CN104030265B - Nitrogen-doped carbon nanometer pipe and preparation method thereof - Google Patents
Nitrogen-doped carbon nanometer pipe and preparation method thereof Download PDFInfo
- Publication number
- CN104030265B CN104030265B CN201310068923.6A CN201310068923A CN104030265B CN 104030265 B CN104030265 B CN 104030265B CN 201310068923 A CN201310068923 A CN 201310068923A CN 104030265 B CN104030265 B CN 104030265B
- Authority
- CN
- China
- Prior art keywords
- nitrogen
- carbon nanotube
- preparation
- nanometer pipe
- doped carbon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of nitrogen-doped carbon nanometer pipe and preparation method thereof, the method comprises the following steps: to be placed in by carbon nanotube under reactor plasma body 1 ~ 2 hour, to obtain the carbon nanotube of modification; The carbon nanotube of described modification is mixed with nitrating agent, dry after fully stirring, in reactor, pass into rare gas element, after making to form inert atmosphere in reactor, be warming up to 800 ~ 900 ° of C, after keeping 0.5 ~ 1h reaction, be down to room temperature; Cleaning is carried out and drying to the solid product of gained, obtains described nitrogen-doped carbon nanometer pipe.In nitrogen-doped carbon nanometer pipe of the present invention and preparation method thereof, the carbon nanotube defect through Cement Composite Treated by Plasma is more, and when carrying out N doping, nitrogen content is higher.And preparation method's cost of the present invention is low, easily realizes large-scale industrial production.
Description
Technical field
The present invention relates to chemical material synthesis field, particularly relate to a kind of nitrogen-doped carbon nanometer pipe and preparation method thereof.
Background technology
Nineteen nineties, carbon material has promoted ultracapacitor, the greatly developing of lithium ion battery as the use of energy storage material.And carbon nanotube is as a kind of carbon material of one dimension, there is very high specific conductivity, and carbon nanotube is very easy to derivatize, so its derivative is also subject to the extensive concern of investigator.
Carbon nano tube derivative mainly contains nitrogen-doped carbon nanometer pipe and boron doped carbon nanometer pipe.Wherein, the many electronics more outer than carbon atom of the nitrogen-atoms in nitrogen-doped carbon nanometer pipe, adulterates in N-type, compare the carbon nanotube not carrying out adulterating and there is better energy-storage property, and the nitrogen content of nitrogen-doped carbon nanometer pipe is higher, energy storage site is more, and its energy-storage property is also better.
At present, the method that the heavy industrialization easily realized prepares nitrogen-doped carbon nanometer pipe is high-temperature hot doping method, but the maximum at present problem of this method to be prepared nitrogen-doped carbon nanometer pipe nitrogen content lower.From the mechanism of N doping, N doping preferentially carries out at unordered place.Therefore, the disordered structure increased on carbon nanotube can have very great help to N doping.
Summary of the invention
The object of the invention is to solve above-mentioned prior art Problems existing and deficiency, provide a kind of nitrogen-doped carbon nanometer pipe and preparation method thereof, the carbon nanotube defect through Cement Composite Treated by Plasma is more, can reach higher nitrogen content when carrying out N doping reaction.
The present invention is directed to above-mentioned technical problem and the technical scheme proposed is: a kind of preparation method of nitrogen-doped carbon nanometer pipe, comprises the steps:
Carbon nanotube to be placed under reactor plasma body 1 ~ 2 hour, to obtain the carbon nanotube of modification;
The carbon nanotube of described modification is mixed with nitrating agent, dry after fully stirring, in reactor, pass into rare gas element, after making to form inert atmosphere in reactor, be warming up to 800 ~ 900 ° of C, after keeping 0.5 ~ 1h reaction, be down to room temperature;
Cleaning is carried out and drying to the solid product of gained, obtains described nitrogen-doped carbon nanometer pipe.
The purity of described carbon nanotube is 99%.
The power that sends of described helium gas plasma is 100 ~ 300W.
Described plasma body is argon plasma or helium gas plasma.
Described nitrating agent is ammoniacal liquor or urea, and the carbon nanotube of described modification and the mass ratio of nitrating agent are 1:1 ~ 1:5.
The time of described stirring is 2 hours, and temperature dry after described stirring is 80 DEG C, the dry time is 6h.
Described rare gas element is argon gas, nitrogen or helium, and flow velocity when described rare gas element passes into is 400ml/min.
The speed of described intensification is 5 ~ 20 DEG C/min.
The operation also dry to described solid product cleaning is as follows: described solid product being added concentration is filter after stirring 4 hours in the hydrochloric acid soln of 10%, cleaner with deionized water wash, is then placed in 60 ° of dry 12h of C vacuum drying oven.
The present invention also comprises the nitrogen-doped carbon nanometer pipe utilizing above-mentioned preparation method to obtain.
