤(3)得到的涂油颗粒料置于通风处,干燥结膜,膜厚度一般为30-50μm,形成包衣,即得成品。
实施例3
本实施例所采用的一种桐油包膜缓释肥的制备方法,其特征在于,制备工艺的具体步骤如下:
(1)加热 取所用桐油加热至71℃,使其溶解熟化,增强自行聚合力。
(2)控温 将步骤(1)熟桐油的温度控制在48℃左右,避免骤热骤冷和痴化。
(3)拌和 按照1:30的比例将步骤(2)的熟桐油喷洒到选好的钾肥氯化钾颗粒料上,再采用搅拌机拌和3~5min,使桐油在颗粒料表面涂抹均匀。
(4)干燥 将步骤(3)得到的涂油颗粒料置于通风处,干燥结膜,膜厚度为20~50μm左右,形成包衣,即得成品。
实施例4
本实施例所采用的一种桐油包膜缓释肥的制备方法,其特征在于,制备工艺的具体步骤如下:
(1)加热 取所用桐油,加热至71℃,使其熔解熟化,增强其自行聚合力。
(2)控温 将步骤(1)熟化的桐油的温度控制在48℃左右,避免骤热骤冷,防止变型和痴化。
(3)拌和 按照1:30的比例,将步骤(2)的熟桐油喷洒到选好的复混氮磷钾化肥颗粒料上,再采用搅拌机拌和3~5min,使桐油在颗粒料表面涂抹均匀。
(4)干燥 将步骤(3)得到的涂油颗粒料置于通风处,干燥结膜,膜厚度一般为10~30μm左右,形成包衣,即得成品。
应用试验1
将实施例2的含桐油的桐油包膜缓释肥和市售氮磷复合肥分别按照每亩50kg施用于地理位置相邻、土壤条件相同的两块大豆试验田,施用不同肥料的两种试验田按照相同的常规方法进行除虫除草管理,收割,称重,结果,使用本发明的桐油包膜缓释肥的大豆每亩增产约14%。
应用试验2
将氮磷复合肥按照每亩50kg和实施例2的含桐油的桐油包膜缓释肥按照每亩35kg的量施用于地理位置相邻、土壤条件相同的两块玉米试验田,施用不同肥料的两种试验田按照相同的常规方法进行除虫除草管理,收割,称重,结果,使用本发明的桐油包膜缓释肥的试验田产量与施用市售化肥的对比试验田产量基本相当。
Claims (5)
1.一种桐油包膜缓释肥,其包括颗粒肥料和包覆该颗粒肥料的包膜,所述包膜由桐油形成。
2.根据权利要求1所述的桐油包膜缓释肥,其中颗粒肥料选自氮肥、钾肥、磷肥、复混肥料、掺混肥料中的一种或多种。
3.根据权利要求1或2所述的桐油包膜缓释肥,其中包覆该颗粒肥料的包膜的厚度为1μm~200μm,优选10μm~100μm,更优选10μm~50μm。
4.根据权利要求1~3任一项所述的桐油包膜缓释肥的制备方法,其特征在于,制备工艺的具体步骤如下:
(1)将桐油加热到65~100℃,优选70-80℃,更优选71℃,使其溶解熟化;
(2)将步骤(1)熟桐油的温度控制在45~50℃,优选48℃左右;
(3)按照1:15~35,优选1:20~30,更优选1:23~27的比例,将步骤(2)的熟桐油喷洒到化肥颗粒料上,再采用搅拌机拌和,使桐油在颗粒料表面涂抹均匀;
(4)将步骤(3)得到的涂油颗粒料干燥结膜,形成包衣,即得成品。
5.根据权利要求1~3任一项所述的桐油包膜缓释肥的制备方法,其特征在于,制备工艺的具体步骤如下:
(1)按照1:20~30的比例,将生桐油喷洒到选好的化肥颗粒料上,再采用搅拌拌和,使桐油在颗粒料表面涂抹均匀;
(2)将涂油颗粒料置于通风处,干燥结膜,形成包衣,即得成品。