CN104030695A - 一种窑头罩顶挂砖 - Google Patents

一种窑头罩顶挂砖 Download PDF

Info

Publication number
CN104030695A
CN104030695A CN201410216518.9A CN201410216518A CN104030695A CN 104030695 A CN104030695 A CN 104030695A CN 201410216518 A CN201410216518 A CN 201410216518A CN 104030695 A CN104030695 A CN 104030695A
Authority
CN
China
Prior art keywords
brick
particle diameter
head cover
mullite
kiln head
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410216518.9A
Other languages
English (en)
Inventor
钱国良
陈东磊
佘广逸
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGXING GUOSHENG REFRACTORY MATERIAL CO LTD
Original Assignee
CHANGXING GUOSHENG REFRACTORY MATERIAL CO LTD
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGXING GUOSHENG REFRACTORY MATERIAL CO LTD filed Critical CHANGXING GUOSHENG REFRACTORY MATERIAL CO LTD
Priority to CN201410216518.9A priority Critical patent/CN104030695A/zh
Publication of CN104030695A publication Critical patent/CN104030695A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种砖，尤其涉及一种窑头罩顶挂砖，旨在解决现有技术中窑头罩顶挂砖使用寿命低的问题。一种窑头罩顶挂砖，按照质量百分比，包括5％～20％的特级矾土、45％～60％的莫来石、5％～10％的棕刚玉、5％～10％的SiC、3％～5％的氧化铝、4％～7％的硅微粉、2％～5％的广西白泥、6.5％～7.5％的高铝水泥、0.1％～0.3％的防爆纤维、0.2％～0.4％的三聚磷酸钠、5.5％～6.5％的水。采用该配方合成的挂砖，各种成分之间的相互搭配，防漏、耐高温、耐腐蚀、隔热效果好，较传统的耐火砖寿命提高了1～1.5倍。

Description

一种窑头罩顶挂砖
技术领域
本发明涉及一种砖，尤其涉及一种窑头罩顶挂砖。
背景技术
为了防止窑炉内的火烧坏窑头罩顶，通常在窑头罩顶的下端挂接一层耐火的挂砖，将火苗和窑头罩顶隔离；现有的窑头罩顶挂砖在长期高温和强腐蚀的作用下，容易损坏，寿命较低，需要经常更换；维修复杂，成本较高。
发明内容
本发明提供了一种窑头罩顶挂砖，旨在解决现有技术中窑头罩顶挂砖使用寿命低的问题。
为了解决以上技术问题，本发明通过以下技术方案实现：一种窑头罩顶挂砖，按照质量百分比，包括5％～20％的特级矾土、45％～60％的莫来石、5％～10％的棕刚玉、5％～10％的SiC、3％～5％的氧化铝、4％～7％的硅微粉、2％～5％的广西白泥、6.5％～7.5％的高铝水泥、0.1％～0.3％的防爆纤维、0.2％～0.4％的三聚磷酸钠、5.5％～6.5％的水。
进一步，按照质量百分比，按照质量百分比，包括10％的特级矾土、51％的莫来石、6％的棕刚玉、6.5％的碳化硅、4％的氧化铝、5.5％的硅微粉、3.5％的广西白泥、7％的高铝水泥、0.2％的防爆纤维、0.3％的三聚磷酸钠、6％的水；综合效果最佳。
进一步，特级矾土的粒径为5～8mm、莫来石的粒径为1～5mm、棕刚玉的粒径不大于1mm、SiC的粒径不大于1mm；挂砖比较密实，隔热效果好，使用寿命长。
进一步，粒径为1～3mm的莫来石质量的百分含量为20％～35％、粒径为3～5mm的质量的百分含量为20％～35％；采用这种配比，挂砖的寿命最长。
进一步，所述SiC为质量分数不小于98％的98SiC，所述硅微粉为质量分数不小于98％的98硅微粉；减少了杂质的含量，耐高温和耐腐蚀效果好。
与现有技术相比本发明的优点是：采用该配方合成的挂砖，各种成分之间的相互搭配，防漏、耐高温、耐腐蚀、隔热效果好，较传统的耐火砖寿命提高了1～1.5倍。
具体实施方式
一种窑头罩顶挂砖，按照质量百分比，包括10％粒径为5～8mm的特级矾土、25.5％粒径为1～3mm的莫来石、25.5％粒径为3～5mm的莫来石、6％粒径不大于1mm的棕刚玉、6.5％粒径不大于1mm的碳化硅、4％的氧化铝、4％的硅微粉、1.5％的金属硅、3.5％的广西白泥、7％的高铝水泥、0.2％的防爆纤维、0.3％的三聚磷酸钠、6％的水。
特级矾土在高温下比较稳定，防腐蚀和高温效果好；莫来石耐高温和耐腐蚀，而且导热系数低；棕刚玉耐腐蚀，膨胀系数低，不开裂性能稳定；广西白泥用于粘结其它配料，粘结效果好；采用上述比例的广西白泥和高铝白泥配合使用粘结强度较单独使用增强了1.3倍；三聚磷酸钠在高温下提高了各种成分的聚合力，使挂砖更加密实。
采用该配方合成的砖体，各种成分之间的相互搭配，防漏、耐高温、耐腐蚀、隔热效果好，采用该配方与上述的结构相配合，较传统的耐火砖寿命提高了1.5倍。
以上所述仅为本发明的具体实施例，但本发明的技术特征并不局限于此，任何本领域的技术人员在本发明的领域内，所作的变化或修饰皆涵盖在本发明的专利范围之中。

Claims (5)

1.一种窑头罩顶挂砖，其特征是：按照质量百分比，包括5％～20％的特级矾土、45％～60％的莫来石、5％～10％的棕刚玉、5％～10％的SiC、3％～5％的氧化铝、4％～7％的硅微粉、2％～5％的广西白泥、6.5％～7.5％的高铝水泥、0.1％～0.3％的防爆纤维、0.2％～0.4％的三聚磷酸钠、5.5％～6.5％的水。
2.根据权利要求1所述的一种窑头罩顶挂砖，其特征是：按照质量百分比，包括10％的特级矾土、51％的莫来石、6％的棕刚玉、6.5％的碳化硅、4％的氧化铝、5.5％的硅微粉、3.5％的广西白泥、7％的高铝水泥、0.2％的防爆纤维、0.3％的三聚磷酸钠、6％的水。
3.根据权利要求1所述的一种窑头罩顶挂砖，其特征是：特级矾土的粒径为5～8mm、莫来石的粒径为1～5mm、棕刚玉的粒径不大于1mm、SiC的粒径不大于1mm。
4.根据权利要求1或3所述的一种窑头罩顶挂砖，其特征是：粒径为1～3mm的莫来石质量的百分含量为20％～35％、粒径为3～5mm的质量的百分含量为20％～35％。
5.根据权利要求1所述的一种窑头罩顶挂砖，其特征是：所述SiC为质量分数不小于98％的98SiC，所述硅微粉为质量分数不小于98％的98硅微粉。
CN201410216518.9A 2014-05-21 2014-05-21 一种窑头罩顶挂砖 Pending CN104030695A (zh)