Compared with prior art, there is following advantage in nitrogen-doped carbon nanometer pipe of the present invention and preparation method thereof:
1. the carbon nanotube defect through Cement Composite Treated by Plasma is more, and when carrying out N doping, nitrogen content is higher.
2. preparation method's cost of the present invention is low, easily realizes large-scale industrial production.
3., compared with other preparation methods, equipment used of the present invention and technique are simple, convenient operation.
Embodiment
Below in conjunction with embodiment, elaboration is further given to the present invention.
Preparation technology's flow process of nitrogen-doped carbon nanometer pipe of the present invention is roughly as follows: carbon nanotube → modified carbon nano-tube → nitrogen-doped carbon nanometer pipe.
Particularly, the preparation process of nitrogen-doped carbon nanometer pipe of the present invention is divided into following steps:
(1) modified carbon nano-tube: by purity be 99% carbon nanotube be placed in that to send power be under the plasma body of 100 ~ 300W, reaction obtains the carbon nanotube of modification for 1 ~ 2 hour;
Wherein, plasma body is hydrogen plasma, argon plasma or helium gas plasma.
(2) nitrogen-doped carbon nanometer pipe is prepared: joined by the carbon nanotube of modification (carbon nanotube of modification and the mass ratio of nitrating agent are 1:1 ~ 1:5) in the reactor of the ethanol solution being dissolved with urea, abundant stirring after 2 hours at 80 DEG C dry 6h, being placed in flow velocity is heat up (temperature rise rate is 5 ~ 20 DEG C/min) to 800 ~ 900 ° of C after the inert gas atmosphere of 400ml/min, is down to room temperature after keeping 0.5 ~ 1h; The selection of reactor is not limited, is preferably test tube;
Wash away the impurity in gained solid product with the hydrochloric acid that concentration is 10% and filter, with solid product described in washed with de-ionized water, in the vacuum drying oven under 60 ° of C, drying 12 hours, obtains nitrogen-doped carbon nanometer pipe.
Wherein, nitrating agent is ammoniacal liquor or urea.
After the process of step (1) (by carbon nanotube through Cement Composite Treated by Plasma), carbon nanotube can produce more defect, follow-up carry out N doping reaction time, the nitrogen content of carbon nanotube can be improved.Nitrating agent urea can be reaction provides nitrogenous source, at high temperature reacts, better can improve the nitrogen content of nitrogen-doped carbon nanometer pipe through the carbon nanotube of modification and nitrogenous source, thus increases the energy storage site of nitrogen-doped carbon nanometer pipe, greatly improves its energy-storage property.
Below be specifically described with the preparation method of embodiment 1 ~ 4 to nitrogen-doped carbon nanometer pipe of the present invention again.
Embodiment 1
(1) modified carbon nano-tube: by purity be 99% carbon nanotube be placed in helium gas plasma under, power is adjusted to 100W, processes 2 hours, obtains modified carbon nanotube;
(2) nitrogen-doped carbon nanometer pipe is prepared: added by the carbon nanotube of modification (mass ratio of carbon nanotube and urea is 1:2) in the test tube of the ethanol solution being dissolved with ammoniacal liquor, stir 2 hours, drying 6 hours at being placed in 80 DEG C, be placed in the argon gas that flow velocity is 400ml/min again, form argon gas atmosphere, 800 ° of C are warming up to 20 ° of C/min temperature rise rates, and keep 1 hour, the argon gas atmosphere being 400ml/min at flow velocity drops to room temperature, the solid product of gained being added concentration is in the HCl solution of 10%, stir 4 hours, filter rear deionized water wash, solid product is placed in 60 ° of C vacuum drying ovens after dry 12 hours, obtain nitrogen-doped carbon nanometer pipe.
Embodiment 2
(1) modified carbon nano-tube: by purity be 99% carbon nanotube be placed in argon plasma under, power is adjusted to 150W, processes 1 hour, obtains modified carbon nanotube;
(2) nitrogen-doped carbon nanometer pipe is prepared: added by the carbon nanotube of modification and be dissolved with (mass ratio of carbon nanotube and urea is 1:3) in the ethanol solution of urea, stir 2 hours, drying 6 hours at being placed in 80 DEG C, be placed in the nitrogen that flow velocity is 400ml/min again, form nitrogen atmosphere, 850 ° of C are warming up to 10 ° of C/min temperature rise rates, and keep 0.5 hour, the nitrogen atmosphere being 400ml/min at flow velocity drops to room temperature, the solid product of gained being added concentration is in the HCl solution of 10%, stir 4 hours, filter rear deionized water wash, solid product is placed in 60 ° of C vacuum drying ovens after dry 12 hours, obtain nitrogen-doped carbon nanometer pipe.
Embodiment 3
(1) modified carbon nano-tube: by purity be 99% carbon nanotube be placed in helium gas plasma under, power is adjusted to 200W, processes 2 hours, obtains modified carbon nanotube;
(2) nitrogen-doped carbon nanometer pipe is prepared: added by the carbon nanotube of modification (mass ratio of carbon nanotube and urea is 1:5) in the test tube of the ethanol solution being dissolved with urea, stir 2 hours, drying 6 hours at being placed in 80 DEG C, be placed in the helium that flow velocity is 400ml/min again, form helium atmosphere, 800 ° of C are warming up to 5 ° of C/min temperature rise rates, and keep 0.5 hour, the helium atmosphere being 400ml/min at flow velocity drops to room temperature, the solid product of gained being added concentration is in the HCl solution of 10%, stir 4 hours, filter rear deionized water wash, solid product is placed in 60 ° of C vacuum drying ovens after dry 12 hours, obtain nitrogen-doped carbon nanometer pipe.
Embodiment 4
(1) modified carbon nano-tube: by purity be 99% carbon nanotube be placed in argon plasma under, power is adjusted to 300W, processes 1.5 hours, obtains modified carbon nanotube;
(2) nitrogen-doped carbon nanometer pipe is prepared: added by the carbon nanotube of modification and be dissolved with (mass ratio of carbon nanotube and urea is 1:1) in the ethanol solution of ammoniacal liquor, stir 2 hours, drying 6 hours at being placed in 80 DEG C, be placed in the argon gas that flow velocity is 400ml/min again, form argon gas atmosphere, 900 ° of C are warming up to 15 ° of C/min temperature rise rates, and keep 1 hour, the argon gas atmosphere being 400ml/min at flow velocity drops to room temperature, the solid product of gained being added concentration is in the HCl solution of 10%, stir 4 hours, filter rear deionized water wash, solid product is placed in 60 ° of C vacuum drying ovens after dry 12 hours, obtain nitrogen-doped carbon nanometer pipe.
Elemental composition analysis is carried out to nitrogen-doped carbon nanometer pipe obtained in above embodiment 1 to 4, draws the per-cent composition data of each principal element content in following table 1.
Table 1
Carbon (%) | Nitrogen element (%) | Oxygen element (%) | |
Embodiment 1 | 89 | 8.9 | 2.1 |
Embodiment 2 | 87.7 | 10.4 | 1.9 |
Embodiment 3 | 84.6 | 13.2 | 2.2 |
Embodiment 4 | 90.3 | 8.1 | 1.6 |
Known from the data above table, higher according to the nitrogen content of the nitrogen-doped carbon nanometer pipe prepared by method of the present invention, all more than 8%, be up to 13.2%.This illustrates, nitrogen-doped carbon nanometer pipe energy storage site of the present invention is many, and energy-storage property is high.
Nitrogen-doped carbon nanometer pipe of the present invention and preparation method thereof, there is following advantage: the carbon nanotube defect through Cement Composite Treated by Plasma is more, when carrying out N doping, nitrogen content is higher, and preparation method's cost is low, easily realize large-scale industrial production, equipment and process used is simple, convenient operation.
Foregoing; be only preferred embodiment of the present invention; not for limiting embodiment of the present invention; those of ordinary skill in the art are according to central scope of the present invention and spirit; can carry out corresponding flexible or amendment very easily, therefore protection scope of the present invention should be as the criterion with the protection domain required by claims.
Claims (6)
1. a preparation method for nitrogen-doped carbon nanometer pipe, is characterized in that, comprises the steps:
Carbon nanotube to be placed under reactor plasma body 1 ~ 2 hour, to obtain the carbon nanotube of modification;
The carbon nanotube of described modification is mixed with nitrating agent, dry after fully stirring, in reactor, pass into rare gas element, after making to form inert atmosphere in reactor, be warming up to 800 ~ 900 DEG C, after keeping 0.5 ~ 1h reaction, be down to room temperature;
Cleaning is carried out and drying to the solid product of gained, obtains described nitrogen-doped carbon nanometer pipe;
Wherein, described plasma body is argon plasma or helium gas plasma, and the power that sends of described plasma body is 100 ~ 300W;
Described nitrating agent is ammoniacal liquor or urea, and the carbon nanotube of described modification and the mass ratio of nitrating agent are 1:1 ~ 1:5.
2. according to preparation method according to claim 1, it is characterized in that, the purity of described carbon nanotube is 99%.
3. preparation method according to claim 1, is characterized in that, the time of described stirring is 2 hours, and temperature dry after described stirring is 80 DEG C, the dry time is 6h.
4. preparation method according to claim 1, is characterized in that, described rare gas element is argon gas, nitrogen or helium, and flow velocity when described rare gas element passes into is 400mL/min.
5. preparation method according to claim 1, is characterized in that, the speed of described intensification is 5 ~ 20 DEG C/min.
6. preparation method according to claim 1, it is characterized in that, the operation also dry to described solid product cleaning is as follows: described solid product being added concentration is filter after stirring 4 hours in the hydrochloric acid soln of 10%, clean with deionized water wash again, be then placed in 60 DEG C of dry 12h of vacuum drying oven.